• Korean Journal of Materials Research
• /
• v.19 no.11
• /
• pp.625-630
• /
• 2009

Embedding of active devices in a printed circuit board has increasingly been adopted as a future electronic technology due to its promotion of high density, high speed and high performance. One responsible technology is to embedded active device into a dielectric substrate with a build-up process, for example a chipin-substrate (CiS) structure. In this study, desmear treatment was performed before Cu metallization on an FR-4 surface in order to improve interfacial adhesion between electroless-plated Cu and FR-4 substrate in Cu via structures in CiS systems. Surface analyses using atomic force microscopy and x-ray photoemission spectroscopy were systematically performed to understand the fundamental adhesion mechanism; results were correlated with peel strength measured by a 90o peel test. Interfacial bonding mechanism between electrolessplated Cu and FR-4 substrate seems to be dominated by a chemical bonding effect resulting from the selective activation of chemical bonding between carbon and oxygen through a rearrangement of C-C bonding rather than from a mechanical interlocking effect. In fact, desmear wet treatment could result in extensive degradation of FR-4 cohesive strength when compared to dry surface-treated Cu/FR-4 structures.

• Proceedings of the Korean Vacuum Society Conference
• /
• 2014.02a
• /
• pp.294-294
• /
• 2014

Developing magnetic thin films with desirable physical properties is a key step to promote research in spintronics. Organic-based magnetic material is a relatively new kind of materials which has magnetic properties in a molecular and microscopic level. These materials have been constructed by the coordination between 3d transition metal and organic materials producing long-range magnetic orders with a relatively high transition temperature. However, these materials were mostly synthesized as a form of powder, which is difficult to study for their physical properties as well as apply for electronic/spintronic devices. In this study, we have employed physical vapor deposition (PVD) to develop a new organic-based hybrid magnetic film that is achieved by the coordination of Fe and tetracyanoquinodimethane (TCNQ). The IR spectra of the grown film show modified CN vibration modes in TCNQ, which suggest a strong bonding between Fe and TCNQ. The thin film has both ferromagnetic and semiconducting behaviors, which is suitable for molecular spintronic applications. The high resolution photoemission (HRPES) spectra also show shift of 1s peak point of nitrogen and the carbon 1s peaks display traces of charge transfer from Fe to TCNQ as well as shake-up features, which suggest strong bonding and anti-bonding nature of coordination between Fe and TCNQ.

• Carbon letters
• /
• v.16 no.3
• /
• pp.192-197
• /
• 2015

In the present work, we propose a molecule (C₁₄H₁₄) that can be used as a building block of hexagonal diamond-type crystals and nanocrystals, including wurtzite structures. This molecule and its combined blocks are similar to diamondoid molecules that are used as building blocks of cubic diamond crystals and nanocrystals. The hexagonal part of this molecule is included in the C₁₂ central part of this molecule. This part can be repeated to increase the ratio of hexagonal to cubic diamond and other structures. The calculated energy gap of these molecules (called hereafter wurtzoids) shows the expected trend of gaps that are less than that of cubic diamondoid structures. The calculated binding energy per atom shows that wurtzoids are tighter structures than diamondoids. Distribution of angles and bonds manifest the main differences between hexagonal and cubic diamond-type structures. Charge transfer, infrared, nuclear magnetic resonance and ultraviolet-visible spectra are investigated to identify the main spectroscopic differences between hexagonal and cubic structures at the molecular and nanoscale. Natural bond orbital population analysis shows that the bonding of the present wurtzoids and diamondoids differs from ideal sp³ bonding. The bonding for carbon valence orbitals is in the range (2s^0.982p^3.213p^0.02)-(2s^0.942p^3.313p^0.02) for wurtzoid and (2s^0.932p^3.293p^0.01)-(2s^0.992p^3.443p^0.01) for diamantane.

• Journal of the Korean Crystal Growth and Crystal Technology
• /
• v.25 no.4
• /
• pp.145-152
• /
• 2015

In this work, we were investigated the effect of the additive gases on the relationship between bonding structure and mechanical properties of the deposited films when the DLC films were deposited on Si-wafer by the rf-PECVD method with the addition of small amounts of carbon dioxide and nitrogen to the mixture gas of methane and hydrogen. The deposition rate of the films increased as the rf-power increased, while it decreased with increasing the amount of additive gases. Also, as the carbon dioxide gas increased, the hydrogen content in the films decreased but the $sp^3/sp^2$ ratio of the films increased. In case of nitrogen gas, the hydrogen content decreased, however the $sp^3/sp^2$ ratio and nitrogen gas flow rate did not show a specific tendency.

• Transactions of the Korean Society of Mechanical Engineers B
• /
• v.33 no.2
• /
• pp.116-123
• /
• 2009

Carbon black, activated carbon and carbon nanotube have been used as supporting materials for precious metal catalysts used in fuel cell electrodes. One-step flame synthesis method is used to coat 2-5nm Pt dots on flame-generated carbon particles. By adjusting flame temperature, gas flow rates and resident time of particles in flame, we can obtain Pt/C nano catalyst-support composite particles. Additional injection of hydrogen gas facilitates pyrolysis of Pt precursor in flame. The size of as-incepted Pt dots increases along the flame due to longer resident time and sintering in high temperature flame. Surface coverage and dispersion of the Pt dots is varied at different sampling heights and confirmed by Transmission electron microscopy (TEM), Energy-dispersive spectra (EDS) and X-ray diffraction (XRD). Crystalinity and surface bonding groups of carbon are investigated through X-ray photoelectron spectroscopy (XPS) and Raman spectroscopy.

• Journal of the Korean Magnetics Society
• /
• v.9 no.5
• /
• pp.263-270
• /
• 1999

The characteristics of lubricant for computer hard disk was investigated by surface analysis technique. The bonding state between carbon and lubricant is analysed to indentify the origin of adhesion. It is found that the thickness of lubricant is increased as pulling-up speed becomes faster and lubricant concentration is increased. The dominant surface contaminants on carbon overcoat are identified with C-OH and CO. The bond strength between carbon and lubricant is enhanced with heat treatment.

• Composites Research
• /
• v.26 no.6
• /
• pp.386-391
• /
• 2013

In this paper, a carbon fiber/epoxy composite-aluminum hybrid wheel for passenger cars was suggested for better performance and a prototype was fabricated and tested. Adhesive bonding between aluminum part and a composite rim part was used, and the bonding length and thickness were determined by finite element analysis. For self alignment and the function of bonding jig the special structure with a groove and a protrusion was applied. To evaluate the performance of the hybrid wheel various FE analyses were carried out. Inner and outer molds were prepared for the composite rim part and the thermoformed composite part was bonded to the aluminum part. Vibration tests revealed that the hybrid wheel had 16% higher resonance frequency and 32% higher damping capacity with 10% weight reduction.

• Korean Journal of Materials Research
• /
• v.15 no.11
• /
• pp.711-716
• /
• 2005

The effects of change in the component of bonding materials in carbon nanotube cathode (CNT-cathode) on field enhancement and field emission characteristics were investigated. The field enhancement factor$\beta$ was dependent on the electrical conductivity of the bonding materials. The use of frit glass as a bonding material showed a higher field enhancement factor and better field emission characteristics than an Ag paste. The reason for why the frit glass showed better field emission characteristics can be summarized as follows. First, a frit glass improves the real aspect ratio of CNTs compared to an Ag paste. Second, the number of CNTs in CNT-cathodes is considerably reduced because the CNTs were extensively oxidized during $390^{\circ}C$ heat treatment in air atmosphere in the case of Ag paste.

• Composites Research
• /
• v.20 no.5
• /
• pp.34-42
• /
• 2007

Strength and failure of adhesively bonded carbon composite-to-aluminum single-lap joints were studied by experiment. The main objective of this study is to investigate the effect of various parameters such as curing pressure for bonding, overlap lengths, and adherend thickness on the failure loads and modes of the bonded Joints with dissimilar materials. Experimental results show that the bonding pressure for composite-to-aluminum dissimilar materials should be 4 atm at the lowest. Failure load of the joints increases as the overlap length increases, but the strength (failure load divided by bonded area) decreases rapidly after the overlap width-to-length ratio is greater than 1. When the adherend thickness increase to double, bonding strength increase $12{\sim}55%$. Major failure mode of the joints is the delamination in the composite laminate and the location of delamination goes deeper into the laminates as the bonding pressure and overlap length increase.

• Journal of the Korean Vacuum Society
• /
• v.18 no.1
• /
• pp.49-53
• /
• 2009

The chemical properties of SiOC film was studied for inter-layer insulator. SiOC film was formed with non polarity due to the appropriate union by the alkyl and hydroxyl group. An amorphous structure of non polarity can induce the low dielectric constant materials. The chemical properties of thin film can define the bonding structure owing to the ionic variation, and the analysis of chemical properties was researched by the carbon content using the FTIR spectra, and induced the film with non polarity. The electrical properties is the electron flow, and is always not the same as the chemical properties. The electrical properties of SiOC film with various flow rate ratios was analyzed and researched the correlation between the chemical properties. SiOC film showed the increasing of the leakage current after annealing process, and abruptly increased the carbon content at some samples. But the sample with increasing the carbon content decreased the leakage current. It means that the chemical properties is not the same as the electrical properties, and the carbon is related with the variation of the bonding structure, and does not contribute the current flow.