• Carbon letters
• /
• 제2권3_4호
• /
• pp.192-201
• /
• 2001

The Carbon/Carbon composite was prepared from 3D carbon fiber preform and coal tar pitch as matrix precursor. In order to evaluate of ablative characteristics of the composite, liquid rocket system was employed Kerosene and liquid oxygen was used as propellants, operating at a nominal chamber pressure of 330 psi and a nominal mixture ratio (O/F) of 2.0. The results of an experimental evaluation were that high density composite exhibited high, while low density composites showed low erosion resistance. The erosion rate against heat flux was highly depended on the density of the materials. The morphology of eroded fiber showed differently according to collision angle with heat flux on the composite. The granular matrix which derived from carbonization pressure of 900 bar was more resistance to heat flux than well-developed flow type matrix.

• 폴리머
• /
• 제24권2호
• /
• pp.237-244
• /
• 2000

탄화 매트릭스의 전구체로 사용된 페놀수지에 세라믹 분말인 이규화몰리브덴 (MoSi$_2$)을 0, 4, 12, 20%의 중량비로 각각 고르게 분산시켜, 여기에 PAN계 탄소섬유를 함침하여 프리프레그법을 이용하여 일방향 탄소섬유/페놀수지 복합재료를 제조하였으며, 이를 다시 탄화(110$0^{\circ}C$) 시켜서 일방향 탄소/탄소 복합재료를 제작하였다. 본 연구에서는 난소/탄소 복합재료에 산화 억제제로 사용된 MoSi$_2$의 첨가량에 따른 복합재료의 산화거동을 산화분위기 하 600-100$0^{\circ}C$의 온도범위에서 조사하였다. 그 결과, MoSi$_2$를 함유한 탄소/탄소 복합재료는 복합재료 내치 기공 감소와 산소에 대한 유동 확산 방지막의 형성으로 인하여 카본 활성종이 방해를 받아 MoSi$_2$를 함유하지 않은 것에 비해 산화속도가 감소되어 내산화성이 향상되었다. 이는 산소의 공격에 대한 보호층을 형성하는 MoSi$_2$ 고유의 특성에 따른 영향이라 사료된다.

• 한국재료학회지
• /
• 제3권3호
• /
• pp.292-299
• /
• 1993

본 연구에서는 탄소/탄소복합재료의 마모특성에 대한 탄소섬유 길이의 영향을 고찰하였다. 매트릭스 precursor로 레졸형의 페놀수지와 강화재로 표면처리를 하지않은 PAN계 단섬유형 탄소섬유를 사용하여 액상함침법으로 1회의 고온열처리 공정과 4회의 탄화공정을 통하여 탄소/탄소복합재료를 제조하였다. Disk-on-disk형의 마모시험기를 통하여 상대 마찰재로 AISI 304 stainliss steel을 사용하여 0.6MPa(61 ${\times}{10^3}$Kg/$m^2$)의 압력과 0.71m/sec의 미끄러짐 속도하에서 측정된 탄소/탄소복합재료의 마찰계수는 0.2-0.3이었다. 마찰계수에 대한 섬유의 길이의 영향은 크게 나타나지 않았지만, 마모 속도는 섬유의 길이가 증가함에 따라 증가하는 경향이 나타났다. 본 실헙 결과를 섬유 강화 플라스틱의 마모 모델을 적용하여 고찰하여 본 결과, 섬유의 길이가 증가함에 따라 탄소/탄소복합재료의 마모 속도가 증가되는 경향은 생성된느 마모조각의 크기가 커기기 때문에 나타난 현상으로 판단되었다.

• Composites Research
• /
• 제12권3호
• /
• pp.75-83
• /
• 1999

Carbon/Phenolic 및 silica/phenolic 내열 복합재료의 강화재의 종류와 적층방향에 따른 비열, 열확산 계수, 열전도도를 분석하였다. Carbon/Phenolic 및 silica/phenolic 복합재료의 비열은 시차 주사 열량법을 이용하여 측정하였으며, 열확산계수는 레이저 섬광법을 이용하여 laminar와 평행방향과 laminar와 직교방향으로 측정하였다. Carbon/Phenolic 및 silica/phenolic 복합재료의 열확산계수는 온도가 증가함에 따라 감소하였다. Carbon/Phenolic 및 silica/phenolic 복합재료의 열전도도를 밀도, 열확산계수 및 비열을 이용하여 계산하였다. 열전도도는 온도가 증가함에 따라 증가하였으며, carbon/Phenolic의 경우 laminar와 평행방향의 열전도도가 laminar와 직교방향의 열전도도보다 2배 높은 이방성을 나타내었으며 이는 carbon 섬유의 열전도도 이방성 때문으로 해석되었다. 이차원 섬유강화 복합재료의 열전도도를 기지와 강화재의 열전도도와 부피분율을 이용하여 해석하였다. Carbon/Phenolic 및 silica/phenolic 복합재료의 열전도도를 적층방향에 따라 강화재와 기지의 열전도도를 이용하여 해석하여 carbon 섬유와 silica 섬유의 열전도도를 계산하였다. 계산된 섬유의 열전도도와 기지의 열전도도로부터 섬유의 부피분율에 따른 복합재료의 상온열전도도를 예측할 수 있었다.

• Advances in materials Research
• /
• 제13권3호
• /
• pp.211-220
• /
• 2024

Polylactic acid or polylactide (PLA) is a biodegradable thermoplastic that can be produced from renewable material to create various components for industrial purposes. In 3D printing technology, PLA is used due to its good mechanical, electrical, printing properties, environmentally friendly and non-toxic properties. However, the physical properties and excellent electrical insulation properties of PLA have limited its application. In this study, with the carbon black (CB) as filler added into PLA, the lattice spacing and morphology were investigated by using X-ray diffraction (XRD) and scanning electron microscope (SEM), respectively. The physical properties of PLA-carbon composite were evaluated by using tensile test, shore D hardness test and density and voids measurement. Impedance test was conducted to investigate the electrical properties of PLA-Carbon composites. The results demonstrate that the inclusion of carbon black as filler enhances the physical properties of the PLA-carbon composites, including tensile properties, hardness, and density. The addition of carbon black also leads to improved electrical conductivity of the composites. Better enhancement toward the electrical properties of PLA-carbon composites is observed with 1wt% of carbon black in N774 grade. The N550 grade with 2wt% of carbon black shows better improvement in the physical properties of PLA-carbon composites, achieving 10.686 MPa in tensile testing, 43.330 in shore D hardness test, and a density of 1.200 g/cm3 in density measurement. The findings suggest that PLA-carbon composites have the potential for enhanced performance in various industrial applications, particularly in sectors requiring improved physical and electrical properties.

• 한국해양공학회지
• /
• 제11권2호
• /
• pp.48-56
• /
• 1997

This work has been investigated in order to study the influence of the moisture absorption on the mechanical pf the glass fiber/epoxy resein composites and the carbon fiber/epoxy resein composites. The types of glass fiber used in the glass fiber/epoxy resein composites were randomly oriented fiber and plain fabric fiber. And carbon fiber.epoxy resein composites was laminated with fabric prepreg which was formed with carbon fiber and epoxy resein. Both composites were immersed up to 100 days in distilled water at $80^{\circ}C$, and then dried up to 3 days in an oven at 80$80^{\circ}C$. Both composites were measured for the weight gain of water(wt.%) and tensile strength through immersion and dry time. Consequently, it was found that the tensile strength of thw glass fiber/epoxy resein composites and the carbon fiber/epoxy resein composites were reduced proportionally to the moisture absortion rate. Also, the tensile strength of glass fiber composites was decreased more than that of the carbon fiber composites. Additionally, it was found that the tensile strength of all composites which decreased by moisture absorption were partly recovered by drying in an oven at 80$80^{\circ}C$.

• 한국정보디스플레이학회:학술대회논문집
• /
• 한국정보디스플레이학회 2007년도 7th International Meeting on Information Display 제7권1호
• /
• pp.897-899
• /
• 2007

Transparent electrodes for a flexible display based on the liquid crystal (LC) were formed by carbon nanotubes (CNTs) on polyethylene terephthalate (PET) substrates. The thin multi wall carbon nanotubes (t-MWNTs) networks for electrodes were obtained by filtration- transfer method from welldispersed CNTs solution.

• Carbon letters
• /
• 제15권2호
• /
• pp.125-128
• /
• 2014

In this study, the effect of stacking sequence on the flexural and fracture properties of carbon/basalt/epoxy hybrid composites was investigated. Two types of carbon/basalt/epoxy hybrid composites with a sandwich form were fabricated: basalt skin-carbon core (BSCC) composites and carbon skin-basalt core (CSBC) composites. Fracture tests were conducted and the fracture surfaces of the carbon/basalt/epoxy hybrid composites were then examined using scanning electron microscopy (SEM). The results showed that the flexural strength and flexural modulus of the CSBC specimen respectively were ~32% and ~245% greater than those of the BSCC specimen. However, the interlaminar fracture toughness of the CSBC specimen was ~10% smaller than that of the BSCC specimen. SEM results on the fracture surface showed that matrix cracking is a dominant fracture mechanism for the CSBC specimen while interfacial debonding between fibers and epoxy resin is a dominant fracture process for the BSCC specimen.

• 한국재료학회지
• /
• 제19권12호
• /
• pp.644-648
• /
• 2009

Temperature dependency of resistivity of the carbon black-polyethylene composites below and above percolation threshold is studied based on the electrical conduction mechanism. Temperature coefficient of resistance of the composites below percolation threshold changed from minus to plus, increasing volume fraction of carbon black; this trend decreased with increasing volume fraction of carbon black. The temperature dependence of resistivity of the composites below percolation threshold can be explained with a tunneling conduction model by incorporating the effect of thermal expansion of the composites into a tunneling gap. Temperature coefficient of resistance of the composites above percolation threshold was positive and its absolute value increased with increasing volume fraction of carbon black. By assuming that the electrical conduction through percolating paths is a thermally activated process and by incorporating the effect of thermal expansion into the volume fraction of carbon black, the temperature dependency of the resistivity above percolation threshold has been well explained without violating the universal law of conductivity. The apparent activation energy is estimated to be 0.14 eV.

• International Journal of Ocean System Engineering
• /
• 제3권3호
• /
• pp.142-146
• /
• 2013

In this study, the effect of Carbon/PEEK composites on the tribological properties has been investigated. Also, its validity has been tested in the capacity of alternative materials of the Ti-based materials used for artificial hip joint. Moreover, this work evaluated the mechanical properties according to the fiber ply orientation, along with the fractured surfaces of the carbon/PEEK composites. The composites with a unidirectional orientation had higher tribological properties than those with a multidirectional orientation. This was caused by the debonding between the carbon fiber and the PEEK, which was proportional to the contact area between the sliding surface and the carbon fiber. The friction test results showed that there were no significant differences in relation to the fiber ply orientation. However, the friction properties of the carbon/PEEK composites were higher than those of the carbon/epoxy composites. In addition, the results showed that a composite that slid in a direction normal to the prepreg lay-up direction had a smaller friction coefficient than one that slid in a direction parallel to the prepreg lay-up direction.