• Korean Journal of Materials Research
• /
• v.5 no.6
• /
• pp.754-762
• /
• 1995

Strontium titanate(SrTiO$_3$) thin film was prepared on Si substrates by RF magnetron sputtering for a high capacitance density required for the next generation of LSTs. The optimum deposition conditions for SrTiO$_3$thin film were investigated by controlling the deposition parameters. The crystallinity of films and the interface reactions between SrTO$_3$film and Si substrate were characterized by XRD and AES respectively. High quality films were obtained by using the mixed gas of Ar and $O_2$for sputtering. The films were deposited at various bias voltages to obtain the optimum conditions for a high quality file. The best crystallinity was obtained at film thickness of 300nm with the sputtering gas of Ar+20% $O_2$and the bias voltage of 100V. The barrier layer of Pt(100nm)/Ti(50nm) was very effective in avoiding the formation of SiO$_2$layer at the interface between SrTiO$_3$film and Si substrate. The capacitor with Au/SrTiO$_3$/Pt/Ti/SiO$_2$/Si structure was prepared to measure the electric and the dielectric properties. The highest capacitance and the lowest leakage current density were obtained by annealing at $600^{\circ}C$ for 2hrs. The typical specific capacitance was 6.4fF/$\textrm{cm}^2$, the relative dielectric constant was 217, and the leakage current density was about 2.0$\times$10$^{-8}$ A/$\textrm{cm}^2$ at the SrTiO$_3$film with the thickness of 300nm.