• Journal of the Microelectronics and Packaging Society
• /
• v.15 no.1
• /
• pp.1-6
• /
• 2008

Thermoelectric properties of calcium cobalt layer structure oxide system, $Ca_3Co_2O_6$ and $Ca_3Co_4O_9$ were investigated at the temperature range of 300 to 1000K for the application of thermoelectric generation. In the composition, the Ca site was partially substituted with Bi, Sr, La, K and the Co site was partially substituted with Mn, Fe, Ni, Cu, Zn. The thermoelectric properties of Bi substituted $Ca_3Co_4O_9$. $Ca_{2.7}Bi_{0.3}Co_4O_9$ for electrical conductivity, Seebeck coefficient and power factor were $85.4({\Omega}$cm)^{-l}, $176.2{\mu}V/K$ and $265.2{\mu}W/K^m$, respectively. The unit thermoelectric couple was fabricated with the p-type of $Ca_{2.7}Bi_{0.3}Co_4O_9$ and n-type ($Zn_{0.98}Al_{0.02}$)O thermoelectrics whose figure-of-merit(Z) were $0.87{\times}10^{-4}/K$ and $0.41{\times}10^4/K$, respectively. The generated thermoelectric power was about 30mV at the temperature difference of 120K in the unit thermoelectric couple.