• 한국주조공학회지
• /
• 제38권4호
• /
• pp.75-81
• /
• 2018

This study examined the effect of the CaMgSn ternary phase on the aging response of the Mg-Sn-Zn alloy. The results revealed that the CaMgSn ternary phase formed in rod-like or needle-like shapes in Mg-3Zn-0.3Ca-xSn (x=1.5, 3, and 5 wt%) alloys and its size decreased as the Sn content increased from 1.5 wt% to 5 wt%. The Mg-3Zn-0.3Ca-5Sn alloy with a relatively fine CaMgSn phase was subjected to solution heat treatment and an aging process. Both the Mg-5Sn-3Zn-0.3Ca and Mg-5Sn-3Zn (base alloy) alloys had similar peak hardness values throughout all aging temperatures but the time-to-peak hardness in the Mg-5Sn-3Zn-0.3Ca alloy was 24-36 hours-earlier than that in the base alloy. Precipitates in the Mg-5Sn-3Zn-0.3Ca alloy were more refined than those in the Mg-5Sn-3Zn alloy and were mostly formed on basal planes. The $Mg_2Sn$ phase formed in either plate-like or rod-like shapes in the Mg-5Sn-3Zn alloy, whereas block-shaped $Mg_2Sn$ particles also formed in the Mg-5Sn-3Zn-0.3Ca alloy.

• 열처리공학회지
• /
• 제27권4호
• /
• pp.185-190
• /
• 2014

The influences of small amount of Sn addition on microstructure and creep resistance of AZ91-0.4%Ca alloy have been investigated. The microstructure of the AZ91-0.4%Ca alloy was characterized by ${\alpha}$-(Mg) dendrite cells surrounded by eutectic ${\beta}(Mg_{17}Al_{12})$ and $Al_2Ca$ phases. The 0.5%Sn addition resulted in the formation of rod-shaped CaMgSn particles with the extinction of $Al_2Ca$. The Sn-containing alloy exhibited better creep resistance below $175^{\circ}C$, but the tendency was reversed above $200^{\circ}C$. The reason was discussed in relation to the change in thermal stability of ${\beta}$ phase in response to the Sn addition.

• 한국주조공학회지
• /
• 제34권6호
• /
• pp.187-193
• /
• 2014

In the present work, the effect of adding Ce on the corrosion behavior of Mg-4Al-2Sn-1Ca alloy was investigated. The studied alloys were fabricated by gravity casting method and a potentiodynamic polarization, A.C. impedance and hydrogen evolution tests were carried out in a 3.5% NaCl solution with pH 7.2 at room temperature to measure the corrosion properties of Mg-4Al-2Sn-1Ca-xCe alloys. The microstructure of the Mg-4Al-2Sn-1Ca alloy was composed of ${\alpha}$-Mg, Mg17Al12, Mg2Sn and CaMgSn phase. Also, a $Al_{11}Ce_3$ phase was newly formed by the addition of Ce. With an increase of the Ce contents, the microstructure became refined and the corrosion resistance improved.

• 한국재료학회지
• /
• 제25권6호
• /
• pp.269-273
• /
• 2015

The effect of adding Ca on the microstructural and mechanical properties of as-cast Mg-11Li-3Zn-1Sn(wt%) alloys were investigated. Mg-11Li-3Zn-1Sn-0.4Mn with different Ca additions (0.4, 0.8, 1.2 wt%) were cast under an $SF_6$ and $Co_2$ atmosphere at $720^{\circ}C$. The cast billets were homogenized at $400^{\circ}C$ for 12h and extruded at $200^{\circ}C$. The microstructural and mechanical properties were analyzed by OM, XRD, SEM, and tensile tests. The addition of Ca to the Mg-11Li-3Zn-1Sn-0.4Mn alloy resulted in the formation of $Ca_2Mg_6Zn_3$, MgSnCa intermetallic compound. By increasing Ca addition, the volume fraction and size of $Ca_2Mg_6Zn_3$ with needle shape were increased. This $Ca_2Mg_6Zn_3$ intermetallic compound was elongated to the extrusion direction and refined to fine particles due to severe deformation during hot extrusion. The elongation of the 0.8 wt% Ca containing alloy improved remarkably without reduction strength due to the formation of fine grain and $Ca_2Mg_6Zn_3$ intermetallic compounds by Ca addition. It is probable that fine and homogeneous $Ca_2Mg_6Zn_3$ intermetallic compounds played a significant role in the increase of mechanical properties.

• 한국주조공학회지
• /
• 제31권5호
• /
• pp.293-301
• /
• 2011

Representative magnesium alloys applied to the die-casting are AZ91, AM60, etc., and the application of these alloys is restricted to components operating at moderate temperatures, due to grain boundary siding of ${\beta}$-phase($Mg_{17}Al_{12}$) at temperatures above $120^{\circ}C$. Heat-resistant magnesium alloys such as AE42, AE44 have been developed, but that have been too burdensome to produce because of the expensive rare earth materials. Research work for the development of low-priced heat-resistant magnesium alloy is actively in progress and positive results are being reported. This study aims to investigate the effect of Ca additions on mechanical properties of Mg-4Al-2Sn heat resistant magnesium alloys. Mg-4Al-2Sn alloys with Ca (0wt.%, 0.3wt.%, 0.7wt.%, 1wt.%) have been produced through the die-casting process for the development of low-priced heat-resistant magnesium alloy, and high temperature tensile tests are performed using the specimens. The results showed that mechanical properties of Mg-4Al-2Sn-xCa increased with the addition of Ca up to 0.7wt.% Ca and further addition of Ca deteriorated the mechanical properties of the alloys. A significant amount of porosity was observed at the sample with 1wt%. Ca and the longer freezing range of the alloy was believed to cause the formation of porosity.

• 한국주조공학회지
• /
• 제28권5호
• /
• pp.221-225
• /
• 2008

The structural and hardness variations of Mg-5Sn-(1,2,3) Ca (wt%) alloys have been investigated during various aging heat treatments followed by solution heat treatment at $500^{\circ}C$ for 24 hrs. Maximum hardness of Hv61 has been obtained for Mg-5Sn-3Ca alloys, when the aging treatment was performed at $200^{\circ}C$ for 24 hrs. The microstructures were critically changed when the content of Ca was more than 1wt%, since CaMgSn and $Mg_{2}Ca$ phases were mainly precipitated during aging treatments. The hardness variations with structural evolutions are discussed with respect to the aging temperatures and times.

• 자원환경지질
• /
• 제45권6호
• /
• pp.623-641
• /
• 2012

장군 연-아연-은 광상은 열수교대형 광상이다. 모암변질시 원소 분산을 알아보기 위해 모암, 열수변질대 및 연-아연-은 광맥에서 시료를 채취하였다. 이 광상은 능망간석화작용과 돌로마이트화작용으로 구성된 열수작용이 현저히 인지된다. 모암은 돌로마이트와 석회암이며 구성광물은 방해석, 돌로마이트, 석영, 금운모 및 흑운모 이다. 연-아연-은 광맥과 접촉한 부분에서 관찰되는 능망간석대는 주로 능망간석이 산출되며 소량 방해석, 돌로마이트, 쿠트나호라이트, 유비철석, 황철석, 황동석, 섬아연석, 방연석 및 황석석 등이 산출된다. 연-아연-은 광맥으로부터 멀어짐에 따라 관찰되는 돌로마이트대는 주로 돌로마이트가 산출되고 소량 방해석, 능망간석, 황철석, 섬아연석, 황동석, 방연석 및 황석석 등이 산출된다. 모암변질시 주원소, 미량 및 희토류원소들간의 상관계수는 $Fe_2O_3(T)$/MnO, Ga/MnO 및 Rb/MnO(돌로마이트 및 석회암)가 정의 상관관계를 갖고 MgO/MnO, CaO/MnO, $CO_2$/MnO 및 Sr/MnO(돌로마이트)와 CaO/MnO 및 Sr/MnO(석회암)가 부의 상관관계를 갖는다. 모암변질시 이득원소들은 $Fe_2O_3(T)$, MnO, As, Au, Cd, Cu, Ga, Pb, Rb, Sb, Sc, Sn 및 Zn 이고 손실원소들은 CaO, MgO, $CO_2$ 및 Sr 이다. 따라서 CaO, $CO_2$, $Fe_2O_3(T)$, MgO, MnO, Ga, Pb, Rb, Sb, Sn, Sr 및 Zn 등의 원소들은 모암이 돌로마이트내지 석회암인 열수교대형 광상의 탐사에 지시원소로서 활용될 수 있을 것이다.

• Corrosion Science and Technology
• /
• 제20권5호
• /
• pp.315-323
• /
• 2021

In this study, we examined corrosion behaviors of two types of Pb alloys for a lead acid battery comparatively. One containing 6.6 wt% Sn, 36 mg/kg Bi, and 612.4 mg/kg Ca was prepared by twin-roll continuous casting. The other containing 5.2 wt% Sn, 30.5 mg/kg Ag, and 557 mg/kg Ca was made by twin-belt continuous casting. Potentiodynamic polarization tests were performed to evaluate corrosion resistance. Cyclic voltammetry was done to examine oxidation and reduction reactions occurring on the surface of each alloy in 4.8 M H₂SO₄ solution. Electrochemical test results implied that the Pb alloy prepared with the twin-belt casting method was less stable than that cast with the twin-roll method. Such results might be due to precipitations formed during the casting process. Rolling did not appear to affect the corrosion behavior of the twin-roll samples with Ag < 10 mg/kg, while it reduced the anodic reaction of Ag on the surface of the twin-belt sample with 30.5 mg/kg Ag.

• 천문학회보
• /
• 제37권1호
• /
• pp.45.2-45.2
• /
• 2012

We present preliminary report for spectral features of SN2011fe(type Ia) in M101 which was detected since late August of 2011.High-resolution spectra were obtained with BOES at the 1.8m telescope in BOAO.A number of Ca II, SiII, SII, OI, MgII, and FeII components are detected at different epochs and evolved.

• 자원환경지질
• /
• 제46권2호
• /
• pp.199-206
• /
• 2013

대현 금-은광상은 Cambro-Ordovician 석회암질 대리암내에 발달된 NE 방향성의 단열대를 따라 형성된 2개의 열수성 석영맥으로 구성된다. 모암변질시 원소 분산과 이득/손실을 알아보기 위해 모암, 열수변질대 및 금-은 광맥에서 시료를 채취하였다. 모암변질시 뚜렷한 변질대가 관찰되지 않으며 구성광물은 주로 방해석, 돌로마이트, 석영과 소량 녹염석 등이다. 이 광상의 광석광물은 유비철석, 자류철석, 황철석, 섬아연석, 황석석, 황동석, 방연석, 에렉트럼, 자연 창연 및 은 광물 등이 산출된다. 분석된 자료를 기초로, 모암은 주로 $SiO_2$, CaO 및 $CO_2$로 구성되며 소량 $Al_2O_3$, $Fe_2O_3(T)$ 및 MgO 등이 함유되어 있다. 광체로부터 모암으로 감에 따라 $SiO_2$, $Fe_2O_3(T)$, MgO, CaO 및 $CO_2$ 함량은 변화 폭이 크게 관찰된다. 모암변질시 모암의 물리-화학적 물성 때문에 원소 분산은 현저히 관찰되지 않으며 단지 광체 주변부에서만 관찰된다. 모암변질시 이득원소들은 $Fe_2O_3(T)$, 총 S, Ag, As, Bi, Cd, Cu, Ni, Pb, Sb, Sn, W 및 Zn이고 손실원소들은 $SiO_2$, MnO, MgO, CaO. $CO_2$ 및 Sr 이다. 따라서 우리의 결과물은 황강리 광화대내 석회암질 대리암을 모암으로 갖는 광상들의 지화학탐사시 활용될 수 있을 것이다.