• Elastomers and Composites
• /
• 제26권4호
• /
• pp.296-303
• /
• 1991

Surface of crystalline silica was sequentially reacted with silane(A 187), liquid $rubber(CTBN{\times}8)$, and vinyl monomer(GMA) in existence of TEA(triethylamine) or BPO(benzoyl peroxide). It was mixed with epoxy resin at a ratio $0{\times}60%$ (vol. % ) of total component. For mixtures, viscous properties were investigated experimentally. 1) Coating ratio depended on pH of mixture and quantity of catalyst. 2) Treated silica represented lower viscosity than untreated. 3) Thixotropic index represented best at silica_content $15{\sim}23%$ and showed more large deviation over $120^{\circ}C$. 4) Relative viscosity followed kernel's at $0{\times}10%$ of silica content and get out of Mooney's at more than 15%.

• 한국초전도ㆍ저온공학회논문지
• /
• 제12권3호
• /
• pp.1-6
• /
• 2010

Since the fiber reinforced polymeric (FRP) composites are considered in next generation of space transportation systems, reliable thermal expansion properties should be well provided for structural design of composite materials. To obtain accurate mechanical behaviors at a cryogenic temperature, precise strain measurement and calibration must be provided. In this work, apparent strains (or thermal output) of temperature self-compensated strain gages were deliberately investigated for epoxy, CTBN modified epoxy and carbon fabric composite system from room temperature to liquid nitrogen temperature. Also, fourth-order thermal output curves were presented for the further calibration. The results showed that the thermal output is heavily dependent on test materials and a large amount of apparent strains were observed for the polymer resins.

• 접착 및 계면
• /
• 제16권3호
• /
• pp.101-107
• /
• 2015

코어/쉘 나노입자, CTBN 변성에폭시, 폴리에스터 폴리올, 폴리우레탄 등과 같은 다양한 종류의 강인화 소재는 에폭시 수지의 주요 단점으로 알려진 취성을 보완하여 낮은 충격 저항성을 개선시키기 위한 방법으로 연구되고 있다. 본 연구에서는 앞서 언급된 강인화 소재를 선정, 접착제 조성물에 첨가하여 기계적 물성을 조사하였다. 강인화 소재 도입에 따른 기계적 강도의 측정은 UTM을 이용한 굴곡 강도와 탄성률 측정 및 Izod 충격 시험기를 사용한 충격 강도 실험을 통해 이루어 졌으며, 그 결과 강인화 소재가 에폭시 경화물의 유연성 및 충격에 대한 저항성 향상에 미치는 긍정적인 효과가 나타남을 관찰하였다. 또한, DMA를 이용한 저장 탄성률 결과는 굴곡 탄성률의 결과와 동일한 경향으로 나타남을 확인하였다. 강인화 소재가 충격 강도 향상에 영향을 주는 이유는 에폭시 수지에 첨가된 강인화 소재의 상 분리 현상에 의한 것이며, 상 분리된 강인화 소재는 에폭시 조성물의 파단면을 관찰한 FE-SEM 이미지에서 관찰하였다.

• 한국복합재료학회:학술대회논문집
• /
• 한국복합재료학회 2004년도 춘계학술발표대회 논문집
• /
• pp.214-217
• /
• 2004

The cure kinetics of blends of epoxy(tetraglycidyl-4,4'-diaminodiphenylmethane ; TGDDM)/curing agent(diaminodiphenyl sulfone ; DDS) resin with amine terminated polyetherimide-CTBN-amine terminated polyetherimide triblock copolymer(ABA) were studied using differential scanning calorimetry under isothermal conditions to determine the reaction parameters such as activation energy and reaction constants. By increasing the amount of ABA in the blends, the final cure conversion was decreased. Lower values of the final cure conversions in the epoxy/ABA blends indicated that ABA hinders the cure reaction between the epoxy and curing agents. 1be value of the reaction order, m, for the initial autocatlytic reaction was not affected by blending ABA with epoxy resin, and the value was approximately 1.0. The value of n for the nth order component in the autocatalytic analysis was increased by increasing the amount of ABA in the blends, and the value increased from 2.0-3.4. A diffusion controlled reaction was observed as the cure conversion increased and the rate equation was successfully analyzed by incorporating the diffusion control term for the epoxy/DDS/ABA blends.

• Composites Research
• /
• 제16권4호
• /
• pp.44-50
• /
• 2003

균열선단에 발생하는 손상역은 재료의 파괴인성 메카니즘을 알 수 있게 하는 중요한 영역이다. 본 연구에서는 고무변성 에폭시 수지의 균열선단 손상역의 생성 및 성장 과정을 음향방출법을 이용하여 조사하였다. 고무변성 에폭시 수지의 고무함량은 5 wt%와 15 wt%로 하였고, 3점 굽힘시험편을 사용하여 모드 I 파괴시험에 대한 각 시험편의 파괴인성값을 구하였다. 또한, 균열선단의 손상역과 그 내부의 고무입자 변형상태를 편광현미경과 원자력간 현미경을 사용하여 관찰하였다. 고무변성 에폭시 수지의 균열선단부의 손상역은 파괴하중의 약 13 % 하중에서 생성이 되어, 약 57 % 하중까지 균열개시 없이 성장하였다. 57 % 하중 근처에서 개시만 균열은 최대하중부근까지 고착-활강거동을 반복하면서 안정 / 불안정 파괴로 진전하였다 이 과정에서 발생한 음향방출신호의 시간-주파수 분석결과, 고투입자 내부에서의 케비테이션 생성단계에서 주파수대역은 0.15 ∼ 0.20 MHz 이었고, 그 후의 안정 및 불안정시의 주파수 대역은 0.20∼0.30MHz 이었다.