• Journal of the Korea institute for structural maintenance and inspection
• /
• v.14 no.5
• /
• pp.72-78
• /
• 2010

A CFRP (Carbon Fiber-Reinforced Plastic) strengthening method is being very widely used to increase the load-carrying capacity of host structures, especially for bridges. However, not only flexure and shear failures but debonding failure also might occur in CFRP strengthened concrete structures. The CFRP debonding failure would cause a collapse accident of the host structure. Therefore, real-time health monitoring about the CFRP bonding condition is strongly required. In this study, a feasibility of the impedance-based damage detection method using PZT sensors is investigated through a series of experimental study monitoring both concrete cracks and CFRP debonding defects.

• KSCE Journal of Civil and Environmental Engineering Research
• /
• v.28 no.4A
• /
• pp.447-456
• /
• 2008

This paper suggests a modified debonding failure model for the externally bonded prestressed CFRP plate strengthening system. In order to reduce the error that may occur in the experimental results, statistical analysis of the experimental results produced by previous researchers was conducted to propose a debonding failure model. The experimental results of beams strengthened with bonded CFRP plates have made it possible to verify the debonding failure occurring before the final failure in the prestressing system. The corresponding strain increased with the effective prestress. Accordingly, the debonding failure model was modified by considering the effective prestress so as to fit with the CFRP prestressing system.

• Journal of the Korea institute for structural maintenance and inspection
• /
• v.15 no.4
• /
• pp.185-192
• /
• 2011

A CFRP (Carbon Fiber-Reinforced Plastic) strengthening method being widely used to increase the load-carrying capacity of structures is very suitable for existing bridge structures. However, not only flexure and shear failures but also debonding failure might be additionally occured in reinforced concrete(RC) beams strengthened with the CFRP plates. The CFRP debonding failure would cause a brittle fracture of the beam. Therefore, health monitoring for the CFRP bonding condition is strongly required. In this study, a feasibility of the impedance-based damage detection method using PZT sensors was investigated through a series of experimental studies for realtime structural health monitoring(SHM) for the CFRP laminated concrete structures.

• Journal of the Korea Concrete Institute
• /
• v.23 no.6
• /
• pp.781-790
• /
• 2011

This paper contains the experimental results on strengthening effect of RC beams strengthened with NSM CFRP reinforcement and various strengthening details. A total of 14 beams have been tested to analyze strengthening effects of NSMR with various reinforcement details. Variables were cross-sectional shape of CFRP reinforcements, strengthening areas, grooves the number and location etc. Test results revealed that failure modes of NSMR showed two types. One was bond failure at interface between concrete and filler and the other was CFRP rupture. Also, failure mode of specimens with two grooves occurred premature bond failure because of superposition of failure surfaces at concrete around grooves. failure mode of MI specimens considered the equivalent section have changed bond failure to CFRP rupture and CFRP efficiency has improved 83% to 100%.

• KSCE Journal of Civil and Environmental Engineering Research
• /
• v.28 no.2A
• /
• pp.289-295
• /
• 2008

The purpose of this study was to examine the flexural behavior of reinforced concrete beams strengthened with CFRP strips. A total of 12 rectangular beams were tested. Test variables in this study were the shapes, bonded length and the number of longitudinal layers of CFRP strips. From the experimental study, flexural capacity of the beams strengthened with CFRP strips significantly increased compared to the reinforced concrete beam without a CFRP strip. Maximum increase of ultimate strength was found about 120% more than the control beam. In this test, most of the strengthened beams failed suddenly due to the debonding of CFRP strips. It is also observed that the debonding of the strip was initiated in the flexural zone of the beam and propagated rapidly to the end of the beam. The ultimate tensile strains of CFRP strips in this test were occurred at the level of 36% of rupture tensile strength of the CFRP strip, and an analytical approach to compute the flexural strength of reinforced beams strengthened with CFRP strips based on the effective stresses was conducted.

• Journal of the Korea institute for structural maintenance and inspection
• /
• v.15 no.5
• /
• pp.101-112
• /
• 2011

This paper shows a study carried out on the estimation of nominal flexural strength for CFRP-plated RC beams failed by intermediate crack debonding. A strength reduction factor is proposed to consider the effect of the intermediate crack debonding for the determination of nominal flexural strength. The proposed factor is derived from experimental data and utilizes the ratio of effective stress(or strain) in the CFRP plate to its ultimate strength(or strain) which is called effective strain model. An analytical equation for the estimation of the nominal flexural strength is formulated as a function of strength reduction factor. The validity, accuracy and efficiency of the proposed factor are established by comparing the analytical results with the experimental data, and the major design codes, as well as a number of factors given by researchers. The analytical results presented in this paper indicate that the proposed factor can effectively estimate the flexural nominal strength of CFRP-plated reinforced concrete beams failed by intermediate crack debonding.

• KSCE Journal of Civil and Environmental Engineering Research
• /
• v.26 no.2A
• /
• pp.301-310
• /
• 2006

Carbon fiber reinforced polymer (CRFP) materials are well suited to the rehabilitation of civil engineering structures due to their corrosion resistance, high strength to weight ratio and high stiffness to weight ratio. Their application in the field of the rehabilitation of concrete structures is increased due to the vast number of bridges and buildings in need of strengthening. However, RC members, strengthened with externally bonded CFRP plates, happened to collapse before reaching the expected design failure load. Therefore, it is necessary to develop the new strengthening method to overcome the problems of previous bonded strengthening method. This problems can be solved by prestressing the CFRP plate before bonding to the concrete. In this study, a total of 21 specimens of 3.3 m length were tested by the four point bending method after strengthening them with externally bonded CFRP plates. The CFRP plates were bonded without prestress and with various prestress levels ranging from 0.4% to 0.8% of CFRP plate strain. All specimen with end anchorage failed by a plate fracture regardless of the prestress levels while the specimen without end anchorage failed by the separation of the plate from the beam due to premature debonding. The cracking loads was proportionally related to the prestress levels, but the maximum loads of specimens strengthened with prestressed CFRP plates were insignificantly affected by the prestress levels.

• Journal of the Korea Concrete Institute
• /
• v.28 no.5
• /
• pp.535-544
• /
• 2016

This paper aims at examining the effects of sustained load and elevated temperature on the time-dependent deformation of a carbon fiber reinforced polymer (CFRP) sheets bonded to concrete as well as the pull-off strength of single-lap shear specimens after the sustained loading period using digital images. Elevated temperature during the sustained loading period resulted in increased slip of the CFRP composites, whereas increased curing time of the polymer resin prior to the sustained loading period resulted in reduced slip. Pull-off tests conducted after sustained loading period showed that the presence of sustained load resulted in increased pull-off strength and interfacial fracture energy. This beneficial effect decreased with increased creep duration. Based on analysis of digital images, results on strain distributions and fracture surfaces indicated that stress relaxation of the epoxy occurred in the 30 mm closest to the loaded end of the CFRP composites during sustained loading, which increased the pull-off strength provided the failure locus remained mostly in the concrete. For longer sustained loading duration, the failure mode of concrete-CFRP bond region can change from a cohesive failure in the concrete to an interfacial failure along the concrete/epoxy interface, which diminished part of the strength increase due to the stress relaxation of the adhesive.

• Journal of the Korea Concrete Institute
• /
• v.14 no.4
• /
• pp.549-555
• /
• 2002

Tensile strength of CFRP (Carbon Fiber Reinforced Polymer) is approximately 10 times higher than that of the steel reinforcement, but the design strength of CFRP is normally limited by unpredictable bond failure between RC and CFRP. Many researches concerned with bond behavior between RC and CFRP have been carried out to prevent the bond failure of RC beam strengthened by CFRP, but the national design code for design bond strength of CFRP has not been constructed. In this study, three beam specimens strengthened by CFRP under the parameters of bonded length were tested to derive the design bond strength of CFRP for the RC flexural members. Each bonded length was calculated based on the bond strength of JCI and CFRP manufacturing company. Also, another two beam specimens strengthened by CFRP were tested to inspect the construction environment effects such as mixing error of epoxy resin, and the amount of epoxy primer. From the test results, it is concluded that the maximum design bond strength of CFRP to RC flexural member is considered to be $\tau$a =8 kgf/㎠.

• Proceedings of the Korea Concrete Institute Conference
• /
• 2008.04a
• /
• pp.169-172
• /
• 2008

Carbon fiber reinforced polymer (CFRP) laminates can be used more efficiently in strengthening applications by applying prestress to the CFRP laminates. A key problem for prestressing with CFRP laminates is anchoring the laminates. These may include fracture to the CFRP laminates due to excessive gripping force or slippage of the CFRP laminates out of the anchorage zone caused by low friction between the anchor device and the lamiantes. The main objective of this study is the development of an applicative mold-type anchorage system for prestressed CFRP laminates through experimental study. The experimental parameters were the type of anchorage detail and the effect of surface treatment. The test results showed that the developed anchor assures 100% CFRP laminate strength.