• Bulletin of the Korean Chemical Society
• /
• 제31권5호
• /
• pp.1257-1261
• /
• 2010

The electrochemical performances of anode composites comprising elemental silicon (Si), silicon monoxide (SiO), and graphite (C) were investigated. The composite devoid of elemental silicon (SiO:C = 1:1) and its carbon coated composite showed reduced capacity degradation with measured values of 606 and 584 mAh/g at the fiftieth cycle. The capacity retention nature when the composites were cycled followed the order of Si:SiO:C = 3:1:4 < Si:SiO:C = 2:2:4 < SiO:C = 1:1 < SiO:C = 1:1 (carbon coated). A comparison of the capacity retention properties for the composites in terms of the silicon content showed that a reduced silicon content increased the stability of the composite electrodes. Even though the carbon-coated composite delivered low capacity during cycling compared to the other composites, its low capacity degradation made the anode a better choice for lithium ion batteries.

• 한국세라믹학회지
• /
• 제56권5호
• /
• pp.453-460
• /
• 2019

To reduce residual pores of composites and obtain a dense matrix, SiC_f/SiC composites were fabricated by chemical vapor deposition (CVI) using SiC nanorods. SiC nanorods were uniformly grown in the thickness direction of the composite preform when the reaction pressure was maintained at 50 torr or 100 torr at 1,100℃. When SiC nanorods were grown, the densities of the composites were 2.57 ~ 2.65 g/㎤, higher than that of the composite density of 2.47 g/㎤ for non-growing of SiC nanorods under the same conditions; grown nanorods had uniform microstructure with reduced large pores between bundles. The flexural strength, fracture toughness and thermal conductivity (room temperature) of the SiC nanorod grown composites were 412 ~ 432 MPa, 13.79 ~ 14.94 MPa·m^1/2 and 11.51 ~11.89 W/m·K, which were increases of 30%, 25%, and 25% compared to the untreated composite, respectively.

• Composites Research
• /
• 제35권3호
• /
• pp.161-174
• /
• 2022

SiC 섬유강화 복합체는 경수형 원자로의 안전성을 획기적으로 향상시킬 수 있는 사고저항성 핵연료 피복관 소재이다. 지르코늄 합금 피복관 및 금속기반 사고저항성 핵연료 피복관에 비해, 중대 사고 환경에서도 우수한 구조적 안정성을 가지고 부식 속도가 매우 낮아, 사고 시 원자로의 온도를 낮추고 사고 진행을 늦출 수 있다. 본 논문에서는 현재 개발되고 있는 사고저항성 SiC 복합체 핵연료 피복관의 개념 및 가동/사고환경에서의 다양한 특성, 상용화를 위해 해결해야 할 다양한 이슈에 대해서 소개하고자 한다.

• 한국주조공학회지
• /
• 제10권1호
• /
• pp.43-49
• /
• 1990

The influences of Cu and Mg addition on wear properties of SiC particulate reinforced Al-Si metal(alloy) matrix composites were investigated. Metal matrix composites were prepared by combination of compocasting and hot pressing techniques. The main results obtained are as follows : 1) The composite with Mg addition exhibits letter wear resistance than that with Cu addition. It is considered that Mg addition improved wettability of matal matrix composite by the strong segregation to the SiC / Al matrix interface. 2) After homogenization treatment, it was found that the interfacial segregation of Mg was predominant, while that of Cu was not detected. 3) The SiC / Al-11Si eutectic composite exhibits better wear resistance than the SiC / Al-6Si hypoeutectic composite does. 4) It seems that the increase in the amount of Mg addition affects on the uniform dispersion of SiC particulates, on the refinement of microstructure and on age hardening and these effects cause wear resistance improvement of composites.

• 한국표면공학회지
• /
• 제52권6호
• /
• pp.310-315
• /
• 2019

The use of a silicon carbide (SiC)-based composite ceramic layer for the mold of a curved cover glass was demonstrated. The stress of SiC/VDR/graphite-based mold structure was evaluated via finite element analysis. The results revealed that the maximum tensile stress primarly occured at the edge region. Moreover, the stress can be reduced by employing a relatively thick SiC coating layer and, therefore, layers of various thicknesses were deposited by means of chemical vapor deposition. During growth of the layer, the orientation of the facets comprising the SiC grain became dominant with additional intense SiC(220) and SiC(004). However, the roughness of the SiC layer increased with increasing thickness of the layer and. Hence, the thickness of the SiC layer needs to be adjusted by values lower than the tolerance band of the curved cover glass mold.

• 한국전기전자재료학회:학술대회논문집
• /
• 한국전기전자재료학회 1997년도 춘계학술대회 논문집
• /
• pp.135-140
• /
• 1997

The influences of ZrB$_2$ additions to SiC on microstructural, DDM(Electrical Discharge Machining), mechanical and electrical properties were investigated. composites were prepared by adding 15, 30, 45 vol.% ZrB$_2$particles as a second phase to SiC matrix. SiC-ZrB$_2$ composites obtained by hot pressing for high temperature structural application were fully dense with the relative densities over 99%. The fracture toughness of the composites were increased with the ZrB$_2$contents. In case of composite containing 30vol.% ZrB$_2$, the flexural strength and fracture toughness showed 45% and 60% increase, respectively compared to that of monolithic SiC sample. The electrical resistivities of SiC-ZrB$_2$ composites decreased significantly with the ZrB$_2$ contents. The electrical resistivity of SiC-30vol.% ZrB$_2$ composite showed 6.50$\times$10$^{-4}$ $\Omega$.cm. Cutting velocity of EDM of SiC-ZrB$_2$ composites are directly proportional to duty factor of pulse width. Surface roughness, however, are not all proportional to pulse width. Higher-flexural strength composites show a trend toward smaller crater volumes, leaving a smoother surface; the average surface roughness of the SiC-ZrB$_2$ 15 vol.% composite with the flexural strengthe of 375㎫ was 3.2${\mu}{\textrm}{m}$, whereas the SiC-ZrB$_2$ 30.vol% composite of 457㎫ was 1.35${\mu}{\textrm}{m}$. In the SEM micrographs of the fracture surface of SiC-ZrB$_2$ composites, the SiC-ZrB$_2$ two phases are distinct; the white phase is the ZrB$_2$and the gray phase is the SiC matrix. In the SEM micrographs of the EDM surface, however, these phases are no longer distinct because of thicker recast layer of resolidified-melt-formation droplets present. It is shown that SiC-ZrB$_2$ composites are able to be machined without surface cracking.

• 한국추진공학회지
• /
• 제26권6호
• /
• pp.21-27
• /
• 2022

C_f/SiC 복합재는 저밀도, 높은 기계적 강도, 우수한 열 안정성을 가지고 있어 로켓 추진기관, 항공 및 군사 분야 등의 고온 응용 산업에 유망한 재료이다. 그러나 용융 실리콘 함침(Liquid Silicon Infiltration, LSI) 공정을 통해 제작된 복합재는 잔존하는 Si에 의하여 물리적, 열적 특성이 저하된다. 본 논문에서는 LSI 공정을 통해 제작된 C_f/SiC 복합재의 내부 Si을 제거하기 위한 방안으로 탈규소화(de-siliconization) 공정을 도입하였다. 최대 5분 동안 옥시아세틸렌 토치 테스트를 진행하고 시편의 산화된 표면과 단면은 3D scanning, X-ray diffraction(XRD), 광학현미경(OM), 전자주사현미경(SEM)으로 분석하였다.

• 한국세라믹학회지
• /
• 제40권5호
• /
• pp.460-467
• /
• 2003

기계적 합금화법에 의해 준비된 복합분말을 이용하여 용사공정에 의해 알루미늄 모재에 Al-SiC$_{p}$ 복합재료 코팅층을 형성하였다. 24h milling 후 복합화된 분말을 제조할 수 있었으며, 이 분말을 용사하여 복합재료 코팅층을 형성할 수 있었다. 코팅층의 두께 및 기공율과 공정변수와 관계를 분석하였으며, 경도의 증가를 확인하였다. 또한 TEM분석에 의해 Al-Si-C-O 화합물의 존재를 확인하였다.

• 한국표면공학회지
• /
• 제43권6호
• /
• pp.255-259
• /
• 2010

In this work, Ni-Co composites incorporated with nano-sized SiC particles in the range of 45-55 nm are prepared by electroplating. The effects of plating duration on the chemical composition, surface morphology, crystalline structures and hardness have been studied. The maximum hardness of Ni-Co-SiC composite coating is approximately 633 Hv at plating duration of 1 h. The hardness is gradually decreased with increasing plating duration, which can be attributed to the growth of crystalline size and the agglomerates of SiC nano-particles. It is therefore explained that the grain refinement of Ni-Co matrix and stable dispersion of SiC particles play an important role for strengthening, which indicate Hall-Petch relation and Orowan model were dominant for hardening of Ni-Co-SiC composite coatings.

• 한국세라믹학회지
• /
• 제30권2호
• /
• pp.123-130
• /
• 1993

Dispersed type Al2O3-SiC composite powders were synthesized from Al-isopropoxide (Al(i-OC3H7)3) and Si(OC2H5)4 precursors by hydrolysis of mixed alkoxides and carbothermal reaction method. The characteristics of the synthesized (dispersed type) Al2O3-SiC composite powders were investigated using XRD, SEM, TEM, BET and particle size analyzer. Carbothermal reaction to produce Al2O3-SiC composite was completed in 10h at 135$0^{\circ}C$ on 3~4㎤/s (0.21~0.28cm/s) of H2 flow rate and about 1/1 of carbon/oxides(=SiO2＋Al2O3) molar ratio. The synthesized powders were observed to have the mean particle size range of 0.4~1.26${\mu}{\textrm}{m}$ and showed finer particle size with increasing SiC content.