• The korean journal of orthodontics
• /
• v.25 no.2 s.49
• /
• pp.223-233
• /
• 1995

The purpose of this study was to evaluate the effects of surface conditioning with $10\%$ polyacrylic acid, etching with $38\%$ phosphoric acid, and polishing with a slurry of pumice on shear bond strengths of light-cured glass ionomer cement, chemically cured glass ionomer cement, and a composite resin to enamel, and to observe the failure patterns of bracket bondings. Shear bond strengths of glass ionomer cements were compared with that of a composite resin. Metal brackets were bonded on the extracted human bicuspids after enamel surface treatments, and samples were immersed in the $37^{\circ}C$ distilled water bath, and shear bond strengths of glass ionomer cements and a composite resin were measured on the Instron machine after 24hrs passed, and the deboned samples were measured in respect of adhesive remnant index. Scanning electron micrographs were taken of enamel surfaces after various treatments. The data were evaluated and tested by ANOVA and Duncan's multiple range test, and those results were as follows. 1. Shear bond strength of light-cured glass ionomer cement showed statistically higher than that of chemically cured glass ionomer cement. 2. Shear bond strengths of light-cured and chemically cured glass ionomer cements to enamel treated with $10\%$ polyacrylic acid and $38\%$ phosphoric acid showed statistically higher than those with a slurry of pumice. 3. According to scanning electron micrographs, enamel surface conditioned with $10\%$ polyacrylic acid is slightly etched and cleaned, that etched with $38\%$ phosphoric acid is severely etched, and that polished with a slurry of pumice is irregulary scretched and not completely cleaned. 4. After debonding, light-cured glass ionomer cement to enamel treated with $10\%$ polyacrylic acid showed less residual materials on the enamel solace than composite resin to enamel etched with $38\%$ phosphoric acid. 5. There was no significant difference in the shear bond strength of light-cured glass ionomer cement to enamel treated with $10\%$ polyacrylic acid and that of composite resin to enamel etched with $38\%$ Phosphoric acid.

• The korean journal of orthodontics
• /
• v.31 no.1 s.84
• /
• pp.137-147
• /
• 2001

Acidic primer is the bonding agent which combines the conditioning and priming agent into the single solution and was originally developed for the dentin bonding system. It is less harmful to the tooth structure and more convenient to manipulate than the traditional etching procedure. The Purpose of this study is to evaluate the shear bond strength of various bonding materials when the enamel is treated with acidic primer for the bracket bonding procedure. Fifty recently extracted human premolars were randomly separated into five groups -Group I using Clearfil Liner Bond 2 adhesive system to the enamel treated with acidic primer, Group II using Transbond XT adhesive system to the enamel treated with acidic primer, Group III using panavia 21 adhesive system to the enamel treated with acidic primer, Group IV using Fuji-Ortho LC adhesive system to the enamel treated with acidic primer, Group V using Transbond XT adhesive system to the enamel treated with 37$\%$ phosphoric acid. The shear bond strength was measured with Instron universal testing machine after storing in $37^{\circ}C$ water bath for 48 hours. After debonding, the teeth and brackets were examined under scanning electron microscope (SEM) and assessed with the adhesive remnant index (ARI). The results were as follows : 1. There were no significant differences in shear bond strength between group III ($8.69{\pm}2.72MPa$), group IV (9.7 ± 3.16 MPa), and group V ($10.48{\pm}2.60MPa$) (p>0.05). 2. The shear bond strength of group III and group IV was significantly higher than that of group I ($1.09{\pm}0.53MPa$), and Group II ($2.70{\pm}1.46MPa$) (p<0.05). 3. The ARI of group IV ($2.1{\pm}1.1$) and group V ($2.9{\pm}0.3$) was significantly higher than that of group I ($0.2{\pm}0.4$), group II ($0.3{\pm}0.9$) and group III ($0.2{\pm}0.4$) (p<0.05). 4. There were no significant difference between the ARI of group IV and group V (p>0.05). This result suggests that the combination of acidic primer and some bonding adhesive can provide sufficient shear bond strength for clinical orthodontics.