• Journal of Nuclear Fuel Cycle and Waste Technology(JNFCWT)
• /
• v.22 no.2
• /
• pp.173-183
• /
• 2024

Vitrification, one of the most promising solidification processes for various materials, has been applied to radioactive waste to improve its disposal stability and reduce its volume. Because the thermal decomposition of dry active waste (DAW) significantly reduces its volume, the volume reduction factor of DAW vitrification is high. The KHNP developed the optimal glass composition for the vitrification of DAW. Since vitrification offers a high-volume reduction ratio, it is expected that disposal costs could be greatly reduced by the use of such technology. The DG-2 glass composition was developed to vitrify DAW. During the maintenance of nuclear power plants, metals containing paper, clothes, and wood are generated. ZrO₂ and HfO₂ are generally considered to be network-formers in borosilicate-based glasses. In this study, a feasibility study of vitrification for DAW that contains metal particulates is conducted to understand the applicability of this process under various conditions. The physicochemical properties are characterized to assess the applicability of candidate glass compositions.

• Journal of the Korean Ceramic Society
• /
• v.47 no.4
• /
• pp.325-328
• /
• 2010

Varying quantities of a high-thermal-expansion glass, 50CaO-20ZnO-$20B_2O_3-10SiO_2$ (CZBS), were added to alumina and sintered at $875^{\circ}C$ for 2 h for low temperature co-firing ceramic (LTCC) applications. As the amount of glass addition increased from 40 wt% to 70 wt%, the apparent density of the sintered product increased from 88.8% to 91.5%, which was also qualitatively confirmed by microstructural observation. When the glass addition was very high, e.g., 70 wt%, an apparent formation of secondary phases such as $CaZn_2AlZnSiAlO_7$, $Ca_2Al(AlSi)O_7$, $Ca_2Al_2SiO_7$, $Ca_2ZnSi_2O_7$ and ZnO, was observed. Both the dielectric constant and the coefficient of thermal expansion increased with the glass addition, which was qualitatively consistent with the analytical models, while the experimental values were lower than the predicted ones due to the presence of pores and secondary phases.

• Journal of Nuclear Fuel Cycle and Waste Technology(JNFCWT)
• /
• v.3 no.4
• /
• pp.335-340
• /
• 2005

The forward dissolution rate of a borosilicate waste glass was determined as an interlaboratory study(ILS) testing program for the evaluation of precision in the measurement of the dissolution rate or a waste glass using a single-pass flow-through(SPFT) test, whose conducting practice has been written for standardization through American Society for Testing and Materials (ASTM). A simulated low-activity waste glass powder with a size of 100/200 mesh was dissolved by lithium buffer solution (pH=10) at 70? under Ar atmosphere. By plotting the dissolution rates as a function of silicon and boron concentration in eluate, the forward dissolution rate of the glass was obtained as about $2.7\times10^{-5}g{\cdot}m{\cdot}s^{-1}$ in our laboratory.

• Korean Journal of Optics and Photonics
• /
• v.35 no.3
• /
• pp.115-120
• /
• 2024

Magneto-optical (MO) materials have attracted much attention, since they can be utilized for various optical applications, such as magnetic field sensors, optical current sensors, optical isolators, and optical circulators. In this study, alumino-borosilicate (ABS) glasses with high concentrations of Dy³⁺ ions were fabricated by a conventional melt-quenching technique, and the dependence of their thermal, optical, and magneto-optical properties on Dy³⁺ ion concentration was investigated. The MO property of the glasses was investigated by measurement of Faraday rotation at 1550 nm. The Faraday rotation angle increased linearly with the increase of Dy³⁺ ion concentration in the glasses. A very high Verdet constant of -6.86 rad/(T·m) was obtained for glass with a Dy³⁺ ion concentration of 30 mol%. In addition, the ABS-Dy glasses showed good thermal stability of greater than 128 ℃ against crystallization, and high optical transmission of 70% in the visible to near-infrared windows of 480-720, 1390-1560, and 1800-2400 nm. Due to the high Verdet constant and good thermal stability, the ABS-Dy glasses in this study could be candidate optical materials for MO device applications at 1550 nm.

• Journal of the Korean Crystal Growth and Crystal Technology
• /
• v.17 no.2
• /
• pp.82-89
• /
• 2007

Glass-ceramics were fabricated by heat-treating a glass at $700^{\circ}C$/10hr which was obtained by melting a glass frit mixed with $40{\sim}80 wt%$ EAF dust at $1300^{\circ}C$/1hr. Dependence of crystal phase and bonding state change upon a compositional change and heat treatment condition were studied and the results was connected to the toxic characterization leaching procedure (TCLP) test data to investigate a chemical durability of the specimens. Increasing dust in a glass shifted the peak around $1000cm^{-1}$ to the lower frequency which was composed of two vibration peaks for the nonbridging oxygen at $960cm^{-1}$ and the bridging oxygen at $1050{\sim}1060cm^{-1}$. Also, the $B_2O_3$ structure of boroxol ring changed to a tetrhedral-, trigonal- and di-borate with dust addition. The Fe-O peaks in the glass-ceramics were observed which is consitent with XRD results of spinel formation. The surface of glass after TCLP test was severely cracked while there was no cracks on a glass-ceramics after TCLP test so the chemical durability of the glass-ceramics is superior than that of glass. The leaching concentration of Fe for the glass-ceramics containing EAF dust 80 wt% is 1/15 times lower than that of glass. The Zn leaching concentration fur the glass-ceramics containing dust < 70 wt% was higher than that of glass but its trend was reversed for the specimen of dust content > 80 wt% which could be concluded as correlated with occurrence of willemite phase.

• Laser Solutions
• /
• v.15 no.3
• /
• pp.16-19
• /
• 2012

We have successfully formed brown colored patterns inside of a transparent borosilicate glass generally known as BK7, laying the focus of near infrared Ti: sapphire femtosecond laser beam in the bulk BK7 glass. It is important to keep the laser power well below the damage threshold of BK7 in forming the color center. According to the low laser power, there was no laser induced mechanical damage such as cracks or threads in the color formed area. From the absorbance spectrum and its gaussian fitting, we found the band gap of BK7, 4.21eV, and three absorption edges.

• Mass Spectrometry Letters
• /
• v.7 no.1
• /
• pp.21-25
• /
• 2016

Dual-channel nano-electrospray has recently become an ionization technique of great promise especially in biological mass spectrometry. This unique approach takes advantage of the mixing processes that occurs during electrospray. Understanding in more detail the fundamental principles influencing spray formation further study of the origins of the mixing processes: (1) in a Taylor cone region, (2) in charged droplets or (3) in both environments. The dual-channel emitters were made from borosilicate theta-shape glass tubes (O.D. 1.2 mm) and had a tip diameters of less than 4 μm. Electrical contact was achived by deposition of a thin film of an appropriate metal onto the surface of the emitter. The experimental investigation of the Taylor cone formation in a dual-channel electrospray emitter has been carried out by injection of polystyrene beads (diameter 3 μm) at very low concentrations into one of the channels of the non-tapered theta-glass tubes. High-speed camera experiments were set up to visualize the mixing processes in Taylor cone regions for dual-channel emitters. Mass spectra from dual nano-electrospray are presented.

• Journal of the Korean Ceramic Society
• /
• v.21 no.1
• /
• pp.41-50
• /
• 1984

The ion-exchange porous glasses were prepared by heat treating and subsequently acid treating the (95-y) $SiO_2$.$yB_2O_3$.$5Na_2O+xAl_2O_3$ glasses with y=55, 45, 35, 25. mole% and x=0, 2, 5, 9 mole% It was then investigated how the cation exchange capacity was affected by the phase separation in these glasses. For that matter such quantities as alkali extraction amount pore volume and specific surface area of the glasses were measured. The phase separation in these glasses was in general suppressed by the addition of $Al_2O_3$ maximally around the composition of 5 mole% $Al_2O_3$ This may be because the micro-phase separation prevailed in the glass of that composition over the macro-phase separation increasing thereby the specific surface area as well as the residual amount Al of after acid-treatment and accordingly the cation exchange capacity. The maximum values of the cation exchange capacity was observed to be about 150meq/100g for the glasses of (40-50) $SiO_2$ (55~45)$yB_2O_3$. $5Na_2O+5Al_2O_3$.

• KSTLE International Journal
• /
• v.5 no.1
• /
• pp.1-6
• /
• 2004

Nano-scale studies on adhesion and friction were conducted in Si-wafer (100) using Atomic Force Microscopy (AFM). Glass (Borosilicate) balls of radii 0.32$\mu\textrm{m}$, 1.25$\mu\textrm{m}$, and 2.5$\mu\textrm{m}$, mounted on cantilever (Contact Mode type NPS) were used as tips. Adhesion and friction between Si-wafer and glass tips were measured at ambient temperature (24${\pm}$1$^{\circ}C$) and humidity (45${\pm}$5%). Friction was measured as a function of applied normal load in the range of 0-160 nN. Results showed that, both adhesion and friction increased with the tip radii. Also, friction increased linearly as a function of applied normal load. The effect of tip size on adhesion and friction was explained as the influence of the capillary force exerted by meniscus and that of the contact area on these parameters respectively. The coefficient of friction was estimated in two different ways, as the slope from the plot of friction force against the applied normal load and as the ratio between the friction force and the applied normal load. Both these estimates showed that the coefficient of friction increased with the tip size. Further, the influence of the adhesion force on the coefficient of friction was also discussed.

• Journal of the Microelectronics and Packaging Society
• /
• v.8 no.3
• /
• pp.31-36
• /
• 2001

Dielectric material which is suitably designed for the application of the high-temperature electrostatic chucks(HTESCS) has been developed. Electrical resistivities and dielectric constants of the dielectric layer satisfy the demands for the proper operation of HTESC, and coefficient of thermal expansion(CTE) of the dielectric material matches well that of the bottom insulator so that it secures stable structure. In order to minimize particle contaminations, borosilicate glass(BSG) is selected as a bonding layer between dielectric layer and bottom insulator, and silver is used as a electrode. BSG is solidly bonded between upper dielectric and bottom insulator, and no diffusions or reactions are observed among silver electrode, dielectric, and glass layers. The chucking characteristics of the fabricated HTESC are found to be superior to those of the commercialized one.