• Nuclear Engineering and Technology
• /
• v.56 no.7
• /
• pp.2828-2834
• /
• 2024

This research intends to recycle bone and incorporate it into concrete for radiation shielding application using Phy-X/PSD software. Cement, sand and granite were mixed in proportion of 0.5 kg:1 kg:1 kg to obtain sample A. Other concretes composing of cement, sand, granite and bone ash was in proportion 0.45 kg:1 kg:1 kg:0.05 kg, 0.1 kg:1 kg:1 kg:0.4 kg and 0.35 kg:1 kg:1 kg:0.15 kg to obtain samples B, C and D respectively. 0.5 water-to-cement (W/C) ratio was adopted throughout the mixes because the control mix contain the normal water quantity for normal hydration of cement. Replacing the bone ash for the cement in the fabricated concretes enhances their densities where the fabricated concretes' density decreased from 2.33 g/cm³ to 2.22 g/cm³ by raising the reinforcing bones fly ash concentration from 0 to 0.15 kg. Additionally, increasing the bones fly ash concentration within the fabricated concretes increases their linear attenuation coefficient (LAC) where the fabricated concretes' μ values at 0.662 MeV reach 0.181 cm^-1, 0.178 cm^-1, 0.174 cm^-1, and 0.171 cm^-1, respectively for concretes A, B, C, and D. The use of other local materials is recommended, as it improves waste management being the major aim of the sustainable development goal.

• Journal of the Korea Concrete Institute
• /
• v.23 no.3
• /
• pp.339-346
• /
• 2011

The effects of mineral admixtures on the bonding properties of cement mortar to polyolefin based synthetic fiber were evaluated. The mineral admixtures consisted of 0%, 5%, 10%, and 15% fly ash, blast furnace slag, and metakaolin in cement. Bond interactions between the cement mortar and the polyolefin based synthetic fiber were determined by Dog-bone bond tests. Bond tests of the polyolefin based synthetic fiber showed an increase in pullout load with the strength of the cement mortar. Also, the interface toughness of polyolefin based synthetic fiber in cement mortar increased as the fly ash, blast furnace slag, and metakaolin contents increased. The microstructure of polyolefin based synthetic fiber surface was examined after the pullout test to analyze the frictional resistant force according to the replacement ratio of fly ash, blast furnace slag, and metakaolin during the pullout process of polyolefin based synthetic fiber in cement mortar. The scratched of polyolefin based synthetic fibers increased with the replacement ratio of fly ash, blast furnace slag, and metakaolin. Also, the interface toughness was enhanced by adhesion forces induced by the fly ash, blast furnace slag, and metakaolin.