• 대한기계학회논문집A
• /
• 제25권1호
• /
• pp.115-126
• /
• 2001

In this paper, through a series of comparative experiments, effects of two different cure processing methods, cocure and precure, on the mechanical properties of honeycomb core materials for aircraft applications are considered. Mass of moisture accumulated into the closed cells of the sandwich panel specimen from the measured mass of moisture diffused to the full saturation state into the elements(skin, adhesive layer, Nomex honeycomb), consisting the honeycomb sandwich specimen has been calculated. Water reservoir of 70$\^{C}$ was used to have specimens absorb moisture to see the influence of moisture absorbed into sandwich panel on its mechanical properties. For the repair condition holding for 2 hours at 177$\^{C}$(350℉) temperature, a pressure due to the vapor expansion in each cell of the sandwich panel, which may result in the local separation of the interface between laminated skin and the surface of the honeycomb, has been estimated by vapor pressure-temperature relation from the thermodynamic steam table and compared to the pressure from the ideal gas state equation. The bonding strengths of the laminated skins on the flat surface of the Nomex honeycomb have been compared by the flatwise tension test and climbing drum peel test performed at room temperature for dry, wet and wet-repair specimens, respectively.

• 한국복합재료학회:학술대회논문집
• /
• 한국복합재료학회 2004년도 추계학술발표대회 논문집
• /
• pp.73-77
• /
• 2004

Failure predictions of composite single-lap bonded joints were performed considering both of composite adherend failure and bondline failure. An elastic-perfectly plastic model of adhesive and a delamination failure criterion are used. The failure prediction results such as failure mode and strength have very good agreements with the test results of joint specimens with various bonding methods and parameters. The influence of variations in the effective strength (that is, adhesion performance) and plastic behavior of adhesive on the failure characteristics of composite bonded joints are investigated numerically. The numerical results show that optimal joint strength is archived when adhesive and delamination failure occur in the same time.

• 한국복합재료학회:학술대회논문집
• /
• 한국복합재료학회 2004년도 춘계학술발표대회 논문집
• /
• pp.232-236
• /
• 2004

The fracture characteristics of unidirectional composite single-lap bonded joints were investigated experimentally and numerically. The effects of bonding method, surface roughness, bondline thickness and the existence of fillet on the failure characteristics and strength of bonded single-lap joints were evaluated experimentally. The failure process, failure mode and the behavior of load-displacement curve was apparently different according to bonding method. The failure load of the specimen co-cured without adhesive was definitely superior to other types of specimens but the specimens co-cured with adhesive film had a less strength than secondary bonded specimens. In the secondary bonded specimens, the lower value of surface roughness and existence of fillet improved the strength of specimens. The strain energy release rates calculated by geometric nonlinear finite element analyses and Virtual Crack Closure Technique for the secondary bonded specimens considering the three types of initial cracks - comer crack, edge crack and delamination crack - were consistent with the test results.

• Steel and Composite Structures
• /
• 제44권4호
• /
• pp.519-529
• /
• 2022

Sandwich structures with the superior mechanical properties such as high stiffness and strength-to-weight ratio, good thermal insulation, and high energy absorption capacity are used today in aerospace, automotive, marine, and civil engineering industries. These structures are composed of moderately stiff, thin face sheets that withstand the majority of transverse and in-plane loads, separated by a thick, lightweight core that resists shear forces. In this research, the finite element technique is used to simulate a sandwich panel with a truss core under axial compressive stress using ABAQUS software. A review of past experimental studies shows that the bondline between the core and face sheets plays a vital role in the critical failure load. Therefore, this modeling analyzes the damage initiation modes and debonding between face sheet and core by cohesive surface contact with traction-separation model. According to the results obtained from the modeling, it can be observed that the adhesive stiffness has a significant influence on the critical failure load of the specimens. To achieve the full strength of the structure as a continuum, a lower limit is obtained for the adhesive stiffness. By providing this limit stiffness between the core and the panel face sheets, sudden failure of the structure can be prevented.

• Composites Research
• /
• 제17권6호
• /
• pp.14-21
• /
• 2004

본 연구에서는 몇 가지 접합 방법에 따라 일방향 복합재료 단일 겹치기 접합 조인트의 파손 과정, 모드 및 강도를 실험적으로 평가하였다 접합 방법으로는 접착제 없는 동시성형, 접착제를 사용한 동시성형 및 이차 접합의 세 가지를 고려하였다 또한 이차 접합 조인트에서 몇 가지 파라미터의 영향도 살펴보았다. 접착제 없는 동시성형 시편은 가장 우수한 조인트 강도를 나타내었다. 이차접합 조인트에서는 접착제 층의 점진적인 파손이 발생하였다. 접착제의 재료 및 접합 강도가 상대적으로 강한 필름 접착제의 동시성형 조인트는 갑작스런 층간분리 파손이 발생하였으며 이차 접합 조인트보다 더 낮은 파손 강도를 나타내었다. 이차 집합 조인트에서 층간분리 파손이 발생하지 않은 것은 접착제 층에서의 균열 진전 및 점진적 파손이 층간분리 파손을 방지한 것으로 보인다. 따라서 복합재료 접합 조인트의 파손 강도는 접착제의 재료 강도 또는 접착 성능과 항상 비례하지 않으며 이것은 복합재료가 층간 분리 파손에 약하기 때문이다.

• Composites Research
• /
• 제18권1호
• /
• pp.1-9
• /
• 2005

본 논문에서는 복합재료 접합 조인트의 다양한 파손 모드를 고려하여 파손 강도를 예측할 수 있는 방법을 제시하였다. 제시된 방법에서는 접착제의 탄성-완전 소성 재료 모델과 층간분리 파손 식을 이용해 접착제 파손 하중과 복합재료 부재의 층간분리 파손 하중을 동시에 계산하였다. 제시된 방법을 유한요소해석에 도입하여 복합재료 Single-Lap 접합조인트의 파손 예측을 수행하였으며 시험결과와 비교하였다 이를 통해 본 방법이 다양한 접합 방법에 따른 실제적인 파손모드 및 파손 하중을 정확하게 예측할 수 있음을 확인하였다. 또한 접착제의 유효강도(또는 접착 성능) 및 소성거동이 복합재료 접합 조인트의 파손 특성에 미치는 영향을 수치적으로 평가하였다. 이를 통해, 복합재료 접합조인트의 파손 강도는 접착제의 접착 성능과 항상 비례하지 않으며 층간분리 파손과 접착제 파손이 동시에 발생하도록 하는 것이 접합 조인트의 강도를 최대로 향상시킬 수 있음을 보였다.

• Composites Research
• /
• 제20권6호
• /
• pp.8-14
• /
• 2007

스킨-보강재 시편 시험을 통해 스킨과 보강재의 분리 파손 특성을 살펴보고 접합방법, 보강재 단면 및 이차 접합 파라미터의 영향을 조사하였다. 본 시험 결과와 이전 시험[1]의 결과를 종합해 볼 때, 보강패널의 스킨-보강재 분리 파손 강도를 판단하는 기준으로 스킨-보강재 시편의 파손 변위를 이용하는 것이 타당하며 동일한 접합 방법을 사용할 경우, closed형 보다 open형 보강재를 사용하는 것이 복합재 보강 패널에서 스킨과 보강재의 분리파손을 방지하는데 유리함을 알 수 있었다. 접합방법으로는 이차접합 및 접착제를 사용한 동시성형이 좋은 파손 강도를 보였으며 접착제 없는 동시성형이 가장 나쁜 파손 강도를 나타내었다. 파손 모드는 이차접합 시편은 주로 계면 파손이 발생하였으며 동시성형 시편은 복합재료의 층간분리 파손이 발생하였다. 이차 접합 시편에서는 접착제 두께가 작을수록 높은 파손 강도를 보였다. Fillet은 시편의 강도에 영향을 미치지 않았다. 표면 조도의 영향은 open형 및 closed형 시편이 다르게 나타났다.