• Restorative Dentistry and Endodontics
• /
• 제24권4호
• /
• pp.647-656
• /
• 1999

The purpose of this study was to investigate the shear bond strength and marginal microleakage of composite to enamel and dentin according to different treatment methods when the applied bonding agent was contaminated by artificial saliva. For the shear bond strength test, the buccal and occlusal surfaces of one hundred twenty molar teeth were ground to expose enamel(n=60) and dentin surfaces(n=60). The specimens were randomly assigned into control and 5 experimental groups with 10 samples in each group. In control group, a bonding system(Scotchbond$^{TM}$ Multi-Purpose plus) and a composite resin(Z-100$^{TM}$) was bonded on the specimens according to manufacture's directions. Experimental groups were subdivided into 5 groups. After polymerization of an adhesive, they were contaminated with at artificial saliva on enamel and dentin surfaces: Experimental group 1 ; artificial saliva was dried with compressed air. Experimental group 2 ; artificial saliva was rinsed with air-water spray and dried. Experimental group 3 ; artificial saliva was rinsed, dried and applied an adhesive. Experimental group 4 ; artificial saliva was rinsed, dried, and then etched using phosphoric acid followed by an adhesive. Experimental group 5, artificial saliva was rinsed, dried, and then etched with phosphoric acid followed by consecutive application of both a primer and an adhesive. Composite resin(Z-100$^{TM}$) was bonded on saliva-treated enamel and dentin surfaces. The shear bond strengths were measured by universal testing machine(AGS-1000 4D, Shimaduzu Co. Japan) with a crosshead speed of 5mm/minute under 50kg load cell. Failure modes of fracture sites were examined under stereomicroscope. The data were analyzed by one-way ANOVA and Tukey's test. For the marginal microleakage test, Class V cavities were prepared on the buccal surfaces of sixty molars. The specimens were divided into control and experimental groups. Cavities in experimental group were contaminated with artificial saliva and those surfaces in each experimental groups received the same treatments as for the shear test. Cavities were filled with Z-100. Specimens were immersed in 0.5% basic fuchsin dye for 24 hours and embedded in transparent acrylic resin and sectioned buccolingually with diamond wheel saw. Four sections were obtained from the one specimen. Marginal microleakages of enamel and dentin were scored under streomicroscope and averaged from four sections. The data were analyzed by Kruskal-Wallis test and Fisher's LSD. The results of this study were as follows. 1. The shear bond strength to enamel showed lower value in experimental group 1(13.20${\pm}$2.94MPa) and experimental group 2(13.20${\pm}$2.94MPa) than in control(20.03${\pm}$4.47MPa), experimental group 4(20.96${\pm}$4.25MPa) and experimental group 5(21.25${\pm}$4.48MPa) (p<0.05). 2. The shear bond strength to dentin showed lower value in experimental group 1(9.35${\pm}$4.11MPa) and experimental group 2(9.83${\pm}$4.11MPa) than in control group(17.86${\pm}$4.03MPa), experimental group 4(15.04${\pm}$3.22MPa) and experimental group 5(14.33${\pm}$3.00MPa) (p<0.05). 3. Both on enamel and dentin surfaces, experimental group 1 and 2 showed many adhesive failures, but control and experimental group 3, 4 and 5 showed mixed and cohesive failures. 4. Enamel marginal microleakage was the highest in experimental group 1 and there was a significant difference in comparison with other groups (p<0.05). 5. Dentin marginal microleakages of experimental group 1 and 2 were higher than those of other groups (p<0.05). This result suggests that treatment methods, re-etching with 35% phosphoric acid followed by re-application of adhesive or repeating all adhesive procedures, will produce good effect on both shear bond strength and microleakage of composite to enamel and dentin if the polymerized bonding agent was contaminated by saliva.

• Restorative Dentistry and Endodontics
• /
• 제25권3호
• /
• pp.399-406
• /
• 2000

광중합형 글래스아이오노머 베이스에 대한 레진 인레이의 접착성을 증가시킬 수 있는 방법을 모색하고자, 이차 중합된 레진 인레이의 내표면을 여러 가지 방법으로 처리한 후 레진 인레이를 광중합형 글래스아이오노머 베이스에 레진 시멘트 접착시 내표면 처리방법이 이들의 접착에 미치는 영향을 평가하고자 하였다. 글래스아이오노머 베이스 제작을 위해서 플라스틱 봉에 직경 7mm, 깊이 2mm의 1급 와동을 형성하고 Fuji II LC를 충전하였으며, 수복용 레진(Charisma$^{(R)}$)을 사용하여 레진 인레이를 제작하였다. 레진 인레이 내면은 $50{\mu}m$ aluminum oxide particles를 이용한 sandblasting 및 silane 처리군, silane 처리군, sandblasting 군, 그리고 무처리 대조군 등 4군으로 나누어 표면처리하였으며 각 군은 22개씩의 시편을 사용하였다. 인레이와 베이스의 표면에 상아질 접착제(One-Step$^{TM}$)를 도포한 후 Choice$^{TM}$를 사용하여 레진시멘트 접착하였다. 접착 양상 평가를 위해 만능시험기로 전단접착강도를 측정하고 파단면을 입체현미경으로 관찰하여 다음과 같은 결과를 얻었다. 1. Sandblasting 및 silane 처리군이 가장 높은 접착강도(10.56${\pm}$1.95MPa)를 나타내었으며, 이는 sandblasting군 및 무처리 대조군에 비해 유의하게 높았다(p<0.05). 2. Silane 처리군(9.77${\pm}$2.04MPa)은 sandblasting 및 silane 처리군과는 접착력에 있어서 통계적으로 유의한 차이를 나타내지 않았으나, sandblasting 군 및 무처리 대조군에 벼해서는 유의하게 높은 접착강도를 나타내었다(p<0.05). 3. Sandblasting만 시행 한 군은 무처리 대조군과 비교시 접착강도에 있어 유의한 차이를 나타내지 않았다(p>0.05). 4. 파단면 관찰 결과, 모든 군에서 일부 접착계면에서의 파절을 포함하는 글래스아이오노머 베이스의 응집 파괴(cohesive failure) 양상이 가장 많이 나타났으며, sandblasting 및 silane 처리군과 silane 처리군에서는 sandblasting 군 및 무처리 대조군에 비해 상대적으로 적은 접 착계면에서의 파절(adhesive failure) 양상을 나타내었다. 5. 전단접착강도와 파절양상의 관계에서, 접착강도가 클수록 응집 파괴(cohesive failure) 양상이 많이 나타나는 경향을 보였다.

• Structural Engineering and Mechanics
• /
• 제63권3호
• /
• pp.317-327
• /
• 2017

The addition of different types of polymers such as SBR, VAE, Acrylic, etc. in concrete and mortar leads to an increase in compressive, tensile and bond strength and decrease in permeability of polymer modified mortar (PMM) and concrete (PMC). The improvement in properties such as bond strength and impermeability makes PMM/PMC suitable for use as repair/retrofitting and water proofing material. In the present study effect of addition of fluoropolymer on the strength and permeability properties of mortar has been studied. In the cement mortar different percentages viz. 10, 20 and 30 percent of fluoropolymer by weight of cement was added. It has been observed that on addition of fluoropolymer in mortar the workability of mortar increases. In the present study all specimens were cast keeping the workability constant, i.e., flow value $105{\pm}5mm$, by changing the amount of water content in the mortar suitably. The specimens were cured for two different curing conditions. Firstly, these were cured wet for one day and then cured dry for 27 days. Secondly, specimens were cured wet for 7 days and then cured dry for 21 days. It has been observed that compressive strength and split tensile strength of specimens cured wet for 7 days and then cured dry for 21 days is 7-13 percent and 12-15 percent, respectively, higher than specimens cured one day dry and 27 days wet. The sorptivity of fluoropolymer modified mortar decreases by 88.56% and 91% for curing condtion one and two, respectively. However, It has been observed that on addition of 10 percent fluoropolymer both compressive and tensile strength decreases, but with the increase in percentage addition from 10 to 20 and 30 percent both the strengths starts increasing and becomes equal to that of the control specimen at 30 percent for both the curing conditions. It is further observed that percentage decrease in strength for second curing condition is relatively less as compared to the first curing condition. However, for both the curing conditions chloride ion permeability of polymer modified mortar becomes very low.

• Advances in environmental research
• /
• 제7권2호
• /
• pp.139-159
• /
• 2018

Green Leaf Volatiles (GLVs) is a class of biogenically emitted oxygenated hydrocarbons that have been identified as a potential source of Secondary Organic Aerosols (SOA) via aqueous oxidation. The physico-chemical properties of GLVs are vital to understanding their fate and transport in the atmosphere via fog processing, but few experimental data are available. We studied the aqueous solubility, 1-octanol/water partition coefficient, and Henry's law constant ($K_H$) of five GLVs at $25^{\circ}C$: methyl jasmonate, methyl salicylate, 2-methyl-3-buten-2-ol, cis-3-hexen-1-ol, and cis-3-hexenyl acetate. Henry's law constant was also measured at temperatures and ionic strengths typical of fog. Experimental values are compared to scarcely-available literature values, as well as estimations using group and bond contribution methods, property-specific correlations and molecular dynamics simulations. From these values, the partition coefficients to the air-water interface were also calculated. The large Henry's law constant of methyl jasmonate ($8091{\pm}1121M{\cdot}atm^{-1}$) made it the most significant GLV for aqueous phase photochemistry. The HENRYWIN program's bond contribution method from the Estimation Programs Interface Suite (EPI Suite) produced the best estimate of the Henry's constant for GLVs. Estimations of 1-octanol/water partition coefficient and solubility are best when correlating an experimental value of one to find the other. Finally, the scavenging efficiency was calculated for each GLV indicating aqueous phase processing will be most important for methyl jasmonate.

• 한국콘크리트학회:학술대회논문집
• /
• 한국콘크리트학회 2008년도 추계 학술발표회 제20권2호
• /
• pp.855-858
• /
• 2008

초고강도 콘크리트의 개발에 따라 철근 압축이음에 대한 연구 필요성이 높아지고 있다. 인장이음과 마찬가지로 압축이음에서도 이음길이와 콘크리트 강도가 가장 큰 영향인자가 되며, 다음으로 압축이음에 영향을 주는 요인으로는 횡방향 보강근과 철근 지름이다. 횡방향 보강근은 이음부에서 발생된 인장응력에 저항하며, 인장이음에서는 철근 순간격 또는 피복두께와 동일한 역할을 수행하는 것으로 평가된다. 휨부재의 인장측에 주로 적용되는 인장이음은 슬래브처럼 횡보강근이 없는 경우도 있다. 그러나 압축이음이 적용되는 부재는 높은 축력이 작용되는 수직부재로, 압축 주근의 좌굴방지, 코어 콘크리트의 구속, 그리고 전단강도의 발현을 위해 횡보강근이 배근된다. 이를 활용함으로써 보다 경제적인 설계가 가능해진다. 본 연구에서는 실제 구조물에서 필연적으로 발생되는 횡방향 보강근에 대한 압축이음의 거동과 강도 특성을 실험을 통해 규명하고자 한다.

• 한국건설순환자원학회논문집
• /
• 제5권4호
• /
• pp.366-374
• /
• 2017

본 연구는 점토와 골재로 구성된 벽돌을 경화하는데 있어 효소 첨가제의 효과를 재료시험과 이미지 프로세싱을 통해 분석하였다. 벽돌의 강도와 밀도 시험에 사용한 벽돌 샘플의 점토/골재 중량비는 70/30, 60/40, 50/50, 40/60, 30/70이였으며, 최대 압축강도와 휨강도는 각각 5MPa와 1.25MPa으로 중량비 60/40에서 발현되었다. 또한 최대 건조단위 중량은 $2.073g/cm^3$으로 중량비 50/50에서 발현되었다. 시험 결과 전반적으로 벽돌의 강도는 효소를 첨가함으로 약 27% 향상되었다. 강도 향상을 위해서는 점토/골재 중량비 60/40, 밀도 향상을 위해서는 점토/골재 중량비 50/50에 효소를 첨가하여 벽돌을 경화하는 것이 효과적인 것으로 확인되었다. 효소 첨가 시 점토-골재 벽돌의 결합구조가 더 치밀해짐을 SEM-EDX 분석과 Matlab을 이용한 이미지 프로세싱을 통해 확인하였으며, 이를 통해 효소가 점토와 골재 간 결합구조를 형성하여 벽돌의 강도와 밀도를 향상시키는 효과가 있는 것으로 판단된다.

• 한국진공학회지
• /
• 제7권4호
• /
• pp.328-333
• /
• 1998

저압 유기금속 화학증착법을 이용하여 (001) InP 기판 위에 격자 일치된 InAlAs 에 피층 성장 결과 620~$700^{\circ}C$범위에서 성장 온도가 증가할수록 산소 유입량의 감소 때문으로 생각되는 광학적 성질의 향상이 관찰되었으나 $750^{\circ}C$이상의 고온에서는 InP완충층의 열화에 의한 결정성의 감소가 발견되었다. 또한, AsH3의 유량이 증가됨에 따라 성장된 InAlAs층의 Al함유량이 증가하는 현상이 관찰되었고, 이는 Al-As와 In-As의 bond strength 차이로 설 명하였다. InGaAs/InAlAs 단일 양자우물구조에서 측정된 우물두께에 따른 photoluminescence peak energy는 계산 값과 잘 일치하였고, high resolution x-ray diffraction 측정을 통하여 뚜렷한 satellite peak와 fine thickness fringe들이 관찰되는 우수 한 계면특성을 가지는 다중 양자우물구조가 성장됨을 확인하였다.

• 대한화학회지
• /
• 제40권4호
• /
• pp.264-272
• /
• 1996

ASED-MO(Atom Superposition and Electoron Delocalization-Molecular Orbtal)이론을 이용하여 Pt(lll)과 ${\upsilon}-Al_2O_3$(III) 표면 모델에 대한 계면간 결합 세기에 관해 연구하였다. $Al^{3+}$의 환원 정도가는 알루미나 뭉치(cluster)에 대한 산소와 알루미늄의 비에 따라 달라진다. $Al^{3+}$의 환원 정도가 크면 클수록 Pt 원소들에 대해 강한 결합 에너지를 가진다. 산소로 덮인 ${\gamma}-Al_{20}_3$(III) 표면과 Pt 계면간 결합이 매우 약하지만 백금의 산화 조건에서의 결합은 매우 강하다. 백금 표면에서 부분적으로 빈 O-2p 띠(band)와 $Al^{3+}$ dangling surface orbital로 전하가 이동하는 전하이동(charge transfer) 메카니즘에 의해 백금과 알루미나 계면간 결합은 가능하다.

• 대한치과교정학회지
• /
• 제27권5호
• /
• pp.771-779
• /
• 1997

본 연구의 목적은 법랑질 표면에 대한 산부식시간의 차이가 법랑질 표면의 부식형태, 교정장치의 전단접착강도 및 탈락 양상에 미치는 영향을 알아보는 것이다. 교정치료를 위해 발거된 하악 소구치의 법랑질을 $37\%$ 인산 용액을 이용하여 동일한 방법으로 각각 5, 10, 15, 30, 45, 60, 90, 120초 동안 부식시킨 후 법랑질 표면을 주사전자현미경으로 관찰하고, 교정장치를 접착한 후 Instron universal testing machine을 이용하여 전단접착강도를 측정하고 교정장치의 탈락 양상을 관찰하여 다음과 같은 결론을 얻었다. 1. 산부식시간을 5-120초 범위에서 변화시켜도 교정장치의 전단접착강도는 통계학적으로 유의성 있는 차이가 없었다(p<0.05). 2. 산부식시간에 따른 교정 장치의 탈락 양상은 15초 이하 부식군(5, 10, 15초)과 30초 이상 부식군(30, 45, 60, 60, 120초) 사이에 차이가 있었다. 즉, 15초 이하 부식군에서는 접착제/법랑질 경계부 탈락이 상대적으로 많았으나, 30초 이상 부식군에서는 접착제/교정장치 경계부 탈락이 많았다. 3. 법랑질 표면의 부식형태는 매우 다양하였으며 동일한 법랑질 표면에서도 여러 가지 형태의 부식 소견이 관찰되었다. 또한 법랑질 부식형태와 교정장치의 접착강도 사이에 연관성을 발견할 수 없었다. 4. 본 연구의 결과는 실험적 조건에서는 부식시간을 5초로 단축하여도 임상적으로 유용한 접착강도를 얻을 수 있음을 보여주고 있다. 그러나, 15초 이하 부식군에서 나타난 탈락 양상에 대해서는 더 많은 연구가 이루어져야 할 것으로 여겨진다.

• Restorative Dentistry and Endodontics
• /
• 제26권5호
• /
• pp.409-417
• /
• 2001

상아질접착제의 광조사가 상아질접착에 미치는 영향을 알아보기 위하여 in vitro에서 접착실험을 하였다. 120개의 발거된 소의 전치 협면 상아질을 노출시키고 산 부식 한 다음 self-priming형 상아질접착제 Prime&Bond$^{\circledR}$NT (Dentsply DeTrey, GmbH, Konstanz, Germany)를 도포 하였으며 600 mW/$\textrm{cm}^2$의 일반광도 또는 1930 mW/$\textrm{cm}^2$의 초고광도 광조사를 각각 20초 및 3초간 시행한 군과 시행하지 않은 군으로 나누어 복합레진 첨가후 광조사하였다. 접착제에 대한 광조사를 시행하지 않은 경우에는 복합레진 첨가 후 초고광도로 3초, 6초 및 12초간 광조사하였다. 접착양상 평가를 위해 만능시험기로 전단접착강도를 측정하고 파단면을 입체 현미경으로 관찰한 바를 일원 및 이원 변량분석법과 카이제곱검사법으로 통계 분석하여 다음과 같은 결과를 얻었다. 1. 상아질접착제를 광조사한 군이 광조사하지 않은 군에 비해 유의하게 높은 전단접 착강도를 나타내었다 (p<0.05). 2. 일반 광도 및 초고광도 광조사에 따른 전단접착강도에는 유의한 차이가 나타나지 않았다 (p>0.05). 3. 상아질접착제를 광조사하지 않고 복합레진 첨가 후 초고광도로 광조사한 군간에 조사시간에 따른 전단접착강도에는 유의 한 차이가 나타나지 않았다 (p>0.05). 4. 파단면 관찰 결과, 모든 군에서 접착계면에서의 파절을 포함하는 혼합파단양상이 가장 많이 나타났으며 군간에는 유의한 차이가 없었다 (p>0.05).