The photopolymerization efficiency and surface hardness of composite resin containing 1,2-phenylpropanedione (PD) and diacetyl (DA) as photoinitiators were studied by IR and Vickers hardness and the results were compared with that of camphorquinone (CQ). Relative photopolymerization efficiency of the photoinitiators increased in the order of DA < CQ < PD. Vickers hardness of composite resin containing the photoinitiators increased in the order of CQ < PD < DA. Thus, PD is a new visible light photoinitiator for dental composite resin with higher photopolymerization efficiency and surface hardness than that of CQ. Mechanical properties such as Vickers hardness, diametral tensile strength, and flexural strength of the experimental resin composite prepared by addition of the photosensitizer into a resin of bis-GMA improved with increasing the photosensitizer content and irradiation time. The resin composite of bis-GMA containing DA or PD shows better mechanical properties than that of CQ.

• Journal of Technologic Dentistry
• /
• v.26 no.1
• /
• pp.49-58
• /
• 2004

Two diketones, 1-phenyl-1,2-propanedione(PD) and 2,3-butanedione (BD) were investigated as new visible light photosensitizers for a dental resin composite of bis-GMA in order to improve photopolymerization effect. And the photopolymerization efficiency of mixed photosensitizers, PD-CQ and DA-CQ, was studied. Photopolymerization effect of photosensitizers were compared with that of camphorquinone(CQ), the most widely used photosensitizer. The photopolymerization efficiency of bis-GMA containing the photosensitizer increased with irradiation time. The increase was in the order: BD < CQ < PD. The photopolymerization efficiency of this mixture was not so efficient as CQ or PD.

• Restorative Dentistry and Endodontics
• /
• v.24 no.4
• /
• pp.604-613
• /
• 1999

This study was performed to evaluate the effect of resin and filler type on the fracture toughness of light-activated composites. Experimental composites were prepared using urethane tetramethacrylate(UTMA) and bisphenol glycidylmethacrylate(Bis-GMA) monomers and five different types of silica fillers. Fracture toughness was measured by a single edge V-notched beam(SEVNB) method, which was discussed from ASTM E399-78. Rectangular bars of $2.5{\times}5{\times}26mm$ were prepared with experimental composites and a notch about 2.25mm deep was carved at the center of the long axis of the specimen using a dental diamond disk driven by a dental micro engine. The flexural test was carried out at a crosshead speed of 0.05mm/min and fracture surfaces were observed under scanning electron microscope. The results obtained were summarized as follows: 1. The fracture toughness values of UTMA-based composites were relatively higher than those of Bis-GMA-based composites. 2. The highest fracture toughness value was observed in the UTMA-based composite containing the $1.5{\mu}m$-spherical fillers. 3 Aging in the distilled water at $37^{\circ}C$ for 10 days showed the increase of fracture toughness, which was severer in the Bis-GMA-based composites than those of UTMA-based composites. 4. The AE amplitude occurring during the fracture toughness tests was the highest at the point of macroscopic fracture.

• Journal of the Korean Applied Science and Technology
• /
• v.26 no.3
• /
• pp.263-268
• /
• 2009

Superporous Hydrogels (SPHs) have been extensively investigated for various biomedical applications due to their fast swelling and superabsorbent properties. In this study, glycol chitosan that is one of most abundant natural polymers was used as a cross-linking agent instead of bisacrylamide (BIS), which is a broadly used crosslinking agent for preparation of SPHs. Glycol chitosan was modified to have reactive vinyl groups by chemical conjugation with glycidyl methacrylate (GMA). The vinyl group-containing glycol chitosan (GC-GMA) was characterized by FT-IR and $^1H$-NMR measurements. SPHs have been prepared in various synthetic conditions to establish the optimum synthetic process for making superporous structure, where the inner pores are interconnected to each other to form a open channel structure. Various SPHs with different GC-GMA contents have been successfully prepared and have been observed to show faster swelling properties than other conventional SPHs. From the study on the swelling behavior of SPHs, the GC-GMA content is considered to be an important factor for controlling their swelling properties.

• Polymer(Korea)
• /
• v.33 no.2
• /
• pp.153-157
• /
• 2009

The resin matrix in the dental composite is generally composed of 2,2-bis[4-(2-hydroxy-3-methacryloyloxy propoxy) phenyl] propane (Bis-GMA) as a base resin and triethylene glycol dimethacrylate (TEGDMA) as a diluent for the reduction of viscosity. The applications of dental composite were often limited in dentistry due to the relatively large amounts of volumetric shrinkage during polymerization and water uptake caused by the addition of TEGDMA to the resin matrix. In this study, in order to solve problems stemmed from the TEGDMA by reducing amount of diluent added to resin matrix, diethylene glycol dimethacrylate (DEGDMA) and ethylene glycol dimethacrylate (EGDMA) were explored as new diluents. A decrease in the volumetric shrinkage and an increase in the mechanical strength were observed by replacing TEGDMA in the dental composite to DEGDMA (or EGDMA). Reduction in the mechanical strength of the dental composite containing DEGDMA (or EGDMA), was not serious in comparison with that of the dental composite containing TEGDMA after water uptake.

• Restorative Dentistry and Endodontics
• /
• v.27 no.1
• /
• pp.77-86
• /
• 2002

Current composites are made with dimethacrylate monomers and silane-treated silica microfillers, either alone or with silane treated glass fillers The main reasons for clinical failure of dental composites are secondary caries, wear and fracture. Most of practitioner want to get a composite which is more tougher under occlusal stress, less polymerization contraction, and better handling properties in application clinically. The aim of this study was to investigate the influence of resin matrix with various flows on the physical proper-ties such as fracture toughness and degree of conversion of the experimental resins. It was hypothesized that flexible or tough resin composites can be designed by judicious choice of monomer composition Various flow resin matrices containing Bis-GMA, UDMA, and TEG-DMA were made by altering the pro-portion of the monomers. After the unfilled resins were light-cured for different light intensity, the fracture toughness(K$_{1c}$) was measured according to ASTM standard using the single edge notched geometry, and degree of conversion(DC) was measured by FTIR. And experimental composites were formulated with variations in the proportion of silanated quartz and strontium glass fillers as 60, 75, and 77wt%. Also, the physical properties of composites with various filer contents were evaluated as same manner. All resulting data were compared by ANOVA/Tukeys test at 0.05 level. The results were as follows; 1. The degree of conversion of high flow resin containing less Bis-GMA was higher than that of low flow unfilled resin 2. While the degree of conversion of unfilled resin was increased according to light intensity for polymerization, there was no significant increase with moderate and high light intensity. Also, the fracture toughness was not increased by high light intensity. 3. The fracture toughness was high in the low flow unfilled resin containing higher contents of Bis-GMA. 4. There was a significant increase for fracture toughness and a tendency for degree of conversion to be reduced when the content of fillers was increased. 5. In the experimental composites, the flow of resin matrix did not affected on the fracture toughness, even, which was decreased as increase of viscosity. These results showed that the physical properties of a dental composite could be attributed to the flow of resin matrix with relative content of monomers. Specific combination of resin monomers should be designed to fulfil the needs of specific indication for use.

• Journal of the Korean Chemical Society
• /
• v.61 no.6
• /
• pp.346-351
• /
• 2017

This study was planned considering the chain length, hydrophilicity, and hydrophobicity of the additives to be used in the polymerization, while various ophthalmic lenses that use various additives with similar water contents were manufactured before their optical and physical properties were compared and analyzed. With regard to the additives required for manufacturing high-, medium-, and low-water content lens groups, HEA (hydroxyethyl acrylate), PVP (polyvinylpyrrolidone), and NMV(N-methyl-N-vinylacetamide) were used as additives for preparing the high-water content lens group, HEMA(2-hydroxyethyl methacrylate), HPMA(hydroxypropyl methacrylate) and BD(1,4-butanediol) were used for the medium-water content lens group. For the low-water content lens group, BMA(buthyl methacrylate), BDDA(1,4-butanediol diacrylate), and Bis-GMA(bisphenol A glycerolate diacrylate) were used, respectively. The average water content of HEA was 40.14%; that of PVP, 39.63%; and that of NMV, 40.52%. The mean of water content was 35.92% for HEMA, 35.74% for BD, and 34.62% for HPMA. For the low-water content lens group, the mean of water content was 26.69% for BMA, 27.76% for BDDA, and 26.14% for Bis-GMA. With regard to the results of the water content measurement using a moisture analyzer, the average water content of the high-water content lens group was 41.34% for HEA, 42.62% for PVP, and 42.73% for NMV. Finally, for the low-water content lens group, the average water content was 28.62% for BMA, 28.82% for BDDA, and 28.32% for Bis-GMA. The measurements of the water contents of the lenses using the two methods showed that the water content and refractive index of the lenses were similar in all the lens groups. The measurements of the contact angles, however, showed a different wettability value for each lens with a similar water content. Also, the change tendency of the lens curvature according to the change of time showed that the change amount became larger and the recovery time became longer from the lens samples with a lower water content to those with a higher water content. Based on these results that will be helpful for the study of ophthalmic lenses.

• Restorative Dentistry and Endodontics
• /
• v.13 no.1
• /
• pp.53-67
• /
• 1988

An investigation was carried out to compare the pulp responses against a few type of composite and streptococcus mutans contamination under the zinc oxide eugenol cement, and also confirmed pulpal responses of various composites with or without base. Seventy eight teeth from 6 dogs were employed and divided into 6 groups. Class V cavities were prepared on each tooth routinely with low speed dental engine. Paper disc about 0.3mm thick was immersed in the BHI broth in which streptococcus mutans had been enriched and the disc was inserted on the cavity floor prior to filling. Scotch bond puls Silux as Bis-GMA system composite resin and Helimolar as urethane system composite resin were adopted. Control group: Zinc-Oxide Eugenol cement filling Experimental groups: Group 1. Scotch bond + Silux filling with Dycal base Group 2. Heliomolar filling with Dycal base Group 3. Scotch bond + Silux filling without base Group 4. Heliomolar filling without base Group 5. Streptococcus mutans application. All cavities were sealed with thick ZOE cement to avoid marginal leakage. Postoperative intervals of 1, 2, 3, 4, 5 and 6 weeks teeth were carefully extracted, processed and stained with Hematoxylin and Eosin. The results were as follows: 1. S. mutans application group and composites without any base showed more severe pupal response than control group and dyca based groups. 2. The experimental group of S. mutans application showed severe response in the early stage compared to the two groups of composite resin without base, but no significant difference was found following periods. 3. The difference of pulpal response is not significant between Bis-GMA system and urethane system. 4. Streptococcus mutans application group and composites without base groups showed the evidence of histologic recovery at the six week cases and the large amount of reparative dentin was the prominent feature. 5. Pulp responses against every material were inclined to normal according to the time elapsed.

• Restorative Dentistry and Endodontics
• /
• v.10 no.1
• /
• pp.135-144
• /
• 1984

This study was undertaken to evaluate the degree of the marginal leakage of composite restoration with 3 brands of dental adhesives by means of the dye penetration at the enamel and dentinal margins. 150 cavities of class V were prepared on the buccal and lingual surfaces of 75 extracted anterior and premolar teeth, which were devided into 3 groups. The cavities were filled with composite resin, Silar$^{(R)}$ (3M) and Heliosit$^{(R)}$ (Vivadent) after application of the dental adhesives, specifically Scotchbond$^{(R)}$ (3M) which is essentially composed with halophosphorus ester of Bis-GMA, Dentin Adhesit$^{(R)}$ (Vivadent) which is polyurethane resin, and Enamel Bond$^{(R)}$ (3M) which is a product of Bis-GMA with low viscosity at internal surfaces and margins of the cavities. All specimens were immersed in $37^{\circ}C$, 0.5% methylene blue solution for 24 hours after thermocycling at $4^{\circ}C$ and $60^{\circ}C$, embedded in acrylic resin, and sectioned with diamond disk into two parts. The sectioned specimens observed with the light microscope. The following results were obtained: 1. The group filled with Scotchbond$^{(R)}$-Silar$^{(R)}$ the other two groups at the enamel margins. 2. No significant difference in the degree of the marginal leakage had appeared between Dentin Adhesit$^{(R)}$-Heliosit$^{(R)}$ group an d Enamel Bond$^{(R)}$-Silar$^{(R)}$ group at the enamel margins. 3. Severe marginal leakage with penetration of dye to the floor of cavity had appeared from the all three groups and no significant difference in the degree of marginal leakage existed between the three groups at the dentinal margins.