• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2006.11a
• /
• pp.374-375
• /
• 2006

The purpose of this paper is to investigate the propriety of biodegradable polymer pad in spite of exchanging from existing polyurethane pad used in CMP(Chemical Mechanical Planarization). Poli 400 of G&P Technology for CMP and Ellipsometer of Rudolph AutoEL-III for measurement were used in this experiment. From this experiment, it is proven that the biodegradable polymer pad is sufficiently suitable in CMP process. Therefore, it is expected that, by using the biodegrable pad CMP manufacturing process, and will be decreased. Especially, wafer scratch can be decreased.

• Elastomers and Composites
• /
• v.34 no.4
• /
• pp.292-298
• /
• 1999

Lactide oligomer with number averagae molecular weight of 460 was synthesized and reacted with poly(oxyteramethylene)glycol(PTMG, Mn = 650) to obtain oligolactide oligomer-terminated PTMG. Polyurethanes were synthesized from the oligolactide-terminated PTMG, 4,4'-diphenylmethane diisocyanate, and 1,4-butanediol. The mechanical and thermal properties of the polyurethanes and PTMG based polyurethane as control were measured by means of DSC and tensile tester. Degradation behavior of these polyurethanes put into a compost was evaluated by variation of mechanical properties, surface state, and weight loss. Modulus and weight significantly decreased with increasing time. The surface of the oligolactide polyurethane put into the compost during 6 weeks had a number of voids. On the other hand, These properties of the PTMG based polyurethane as control did not change. These results suggest that the novel polyurethanes incorporated oligolactide easily degrade under biodegradable condition.

• Laser Solutions
• /
• v.17 no.4
• /
• pp.14-19
• /
• 2014

Laser beam was applied on the boundary of the polyurethane and biodegradable polyacetate polymers. The distributed laser passed through the polyurethane layer and heated the polyacetate layer, then the soften acetate was squeezed thorough the 1mm square slots of polyurethane for the mechanical joining. The surface roughness ranging between $0.28{\mu}m$ and $3.06{\mu}m$ had almost no effect on joining strength, but the optical properties of HD (High Definition) and UHD (Ultra High Definition) mode affected laser beam transmittance. The optimum laser power was found to be between 8watt and 10watt with 500mm/min of scanning speed. The joining boundary was characterized by optical and SEM analysis. Based on the experiment and characterization results, the laser energy was effective for the polymer joining and efficiency of joining.

• Journal of Adhesion and Interface
• /
• v.20 no.4
• /
• pp.140-145
• /
• 2019

In view of environmental considerations, the control of carbon dioxide (CO₂) and volatile organic compounds (VOCs) is one of important issues in the film and coating industries. Therefore, UV-curable system has been developed due to minimize emissions of VOCs and reduce CO₂ emission due to low energy consumption from fast curing. Also, biodegradable polymers economically are attractive because of environmental and economic concerns associated with huge waste plastics. In this study, UV-curable polyurethane acrylates with different compositions of biodegradable polylactide (PLA) diol and poly(ethylene glycol) as diols were synthesized and curing reaction of their end-capped acrylates was performed by UV exposure. Tensile strength, elongation, and Tg of the UV-cured polyurethane acrylates increased with PLA diol content in the diol while their hydrophilicity and thermal stability increased with the PEG content. These results indicated a property of UV-cured polyurethane acrylates could be controlled by environment-friendly diols.

• Journal of Adhesion and Interface
• /
• v.17 no.1
• /
• pp.21-28
• /
• 2016

Foam-type biodegradable polyurethane adhesives were developed as a non-lethal weapon against illegal fishing boats. The adhesives were prepared from a hardener of polymeric methylene diphenyl diisocyanate (MDI) and a base composed of polyester and/or polyether polyols. In order to accelerate biodegradability, starch, dextrin, and amylase were added into the base, and which present about 34% degradability within 4 weeks confirmed by OECD 301C method. For proper mixing and corresponding prompt foam reaction, viscosities of hardener and base compositions were investigated in the temperature ranges from 0 to $50^{\circ}C$. For fast completion of the foam forming and corresponding adhesion, rising time was recorded in the same temperature range, and the rising time of the adhesive was varied within around 1 minute. T-peel adhesion tests with cotton fabrics were performed which showed 20.78 N/cm and 11.95 N/cm as the maximum and the average values, respectively.

• Korean Chemical Engineering Research
• /
• v.51 no.3
• /
• pp.382-387
• /
• 2013

Biodegradable polyurethane (PU)/clay nanocomposite films were prepared via extrusion compounding process followed by casting film process. Organically modified montmorillonite (denoted as C30B) with a large amount of hydroxyl groups on its surface was used for the formation of strong bonding with PU resin. From both XRD analysis and TEM observations, the intercalated and exfoliated structure, and dispersion state of silicate platelets in the compounded nanocomposite films were confirmed. In addition, the rheological and tensile properties, optical transparency, oxygen permeability of the prepared nanocomposites were investigated as a function of added nanoclay content, and moreover based on these results, the corelation between the morphology and the resulting properties of the nanocomposites could be presented. The inclusion of nanoclays at appropriate content resulted in remarkable improvement in the nanocomposite performance including tensile modulus, elongation, transparency, and oxygen barrier property, however at excess amount of nanoclays, reduction or very slight increase was observed due to poor dispersion. The biodegradability of the prepared nanocomposite film was evaluated by examining the deterioration in the barrier and tensile properties during degradation period under compost.

• Journal of Forest and Environmental Science
• /
• v.31 no.4
• /
• pp.297-302
• /
• 2015

With the intention to solve environmental problems caused by synthetic plastics from petroleum resources, biodegradable polyurethane foams and thermosetting moldings were prepared from biomass, such as wood and wheat bran by liquefaction method. Biodegradability of these biomass-based polymeric materials was investigated. In activated sludge, polyurethane foams from liquefied wheat bran and thermosetting molding from phenolated wood were decomposed approximately 14% and 29% for 20 days, respectively. One of the wood fungi, Coriolus versicolor was able to grow without supplemental nutrition, only with distilled water and polyurethane foam as a nutrition source. Risk assessments were also conducted and results showed that estrogenicity, mutagenicity, and carcinogenicity were not observed in the extractives of biomass- based polymeric materials.

• Archives of Plastic Surgery
• /
• v.42 no.2
• /
• pp.186-193
• /
• 2015

Background Polyurethane coating of breast implants has been shown to reduce capsular contracture in short-term follow-up studies. This 30-year study is the longest examination of the use of polyurethane-coated implants and their correlation with capsular contracture. Methods This study evaluates the senior surgeon's (F.D.P.) experience with the use of polyurethane-coated implants in aesthetic breast augmentation in 382 patients over 30 years. Follow-up evaluations were conducted for six months after surgery. After the six-month follow-up period, 76 patients returned for reoperation. The gross findings, histology, and associated capsular contracture were noted at the time of explantation. Results No patient during the six-month follow-up period demonstrated capsular contracture. For those who underwent reoperation for capsular contracture, Baker II/III contractures were noted nine to 10 years after surgery and Baker IV contractures were noted 12 to 21 years after surgery. None of the explanted implants had macroscopic evidence of polyurethane, which was only found during the first five years after surgery. The microscopic presence of polyurethane was noted in all capsules up to 30 years after the original operation. Conclusions An inverse correlation was found between the amount of polyurethane coating on the implant and the occurrence of capsular contracture. Increasingly severe capsular contracture was associated with a decreased amount of polyurethane coating on the surface of the implants. No contracture occurred in patients whose implants showed incomplete biodegradation of polyurethane, as indicated by the visible presence of polyurethane coating. We recommend research to find a non-toxic, non-biodegradable synthetic material as an alternative to polyurethane.

• Journal of Fashion Business
• /
• v.8 no.1
• /
• pp.141-155
• /
• 2004

Chitosan, the natural biodegradable polymer derived from chitin by de- acetylation, has been widely applied to the textile finishing processes for excellent anti-microbial characteristic and handle improvement of fabric. The purpose of this study is to investigate the change of handle when cotton fabric is treated with chitosan-polyurethane mixed solution. The viscosity values of chitosan solutions were 8cps and 50cps, and the wet-pick-up% was maintained at 90%. In case of mixing with water soluble polyurethane, the mixture ratio of chitosan and polyurethane was settled on the solid content ratio of 1:0, 1:0.5, 1:1, 1:2. Also the change of physical properties by neutralization in NaOH solution was studied. The results can be summarized up as follows : 1. Extensibility(EM) and tensile energy(WT) of cotton fabric treated with chitosan are decreased, but bending rigidity(B) is remarkably increased. With the addition of polyurethane, the decrease of EM and WT is weakened and the increase of B is weakened. The case of neutralization is similar to the case of polyurethane addition. 2. By treating fabric with chitosan, FUKURAMI(Fullness and softness) is decreased, but KOSHI(Stiffness), SHARI(Crispness), HARI(Anti-drape Stiff ness) are increased. With the addition of polyurethane, the decrease of FUKURAMI is diminished and the increase of KOSHI, SHARI, HARI are diminished. 3. As the viscosity of chitosan solution increased, the air permeability value increased. The addition of polyurethane decreased the air permeability.

• Polymer(Korea)
• /
• v.25 no.1
• /
• pp.41-48
• /
• 2001

Polyurethane(PU) microgels were synthesized from poly(caprolactone) diol(PCD) and/or poly(ethylene glycol)(PEG), diisocyanate and 1,2,6-hexane triol by solution polymerization method. A critical gelation concentration of the PU microgels with, mole ratios of PCD/PEG were the important factors influencing the formation and property microgel or macrogels. The physical and thermal properties of the PU microgels prepared with depending upon the structure of diisocyanate, mole ratio of PCD/PEG, and molecular weight of PEG were investigated. It was found that PU microgels were distributed by polydisperse, spherical small particles below 300nm and showed the properties of low viscosity.