The n-type $(95%Bi_2Te_3-5%Bi_2Se_3)$ compound was newly fabricated by gas atomization and hot extrusion, which is considered to be a mass production technique of this alloy. The effect of powder size on thermoelectric properties of 0.04% $SbI_3$ doped $95%Bi_2Te_3-5%Bi_2Se_3$ alloy were investigated. Seebeck coefficient $({\alpha})$ and Electrical resistivity $(\rho)$ increased with increasing powder size due to the decrease in carrier concentration by oxygen content. With increasing powder size, the compressive strength of $95%Bi_2Te_3-5%Bi_2Se_3$ alloy was increased due to the relative high density. The compound with ${\sim}300\;{\mu}m$ size shows the highest power factor among the four different powder sizes. The rapidly solidified and hot extruded compound using $200[\sim}300{\mu}m$ powder size shows the highest compressive strength.

• 한국분말야금학회:학술대회논문집
• /
• 한국분말야금학회 2006년도 Extended Abstracts of 2006 POWDER METALLURGY World Congress Part 1
• /
• pp.459-460
• /
• 2006

N-type $Bi_2Te_3-Sb_2Te_3$ solid solutions doped with 1$CdCl_2$ was prepared by melt spinning, crushing and vacuum sintering processes. Microstructure, bending strength and thermoelectric property were investigated as a function of the doping quantity from 0.03wt.% to 0.10wt.% and sintering temperature from $400^{\circ}C$ to $500^{\circ}C$, and finally compared with those of conventionally fabricated alloys. The alloy showed a good structural homogeneity as well as bending strength of $3.88Kgf/mm^2$. The highest thermoelectric figure of merit was obtained by doping 0.03wt.% and sintering at $500^{\circ}C$.

• 한국분말재료학회지
• /
• 제3권4호
• /
• pp.246-252
• /
• 1996

$Bi_{2}Te_{3}-Sb_{2}Te_{3}$, $Bi_{2}Te_{3}-Bi_{2}Se_{3}$ solid solutions are of great interest as materials for thermoelectric energy conversion. One of the key technologies to ensure the efficiency of thermoelectric device is to obtain chemically homogeneous solid solutions. In this work, the new process with rapid solidification followed by hot pressing was investigated to produce homogeneous thermoelectric materials. Characteristics of the materials were examined with XRD, SEM, EPMA-line scan and bending test. Property variations of the materials were investigated as a function of variables, such as excess Te quantity and hot pressing temperature. Quenched ribbons are very brittle and consisted of homogeneous $Bi_{2}Te_{3}$, $Sb_{2}Te_{3}$ solid solutions. When the process parameters were optimized, the maximum figure of merit was 3.073$\times$$10^{-3}K^{-4}$. The bending strength of the material, hot pressed at 45$0^{\circ}C$, was 5.87 kgf/${mm}^2$.

• 한국분말재료학회지
• /
• 제20권5호
• /
• pp.345-349
• /
• 2013

Carbon nanotube-dispersed bismuth telluride matrix (CNT/$Bi_2Te_3$) nanopowders were synthesized by chemical routes followed by a ball-milling process. The microstructures of the synthesized CNT/$Bi_2Te_3$ nanopowders showed the characteristic microstructure of CNTs dispersed among disc-shaped $Bi_2Te_3$ nanopowders with as an average size of 500 nm in-plane and a few tens of nm in thickness. The prepared nanopowders were sintered into composites with a homogeneous dispersion of CNTs in a $Bi_2Te_3$ matrix. The dimensionless figure-of-merit of the composite showed an enhanced value compared to that of pure $Bi_2Te_3$ at the room temperature due to the reduced thermal conductivity and increased electrical conductivity with the addition of CNTs.

• 한국분말재료학회지
• /
• 제23권2호
• /
• pp.126-131
• /
• 2016

The recent rise in applications of thermoelectric materials has attracted interest in studies toward the fabrication of thermoelectric materials using mass production techniques. In this study, we successfully fabricate n-type $Bi_2Te_{2.7}Se_{0.3}$ material by a combination of mass production powder metallurgy techniques, gas atomization, and spark plasma sintering. In addition, to examine the effects of hydrogen reduction in the microstructure, the thermoelectric and mechanical properties are measured and analyzed. Here, almost 60% of the oxygen content of the powder are eliminated after hydrogen reduction for 4 h at $360^{\circ}C$. Micrographs of the powder show that the reduced powder had a comparatively clean surface and larger grain sizes than unreduced powder. The density of the consolidated bulk using as-atomized powder and reduced atomized powder exceeds 99%. The thermoelectric power factor of the sample prepared by reduction of powder is 20% better than that of the sample prepared using unreduced powder.

• 한국분말야금학회:학술대회논문집
• /
• 한국분말야금학회 2006년도 Extended Abstracts of 2006 POWDER METALLURGY World Congress Part2
• /
• pp.1223-1224
• /
• 2006

The p-type $(Bi_{0.2}Sb_{0.8})_2Te_3/(Pb_{0.7}Sn_{0.3})$Te functional gradient material (FGM) was fabricated by hot-pressing the mechanically alloyed $(Bi_{0.2}Sb_{0.8})_2Te_3$ and the 0.5 at% $Na_2Te-doped$ $(Pb_{0.7}Sn_{0.3})Te$ powders. Also, the n-type $Bi_2(Te_{0.9}Se_{0.1})_3/PbTe$ FGM was processed by hot-pressing the mechanically alloyed $Bi_2(Te_{0.9}Se_{0.1})_3$ and the 0.3 wt% Bi-doped PbTe powders. With ${\Delta}T$ larger than $300^{\circ}C$, the p-type $(Bi_{0.2}Sb_{0.8})_2Te_3/(Pb_{0.7}Sn_{0.3})Te$ FGM exhibited larger thermoelectric output power than those of the $(Bi_{0.2}Sb_{0.8})_2Te_3$ and the 0.5 at% $Na_2Te-doped$ $(Pb_{0.7}Sn_{0.3})Te$ alloys. For the n-type $Bi_2(Te_{0.9}Se_{0.1})_3/PbTe$ FGM, the thermoelectric output power superior to those of the $Bi_2(Te_{0.9}Se_{0.1})_3$ and the 0.3 wt% Bi-doped PbTe was predicted at ${\Delta}T$ larger than $300^{\circ}C$.

• 한국분말재료학회지
• /
• 제5권1호
• /
• pp.50-56
• /
• 1998

A new process using rapid solidification (melt spinning method) followed by pressing and sintering was investigated to produce the n-type thermoelectric ribbons of 90% $Bi_2Te_3$+10% $Bi_2Se_3$ doped with $CdCl_2$. Quenched ribbons are very brittle and consisted of homogeneous $Bi_2Te_3-Bi_2Se_3$ pseudo-binary solid solutions. Property variations of the materials was investigated as a function of variables, such as dopant $CdCl_2$ quantity and sintering temperature. When the process parameters were optimized, the maximum figure of merit was $2.146{\times}10^{-3}K^{-1}$.

• 한국분말재료학회지
• /
• 제17권6호
• /
• pp.494-498
• /
• 2010

The p-type thermoelectric compounds of $Bi_2Te_3$ based doped with 3wt% Te were fabricated by a combination of rapid solidification and spark plasma sintering (SPS) process. The effect of holding time during spark plasma sintering (SPS) on the microstructure and thermoelectric properties were investigated using scanning electron microscope (SEM), X-ray diffraction (XRD) and thermoelectric properties. The powders as solidified consisted of homogeneous thermoelectric phases. The thermoelectric figure of merit measured to be maximum ($3.41{\times}10^{-3}/K$) at the SPS temperature of $430^{\circ}C$.

• 한국분말야금학회:학술대회논문집
• /
• 한국분말야금학회 2006년도 Extended Abstracts of 2006 POWDER METALLURGY World Congress Part 1
• /
• pp.77-78
• /
• 2006

• 한국표면공학회지
• /
• 제50권2호
• /
• pp.114-118
• /
• 2017

Bismuth telluride ($Bi_2Te_3$) and its alloys are well-known thermoelectric materials for ambient temperature applications. In this study, the dissolved Bi-Te precursor solution was used to synthesis metallic $Bi_2Te_3$ powder via ultrasonic spray pyrolysis and reduction process. The droplets of the Bi-Te precursor solution were decomposed to Bi-Te oxide powders by ultrasonic spray pyrolysis. The spherical $Bi_2Te_3$ powders were synthesized by reduction reaction in atmosphere of hydrogen gas at the temperature above $375^{\circ}C$ for 6h. The reduced $Bi_2Te_3$ powders have a mean particle size of $1.5{\mu}m$. The crystal structure of the powder was evaluated by X-Ray diffraction(XRD), and the microstructure with size and shape powders was observed by fieldemission scanning electron microscope(FE-SEM) and transmission electron microscope(TEM).