• Journal of the Korea Furniture Society
• /
• v.25 no.3
• /
• pp.223-232
• /
• 2014

To make metalized wood composites of 10 different korean wood species, it was tested by Low temperature melting Bi-Sn alloy injection method at high temperature and high pressure condition. Metalized wood composite of each wood species had light ash color, but still maintained its own natural wood grain and wood figures. It was evaluated on coating properties. Furthermore, it also was check on effect of coating as like a changes of main color, wood grain and wood figures. The results of test were following as; a coating properties as like a cold resistance, heat resistance, acid resistance, alkali resistance, durability of abrasion, and cross-cut test was proper on the conditions of the KS standard. And, In aspect of color changes, the metalized wood composites of 10 different korean wood species had a light ash color, but still maintained its own natural wood grain and wood figures. Also, the more weight per gain of alloy is, the more grey background of metalized wood composite is.

• ETRI Journal
• /
• v.38 no.6
• /
• pp.1163-1171
• /
• 2016

Integration technologies involving flexible substrates are receiving significant attention owing the appearance of new products regarding wearable and Internet of Things technologies. There has been a continuous demand from the industry for a reliable bonding method applicable to a low-temperature process and flexible substrates. Up to now, however, an anisotropic conductive film (ACF) has been predominantly used in applications involving flexible substrates; we therefore suggest low-temperature lead-free soldering and bonding processes as a possible alternative for flex-on-flex applications. Test vehicles were designed on polyimide flexible substrates (FPCBs) to measure the contact resistances. Solder bumping was carried out using a solder-on-pad process with Solder Bump Maker based on Sn58Bi for low-temperature applications. In addition, thermocompression bonding of FPCBs was successfully demonstrated within the temperature of $150^{\circ}C$ using a newly developed fluxing underfill material with fluxing and curing capabilities at low temperature. The same FPCBs were bonded using commercially available ACFs in order to compare the joint properties with those of a joint formed using solder and an underfill. Both of the interconnections formed with Sn58Bi and ACF were examined through a contact resistance measurement, an $85^{\circ}C$ and 85% reliability test, and an SEM cross-sectional analysis.

• Journal of the Microelectronics and Packaging Society
• /
• v.20 no.2
• /
• pp.17-22
• /
• 2013

We investigated the optimum bonding conditions for thermo-compression bonding of electrodes between flexible printed circuit board(FPCB) and rigid printed circuit board(RPCB) with Sn-58Bi solder as interlayer. In order to figure out the optimum bonding conditions, peel test of FPCB/RPCB joint was conducted. The peel strength was affected by the bonding conditions, such as temperature and time. The fracture energies were calculated through F-x (Force-displacement) curve during peel test and the relationships between bonding conditions and fracture behaviors were investigated. The optimum condition for the thermo-compression bonding with Sn-58Bi solder was found to be temperature of $195^{\circ}C$ and time of 7 s.

• Journal of Welding and Joining
• /
• v.31 no.3
• /
• pp.4-10
• /
• 2013

In electronic industry, the trend of future electronics will be flexible, bendable, wearable electronics. Until now, there is few study on bonding technology and reliability of bonding joint between chip with micro solder bump and flexible substrate. In this study, we investigated joint properties of Si chip with eutectic Sn-58Bi solder bump on Cu pillar bump bonded on flexible substrate finished with ENIG by flip chip process. After flip chip bonding, we observed microstructure of bump joint by SEM and then evaluated properties of bump joint by die shear test, thermal shock test, and bending test. After thermal shock test, we observed that crack initiated between $Cu_6Sn_5IMC$ and Sn-Bi solder and then propagated within Sn-Bi solder and/or interface between IMC and solder. On the other hands, We observed that fracture propated at interface between Ni3Sn4 IMC and solder and/or in solder matrix after bending test.

• Proceedings of the Korean Institute of Surface Engineering Conference
• /
• 2012.05a
• /
• pp.150-150
• /
• 2012

본 연구는 1차원 나노 구조의 합성과 기초적 분석에 관한 연구로써 특히 무기 산화물 나노재료를 그 대상으로 하였다. 내용으로는 첫째, 1차원 코어 나노와이어의 합성을 하였고 Thermal evaporation, substrate의 가열, 그리고 MOCVD 를 사용한 결과들을 나열한다. 둘째, 코어-쉘 나노와이어를 제작하기 위하여 특히 쉘층의 제작방법을 연구하였는데 PECVD, ALD, 그리고 sputtering에 의한 결과들을 나열하고 간단히 설명한다. Thermal evaporation에 의한 1차원 나노와이어 합성의 경우는 MgO의 예를 들었는데 MgO 나노와이어는 Au가 증착된 기판을 열처리하여 Au dot를 형성하고 이의 morphology를 조절하여 최적의 나노와이어 합성조건을 선정하였다. 이로써 기판 morphology가 나노선의 성장및 형상에 영향을 준다는 사실을 알게 되었다. 이 사실은 In2O3기판을 사용하고 이의 표면거칠기를 열처리로 조절하므로써 역시 나노와이어의 성장을 촉진하는 방법을 찾아내었다. 또한 thermal evaporation공법은 source분말의 선택에 따라 다양한 소재를 제작가능하다는 결과를 제시하였다. 예를 들면 SiOx 층이 precoating된 chamber내에서 MgO 나노선을 합성하는 것과 동일한 조건으로 실험을 진행하면 Mg2SiO4 나노와이어가 형성된 것을 확인하였다. 또한 Sn과 MgB2 분말을 함께 적용할 경우 Sn tip을 가진 MgO 나노와이어를 얻을 수 있었다. 이는 Sn이 동시에 촉매의 역할을 하였기 때문일 것으로 추정된다. 한편 Sn과 Bi 혼합분말을 적용한 경우 Bi2Sn2O7 신소재 tip을 포함한 SnO2 나노와이어를 얻을 수 있었다. 이 경우 Bi원자가 적절한 촉매의 역할을 수행한 것으로 사료된다. Substrate의 가열공법에서는 Si wafer상에 각종 금속 즉 Au, Ag, Cu, Co, Mo, W, Pt, Pd등 초박막을 DC sputter 로 형성한후 annealing하는 기술을 사용하였다. 특기할 만한 것은 Co를 사용한 경우 나노와이어의 spring구조를 얻을 수 있었다는 점이다. MOCVD에 의하여는 Ga2O3및 Bi2O3 나노와이어를 비교적 저온에서 합성하였고 In2O3의 경우는 독특한 나노구조를 형성하였고 이의 결정학적 특성에 대하여 조사하였다.

• Korean Journal of Materials Research
• /
• v.15 no.1
• /
• pp.14-18
• /
• 2005

Ni-Cr-Sn-Bi alloys were prepared by air melting and sand casting method and their anti-galling behaviors were examined. Anti-galling properties were dominantly influenced by Bi-rich low temperature precipitates. Alloying effects on the anti-galling properties were investigated for several alloying elements to improve anti-galling properties of the alloy. An alloy with $1-3wt\%$ of Te showed markedly improved anti-galling properties. Metallographic and tribological tests were carried out to find out reasons for excellent properties. It was found that Te containing alloy has finely distributed precipitates of Bi-rich phase. The addition of Te changed the morphology of the Ni-rich primary phase from globular to fine dendritic. As a result, the anti-galling phase precipitated between dendrite arms with fine distribution showed excellent anti-galling properties.

• Journal of Welding and Joining
• /
• v.30 no.5
• /
• pp.64-69
• /
• 2012

Sn-Bi eutectic alloy has been widely used as one of the key solder materials for step soldering at low temperature. The Sn-58Bi solder paste containing chloride flux was adopted to compare with that using the chloride-free flux. The paste was applied on the electroless nickel-immersion gold (ENIG) surface finish by stencil printing, and the reflow process was then performed at $170^{\circ}C$ for 10 min. After reflow, the solder joints were aged at $125^{\circ}C$ for 100, 200, 300, 500 and 1000 h in an oven. The interfacial microstructures were obtained by using scanning electron microscopy (SEM), and the composition of intermetallic compounds (IMCs) was analyzed using energy dispersive spectrometer (EDS). Two different IMC layers, consisting of $Ni_3Sn_4$ and relatively very thin Sn-Bi-Ni-Au were formed at the solder/surface finish interface, and their thickness increased with increasing aging time. The wettability of solder joints was investigated by wetting balance test. The mechanical property of each aging solder joint was evaluated by the ball shear test in accordance with JEDEC standard (JESD22-B117A). The results show that the highest shear force was measured when the aging time was 100 h, and the fracture mode changed from ductile fracture to brittle fracture with increasing aging time. On the other hand, the chloride flux in the solder paste did not affect the shear force and fracture mode of the solder joints.

• Proceedings of the Korean Institute of Surface Engineering Conference
• /
• 2018.06a
• /
• pp.81-81
• /
• 2018

Bi-Te계 열전소자는 상온에서의 열전 효율이 우수하기 때문에 항공, 컴퓨터 등의 열전발전 또는 열전냉각 모듈에 널리 사용된다. 이 열전소자를 활용한 열전모듈은 다수의 n형 및 p형 열전소자가 세라믹 위에 형성된 Cu 전극에 전기적으로 직렬이 되도록 서로 솔더링 접합이 되어 있는 구조를 가지고 있다. 이처럼 직렬 연결된 방식에서는 높은 접합강도를 필요로 한다. 열전모듈 제작 시 Bi-Te 계 소자를 바로 Cu 기판에 접합시키면 솔더에 들어있는 Sn과 기판의 Cu가 접합하는 과정에서 소재 내로 확산하여 접합강도를 저하시킨다. 이러한 열전모듈의 접합강도 저하를 막기 위해 무전해 Ni-W-P 도금층을 확산 방지층으로 적용하였다. 본 연구에서는 Ni-W-P 도금이 Bi-Te 계 열전 모듈의 접합강도에 미치는 영향을 조사하였다. 본 연구에서는 Bi-Te계 열전소자에 양호한 밀착성을 가지는 Ni-W-P 도금층을 형성시키기 위해서 알루미나 분말을 이용한 sand-blasting 방법을 사용하여 Bi-Te 소재 표면에 분사하는 방법으로 표면을 거칠게 하였다. 그 후 무전해 Ni-W-P 도금을 $85^{\circ}C$에서 20분간 실시하여 약 4um의 Ni-W-P 도금층을 형성시켰다. 열전 모듈은 Sn-Ag-Cu 솔더를 사용하여 제작하였으며 접합강도는 Bonding tester를 사용하여 측정하였다. 제작한 열전 모듈의 단면 및 파단면 관찰을 통하여 접합강도가 변하는 요인을 조사하였다. 제작한 열전 모듈의 단면을 FE-EPMA로 관찰한 결과 Ni-W-P 도금층이 Bi-Te 소자와 Sn과 Cu사이의 확산을 방지하는 확산방지층 역할을 하는 것을 관찰할 수 있었다. 또한 열처리 전 열전모듈과 200도, 150시간 열처리 후 접합강도를 각각 측정해 본 결과, 열처리 후의 접합강도가 상승하는 것을 확인 할 수 있었다. 따라서 Bi-Te계 열전모듈 제작에 무전해 Ni-W-P 도금층을 형성시키므로 인해 확산방지층의 생성과 접합강도의 상승에 도움을 주었다.

• Journal of the Microelectronics and Packaging Society
• /
• v.7 no.2
• /
• pp.47-53
• /
• 2000

The fluxless wetting properties of TSM-coated glass substrate were evaluated by the wetting balance method. We could estimate the wettability of the TSM with new parameters obtained from the wetting balance test for one side-coated specimen. It was more effective in wetting to use Cu as a wetting layer and Au as a protection layer than to use Au itself as a wetting layer. The SnSb solder showed better wettability than SnAg, SnBi, and SnIn solders. The contact angle of the one side-coated glass substrate to the Pb-free solders could be calculated from the farce balance equation by measuring the static force and the tilt angle.

• Journal of Welding and Joining
• /
• v.21 no.3
• /
• pp.92-98
• /
• 2003

This paper describes the numerical prediction of the thermal fatigue life of a $\mu$BGA(Micro Ball Grid Array) solder joint. Finite element analysis(FEA) was employed to simulate thermal cycling loading for solder joint reliability. Strain values, along with the result of mechanical fatigue tests for solder alloys were then used to predict the solder joint fatigue life using the Coffin-Manson equation. The results show that Sn-3.5mass%Ag solder had the longest thermal fatigue life in low cycle fatigue. Also a practical correlation for the prediction of the thermal fatigue life was suggested by using the dimensionless variable ${\gamma}$, which was possible to use several lead free solder alloys for prediction of thermal fatigue life. Furthermore, when the contact angle of the ball and chip has 50 degrees, solder joint has longest fatigue life.