• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2005.07a
• /
• pp.284-285
• /
• 2005

Bi-2223 High-Temperature Superconducting(HTS) tape is one of the most widely used HTS tape for power application. Characteristics of the over current of HTS tape with different sheath are described. This paper presents the basic properties such as temperature and resistivity rise of the Bi-2223 HTS tape which is exposed to the over current. It is expected that results from this study can be utilized as basic data in designing superconducting power devices.

• Progress in Superconductivity and Cryogenics
• /
• v.6 no.1
• /
• pp.1-5
• /
• 2004

Long length of Bi-2223/Ag superconducting wives were fabricated by stacking and drawing process with advanced heat-treatment schedules. Intermediate annealing was carried out to increase the homogeneity and uniformity of the superconducting filaments embedded in the silver matrix. Phase modification from tetragonal to orthorhombic Bi-2212 by pre heat treatment(PHT) was executed to improve the texture and phase transformation of Bi-2223. Drawing stress was measured to predict the sausaging and stress limit. Rolling Parameters such as thickness. width and winding tension were investigated to roll the tape with uniformity. 1 km length of Bi-2223/Ag superconducting wires were fabricated without any breakage. Critical current (Je) of 270 m length of superconducting tapes was measured over than $70 A/cm^2$ continuously after final sintering.

• Proceedings of the Korea Institute of Applied Superconductivity and Cryogenics Conference
• /
• 2002.02a
• /
• pp.351-354
• /
• 2002

In most of electrical applications using Bi-2223/Ag HTS tapes, bending and tension stresses are essentially applied to the tape. Therefore, the critical current of the Bi-2223/Ag tape is degraded by increasing the deformation stress, though brittle superconducting filaments are embedded in the reinforced Ag alloy sheath. It is needed to understand bending and tension properties of HTS tapes at room temperature and cryogen to make superconducting magnet, cable and etc. using Bi-2223/Ag HTS tapes. Actually, bending and tension stress applied to the tapes simultaneously, when winding the tapes on former for applications. In this study, the effect of mechanical deformations, bending and tension, on the critical current of Bi-2223/Ag tape was investigated.

• Progress in Superconductivity and Cryogenics
• /
• v.4 no.1
• /
• pp.40-44
• /
• 2002

Influences of bending strain on the critical current (Ic) were investigated in Bi-2223 superconducting tapes at 77K. The effect of bending mode on the Ic degradation behavior was discussed in viewpoints of test procedure, n-value and damage morphology Especially, in this paper, we reported the Ic behavior in Ag alloy/Bi-2223 multifilamentary superconducting tapes under bending occurred within a width plane of the tape which was called as a hard bending. The Ic degradation under hard bending appeared significantly as compared with that under easy bending. The n-value decreased slightly with the increase in bending strain under the hard bending.

• Proceedings of the Materials Research Society of Korea Conference
• /
• 1996.11a
• /
• pp.168-168
• /
• 1996

• Progress in Superconductivity and Cryogenics
• /
• v.1 no.2
• /
• pp.15-19
• /
• 1999

For large scale applications of high temperature superconductor (HTS) such as transmission cables, motors and generators, long length of flexible HTS conductor is required. Currently, Bi-2223 HTS tape is capable of being fabricated in longer than 100 m length by industrial processes. In this study, we fabricated 100 m 19 filamentary Bi-2223 ($Bi_{1.8}Pb_{0.4}Sr_2Ca_2O_{10+x}$) HTS tape by PIT (Power in Tube) process. Critical current(IC) of this long length tape was measured 18.5 A at 77K, self field. Critical current of 100 m length tape was mainly resulted from the increase of inhomogeneity in oxide from the increase of inhomogeneity in oxide layer. Engineering critical current (Je=Ic/total tape cross-section area) that is important factor for practical applications and fabrication cost was measured 2.2 kA/cm2.

• Proceedings of the Korea Institute of Applied Superconductivity and Cryogenics Conference
• /
• 2001.02a
• /
• pp.193-196
• /
• 2001

This paper deals with the fabrication and characteristic experiment of a high-Tc superconducting(HTSC) power supply using by Bl-2223 tape. The purpose of this research is to apply real HTSC load. This system consists of two heaters, an electromagnet, a Bi-2223 solenoid and a Bi-2223 pancake load. In the experiment. 17sec and 8.5sec were used for pumping period. Mechanism of the superconducting switch is used for heater-trigger. In experiment, the pumping-current has reached about 1.2A.

• Progress in Superconductivity
• /
• v.4 no.2
• /
• pp.162-167
• /
• 2003

The critical current value of Bi-2223/Ag tape can be influenced by various factors. In particular, it was known that properties of precursor powders could affect the formation of Bi -2223 and grain growth rate of the same. Since, moistures and organic matters can easily contaminate the precursor powders of Bi-2223 tapes and degrade properties of superconductors, the precursor powders should be kept in optimal conditions to minimize contamination. In this study, the effect of moisture and organic matters has been investigated. A Bi-2223/Ag tape contaminated with a large amount of moisture and organic matter has been characterized by low critical current values and bubbling. It has been found that as the quantity of moisture increases, the Bi-2223 phases are formed at lower temperature and the amount of non-superconducting phase increases.

• Progress in Superconductivity and Cryogenics
• /
• v.7 no.2
• /
• pp.31-34
• /
• 2005

There are many kinds of high temperature superconducting (HTS) application using Bi-2223 tape which is the most commercialized HTS material. Also, resistive superconducting fault current limiters (SFCLs) have been developed using many kinds of superconducting material such as YBCO thin film, Bi-2212 bulk and so on. However, SFCL using Bi-2223 tape has never been developed. This paper deals with the feasibility study on SFCL using Bi-2223 wire. The over-current behaviors of Bi-2223 short-length sample were measured. To make the resistive SFCL, two small-scale bifilar winding modules using 7m Bi-2223 wire were fabricated; i.e. solenoid type bifilar coil and pancake type one. The short-circuit tests of the coils were successfully performed up to 16 V$_{rms}$ From these tests, the current limiting capabilities of Bi-2223 bifilar coils were confirmed and current limiting performances between two winding types were compared. In addition, the feasibility of resistive SFCL using another HTS wire, i.e. YBCO coated conductor, was also investigated.

• Journal of the Korean Institute of Electrical and Electronic Material Engineers
• /
• v.14 no.1
• /
• pp.69-73
• /
• 2001

In this study, we fabricated Bi-2223/Ag high temperature superconducting tapes using PIT(Powder-In-Tube) process to apply the superconducting magnet, cable and etc. It is inevitable to deform the superconducting taps with axial strain for application. Therefore, for the characterization of the strain sensitivity of the superconducting properties, the degradation of Bi-2223/Ag tapes due to axial strain were investigated by measuring the critical current as a function of applied tension strain and external magnetic field. The critical current of Bi-2223/Ag tapes were decreased slightly up to 0.3∼0.4% applied strain but, drastically decreased more than these strains. Superconducting filament cores consisted of brittle ceramic fibers were broken easily by the large strain and current path were decreased simultaneously.