BSCCO thin films have been fabricated by epitaxy growth at an ultra-low growth rate. The growth rates of the films was set in the region from 0.17 to 0.27 nm/min. MgO(100) was used as a substrate. In order to appreciate stable existing region of Bi 2212 phase with temperature and ozone pressure, the substrate temperature was varied between 655 and 820 $^{\circ}C$ and the highly condensed ozone gas pressure(PO3) in vacuum chamber was varied between $2.0{\times}10^{-6}$ and $2.3{\times}10^{-5}$ Torr. Bi 2212 phase appeared in the temperature range of 750 and 795 $^{\circ}C$ and single phase of Bi 2201 existed in the lower region than $785\;^{\circ}C$. Whereas, $PO_3$ dependance on structural formation was scarcely observed regardless of the pressure variation. And high quality of c-axis oriented Bi 2212 thin film with $T_c$(onset) of about 90 K and $T_c$(zero) of about 45 K is obtained. Only a small amount of CuO in some films was observed as impurity, and no impurity phase such as $CaCuO_2$ was observed in all of the obtained films.

• 한국전기전자재료학회:학술대회논문집
• /
• 한국전기전자재료학회 2006년도 학술대회 및 기술세미나 논문집 디스플레이 광소자
• /
• pp.70-73
• /
• 2006

High quality $Bi_2Sr_2Ca_nCu_{n+1}O_x$ superconducting thin films fabricated by using the evaporation method at various substrate temperatures, $T_{sub}$, and ozone gas pressures, $pO_3$. The correlation diagrams of the $Bi_2Sr_2Ca_nCu_{n+1}O_x$ phases with $T_{sub}$ and $pO_3$ are established in the 2212 arid 2223 compositional films. In spite of 2212 compositional sputtering, Bi2201 and Bi2223 as well as Bi2212 phases come out as stable phases depending on $T_{sub}$ and $pO_3$. From these results, the thermodynamic evaluation of ${\Delta}H$ and ${\Delta}S$, which are related with Gibbs' free energy change for single Bi2212 or Bi2223 phase, was performed.

• 한국전기전자재료학회:학술대회논문집
• /
• 한국전기전자재료학회 2003년도 제5회 학술대회 논문집 일렉트렛트 및 응용기술연구회
• /
• pp.61-64
• /
• 2003

This paper presents Bi thin films have been fabricated by atomic layer-by-layer deposition and co-deposition at an IBS method. The growth rates of the films was set in the region from 0.17 to 0.27 nm/min. Mg(100) was used as a substrate. In order to appreciate stable existing region of Bi 2212 phase with temperature and ozone pressure, the substrate temperature was varied between 655 and $820^{\circ}C$ and the highly condensed ozone gas pressure$(PO_3)$ in vacuum chamber was varied between $2.0{\times}10^{-6}$ and $2.3{\times}10^{-5}$ Torr. Bi 2212 phase appeared in the temperature range of 750 and $795^{\circ}C$ and single phase of Bi 2201 existed in the lower region than $785^{\circ}C$. Whereas, $O_3$ dependance on structural formation was scarcely observed regardless of the pressure variation. And high quality of c-axis oriented Bi 2212 thin film with $T_c$(onset) of about 90 K and $T_c$(zero) of about 45 K is obtained. Only a small amount of CuO in some films was observed as impurity, and no impurity phase such as $CaCuO_2$ was observed in all of the obtained films.

• 한국전기전자재료학회:학술대회논문집
• /
• 한국전기전자재료학회 2007년도 하계학술대회 논문집 Vol.8
• /
• pp.486-487
• /
• 2007

$Bi_2Sr_2Ca_{n-1}Cu_nO_x$(n=0, 1, 2) thin films have been fabricated by co-deposition at an ultra-low growth rate using ion beam sputtering(IBS) method. The growth rates of the films was set in the region from 0.17 to 0.27 nm/min. MgO(100) was used as a substrate. In order to appreciate stable existing region of Bi 2212 phase with temperature and ozone pressure, the substrate temperature was between 655 and $820^{\circ}C$ and the highly condensed ozone gas pressure in vacuum chamber was varied between $2{\times}10^{-6}{\sim}4{\times}10^{-5}$ Torr. Bi 2212 phase appeared in the temperature range of 750 and $795^{\circ}C$ and single phase of Bi 2201 existed in the lower region than $785^{\circ}C$. Whereas, $PO_3$ dependance on structural formation was scarcely observed regardless of the pressure variation.

• 한국전기전자재료학회논문지
• /
• 제15권4호
• /
• pp.308-313
• /
• 2002

Samples with the norminal composition, $Bi_{2-x}Au_xSr_2CaCu_2O_{8+\delta}$ (x = 0, 0.05. 0.1, 0.15) were prepared by the solid-state reaction method. The superconducting properties, x-ray powder diffraction patterns, critical temperature and microstructure of surface were measured the samples. x-ray patterns show the single phase(2212) nature of the samples. But, the peaks of 2201 at $2\theta=30^{\circ}$ and Au peak at $2\theta=38.31^{\circ}$ are observed in the Au additive samples. The grain sire are enlarged with the increase of x. As the result of enlargement the grain size, the onset and offset critical temperature($T_c^{on}$,$T_c^{zero}$) increased with increase of x.

• 한국결정학회:학술대회논문집
• /
• 한국결정학회 2003년도 춘계학술연구발표회
• /
• pp.24-24
• /
• 2003

고온초전도 BSCCO 2223 ((Bi, Pb)₂Sr₂Ca₂Cu₃O/sub x/) 선재의 특성을 향상시키기 위해서는 반복적인 인발 및 압연과정을 통한 texturing향상, BSCCO 2223입자의 배향성 증대, 피복재내 초전도체의 충진율(밀도)향상, 이차상의 부피분율 감소등이 이루어져야 한다. 최적 열처리 조건을 통하여 열처리 시에 형성되는 이차상인 (Bi,Pb)₂Sr₂CuO/sub y/ (2201, amorphous phase)를 조절하면서, (Ca,Sr)₂CuO₃ (2/1 AEC), (Ca,Sr)/sub 14/Cu/sub 24/O/sub 41/ (14/24 AEC)와 같은 이차상들의 부피분율 및 크기를 감소시켜야만 한다. 본 실험에서는 BSCCO 2223 선재의 특성을 향상시킬수 있는 최적의 열처리 조건 확립 및 기계적 공정시 나타나는 여러 가지 문제점을 개선하여 높은 임계전류를 가지는 선재의 특성을 분석하고자 하였다. 최종적으로 제조된 선재는 2223상 결정이 피복재(Ag)와 평행하게 길게 성장하며, AEC상의 크기와 부피분율이 감소할수록 더 높은 임계전류특성을 나타내었다(I/sub c/～70A, J/sub c/～42,000 A/㎠). 또한 이 선재에서 나타나는 여러 가지 이차상들을 분석하기 위하여 XRD, SEM, EDS 분석을 행하였다.

• Progress in Superconductivity
• /
• 제4권1호
• /
• pp.90-93
• /
• 2002

The sintering process of BSCCO 2223 tapes is a complex process that is very sensitive to parameters, such as temperature, oxygen partial pressure, heating and cooling rate and holding time. During the first heat treatment, 2212 phase of precursor powder is partially transformed into 2223 phase and some residual secondary phases, such as $(Bi,Pb)_2$$Sr_2$CuO／sub y／(2201), $(Ca,Sr)_2$CuO／sub y／(2/1AEC), (Ca,Sr)／sub 14／Cu／sub 24／O／sub 41／(14／24 AEC) etc. The secondary phases are difficult to be removed from the BSCCO 2223 matrix on the heat treatment. These secondary phases degrade the critical current density. In order to minimize the amount and size of alkaline earth cuprate(AEC) particles step heat treatment is applied during the first heat treatment under the varying atmosphere. Experimental results showed that by adapting the step heat treatment process, the amount and particle size of the secondary phases in the final tapes are decreased. Consequently, the BSCCO 2223grain texture and Jc properties are improved.