• 대한치과보철학회지
• /
• 제33권3호
• /
• pp.584-609
• /
• 1995

The purpose of this study was to evaluate the difference of the galvanic corrosion behaviour of the titanium in contact with gold alloy, silva-palladium alloy, and nickel-chromium alloy using the immersion and electrochemical method. And the effects of galvallit couples between titanium and the dental alloys were assessed for their usefulness as materials for superstructure. The immersion method was performed by measuring the amount of metal elementsreleased by Inductivey coupled plasma emission spectroscopy(ICPES) The specimen of fifteen titanium plates, the five gold alloy, five silver-palladium, five nickel-chromium plates, and twenty acrylic resin plates ware fabricated, and also the specimen of sixty titanium plugs, the thirty gold alloy, thirty silver-palladium, and nickelc-hromium plugs were made. Thereafter, each plug of gold alloy, silver-palladium, and nickel-chromium inserted into the the titanium and acrylic resin plate, and also titanium plug inserted into the acrylic resin plate. The combination specimens uf galvanic couples immersed in 70m1 artificial saliva solution, and also specimens of four type alloy(that is, titanium, gold, silver-palladium and nickel-chromium alloy) plugs were immersed solely in 70m1 artificial sativa solution. The amount of metal elements released was observed during 21 weeks in the interval of each seven week. The electrochemical method was performed using computer-controlled potentiosta(Autostat 251. Sycopel Sicentific Ltd., U.K). The wax patterns(diameter 11.0mm, thickness,in 1.5mm) of four dental casting alloys were casted by centrifugal method and embedded in self-curing acrylic resin to be about $1.0cm^2$ of exposed surface area. Embedded specimens were polished with silicone carbide paper to #2,000, and ultrasonically cleaned. The working electrode is the specimen of four dental casting alloys, the reference electrode is a saturated calmel electrode(SCE) and the ounter electrode is made of platinum plate. In the artificial saliva solution, the potential scanning was carried out starting from-700mV(SCE) TO +1,000mV(SCE) and the scan rate was 75mV/min. Each polarization curve of alloy was recorded automatically on a logrithmic graphic paper by XY recorder. From the polarization curves of each galvanic couple, corrosion potential and corrosion rates, that is, corrosion density were compared and order of corrosion tendency was determined. From the experiments, the following results were obtained : 1. In the case of immersing titanium, gold alloy, silver-palladium alloy, and nickel-chromium alloysolely in the artificial saliva solution(group 1, 2, 3, and 4), the total amount of metal elements released was that group 4 was greater about 2, 3 times than group 3, and about 7.8 times than group 2. In the case of group 1, the amount of titanium released was not found after 8 week(p<0.001). 2. In the case of galvanic couples of titanium in contact with alloy(group 5, 6), the total amount of metal elements released of group 5 and 6 was less than that of group 7, 8, 9, and 10(p<0.05). 3. In the case of galvanic couples of titanium in contact with silver-palladium alloy(group 7, 8), the total amount of metal elements released of group 7 was greater about twice than that of group 5, and that of group 8 was about 14 times than that of group 6(p<0.05). 4. In the case of galvanic couples of titanium in contact with nickel-chromium alloy(group 9, 10), the total amount of metal elements released of group 9 and 10 was greater about 1.8-3.2 times than that of group 7 and 8, and was greater about 4.3~25 times than that of group 5 and 6(p<0.05). 5. In the effect of galvanic corrosion according to the difference of the area ratio of cathode and anode, the total amount of metal elements released was that group 5 was greater about 4 times than group 6, group 8 was greater about twice than group 7, and group 10 was greater about 1.5 times than group 9(p<0.05). 6. In the effect of galvanic corrosion according to the elasped time during 21 week in the interval of each 7 week, the amount of metal elements released was decreased markedly in the case of galvanic couples of the titanium in contact with gold alloy and silver-palladium alloy but the total amount of nickel and beryllium released was not decreased markedly in the case of galvanic couples of the titanium in contact with nickel-chromium alloy(p<0.05). 7. In the case of galvanic couples of titanium in contact with gold alloy, galvanic current was lower than any other galvanic couple. 8. In the case of galvanic couples of titanium in contact with nickel-chromium alloy, galvanic current was highest among other galvanic couples.

• Radiation Oncology Journal
• /
• 제24권4호
• /
• pp.280-284
• /
• 2006

목 적: 원자력의학원에 설치되어 있는 MC50 사이클로트론에서 생성되는 중성자선의 의학적 이용을 위하여 생물학적 특성을 평가하고자 하였다. 대상 및 방법: 35 MeV 양성자를 15 mm 베릴륨 표적에 부딪혀서 생성된 중성자선에 대하여 물리적 방사선선량을 측정한 후 체외실험(in-vitro)을 하였다. EMT-6 세포주(cell line)를 이용하여 $0{\sim}5\;Gy$의 중성자선을 조사 후 생존분획(surviving fraction)을 구하였다. 또한 감마선의 효과를 피하기 위하여 납차폐를 한 후에 동일 조건에서 생존분획을 구하였다. 엑스선 실험에서는 0, 2, 5, 10, 15 Gy를 조사 후 생존분획을 측정하였다. 결 과: MC50의 중성자선은 조사야 $26{\times}26\;cm^2$, 전류 $10{\mu}A$, 깊이 2 cm에서 84%의 중성자와 16%의 감마선으로 구성되어 있었고, 총선량률은 9.25 cGy/min이었다. 엑스선을 이용하여 측정한 생존분획곡선은 선형이차함수모델 (linear quadratic model)을 적용하였을 때 ${\alpha}/{\beta}$비는 0.611 (${\alpha}=0.0204,\;{\beta}=0.0334,\;R^2=0.999$)이었다. 중성자선에 있어서 생존분획곡선은 저선량 영역에서 어깨영역(shoulder area)을 가지고 있었고, 모든 실험에서 선형이차함수모델에 잘 맞았다. ${\alpha}$의 평균값은 -0.315 (범위, $-0.254{\sim}-0.360$)였고, ${\beta}$값은 0.247 (범위, $0.220{\sim}0.262$)이었다. 납차폐를 하였을 때에도 생존분획곡선에서 어깨영역은 없어지지 않았다. 중성자선의 RBE (relative biological effectiveness) 값은 생존분획이 0.1일 때 $2.07{\sim}2.19$ 범위였고, 0.01일 때 $2.21{\sim}2.35$였다. 결 론: MC50에서 생성된 중성자선은 상당량의 감마선을 내포하고 있으며 이것이 생존분획곡선에서 어깨영역이 나타나는 데에 기여하였을 것이다. MC50의 중성자선의 RBE 값은 약 2.2였다.