• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2002.04a
• /
• pp.50-54
• /
• 2002

Influences of bending strain on the critical current ($I_c$) in Ag-sheathed Bi-2223 superconducting tapes at 77K were investigated. The effect of bending mode on the bending strain characteristics was discussed in viewpoints of sample geometry, n-value and damage morphology. Especially, in this paper, we reported the $I_c$ behavior in Ag alloy sheathed Bi-2223 multifilamentary superconducting tapes under hard bending. As a result, $I_c$ degradation behavior of the hard bending appeared remarkably than the case of easy bending, but it did not influence greatly on the n-value.

• Progress in Superconductivity and Cryogenics
• /
• v.6 no.1
• /
• pp.6-11
• /
• 2004

The influences of mixed strain mode of bending-tension on the critical current. Ic in externally reinforced Bi-2223 tapes and their interaction were investigated in this study. A test fixture which providing a mixed deformation mode of bending-tension to HTS tapes has been newly devised. When the total strain induced in the tape in the mixed strain mode was expressed by the superposition of the bending and tensile strains the irreversible strain for the critical current degradation of Bi-2223 tapes increased, as compared with the simple bending mode case. The $I_c$ degradation at the region exceeding the irreversible strain showed a medium between the simple bending case and the simple tension case. As the initial bending strain imparted increased , namely as the diameter of mandrel adopted decreased. the apparent irreversible strain in Bi-2223 tapes increased . but the increment became smaller As a result. it can be found that the tension to be applied to bent Bi-2223 tapes during cabling should be smaller. as the mandrel diameter becomes smaller.

• Proceedings of the Korea Institute of Applied Superconductivity and Cryogenics Conference
• /
• 2003.10a
• /
• pp.134-138
• /
• 2003

The influences of mixed mode of bending-tension on the Ic degradation and their interaction on the strain effect were evaluated in this study. A test fixture which applies a mixed deformation mode of bending-tension to HTS tapes has been newly devised. When the strain induced in the tape due to the mixed deformation mode was expressed as a total tensile strain, the irreversible strain to the critical current degradation of Bi-2223 tapes increased when compared with the case of simple bending mode, and the value at both ends were larger than that at the central region of the bend part. The Ic degradation behavior at the region exceeding the irreversible strain showed quiet a rapid drop of the Ic when compared with the simple bending cases. As the applied bending strain increased namely as the diameter of mandrel adopted decreased, the apparent irreversible strain of Bi-2223 tapes increased However, the increment decreased as the mandrel diameter decreased. As a result, it could be found that the tension to be applied to the Bi-2223 tapes during cabling of HTS tapes should be smaller, as the mandrel diameter becomes smaller.

• Progress in Superconductivity and Cryogenics
• /
• v.11 no.4
• /
• pp.12-15
• /
• 2009

The $I_c$ degradation behavior of critical current in differently processed YBCO and SmBCO CC tapes with IBAD template has been investigated. It has been known that the residual strain in the CC tape will influence the shape of the $I_c$-strain window; $I_c$ may show a peak value if there exist a residual strain induced in the tape during manufacturing. The difference of residual strain may be resulted from the adopted different deposition techniques. In this study, bending test of CC tapes has been done using the Goldacker bending test rig which can produce both compressive and tensile bending strain continuously or alternately to the sample. For SmBCO CC tapes, in continuous compressive bending test, $I_c$ showed a minimal increase and did not degrade up to the largest strain that can be applied using the bending rig equivalent to 1.15% based on the sample thickness. However, in the case of alternate application of compressive and tensile bending strain, $I_c$ showed a larger degradation and a lower reversible limit when compared with the case of continuous application of the bending strain. When $I_c$ started to degrade significantly at the tension side, the reversibility ended, also at the compression side which is resulted from the permanent deformation like delamination or cracks that was induced due to tensile bending strain.

• Journal of the Korean Wood Science and Technology
• /
• v.26 no.4
• /
• pp.13-19
• /
• 1998

Stress relaxation tests have been performed under five different tensile strain levels and five different bending strain levels. Three different theoretical models have been developed based on four-element Burger's model, viscoelastic theory and viscous-viscoelastic theory. Experimental data were used to obtain parameters of the models and to verify accuracy of the models. Among the three theoretical models developed in this study, three-integral model (Model 3) based on viscous-viscoelastic theory showed the most exact estimations of stress relaxation under both tensile and bending strains and their correlation coefficients were greater than 0.99 for all the strain levels. Model 1 showed little initial stress relaxation. Model 2 showed excessive initial relaxation and, then, no relaxation after about 20 minute of strain application. Stress retention under strain decreased as strain increased, which means increased stress relaxation as strain increases. When the strain level was less than proportional limit, the effect of strain level on stress relaxation was not clearly shown. However, this effect was increased as strain level increased when strain level was greater than proportional limit.

• Journal of the Korean Institute of Electrical and Electronic Material Engineers
• /
• v.20 no.6
• /
• pp.541-545
• /
• 2007

The critical current degradation behaviors of multifilamentary Bi-2223 superconducting tapes under pressurized liquid nitrogen were investigated using a r-shaped sample holder which gives a series of bending strains to tape. Three kinds of externally-reinforced Bi-2223 tapes with different hermeticity were used as samples. The tape with the thicker reinforcement layer had a better bending strain tolerance of $I_c$, but when the bending strain was calculated at the outermost filament, the $I_c$ degradation behavior became identical. For all samples, $I_{c0}$ decreased with the increase of applied pressure, but the $I_c$ degradation behavior with bending strain at each pressure level was similar. Furthermore, after depressurization from 1 MPa to atmospheric pressure, $I_c$ was completely recovered to its initial values. When the samples were warmed up to room temperature after pressurization tests, the ballooning damage occurred at lower bending strain regions. The region where ballooning was observed was identical to the one where the significant $I_c$ degradation occurred.

• Structural Engineering and Mechanics
• /
• v.53 no.1
• /
• pp.17-26
• /
• 2015

The cross sections of hollow cylindrical tubes ovalise under a pure bending condition, and this reduces their flexural stiffness as their curvatures increase. It is important to accurately evaluate this phenomenon, known as the 'Brazier effect', to understand the bending behaviour of the systems considered. However, if the tubes are supported by an elastic medium or foundation, the ovalisation displacements of their cross sections may decrease. From this point of view, the purpose of this research is to analytically investigate the bending characteristics of single- and double-walled elastic tubes contacted by an elastic material by considering the Brazier effect. The Brazier moment, which is the maximum moment-carrying capacity of the ovalised cross section, can be calculated by introducing the strain energy per unit length of the tube in terms of the degree of ovalisation for the tube and the curvature. The total strain energy of the double-walled system is the sum of the strain energies of the outer and inner tubes and that of the compliant core. Results are comparatively presented to show the variation in the degree of ovalisation and the Brazier moment for single- and double-walled tubes.

• Progress in Superconductivity and Cryogenics
• /
• v.12 no.2
• /
• pp.5-8
• /
• 2010

In this study, the effect of bending strain on the transport property and critical current of lap and butt-jointed (non-laminated) BSCCO tapes has been investigated. The samples were joined using a mechanically controlled jointing procedure. To achieve a uniform thickness at the joint a single point loading contact has been devised. GFRP mandrels with different bending radii which support the sample during bending have been used. $I_c$ have been measured at 77 K and self field. In the case of easy bending test for jointed BSCCO tapes, sudden degradation of $I_c$ is caused by the local strain concentration due to non uniform deformation at the edge parts of the joint. In the case of hard bending test of jointed BSCCO tapes transverse macroscopic crack at specific subsection caused a large $I_c$ degradation. The transport property of jointed BSCCO tapes in each bending mode was discussed with the damage morphology occurred.

• Transactions of the Korean Society of Mechanical Engineers A
• /
• v.34 no.3
• /
• pp.341-346
• /
• 2010

The effect of specimen geometry on the bending and tensile strengths of dissimilar joints ($\beta-Si_3N_4/S45C$) with copper interlayers was evaluated. The average bending strength of specimens with circular cross sections was higher than that of specimens with rectangular cross sections. The crack initiation stress ($\sigma_i$) was successfully determined by the acoustic emission (AE) method and was approximately 60~80% of the bending strength. The residual stresses near the interfaces on the ceramic side were measured by X-ray diffraction before conducting the bending test. The bending strength and the crack initiation stress decreased with an increase in the residual stresses. The effect of the bending strain component was evaluated by the tensile testing; the tensile strength decreased with an increase in the bending strain component and was approximately 80% of the bending strength.

• Progress in Superconductivity and Cryogenics
• /
• v.4 no.1
• /
• pp.40-44
• /
• 2002

Influences of bending strain on the critical current (Ic) were investigated in Bi-2223 superconducting tapes at 77K. The effect of bending mode on the Ic degradation behavior was discussed in viewpoints of test procedure, n-value and damage morphology Especially, in this paper, we reported the Ic behavior in Ag alloy/Bi-2223 multifilamentary superconducting tapes under bending occurred within a width plane of the tape which was called as a hard bending. The Ic degradation under hard bending appeared significantly as compared with that under easy bending. The n-value decreased slightly with the increase in bending strain under the hard bending.