• Journal of Ceramic Processing Research
• /
• v.22 no.1
• /
• pp.66-73
• /
• 2021

Ceramics have high hardness, corrosion resistance, and abrasion resistance, but are easily fractured by micro crack. Many studies on self-healing have been conducted to eliminate the risk of micro crack on the surface. SiO2 is self-healing material, in which Si and O2 are combined. TiO2-added Si3N4/SiC composites were sintered. The SiO2 colloid was coated on the surface, and heat treated. The bending strength and abrasion characteristics were evaluated. The specimen with SiO2 colloid coating had higher strength than that of the uncoated specimen, and the strength of TiO2-added specimen also increased. The friction coefficient and wear loss of SiO2 colloid coated specimens were smaller than those of the uncoated specimens. The friction coefficient and wear loss of TiO2-added specimens were smaller than those without additives. The friction coefficient and wear loss decreased with increasing bending strength. Friction coefficient and wear loss according to the heat treatment temperature showed the reverse tendency to the bending strength. Therefore, TiO2-added ceramic will ensure economic efficiency.

• Proceedings of the Korea Concrete Institute Conference
• /
• 2000.10b
• /
• pp.1121-1126
• /
• 2000

The purpose of this study is to clarify chemical resistance of polymer-cement slurry coated reinforcing bars. Polymer cement slurry coated reinforcing bars were showed the good state to the bending resistance, impact resistance, adhesive strength, but exact data of the chemical resistance do not exist. Through the experimental, it is to certify chemical resistance of polymer cement slurry coated reinforcing bars. In this study, polymer cement slurry coated reinforcing bars are prepared with two types of polymer, polymer-cement ratios of 50%, 100%, 150%, coating thickness, curing periods of 3, 7, 28days, and tested for chemical resistance as KS(Korea Standard). From the test results, chemical resistance of polymer cement slurry coated reinforcing bars used by acrylic and St/BA emulsion were showed excellent without concerned polymer-cement ratios, curing period except for 1% aqueous solution $H_2SO_4$. But polymer cement coated reinforcing bar used by acrylic emulsion is inferior to aqueous solution NaOH.

• Transactions of the Korean Society of Automotive Engineers
• /
• v.2 no.6
• /
• pp.1-8
• /
• 1994

To enhance the strength of gears for transmission, Generally caburizing heat treatment is applied. But there are some problems in this technology the distortion of gears during heat treatment process, and the discontinuity of manufacturing process. For these reasons, the high frequency induction hardening process is widely used. This method is one of the surface hardening process to improve the wear resistance and fatigue life of the machine components. In this study, to compare the bending fatigue strength of caburized gear with that of induction hardened gear, bending fatigue testing of gears with two different cases was performed by using an electrohydraulic servo-controlled fatigue testing machine and double tooth bending fatigue test fixture. Fatigue life distributions at constant stress levels were established directly from fatigue data. For gear design, the fatigue strength distribution at specified life is more important. This distribution is obtained by statical transformation from fatigue life distribution. Reliability of bending fatigue strength was estimated by P-S-N curves and Weibull distribution.

• Journal of Korean Association for Spatial Structures
• /
• v.20 no.4
• /
• pp.141-147
• /
• 2020

Single-layered grid space steel roof structure is an architectural system in which the structural ability of the nodal connection system greatly influences the stability of the entire structure. Many bolt connection systems have been suggested to enhance for better construct ability, but the structural behavior and maximum resistance of the connection system according to the size of bolt clearance play were difficult to identify. In particular, the identification of bending stiffness of the connection system is very important due to the characteristics of shell structures in which membrane stresses based on bending force effect significantly. To identify effective structural behavior and maximum bearing force, four representative nodal connection systems were selected and nonlinear numerical analysis were performed. The numerical analysis considering the size of the bolt clearance were performed to investigate structural behavior and maximum values of the bending force. In addition, the type of effective nodal connection system were evaluated. As a result, the connection system, which has two shear plane, represented high bending stiffness.

• Proceedings of the Korea Concrete Institute Conference
• /
• 1994.04a
• /
• pp.158-162
• /
• 1994

Test results to evaluate the mechanical properties of epoxy-coated bars and corrosion protection characteristics of epoxy coating on the bars are described. The results show good adhesion and abrasion resistance satisfying the requirements in relevant standards. The test results also show that for a coating thickness ranging from 150${\mu}{\textrm}{m}$ to 300${\mu}{\textrm}{m}$, satisfactory results are obtained regarding bendability. Cautions shall be required when bending epoxy-coated bars at a high bending degree and at a low temperature. The results of accelerated corrosion tests show good corrosion resistance. However, surface defects from the steel itself and insufficient blast-clean process form weak points resulting blistering or disbonding of the coating. The use of epoxy-coated bars is expected to help protect corrosion of reinforcement and extend the service life of reinforced concrete structures.

• Textile Coloration and Finishing
• /
• v.18 no.3 s.88
• /
• pp.23-30
• /
• 2006

The bending properties, wrinkle resistance, and fabric retention behaviors of cotton knitted fabrics in the wale and course directions were studied for their dependence upon resin finishing, knit structure, and washing cycles. Stiffness, wrinkle recovery angles, and dimensional stability were investigated before and after resin finishing and laundering. It has been found that any change in the physical properties of the knitted fabrics with respect to knit structure and fabric directions are related to accompanying modifications to the state of the fiber properties. The decrease of fabric shrinkage rates and wrinkle recovery properties from increasing laundering cycles is related with resin incorporated on the fiber surface. This study shows that resin finishing on knitted fabrics can be performed only to improve fabric retention properties with reduced wrinkle recovery properties.

• Proceedings of the Korean Society for Technology of Plasticity Conference
• /
• 2006.05a
• /
• pp.300-303
• /
• 2006

Sandwich panel with inner structure is expected to find many applications because of high stiffness to mass ratio. However, low resistance to the pressure in the thickness direction may become a weak point in the forming process. Two pyramid type designs for inner structure are considered. For the resistance characteristics in the thickness direction, finite element simulations are carried out. For one design, experimental results are provided. It is shown that simulation can give a reasonable agreement with experiment. The reasons for the discrepancy are discussed mainly in the geometrical viewpoint. It is observed that most of deformation depends on bending mode. Two designs are compared using simulation.

• Journal of the Korea Furniture Society
• /
• v.26 no.4
• /
• pp.392-397
• /
• 2015

This study was carried out to analyze the effects on mechanical properties of deteriorated wood member by outdoor condition. The surface color, mechanical properties and structural stability of traditional wooden structures, exposed in water and UV, could be changeable. For the purpose, accelerated weathering test based on outdoor condition was carried out. The weathering time levels were composed 0, 500, 1000, 1,500 and 2,000 hours and mechanical properties were evaluated on each specimen according to weathering time level. Bending properties were decreased on weathering but recovered after 1,000 hours. Fatigue and impact strength were decreased to 1,000 hours and did not changed since then. Abrasion resistance was minimized in 1,000 hours. This results could be utilized for effectively stability management of traditional wooden structures and members.

• Journal of Surface Science and Engineering
• /
• v.27 no.2
• /
• pp.74-82
• /
• 1994

The structure and properties such as adhesion and corrosion resistance of Cr and $Cr_2O_3$ films, deposited on steel plates by the vacuum evaporation method, were investigated. According to the ESCA and AES analy-sis, it could be concluded that chromium oxide with uniform composition could be formed on the steel sub-strate. The deposited Cr and $Cr_2O_3$ films had high adhesion strength, and they did not peeled off by the tape test. The adhesion property, however, was deteriorated as the film thciknes increased. After bending of the deposited specimen many cracks were observed by SEM, and they were assumed to have propagated along co-lumnar boundaries by the bending test. The corrosion resistance of the films was not generally good, which in-dicates that the films had a porous structure with a large number of defects such as pin holes and voids.

• Proceedings of the Korean Vacuum Society Conference
• /
• 2013.02a
• /
• pp.429-429
• /
• 2013

We present a systematic study of the electrical, optical and electromechanical properties of flexible graphene/metal grid hybrid transparent conductive electrodes using 4-point prove method, ultraviolet/visible spectrometer and inner/outer bending test system. The hybrid electrodes were synthesized by depositing a silver grid on a graphene surface. The sheet resistance of hybrid electrodes was as low as 30 Ω/square, while the transmittance was 90%. The electromechanical properties as a function of the change of bending radius were evaluated by measuring the change in resistance. The result will be presented in detail. We believe that these results will provide useful information for the flexible optoelectronic devices based on graphene transparent electrodes.