• Korean Journal of Materials Research
• /
• v.8 no.6
• /
• pp.538-544
• /
• 1998

The spallation of a thermal barrier coating layer depends on the formation of brittle spinels. thermal expansion mismatch between ceramic and metal. the phase transformation of a ceramic layer and residual stress of coating layer. In this work. the formation mechanism of oxide scale formed by oxidation treatment at 90$0^{\circ}C$ was investigated in order to verify oxidation behavior at the interface between E-beam coated $Zr0_2$-7wt.% $Y_20_3$ and plasma sprayed CoNiCrAIY. Some elements distributed in the bond coating layer were selectively oxidized after oxidation. At the initial time of oxidation. AI-depletion zone and $\alpha$-$Al_O_3$,O, were formed at the bond coating layer by the AI-outward diffusion. After layer grew until critical thickness. spinels. $Cr_20$, and $C0_2CrO_4$ by outward diffusion of Co. Cr, Ni were formed. It was found that the formation of spinels may be related to the spallation of $Zr0_2$-7wt.% $Y_20_3$ during isothermal oxidation.

• Journal of the Microelectronics and Packaging Society
• /
• v.26 no.4
• /
• pp.101-105
• /
• 2019

The adhesion reliability of the epoxy molding compound (EMC) and the printed circuit board (PCB) interface is critical to the quality and lifetime of the chip package since the EMC protects PCB from the external environment during the manufacturing, storage, and shipping processes. It is necessary to measure adhesion energy accurately to ensure product reliability by optimizing the manufacturing process during the development phase. This research deals with the measurement of EMC/PCB interfacial adhesion energy of chip package that has warpage induced by the coefficient of thermal expansion (CTE) mismatch. The double cantilever beam (DCB) test was conducted to measure adhesion energy, and the spring back force of specimens with warpage was compensated to calculate adhesion energy since the DCB test requires flat substrates. The result was verified by comparing the adhesion energy of flat chip packages come from the same manufacturing process.

• The Korean Journal of Petroleum Geology
• /
• v.10 no.1_2 s.11
• /
• pp.18-22
• /
• 2004

To identify and interpret the distribution and the characteristics of the gas hydrate layers in the Ulleung Basin, we have surveyed and gathered the multi-channel seismic data, Chirp sub-bottom profiler, SeaBeam and 12 m piston core samples since 1996. In previous works, high-resolution seismic profiles showed acoustic anomalies such as acoustic void, acoustic turbidity and pock mark which indicate the presence of gas-charged sediments. The patterns of horizontal degassing cracks originated from free methane expansion is the strong indicator of shallow gas-charged sediments in the core samples. The observation of submarine slides and slumps from destabilizing the sediments in the southern part of the Ulleung Basin may also point out that the gas had been released from gas hydrate dissociation during lowstand of sea level. The multi-channel seismic data show BSR, blanking and phase reversal. The gas hydrate layers above which large-scale shallow gases are distributed exist at the depth of about 200 m from the sea-floor with water depth of 2,100 m. From the interpretation of seismic sections in the southern Ulleung Basin, gas hydrate layers occur in the Pleistocene-Holocene sediments. These gas-charged sediments, acoustic anomalies and BSR may be all related to the existence of gas hydrate layers in the study area.

• Journal of the Computational Structural Engineering Institute of Korea
• /
• v.34 no.4
• /
• pp.255-262
• /
• 2021

In this study, a jointless bridge that integrates the superstructure and abutment without installing an expansion joint was analyzed. An example of a jointless bridge that has been introduced in Korea since 2009. Owing to the short period of use and lack of experience in design, construction, and maintenance, there is insufficient information regarding the long-term behavior of jointless bridges. When analyzing numerous bridges, the numerical analysis model must maintain the numerical values used and ensure the convenience of model construction. In this study, sensitivity analysis was performed to select a numerical model for various types of jointless bridges using commercial finite element programs, MIDAS Civil and ABAQUS 2018. According to a solid element-based model, we analyzed the mean and maximum relative errors between structural models. Consequently, it was found that the beam element-based model exhibits a significantly small relative error in comparison to the shell element, where a relatively large error was recorded. Therefore, the optimal numerical analysis model, a practical model that maintains the similarity and precision of the displacement shape cause by relative error, was judged to be the most suitable for jointless bridges based on the shell element.

• Journal of the Korea Institute of Building Construction
• /
• v.2 no.2
• /
• pp.165-172
• /
• 2002

A reinforced concrete building neighboring in Pusan or Ulsan where is directly exposed to salt water contrasting with other in land areas contains much salt content percolated from the outside that the high salt content percolates and diffuses through the inside of reinforced concrete; therefore, an immovable tunic surrounding it begins to be destroyed and eroded with high speed. At the time, the cross-sectional area and volume expansion of re-bar reinforcing result in being cracks make a rapid progress gradually until they appear in the surface of the one, the phenomenon such as being a thin layer or falling off the part of it causes a lowering of its durability and might collapse the concrete construction. So far, we've investigated into salt content of reinforced concrete constructions neighboring in a seaside district and damage by carbonation, and we came to a conclusion as follows: $\circled1$ Under the oceanic circumstance a concrete construction is influenced by sea water directly that contains much amount of salt content contrasting with other constructions on inland areas. $\circled2$ Because of chloride penetration the carbonation of reinforced concrete made a rapid progress until more than the covering thickness of re-bar. $\circled3$ An old reinforced concrete building which has been piled up salt injury and proceeding the carbonation of its cross-sectional area. $\circled4$ According to rapidly cracking from the inside to surface of reiforced concrete, the phenomenon of being a thin layer or falling off the part of reinforced concrete results in a lowering of durability and shortening the life-time of concrete construction itself.

• KSCE Journal of Civil and Environmental Engineering Research
• /
• v.11 no.4
• /
• pp.45-54
• /
• 1991

The closed forms of mass matrix with rotational inertia matrix are developed for free vibration analysis in space structures containing linearing tapered members with cross section of thin-walled tube. The exact displacement functions are used for formulating mass matrix. The very small slopes of the tapered member are used in usual practice, such that the series expansion forms of these are also developed to avoid numerical failure in vibration analysis. Significant improvements of accuracy and efficiency of free vibration analysis are achieved by using the mass matrices developed in this study. Frequencies of free vibration of tapered members are compared with solutions based upon stepped representation of beam element.

• Progress in Superconductivity and Cryogenics
• /
• v.13 no.1
• /
• pp.1-5
• /
• 2011

[ $CeO_2$ ]has been widely used for single buffer layer of coated conductor because of superior chemical and structural compatibility with $ReBa_2Cu_3O_{7-{\delta}}$(Re=Y, Nd, Sm, Gd, Dy, Ho, etc.). But, the surface of $CeO_2$ layer showed cracks because of the large difference in thermal expansion coefficient between metal substrate and deposited $CeO_2$ layer, when thickness of $CeO_2$ layer exceeds 100 nm on the biaxially textured Ni-3%W substrate. The deposition rate has been limited to be less than 6 $\AA$/sec in order to get a good epitaxy. In this research, we deposited $CeO_2$ single buffer layers on biaxially textured Ni-3%W substrate with 2-step process such as thin nucleation layer(>10 nm) with low deposition rate(3 $\AA$/sec) and thick homo epitaxial layer(>240 nm) with high deposition rate(30 $\AA$/sec). Effect of deposition temperature on degree of texture development was tested. Thick homo epitaxial $CeO_2$ layer with good texture without crack was obtained at $600^{\circ}C$, which has ${\Delta}{\phi}$ value of $6.2^{\circ}$, ${\Delta}{\omega}$ value of $4.3^{\circ}$ and average surface roughness(Ra) of 7.2 nm within $10{\mu}m{\times}10{\mu}m$ area. This result shows the possibility of preparing advanced Ni substrate with simplified architecture of single $CeO_2$ layer for low cost coated conductor.

• Journal of the Korean Institute of Electrical and Electronic Material Engineers
• /
• v.18 no.4
• /
• pp.344-349
• /
• 2005

The optical and electrical characteristics of plasma display panel(PDP) using the vacuum in-line sealing technology compared with the conventional sealing process in this research. This PDP consisted of MgO protecting layer by e-beam evaporation and battier rib, transparent dielectric layer, dielectric layer, and electrodes by screen printer and then sealed off on Ne-Xe(4 ％) 400 Torr and 430。C. The brightness and luminous efficiency were good as the base vacuum level was higher, and it was to check the advantage of high vacuum level sealing, one of the strong points of the vacuum in-line sealing process. However, the brightness and luminous efficiency was dropped sharply because of a crack on MgO protecting layer by the difference of the expansion and contraction stress on high temperature in the vacuum states between MgO and substrate. Fortunately, the crack was prevented by MgO was deposited on higher temperature than 300。C. Finally, the PDP, was fabricated by the vacuum in-line sealing process, resulted the lower brightness than processing only the thermal annealing treatment in the vacuum chamber, but the luminous efficiency was increased by the reducing power consumption with the decreasing luminous current. The vacuum in-line sealing technology was not to need the additional thermal annealing process and could reduce the fabrication process and bring the excellent optical and electrical properties without the crack of MgO protecting layer than the conventional sealing process.

• JSTS:Journal of Semiconductor Technology and Science
• /
• v.2 no.4
• /
• pp.259-267
• /
• 2002

We present a novel 3D fabrication method with single X-ray process utilizing an X-ray mask in which a micro-actuator is integrated. An X-ray absorber is electroplated on the shuttle mass driven by the integrated micro-actuator during deep X-ray exposures. 3D microstructures are revealed by development kinetics and modulated in-depth dose distribution in resist, usually PMMA. Fabrication of X-ray masks with integrated electrothermal xy-stage and electrostatic actuator is presented along with discussions on PMMA development characteristics. Both devices use $20-\mu\textrm{m}$-thick overhanging single crystal Si as a structural material and fabricated using deep reactive ion etching of silicon-on-insulator wafer, phosphorous diffusion, gold electroplating, and bulk micromachining process. In electrostatic devices, $10-\mu\textrm{m}-thick$ gold absorber on $1mm{\times}1mm$ Si shuttle mass is supported by $10-\mu\textrm{m}-wide$, 1-mm-long suspension beams and oscillated by comb electrodes during X-ray exposures. In electrothermal devices, gold absorber on 1.42 mm diameter shuttle mass is oscillated in x and y directions sequentially by thermal expansion caused by joule heating of the corresponding bent beam actuators. The fundamental frequency and amplitude of the electrostatic devices are around 3.6 kHz and $20\mu\textrm{m}$, respectively, for a dc bias of 100 V and an ac bias of 20 VP-P (peak-peak). Displacements in x and y directions of the electrothermal devices are both around $20{\;}\mu\textrm{m}$at 742 mW input power. S-shaped and conical shaped PMMA microstructures are demonstrated through X-ray experiments with the fabricated devices.

• The korean journal of orthodontics
• /
• v.50 no.5
• /
• pp.346-355
• /
• 2020

The treatment of skeletal Class III malocclusion in adolescents is challenging. Maxillary protraction, particularly that using bone anchorage, has been proven to be an effective method for the stimulation of maxillary growth. However, the conventional procedure, which involves the surgical implantation of mini-plates, is traumatic and associated with a high risk. Three-dimensional (3D) digital technology offers the possibility of individualized treatment. Customized mini-plates can be designed according to the shape of the maxillary surface and the positions of the roots on cone-beam computed tomography scans; this reduces both the surgical risk and patient trauma. Here we report a case involving a 12-year-old adolescent girl with skeletal Class III malocclusion and midface deficiency that was treated in two phases. In phase 1, rapid maxillary expansion and protraction were performed using 3D-printed mini-plates for anchorage. The mini-plates exhibited better adaptation to the bone contour, and titanium screw implantation was safer because of the customized design. The orthopedic force applied to each mini-plate was approximately 400-500 g, and the plates remained stable during the maxillary protraction process, which exhibited efficacious orthopedic effects and significantly improved the facial profile and esthetics. In phase 2, fixed appliances were used for alignment and leveling of the maxillary and mandibular dentitions. The complete two-phase treatment lasted for 24 months. After 48 months of retention, the treatment outcomes remained stable.