• Journal of Welding and Joining
• /
• 제11권1호
• /
• pp.52-61
• /
• 1993

Laser welding of ASTM no. 1060 Al plate with a pulsed Nd: YAG laser of 200W average power was performed for end capping of KMRR nuclear fuel elements In this research, we performed basic welding experiments. Firstly, laser output parameters which affect laser welding parameters were studied by changing laser input parameters for effective welding of 1060 Al plates. We found that laser power density and pulse energy are important parameters for smooth bead shape. Secondly, welding parameters which affect weld width-to-depth ratio were studied by changing power density and pulse energy, shielding gas, and defocusing. We found that power density must be higher than 0.3 Mw/cm$^{2}$ pulse energy must be higer than 3 J. travel speed must not exceed 200mm/sec, laser focus must be existed beneath 2-3mm from plate surface and helium is proper shielding gas. Thirdly, we studied the weld defects of Al-1060 such as crack and porosity in lap-joint welding. We designed new welding geometry for crack free welding of Al-1060 plates, and obtained crack free weldment but with lack of fusion. However, with Ti, Zr grain refiner elements, we can weld Al plates without solidification hot crack. Finally, we studied the origin of porosity by changing shielding gas. And we found that porosity was resulted from entrapment of shielding gas by the collapsing keyhole.

• 대한용접접합학회:학술대회논문집
• /
• 대한용접접합학회 2009년 추계학술발표대회
• /
• pp.202-204
• /
• 2009

Erosion is a common failure mode of materials frequently encountered in plant and power industry. Although the erosion resistance of Fe-base alloy has been inferior to the other expensive materials, it is expected that the strain-induced martensitic transformation can impart high erosion resistance to Fe-base alloy. The key technology to develop Fe-base metal cored welding wire for erosion resistant overlay welding may include the strain-induced metallurgy for hardening rate control and the welding flux metallurgy for dilution control. Sophisticated studies showed that the strain-induced martensitic transformation behavior was related to the critical strain energy which was dependent on the alloy composition. Dilution and bead shape of overlay weld were proved to be affected by metal transfer mode during gas tungsten arc welding and elements in welding fluxes. It was considered that the highly erosion resistant Fe-base overlay weld could be achieved by precise control of alloy composition to have proper level of critical strain energy for energy absorption and welding flux formulation to have small amount of deoxidizing metallic elements for dilution.

• Journal of Welding and Joining
• /
• 제28권3호
• /
• pp.73-78
• /
• 2010

The purpose of this study is to develop the control technology of the welding distortion caused by Auto NG-GTA(Narrow Gap-GTA) welding process at the STS 304 multi-pass butt weldment. Heat input model for Auto NG-GTA welding process was established and verified by measuring temperature change and molten pool shape at the bead-on-plate weldment. With the heat input model developed, the effect of tension load on the welding distortion at the STS 304 multi-pass butt weldment was evaluated using the thermo-elasto-plastic FE analysis. In accordance with FEA results, the angular distortion and transverse shrinkage sharply decreased with an increase in tension load. This result indicated that tensioning method was an effective countermeasure against the welding distortion of the STS 304 multi-pass butt weldment.

• Journal of Welding and Joining
• /
• 제28권2호
• /
• pp.47-53
• /
• 2010

According to the research report for the recent a few years, the dissimilar welding of Cu and STS 304 alloy have been presented that a weldability is very poor. This article present a study on Lap joint by Electron beam welding dissimilar materials. The weld metals was constituted between pure copper and STS 304 steel. The experiment was performed with 125mA welding current, 520mA focusing current. The Vacuum condition of chamber is 5${\times}$10-5torr and welding speed is 300mm/min. Showing the bead shape of weld metal, the thickness of the stainless 304 using as the protect materials is 3mm and the thickness of a copper is 15mm. The analysis about the microstructure were carried out in which it was observed with SEM. The results showed that complex heterogeneous fusion zone microstructure characterized both by rapid cooling and mixing of the molten metal, however the liquation crack was formated in the fusion line.

• 한국레이저가공학회지
• /
• 제8권1호
• /
• pp.19-25
• /
• 2005

Pulse laser welding of AISI 304 stainless steel plate was simulated to optimize welding conditions by using commercial finite element code MARC. Due to geometric symmetry, a half model of AISI 304 stainless steel plate was considered. for the heat transfer analysis, user subroutines were applied to boundary condition. The material properties such as conductivity, specific heat, and mass density were given as a function of temperature and the latent heat associated with a given temperature range was considered. A moving heat source was designed on the basis of experimental data. As a result, Nd:YAG laser welding for AISI 304 stainless steel was successfully simulated and it should be useful to determine optimal welding condition.

• 한국레이저가공학회지
• /
• 제8권1호
• /
• pp.27-37
• /
• 2005

During laser spot welding of the braun tube electron gun, phenomena such as serious spattering and oxidative reaction, etc. were occurred. The spatter occurred from weld pool affects the braun tube, namely it blocks up a very small hole on the shadow mask and causes short circuit between two poles of the electron gun. We guessed that high power density and oxidative reaction are main sources of these problems. So, we studied to prevent and to reduce spatter occurring in spot welding of the braun tube electron gun using pulsed Nd:YAG laser. The characteristics of laser output power was estimated, and the loss of laser energy by optical parameter and spatter was measured by powermeter. The effects of welding parameters, laser defocused distance and incident angle, were investigated on the shape and penetration depth of the laser welded bead in flare and flange joints. From these results, the laser peak power was a major factor to control penetration depth and to occur spatter. It was found that the losses of laser energy by optic parameter and sticked spatter affect seriously laser weldability of thin sheets.

• 한국소성가공학회:학술대회논문집
• /
• 한국소성가공학회 2005년도 추계학술대회 논문집
• /
• pp.467-471
• /
• 2005

In this paper, experimental methods about the flow behavior of thin polymer film by various edge patterns in the spin coating process for stable cover layer coating of a blu-ray disc is described. The blu-ray disc, a next-generation optical disc format over 25GB, consists of a 1.1m thick substrate and a 0.1mm tick cover layer. Generally, cover layer on the blu-ray disc is made by the polymer spin coating process. However, it is hard to secure sufficient coating uniformity around the rim on the cover layer. In order to get the uniform thickness deviation and to minimize the bead around the rim, the edge of the disc substrate can be modified into various patterns, such as normal plain, trench, step and chamfer pattern, etc, around the rim on the disc and experimented with various parameters, such as surface tension, viscosity, coating time, temperature and rotation speed, etc. And the optimal shape of the rim was tried to get by 3 dimensional computer simulation of the polymer expulsion process.

• Journal of Welding and Joining
• /
• 제19권1호
• /
• pp.49-57
• /
• 2001

In this study, the residual stress fields of multi-pass welded were analyzed by FEA under various geometrical conditions. In order to estimate the effects of pipe geometries on residual stress distribution, welding processes of each model were performed under the same heat cycles. And then, the influence of cutting off the weld bead on the residual stress redistribution was also estimated. From the results, in the range of t/D=0.05, axial residual stresses on the outer surface of the welded pipe were linearly decreased with pipe diameter increase. On the other hand, hoop residual stresses were not influenced by them. And both axial and hoop residual stresses on the outer surface of the welded pipe were increased with pipe diameter increase. But, when t/D was smaller than 0.05, they were converged in the nearly same value. The maximum residual stresses were generated at around HAZ. It in therefore necessary to consider them in welding design, strength evaluation, and analysis of fracture characteristics.

• 대한용접접합학회:학술대회논문집
• /
• 대한용접접합학회 2005년도 추계학술발표대회 개요집
• /
• pp.114-116
• /
• 2005

There are some problems when weld gray cast iron which is used well in automobile industry with auto MIG welding. the problems are followed like this 1) Occurrence of porosity and hardening organization. 2) Occurrence of crack due to lower elongation of gray cast iron when restraint stress works on. 3) Occurrence of porosity and unstable bead shape due to unstable arc under low current MIG welding.. especially there is a restraint on chemical composition of weld metal because the weldment demands more than 570Hv hardness. so it is hard to use Fe-Ni wire to prevent cracks occured on weldment and new welding method is needed to resolve that problems. This study shows how to prevent porosity and cracks occurring when weld gray cast iron trimming die and shows a new welding method for press die of gray cast iron

• 한국레이저가공학회지
• /
• 제11권4호
• /
• pp.21-28
• /
• 2008

Remote Laser welding technology for manufacturing automotive body is studied. Laser welding and industrial robot systems are used for the robot based laser welding system. The laser system is used 1.6kW Fiber laser(YLR-1600) of IPG. The robot system is used HX130-02 of Hyundai Heavy Industry(payload : 130kg). The robot based laser welding system is equipped with laser scanner system for remote laser welding. The welding joints of steel plate and steel plate coated with zinc are butt and lapped joints. The quality test of the laser welding are through the observation the shape of bead on plate and cross-section of welding part. During past three years the laser system, 4kW Nd:YAG laser (HL4006D) of Trumpf was used and the robot system, IRB6400R of ABB (payload:120kg) was used. The new laser source, robot and laser scanner system are used to increase the processing speed and to improve the process efficiency. This paper introduces the robot based remote laser welding system to resolve the limited welding speed and accuracy of the conventional laser welding system.