• Textile Coloration and Finishing
• /
• v.22 no.1
• /
• pp.77-82
• /
• 2010

Highly conductive yarn was successfully obtained using electroless nickel plating method with palladium activation. In the presence of palladium seed on surface of fibers as a catalyst, continuos nickel layer produced on surface of fibers by reducing $Ni${2+}$ ion in the electroless plating bath to $Ni^0$. It was found that the Pd-activation using $SnCl_2$ and $PdCl_2$ to deposit palladium seeds on the surface of fibers plays a key role in the subsequent electroless plating of nickel. It also found that electroless nickel plating on the fibers can induce the nickel-plated $ELEX^{(R)}$ fibers to improve the electrical conductivity of the fibers. The thickness of nickel coating layer on the Pd-activated $ELEX^{(R)}$ fibers and specific conductivity of the fiber were increased through electroless plating time. The temperature of nickel plating bath was very effective to enhance the nickel deposition rate.

• Journal of the Korean institute of surface engineering
• /
• v.36 no.3
• /
• pp.242-250
• /
• 2003

Electrodeposition of Ni was carried out on copper substrate from Ni Sulfamate bath by DC and high frequency pulse current. During the electroplating, bath temperature was steady $60^{\circ}C$ , agitation was applied. Morphology and surface roughness of electrodeposits was investigated with the AFM. Crystalline structure of electrodeposits was investigated with XRD. Also, surface electric resistivity was investigated with 4-point probe. The result of crystalline structure by X-ray diffractometer, in the case of DC, <200> direction was dominant growing direction. But in the case of PC, the ratio of <200> direction vs. other direction decreased. As the pulse frequency increased, the enhanced properties of deposits were shown. With increasing frequency, the degree of surface properties increased DC more than that of PC, eg surface morphology, roughness and the degree of compactness of grains. With increasing duty cycle, the surface properties such as the degree of the morphology, roughness and electroconductivity was deteriorated.

• Fibers and Polymers
• /
• v.7 no.2
• /
• pp.174-179
• /
• 2006

Dyeing and color fastness properties of a reactive disperse dye containing an acetoxyethylsulphone group on PET, Nylon, silk and N/P fabrics were examined. The reactive disperse dye exhibited almost the same dyeing properties on PET fabric as a conventional disperse dye except the level of dye uptake. The most appropriate pH and dyeing temperature for the dyeing of Nylon fabric were 7 and $100^{\circ}C$ respectively. The build-up on Nylon fabric was good and various color fastnesses were good to excellent due to the formation of the covalent bond. Application of the reactive disperse dye on silk fabric at pH 9 and $80^{\circ}C$ yielded optimum color strength. The rate of dyeing on Nylon fabric was faster than that on PET fabric when both fabrics were dyed simultaneously in a dye bath, accordingly color strength of the dyed Nylon was higher. The reactive disperse dye can be applied for one-step and one-bath dyeing of N/P mixture fabric with good color fastness.

• Proceedings of the KIEE Conference
• /
• 1997.07d
• /
• pp.1436-1438
• /
• 1997

In this paper, CdS thin films, which were widely used window layer of the CdS/CdTe and the CdS/$CuInSe_2$ heterojunction solar cell, were grown by chemical bath deposition, and The properties were investigated in detail. Cadmium acetate and thiourea were used as cadmium and sulfur source, respectively. And Ammonium acetate was used as the buffer solution. Also Ammonia was used for controlling pH concentration. The reaction velocity was increased with increasing reaction temperature and decreasing pH concentration. The crystal structure of CdS films grown with various pH concentration had the hexagonal structure with (002) plane peak. In the range of pH $9{\sim}9.5$, the intensity of the peak was highest, and as increasing pH concentration, decreased the intensity of the peak except pH12.

• Journal of the Korean Institute of Telematics and Electronics A
• /
• v.30A no.11
• /
• pp.99-104
• /
• 1993

We analyzed the D.I. water used in wet cleaning process of semiconductor device manufacturing both at the D.I. water plant and at the wafer cleaning bath to detect the impurity source of D.I. water contamination. This shows that the quantity of impurity is related to the resistivity of D.I. water, and we found that the cleanliness of the wafer surface processed in D.I. water bath was affected by the degree of the ionic impurity contamination. So we evaluated the cleaning effect as different method for Fe ion, having the best adsoptivity on wafer surface. Moreover the temperature effect of the D.I. water is investigated in case of anion in order to remove the chemical residue after wet process. In addition to the control of D.I. water resistivity, chemical analysis of impurity control in D.I. water should be included and a suitable cleaning an drinsing method needs to be investigated for a high yielding semiconductor device.

• Fashion & Textile Research Journal
• /
• v.3 no.3
• /
• pp.283-289
• /
• 2001

Shrink resist finishing of wool fabric was carried out with Monoethanol aminesulphite (MONAMIN BTN) shrink resist agent after chlorination with Dichloro isocyanuric acid (DCCA). The purpose of this study is to investigate the effect of treating conditions, such as concentrations of DCCA and MONAMIN BTN, pH of treating bath, dyeing times, curing times and temperatures, on dyeing property of wool fabrics. K/S values and fastness properties of dyed wool fabrics were measured. The K/S values of dyed fabrics were increased gradually with increasing concentration, and decreased with increasing curing time. The optimum dyeing time and curing temperature were 60 min and $140^{\circ}C$, respectively. Also it seems likely that the shrink resist finishing carried out at 3% (o.w.f.) of MONAMIN BTN and pH 7 of resin treating bath is effective in increasing K/S values. Light fastness of fabric dyed was very poor and the fastness of fabric dyed was not influenced by the treatment conditions.

• Journal of the Optical Society of Korea
• /
• v.19 no.3
• /
• pp.217-221
• /
• 2015

Developing a metallization that has low cost and high efficiency is essential in solar-cell industries, to replace expensive silver-based metallization. Ni/Cu two-step metallization is one way to reduce the cost of solar cells, because the price of copper is about 100 times less than that of silver. Alkaline electroless plating was used for depositing nickel seed layers on the front electrode area. Prior to the nickel deposition process, 2% HF solution was used to remove native oxide, which disturbs uniform nickel plating. In the subsequent step, a nickel sintering process was carried out in $N_2$ gas atmosphere; however, copper was plated by light-induced plating (LIP). Plated nickel has different properties under different bath conditions because nickel electroless plating is a completely chemical process. In this paper, plating bath conditions such as pH and temperature were varied, and the metal layer's structure was analyzed to investigate the adhesion of Ni/Cu metallization. Average adhesion values in the range of 0.2-0.49 N/mm were achieved for samples with no nickel sintering process.

• Current Photovoltaic Research
• /
• v.7 no.2
• /
• pp.33-37
• /
• 2019

In this paper, we compared the performance of $Cu(In,Ga)(S,Se)_2$ (CIGSSe) thin film solar cell with CdS buffer layer deposited by irradiating 365 nm UV light with 8 W power in Chemcial Bath Deposition (CBD) process. The effects of UV light irradiation on the thin film deposition mechanism during CBD-CdS thin film deposition were investigated through chemical and electro-optical studies. If the UV light is irradiated during the solution process, the hydrolysis of Thiourea is promoted even during the same time, thereby inhibiting the formation of the intermediate products developed in the reaction pathway and decreasing the pH of the solution. As a result, it is suggested that the efficiency of the CdS/CIGSSe solar cell is increased because the ratio of the S element in the CdS thin film increases and the proportion of the O element decreases. This is a very simple and effective approach to control the S/O ratio of the CdS thin film by the CBD process without artificially controlling the process temperature, solution pH or concentration.

• Analytical Science and Technology
• /
• v.36 no.4
• /
• pp.152-160
• /
• 2023

Adenosine and cordycepin are bioactive compounds with health benefits. Therefore, both substances are often used to assess the quality of Cordyceps products. Optimization and validation of the HPLC/DAD method for determining two nucleosides were studied. The samples were prepared using an ultrasound-assisted extraction (ultrasonic bath). The result was optimal conditions for aqueous extraction, an extraction time of 35 min, and an extraction temperature of 40 ℃. The Chromatographic separation was achieved using a reverse phase column (InfinityLab Poroshell 120 EC-C18, 4.6 × 250 mm, 2.7 ㎛) at 30 ℃ with a mobile phase gradient elution of water and methanol at a flow rate of 0.7 mL/min. The eluents were monitored via a diode array detector at 260 nm. Two nucleosides were separated by less than 12 min after injection. The developed method was found to be excellent linear (r² > 0.9999), accurate (% recovery 95.34-98.51), and precise (% relative standard deviation < 2.0). The limit of detection (LOD) and quantification (LOQ) were 0.45 and 1.38 mg/mL for adenosine and 0.47 and 1.43 mg/mL for cordycepin, respectively. This method was satisfactory for simultaneously quantitating two nucleoside contents, which were used to evaluate Cordyceps products.

• CELLMED
• /
• v.4 no.1
• /
• pp.3.1-3.8
• /
• 2014

Spa represents a treatment widely used in many rheumatic diseases (RD). The mechanisms by which immersion in mineral or thermal water ameliorates RD are not fully understood. The net benefit is probably the result of a combination of factors, among which the mechanical, thermal and chemical effects are most prominent. Buoyancy, immersion, resistance and temperature play important roles. According to the gate theory, pain relief may be due to the pressure and temperature of the water on skin; heat may reduce muscle spasm and increase the pain threshold. Mud-bath therapy increases plasma ${\beta}$-endorphin levels and secretion of corticotrophin, cortisol, growth hormone and prolactin. It has recently been demonstrated that thermal mud-bath therapy induces a reduction in circulating levels of prostaglandin E2, leukotriene B4, interleukin-$1{\beta}$ and tumour necrosis factor-${\alpha}$, important mediators of inflammation and pain. Furthermore, balneotherapy has been found to cause an increase in insulin-like growth factor-1, which stimulates cartilage metabolism, and transforming growth factor-${\beta}$. Beneficial anti-inflammatory and anti-degenerative effects of mineral water were confirmed in chondrocytes cultures, too. Various studies in vitro and in humans have highlighted the positive action of mud-packs and thermal baths, especially sulphurous ones, on the oxidant/antioxidant system. Overall, thermal stress has an immunosuppressive effect. Many other non-specific factors may also contribute to the beneficial effects observed after spa therapy in some RD, including effects on cardiovascular risk factors (e.g. adipokines) and changes in the environment, pleasant surroundings and the absence of work duties.