• Tribology and Lubricants
• /
• 제17권6호
• /
• pp.459-466
• /
• 2001

In this study, the effects of oxide layer formed on the contact parts of TiN coated ball and steel disk on friction characteristics in various sliding conditions were investigated. AISI52100 steel ball was used for the substrate of coated ball specimens, which were prepared by depositing TiN coating with 1(m in coating thickness. AISI1045 steel was used for the disk type counter-body. To investigate the effect of oxide layer on the contact parts of two materials, the tests were performed both in air for forming oxide layer on the contact parts and in nitrogen environment to avoid oxidation. From the test results, the frictional characteristic between the two materials was predominated by iron oxide layer that formed on wear tract of counter-body and this layer caused friction transition and high friction. And the adhesive wear occurred from steel disk to TiN coated ball caused the formation of oxide layer on counter parts between the two materials.

• 한국정밀공학회지
• /
• 제20권1호
• /
• pp.179-186
• /
• 2003

This paper is to investigate the wear behavior of submerged-arc claddings by the wear test with a ball-on-disk type wear testing machine in air. The specimens were clad with Stoody105 alloy wire on a medium carbon steel (SM45C) substrate by submerged-arc cladding process under different welding parameters. The wear behavior of the cladding through ball-on-disk test has been studied under the wear load from 5 to 16 N and the sliding speed from 8 to 35 cm/s. The weight loss of the specimen was measured. Scanning electron micrographs of the worn surface show a layer of oxide film formed on the worn surface. Oxidation wear mechanism controls the wear process. The spatting of the oxide is caused by the repeated rubbing fatigue mechanism.

• 한국정밀공학회:학술대회논문집
• /
• 한국정밀공학회 2002년도 춘계학술대회 논문집
• /
• pp.844-847
• /
• 2002

This paper is to investigate the wear behavior of submerged-arc clad materials by the wear test with a ball-on-disk type wear testing machine in air. The specimens were clad with Stoody105 alloy wire on a carbon steel (SM45C) substrate by submerged-arc cladding process under different welding parameters. The wear behavior of the cladding through ball-en-disk test has been studied under the wear load from 5N to 16N and sliding speed from 8cm/s to 35cm/s. The weight of the specimen loss was measured. Scanning electron micrographs of the worn surface show a layer of oxide film formed on the worn surface. Oxidation wear mechanism controls the wear process. The spalling of the oxide is caused by the repeated rubbing fatigue mechanism.

• 열처리공학회지
• /
• 제27권2호
• /
• pp.65-71
• /
• 2014

SMF9060 material is a Fe-based powder sintered alloy that is used for several automobile components such as Synchronize Hub, oil pump and transmission. These components are required excellent wear resistance and durability. In this study, we have performed a dry wear test at the ambient air and Ar gas conditions in the room temperature, and a lubricant wear test at the room temperature and engine oil temperature of $100^{\circ}C$. The amount of wear volume and coefficient friction are measured by a Profilometer and a Ball on disk type wear tester. The wear volume in Ar gas condition was a little higher than that in the ambient air condition. However the wear volume in the lubricant wear condition was much lower than in the dry wear condition. XRD analysis of the debris in Ar gas condition showed that the oxide film was not formed.

• 대한의용생체공학회:의공학회지
• /
• 제20권1호
• /
• pp.99-106
• /
• 1999

인공관절용 재료의 내마모성 향상을 목적으로 초고분자량 폴리에틸렌(UHMWPE)을 가교시켜 기계적 성질과 내마모성을 조사하였다. 가교제로 dicumyl peroxide(DCP)를 사용하고 가교보조제로 triallyl cyanurate(TAC)를 사용하여 용융상태에서 UHMWPE를 가교시켰다. DCP와 TAC의 함량이 증가할수록 가교된 초고분자량 폴리에틸렌(XUMPE)의 젤 함량은 증가하고 녹는점, 결정화온도, 결정화도, 인장성질은 감소하였다. Pin-on-disk 마모시험과 작은 하중을 가한 ball-on-disk 마모시험에서는 기계적 성질의 감소에도 불구하고 XUMPE의 마모부피가 UHMWPE보다 감소하였다. 이 두 시험에서의 마모는 주로 변형에 의한 것으로 판단되었으며, 마모부피는 Hertz 접촉 이론으로 계산한 최대접촉응력과 XUMPE의 항복강도의 비에 비례함을 보였다. 큰 하중을 가한 ball-on-disk 마모시험에서는 기계적 성질이 낮을수록 더 큰 마모부피를 보였으며, 마모자국의 표면거칠기와 마찰계수도 증가하였다. 이는 인장강도를 넘는 응력이 가해졌을 때 항복강도와 인장강도가 더 낮은 XUMPEDml 변형과 파괴가 촉진되기 때문으로 생각되었다.

• 한국윤활학회:학술대회논문집
• /
• 한국윤활학회 2001년도 제34회 추계학술대회 개최
• /
• pp.109-116
• /
• 2001

In this study, the effects of oxide layer formed on the contact parts of TiN coated ball and steel disk in sliding are investigated. Also wear mechanism to form the oxide layer and the characteristics of the oxide layer formation are investigated. AIS152100 steel ball is used for the substrate of coated ball specimens. Two types of coated ball specimens were prepared by depositing TiN coating with 1 and 4um in coating thickness. AISI1045 steel is used for the disk type counter-body. To investigate the effect of oxide layer on the contact parts of the two materials, the tests were performed both in ambient for forming oxide layer on the contact parts and in nitride environment to avoid oxidation. And to study the effects of surface roughness of counter-body, TiN coating thickness and contact load of sliding test on the characteristics of oxide layer formation on counter-body, various tests were carried out. From the results, the friction characteristics between the two materials was predominated by iron oxide layer that formed on wear track on counter-body and this layer caused the high friction. And the formation rate of the oxide layer on wear track increased as the real contact area between the two materials increased as the contact load increased, the TiN coating thickness decreased and the surface of counter-body smoothened.

• 대한기계학회논문집A
• /
• 제27권3호
• /
• pp.335-342
• /
• 2003

In this study, the effects of oxide layer formed on the contact parts of TiN coated ball and steel disk in sliding are investigated. Also wear mechanism to from the oxide layer and the characteristics of the oxide layer formation are investigated. AISI 52100 steel ball is used for the substrate of coated ball specimens. Two types of coated ball specimens were prepared by depositing TiN coating with 1 and 4 ${\mu}{\textrm}{m}$ in coating thickness. AISI 1045 steel is used for the disk type counter-body. To investigate the effect of oxide layer on the contact parts of the two materials, the tests were performed both in air for forming oxide layer on the contact parts and in nitrogen environment to avoid oxidation. And to study the effects of surface roughness of counter-body, TiN coating thickness and contact load of sliding test on the characteristics of oxide layer formation on counter-body, various tests were carried out. From the results, the friction characteristics between the two materials was predominated by iron oxide layer that formed on wear track on counter-body and this layer caused the high friction. And the formation rate of the oxide layer on wear track increased as the real contact area between the two materials increased as the contact load increased, the TiN coating thickness decreased and the surface of counter-body smoothened.

• 한국소성가공학회:학술대회논문집
• /
• 한국소성가공학회 2009년도 추계학술대회 논문집
• /
• pp.354-357
• /
• 2009

The effect of texture of an extruded OFHC Cu rod on its sliding wear has been explored. Disk specimens with three different orientations were machined from the Cu rod for the wear test; surfaces of the disk were perpendicular ($0^{\circ}$), inclined with a specific angle ($45^{\circ}$), and parallel ($90^{\circ}$) to the extrusion axis of the rod. The texture was analyzed using an X-ray goniometer by measuring {111}, {200}, and {220} pole figures of each specimen. The analyzed texture was correlated with wear-test results of the Cu specimen. Dry sliding wear tests were performed at room temperature using a pin-on-disk wear tester against an Al2O3 ball. Applied load, sliding distance, sliding speed were fixed as 20 N, 200 m, and 0.5 m/sec, respectively. The $45^{\circ}$-inclined (to the extrusion axis) disk specimen showed the lowest wear resistance with the least data scatters. It has been found that distribution of cube texture strongly influences wear rate of the extruded Cu rod.

• Tribology and Lubricants
• /
• 제11권5호
• /
• pp.144-149
• /
• 1995

Use of high-quality basestocks is increasing to produce high-performance lubricants. However, their tribological characteristics have not been understood clearly yet. In this study, a newly developed basestock from a fuel hydrocracker and a poly-alpha-olefin are selected and investigated on the properties of lubricants formulated with them. The Lubricants are prepared by blending the basestocks with typical additives such as a zinc dialkyldithiophosphate, a dispersant, a detergent and a dispersant-inhibitor package. Frictional and wear-preventing properties are investigated using an oscillating-type wear-testing machine. The contact is a ball-on-disk mode and the testing temperature is varied from room temperature to 200$^{\circ}$C. The results show that their frictional property is varied significantly and that the non-conventional oils result in lower friction and lower wear compared with conventional lubricants, especially at the higher temperatures.

• 한국윤활학회:학술대회논문집
• /
• 한국윤활학회 1998년도 제28회 추계학술대회
• /
• pp.292-299
• /
• 1998

The effect of characteristic of surface roughness on friction and sliding wear was studied experimentally with ball-on-disk type wear tester. The test was conducted with specimens those have varying arithmetic mean value, skewness and kurtosis under the condition of different load, sliding speed and lubricant viscosity. The surface of the lower skewness in negative value or the highel kurtosis tends to have low friction for the same arithmetic mean value. There is optimum arithmetic mean value surface roughness for operating variables have load, speed, etc.