A lithiated compound $Li_{0.1}Pr^{3+}Ba_2Cu_3O_y$ has been successfully prepared by electrochemical method, which is achieved with a two electrode cell of the type: Metal(Li)/($Li^+\;,\;ClO_4^-$) + propylene carbonate/$PrBa_2Cu_3O_y$. All Pr ions in the lithiated compound are stabilized with a trivalent state as the other rare earths (Ⅲ) substituted in the 90K superconductor lattice ($Y_{1-x}Ln_x^-Ba_2Cu_3O_{7-{\delta}}$). Powder X-ray diffraction analysis shows that both compounds, $PrBa_2Cu_3O_y$ and $Li_{0.1}PrBa_2Cu_3O_y$ are isostructural with the 90 K superconductor, ($YBa_2Cu_3O_{7-{\delta}}$), nevertheless both of them are non-metallic and also non-superconducting down to 10 K. Magnetic susceptibility ${\chi}$ vs. temperature data indicate that Curie contribution from the magnetic ions (Pr and Cu) is weakened on the one hand, but on the other hand temperature-independent part of susceptibility ${\chi}_o$ increases depending upon the rate of lithium intercalation in $PrBa_2Cu_3O_y$ lattice.

• The Korean Journal of Ceramics
• /
• 제5권4호
• /
• pp.379-385
• /
• 1999

Minute boehmite crystals with high aspect rations, which were hydrothermally synthesized from gibbsite in $Ba(OH)_2$ solution, occluded Ba with the Ba/Al molar ratio of about 0.03 in their interlayers. Their surface areas were about 14$\m^2$/g. The Ba-intercalated bohemite samples were partly used for producing $BaAl_{12}O){19}$ with low sinterability by externally supplementing $Ba(OH)_2$, and for forming transient aluminas. The surface area of $BaAl_{12}O){19}$ obtained by firing at $1500^{\circ}C$ for 3 h was 5.3$\m^2$/g, which was significantly lower than 12$\m^2$/g of the sol-gel origin. While a mixture ${\gamma}$-alumina and BaO is known to from $BaAl_{12}O){19}$ at $1200^{\circ}C$, solid state reaction between η-alumina transformed from the Ba-intercalated boehmite and BaO formed from $Ba(OH)_2$ deposited on the boehmite started above $1300^{\circ}C$. This suggests that large sized $Ba^{2+}$ ion occluded in η-alumina considerably suppresses the diffusion of $Al^{3+}$ ion. The surface area of the Ba-intercalated boehmite fired at $1400^{\circ}C$ for 3h was as high as 14$\m^2$/g indicative of its potential applicability to combustion catalysts. But it was decreased to 5.0$\m^2$/g after firing at $1500^{\circ}C$ for 3 h, accompanied by abrupt formations of $\alpha$-alumina and $BaAl_{12}O){19}$ as main products. The suppression of $\alpha$-alumina formation up to $1400^{\circ}C$ also suggests the significant blocking effect of $Ba^{2+}$ ion on the diffusion of the component ions.

• 한국세라믹학회지
• /
• 제25권2호
• /
• pp.154-160
• /
• 1988

Almost single phase of Y1Ba2Cu3Ox, which exhibits the onset of superconducting transition at 90K, has been prepared via a conventional ceramic processing route followed by an anneal for a period of 10 hours at 45$0^{\circ}C$ in an atmosphere of 100% O2. The mean value for the oxygen content has been determined as x=6.85$\pm$0.02 by an iodometric titration technique. X-ray photoemission spectra are found to be consistent with a mixture of the d8(Cu3+) and d9(Cu2+) as the ground state and reveals that the local concentration of Cu3+ decreases with depth from the surface where x corresponds to 7.0. This is explained as being associated with the intercalation of oxygen during cooling from the annealing temperature.