• Journal of the Korean Society of Propulsion Engineers
• /
• v.7 no.4
• /
• pp.73-79
• /
• 2003

The tensile strength test and the analysis for the section of brazing were performed in the cases of materials used for combustion chamber of regeneratively cooled liquid rocket engine. BNi-2 and BNi-7 based on nickel were used for brazing as filler metal. The properties of material and filler metal were analyzed by tensile strength test and metal microscope for 12 specimens. The tensile-strength of brazing for chrome-copper alloy and other kinds of alloy was higher than that of chrome-zirconium-copper alloy and other kinds of alloy The tensile strength in the case of BNi-2 as filler metal was higher than that of BNi-7 because the wetting property of BNi-2 was better than that of BNi-7.

• Korean Journal of Materials Research
• /
• v.17 no.3
• /
• pp.142-146
• /
• 2007

Vacuum brazing method has been coming to an important process as one of the new fabricating techniques of metals and alloys. In this study, a vacuum brazing of SUS304 stainless steel with BNi-2 filler metal was carried out in $1{\times}10^{4}$ Torr of vacuum atmosphere. The formation of brittle intermetallic compounds in brazed joints between SUS304 stainless steel and BNi-2 filler metal is a major concern, since they considerably degrade the mechanical properties of joints. To obtain enough stable joining strength, it is necessary to understand the unique properties of brazing process with Ni-based filler metals containing boron. So, in this research we investigated the performance of SUS304/BNi-2 brazed system and the brazed joint properties were evaluated at room temperature by using tensile test. Metallurgical and fractographic analysis were used to characterize the microstructure, the mechanisms of brazing, and joint failure modes.

• Korean Journal of Materials Research
• /
• v.17 no.3
• /
• pp.179-183
• /
• 2007

A plate heat exchanger (PHE) normally uses vacuum brazing technology for connecting plates and fins. However, the reliability of high temperature brazing, especially with nickel-based filler metals containing boron the formation of brittle intermetallic compounds (IMCs) in brazed joints is of major concern. since they considerably degrade the mechanical properties. This research was examined the vacuum brazing of commercially SUS304 stainless steel with BNi-2 (Ni-Cr-B-Si) filler metal, and discussed to determine the influence of brazing temperatures on the microstructure and mechanical strength of brazed joints. In the metallographic analysis it is observed that considerable large area of Cr-B intermetallic compound phases at the brazing layer and the brazing tensile strength is related to removal of this brittle phase greatly. The mechanical properties of brazing layer could be stabilized through increasing the brazing temperature over $100^{\circ}C$ more than melting temperature of filler metals, and diffusing enough the brittle intermetallic compound formed in the brazing layer to the base metal.

• Korean Journal of Materials Research
• /
• v.17 no.6
• /
• pp.342-346
• /
• 2007

Microstructure and tensile strength of the vacuum brazed stainless steel were investigated in this study. For vacuum brazing of the stainless steel 303 and 304, the BNi-2, 3, 4 and 7 were used as filler metals. Among these filler metals, the BNi-2 showed excellent wettability at $1050^{\circ}C$. Indeed, the brazed stainless steel using the BNi-2 showed the highest tensile strength (483 MPa) among all brazed specimens. This is attributed to degree of interfacial reaction between the filler metal and stainless steel. Brazed stainless steel with BNi-2, 3 filler metals showed almost elastic deformation followed by plastic yielding and strain hardening up to a peak stress. On the other hand, it is likely that the fracture of the brazed specimens with BNi-4, 7 was occurred in elastic range without plastic yielding up to a peak stress.

• The KSFM Journal of Fluid Machinery
• /
• v.19 no.3
• /
• pp.48-52
• /
• 2016

Microstructure and tensile strength of the vacuum brazed stainless steel(STS304) and WC-8 %Co were investigated. For brazing, the BNi-2, 3(A.W.S standard) were used as filler metals. It was found that metallic compounds of W-Ni were observed at the between WC metrix and brazed layer. Among these filler metals, the BNi-2 showed excellent wettability, but tensile strength was lower than BNi-3. The fracture of the brazed specimens with BNi-2 was occurred at the between WC metrix and brazed layer. The fracture of the brazed specimens with BNi-3 was occurred at the between WC metrix and brazed layer, and between brazed layer and stainless steel.

• Korean Journal of Materials Research
• /
• v.15 no.6
• /
• pp.399-407
• /
• 2005

The effect of IN738 additive powder on microstructure and mechanical properties of the wide-gap region brazed with BNi-3 filler metal powder was investigated. The wide-gap brazing was conducted in a vacuum of $2\times10^{-5}torr\;at\;1200^{\circ}C$ with various powder mixing ratios of additive to filler powders. The microstructures of the wide-gap brazed region were analyzed by SEM and AES. The region brazed with only BNi-3 filler metal powder had a microstructure consisted of proeutectic, binary eutectic and ternary eutectic structure, while that brazed with a mixture of IN738 additive powder and BNi-3 filler metal powder had a microstructure consisted of IN738 additive powder, binary eutectic of $Ni_3B-Ni$ solid solution and (Cr, W)B. The fracture strength of the wide-gap brazed region was about 680 MPa regardless of the additive powder mixing ratios. Cracks were initiated at the (Cr, W)B and binary eutectic of $Ni_3B-Ni$ solid solution, and propagated through them in the wide-gap brazed region, which lowered the fracture strength of the region.

• 연구논문집
• /
• s.27
• /
• pp.201-208
• /
• 1997

To improve the joining characteristics of metallic converter substrate for exhaust gas cleaning, high temperature brazing process has been studied. In this study, the effect of chemical composition of brazing filler metal on the oxidation behavior of brazed joints was investigated closely. Brazing was carried out at $1200^\circC$ in vacuum furnace using nickel-based filler metals : BNi-5 powder(Ni-Cr-Si base alloy) and MBF-50 foil(Ni-Cr-Si-B). The MBF-50 containing 1-1.5 wt%B showed relatively poor oxidation resistance of the brazed joints compared to BNi-5, because of the faster invasion of oxygen through the Kirkendal voids along the interface of mother alloy/filler metal.

• Korean Journal of Materials Research
• /
• v.17 no.6
• /
• pp.293-297
• /
• 2007

Microstructure and tensile strength of the vacuum brazed stainless steel(STS303) and Cu were investigated. For brazing, the BNi-2, 3, 4, 6 and 7 (A.W.S standard) were used as filler metals. The Oxides such as $Cr_2O_3$ and $SiO_2$ were observed at brazed layers between STS303 and Cu matrix. Also, the intermetallic compounds of Cr-B and Ni-P were observed at brazed layers. Brazed STS303-Cu specimens with BNi-2, 3, 4 filler metals showed almost elastic deformation followed by plastic yielding and strain hardening up to a peak stress. On the other hand, it is likely that the fracture of the brazed specimens with BNi-6 and 7 was occurred in elastic range without plastic yielding up to a peak stress. Among these filler metals, the BNi-2 brazed at $1050^{\circ}C$ showed excellent wettability and the highest tensile strength (101.6MPa).

• 연구논문집
• /
• s.29
• /
• pp.141-149
• /
• 1999

Brazing of Fe-Cr-Al alloy was carried out at $1200^{\circ}C$ in vacuum furnace using nickel-based filler metals : BNi-5 powder(Ni-Cr-Si-Fe base alloy} and MBF-50 foil (Ni-Cr-Si-B). The effect of boron content on the stability of oxide scale on the brazed joint was investigated by means of cyclic oxidation test performed at $1050^{\circ}C$ and $1200^{\circ}C$. Apparently, the joints brazed with MBF-50 containing boron showed relatively stable oxidation rates compared to boron-free BNi-5 at both temperatures. However, it was considered that the slower weight loss of MBF-50 brazed specimen wasn’t resulted from the low oxidation rate but from the spallation of oxide layer. The oxide layer consisted of thick spinel oxide on the surface and $Al_2 O_3$ internal oxide layer along the interface between mother alloy and braze, the mother alloy was also eroded seriously by the formation of spinel oxides such as $FeCr_2 O_4$ and $NiCr_2 O_4$ on the surface, likely to be induced by the change of oxide forming mechanism due to diffusion of boron from the braze. On the contrary, the joint brazed with BNi-5 showed the good oxidation resistance during the cyclic oxidation test. It seems that the oxidation can be retarded by the formation of stable $Al_2 O_3$ layer at the surface.

• Journal of the Korean Society of Mechanical Technology
• /
• v.13 no.2
• /
• pp.137-143
• /
• 2011

Fuel Test Loop(FTL) is a facility which could conduct a fuel irradiation test at HANARO(High-flux Advanced Neutron Application Reactor). FTL simulates commercial NPP's operating conditions such as the pressure, temperature and neutron flux levels to conduct the irradiation and thermo-hydraulic tests. The In-Pile Test Section(IPS) installed in HANARO FTL is designed as a pressure vessel design conditions of $350^{\circ}C$, 17.5MPa. The instrumentation MI-cables for thermocouples, SPND and LVDT are passed through the sealing plug, which is in the pressure boundary region and is a part of instrumentation feedthrough of MI-cable. In this study, the brazing method and performance test results are introduced to the sealing plug with BNi-2 filler metal, which is selected with consideration of the compatibility for the coolant. The performance was verified through the insulation resistance test, hydrostatic test, and helium leak test.