• Journal of the Korean Crystal Growth and Crystal Technology
• /
• v.13 no.6
• /
• pp.272-278
• /
• 2003

$Bi_4Ti_3O_{12}$ (BIT) and $(Bi_{3.25}La_{0.75})(Ti_{2.97}V_{0.03})O_{12}$ (BLTV) thin films were deposited on ITO/glass substrates by metal organic chemical vapor deposition (MOCVD) using ultrasonic spraying. After deposition of the films in oxygen atmosphere for 30 min, the films were heated by rapid thermal annealing (RTA) method, especially direct insertion, at various temperatures. The films were investigated on phase formation temperature, microstructure and electrical properties. From x-ray diffraction (XRD) patterns, the perovskite phase formation temperature of BLTV thin film was about $600^{\circ}C$ which was lower than that of BIT, $650^{\circ}C$. The leakage current of the BLTV thin film was measured to be $1.52\times 10^{-9}$A/$cm^2$ at an applied voltage of 1 V. The remanent polarization (Pr) and coercive field (Ec) values of the BLTV film deposited at $650^{\circ}C$ were $5.6\muC/cm^2$ and 96.5 kV/cm, respectively.