• 한국치위생학회지
• /
• 제20권4호
• /
• pp.535-543
• /
• 2020

Objectives: The aim of this study was to investigated the surface roughness and change in the amount of adhesion of Streptococcus mutans to the commercial pit and fissure sealant containing cerium oxide nano particles(CNPs). Methods: The CNPs was incorporated into a commercial pit and fissure sealant at 0-4.0 wt%. Disk Specimens (ϕ 10 mm × 2 mm) were prepared by light polymerization the front and back for 40s. Average surface roughness was measured and Streptococcus mutans adhesion was observed under confocal laser scanning microscopy (CLSM) after 24 hour. Data were statistically analyzed by one-way ANOVA and Tukey HSD^a post-hoc test. Results: Difference of the surface roughness(Ra) between groups was not statistically significant in both non CNPs group and CNPs group(p>0.05). In CNPs group, the amount of S. mutans adhesion was significantly different between control group and decreased in order of CNPs 4.0, CNPs 0.5, CNPs 1.0 and CNPs 2.0(p<0.05). Conclusions: Within the limitation of this study, these aspects of oral bacteria performances suggest potential usefulness of the CNPs incorporation, especially CNPs 1% and 2%, in pit and fissure sealant for inducing antibacterial effect.

• Transactions on Electrical and Electronic Materials
• /
• 제9권2호
• /
• pp.73-78
• /
• 2008

We investigated for comparison of large-area i-a-Si:H and p-a-SiC:H film quality like thickness uniformity, optical bandgap and surface roughness using both ICP-CVD and PECVD on the large-area substrate(diameter of 100 mm). As a whole, films using ICP-CVD could be achieved much uniform thickness and bandgap of that using PECVD. For i-a-Si:H films, its uniformity of thickness and optical bandgap were 2.8 % and 0.38 %, respectively. Also, thickness and optical bandgap of p-a-SiC:H films using ICP-CVD could be obtained at 1.8 % and 0.3 %, respectively. In case of surface roughness, average surface roughness (below 5 nm) of ICP-CVD film could be much better than that (below 30 nm) of PECVD film. HIT solar cell with 2 wt%-AZO/p-a-SiC:H/i-a-Si:H/c-Si/Ag structure was fabricated and characterized with diameter of 152.3 mm in this large-area ICP-CVD system. Conversion efficiency of 9.123 % was achieved with a practical area of $100\;mm\;{\times}\;100\;mm$, which can show the potential to fabrication of the large-area solar cell using ICP-CVD method.

• Restorative Dentistry and Endodontics
• /
• 제44권2호
• /
• pp.19.1-19.9
• /
• 2019

Objectives: The purpose of this study was to evaluate the cyclic fatigue, bending resistance, and surface roughness of EdgeEvolve (EdgeEndo) and ProTaper Gold (Dentsply Tulsa Dental Specialties) nickel-titanium (NiTi) rotary files. Materials and Methods: The instruments (n = 15/each) were tested for cyclic fatigue in single- ($60^{\circ}$ curvature, 5-mm radius) and double-curved (coronal curvature $60^{\circ}$, 5-mm radius, and apical curvature of $30^{\circ}$ and 2-mm radius) artificial canals. The number of cycles to fracture was calculated. The bending resistance of both files were tested using a universal testing machine where the files were bent until reach $45^{\circ}$. Scanning electron microscopy and x-ray energy-dispersive spectrometric analysis were used for imaging the fractured segments, while the atomic force microscope was used to quantify the surface roughness average (Ra). Results: EdgeEvolve files exhibited higher cyclic fatigue resistance than ProTaper Gold files in single- and double-curved canals (p < 0.05) and both files were more resistant to cyclic fatigue in single-curved canals than double-curved canals (p < 0.05). EdgeEvolve files exhibited significantly more flexibility than did ProTaper Gold files (p < 0.05). Both files had approximately similar Ni and Ti contents (p > 0.05). EdgeEvolve files showed significantly lower Ra values than ProTaper Gold files (p < 0.05). Conclusions: Within the limitation of this study, EdgeEvolve files exhibited significantly higher cyclic fatigue resistance than ProTaper Gold files in both single- and double-curved canals.

• 한국표면공학회:학술대회논문집
• /
• 한국표면공학회 2016년도 추계학술대회 논문집
• /
• pp.105-105
• /
• 2016

Recently, high power impulse magnetron sputtering (HIPIMS) has attracted considerable attentions due to its high potential for industrial applications. By pulsing the sputtering target with high power density and short duration pulses, a high plasma density and high ionization of the sputtered species can be obtained. HIPIMS has exhibited several merits such as increased coating density, good adhesion, microparticle-free and smooth surface, which make the HIPIMS technique desirable for synthesizing hard coatings. However, hard coatings present intrinsic defects (columnar structures, pinholes, pores, discontinuities) which can affect the corrosion behavior, especially when substrates are active alloys like steel or in a wear-corrosion process. Atomic layer deposition (ALD), a CVD derived method with a broad spectrum of applications, has shown great potential for corrosion protection of high-precision metallic parts or systems. In ALD deposition, the growth proceeds through cyclic repetition of self-limiting surface reactions, which leads to the thin films possess high quality, low defect density, uniformity, low-temperature processing and exquisite thickness control. These merits make ALD an ideal candidate for the fabrication of excellent oxide barrier layer which can block the pinhole and other defects left in the coating structure to improve the corrosion protection of hard coatings. In this work, CrN/Al2O3/CrN multilayered coatings were synthesized by a hybrid process of HIPIMS and ALD techniques, aiming to improve the CrN hard coating properties. The influence of the Al2O3 interlayer addition, the thickness and intercalation position of the Al2O3 layer in the coatings on the microstructure, surface roughness, mechanical properties and corrosion behaviors were investigated. The results indicated that the dense Al2O3 interlayer addition by ALD lead to a significant decrease of the average grain size and surface roughness and greatly improved the mechanical properties and corrosion resistance of the CrN coatings. The thickness increase of the Al2O3 layer and intercalation position change to near the coating surface resulted in improved mechanical properties and corrosion resistance. The mechanism can be explained by that the dense Al2O3 interlayer acted as an excellent barrier for dislocation motion and diffusion of the corrosive substance.

• 한국가구학회지
• /
• 제13권1호
• /
• pp.27-37
• /
• 2002

This study was investigated with the surface properties such as physical and accelerated tests of wood-based floorings. In physical test, hardness and abrasion resistance values of laminate floorings were higher than those of others. The center line average surface roughness($R_a$) of imported laminate flooring was highest value($1.34{\mu}m$) and that of imported solid wood flooring was lowest value($0.62{\mu}m$). In cold resistance and moist heat resistance, no defects were found on the surface of all flooring (crack, blistering, peeling, and gloss loss etc.) after testing. Wet-cold-dry cycle test showed that plywood flooring appeared some cracks. In accelerated weathering test, color difference increased with increasing Xenon arc light irradiation

• 한국전기전자재료학회:학술대회논문집
• /
• 한국전기전자재료학회 1996년도 추계학술대회 논문집
• /
• pp.320-325
• /
• 1996

The influences of ZrB$_2$additives to the SiC and pulse width on electrical discharge machining of SiC-ZrB$_2$electroconductive ceramic composites were investigated. IIigher-flexural strength materials show a trend toward smaller crater volumes, leaving a soother surface; the average surface roughness of the SiC-ZrB$_2$15 Vol.% Composite with the flexural strength of 375㎫ was 3.2${\mu}{\textrm}{m}$,whereas the SiC-ZrB$_2$30 Vol.% composite of 457㎫ was 1.35${\mu}{\textrm}{m}$. In the SEM micrographs of the fracture surface of SiC-ZrB$_2$composites, the SiC-ZrB$_2$two phaes are distinct; the white phase is the ZrB$_2$. In the micrograph of the EDM surface, however, these phases are no longer distinct because of thicker recast layer of resolidified-melt-formation droplets present.

• 한국소성가공학회:학술대회논문집
• /
• 한국소성가공학회 2009년도 춘계학술대회 논문집
• /
• pp.282-285
• /
• 2009

Selective laser sintering (SLS) is a fast growing process of rapid production fur metallic based parts. To restore damaged mold surface using SLS, single layer experiments of $20{\mu}m$ Fe-Cr powder was performed under various heat input. Process window of $20{\mu}m$ Fe-Cr powder provided feasible process parameters for the smooth regular surface. To estimate coherence between melted powder and basematal, tendency of hardness distribution has been observed. Hardness of melted zone and remelted zone was diversified from 5GPa to 6.5GPa. It is over 2 times compared of hardness of basemetal. Average surface roughness of each direction on surface of melted powder was measured. Experimental results show that the mold restoring process using SLS can be successfully applied in the mold repair industry.

• 한국세라믹학회지
• /
• 제36권4호
• /
• pp.417-424
• /
• 1999

Laser lapping of diamond films is performed with focused beam of copper vapor laser. Both spherical and rod-shape laser beam are used. Diamond surface is scanned at various scan speeds(0,125, 0.5, 0.75 mm/sec) and baem shifts (5, 10, 20, 40, 100$\mu\textrm{m}$) At 0.125 mm/sec 10$\mu\textrm{m}$ scan condition the level difference of di-amond surface of about 700$\mu\textrm{m}$ over 20 mm is reduced to 200$\mu\textrm{m}$ In addition surface roughness is also im-proved from 3.53$\mu\textrm{m}$ to 2.47$\mu\textrm{m}$ at 5$\mu\textrm{m}$ beam shift. But at higher beam shift than 10$\mu\textrm{m}$ laser scan makes the surface rougher which is considered to be due to the non uniform spatial distribution of laser en-ergy. It is concluded that homogenized laser beam with high average power is needed for large area laser lapping of diamond films at appreciable rates.

• Corrosion Science and Technology
• /
• 제8권5호
• /
• pp.193-196
• /
• 2009

For the estimation of uncertainty in potentiodynamic polarization resistance measurement, the type A uncertainty was measured using type 316 stainless steel in an acidified NaCl solution. Sensitivity coefficients were determined for measurand such as scan rate of potential, temperature of solution, concentration of NaCl, concentration of HCl, surface roughness of specimen and flow rate of purging gas. Sensitivity coefficients were large for the measurand such as the scan rate of potential, temperature of solution and roughness of specimen. However, the sensitivity coefficients were not the major factors influencing the combined standard uncertainty of polarization resistance due to the low values of uncertainty in measurements of the measurands. A major influencing factor was the concentration of NaCl. The value of type A uncertainty was 1.1 times the value of type B uncertainty, and the combined standard uncertainty was 10.5 % of the average value of polarization resistance.

• KSTLE International Journal
• /
• 제6권1호
• /
• pp.21-27
• /
• 2005

A technique for a wear volume calculation is improved and verified in this research. The wear profile data measured by a surface roughness tester is used. The present technique uses a data flattening, the FFT and the windowing procedure, which is used for a general signal processing. The measured value of an average roughness of an unworn surfnce is used for the baseline of the integration for the volume calculation. The improvements from the previous technique are the procedures of the data flattening and the determination of a baseline. It is found that the flattening procedure efnciently manipulates the raw data when the levels of it are not horizontal, which enables us to calculate the volume reasonably well and readily. By comparing it with the weight loss method by using artificial dents, the present method reveals more volume by aroung 3~10%. It is attributed to the protruded region of the specimen and the inaccuracy and data averaging during the weght loss measurement. From a thorough investigation, it is concluded that the present technique can provide an accurate wear volume.