• Korean Journal of Metals and Materials
• /
• v.46 no.11
• /
• pp.708-712
• /
• 2008

The influence of high temperature gas nitriding (HTGN) in STS347 and STS310S steels was experimentally investigated. The HTGN was carried out at $1,050^{\circ}C{\sim}1,150^{\circ}C$ for 10 hrs in a gaseous atmosphere containing $1kg/mm^2$ of nitrogen. After HTGN, fine precipitates of $Cr_2N$ and NbN appeared in austenite on the surface of STS 347, while nitrogen pearlite, which was layeredof $Cr_2N$ and austenite alternatively, appeared in austenite on the surface of STS 310S. The surface hardness of HTGN-treated, STS 347 and STS 310S specimens was 250~360 Hv and 270~400 Hv, respectively, depending on the temperature of HTGN. The nitrogen content was analyzed 1.4 wt% and 1.6 wt% at the surface layer of STS 347 and STS 310S steels, respectively. In addition, an improvement in the corrosion resistance of HTGN treated specimens was observed.

• Journal of the Korea institute for structural maintenance and inspection
• /
• v.22 no.1
• /
• pp.81-89
• /
• 2018

Austenitic stainless steels have excellent corrosion resistance, durability and fire resistance. Especially, since STS304L among austenitic types is a low-carbon variation of STS304 and has excellent intergranular corrosion resistance, it can often be used under the welded condition without heat treatment after field welding. This paper investigated ultimate behaviors such as ultimate strength and weld metal fracture mechanism of STS304L fillet-welded connections with TIG(tungsten inert gas) welding through test results. Main variables of specimens are weld length and welding direction against loading. Fracture of specimens are classified into three modes(tensile fracture, shear fracture and block shear fracture). Ultimate strengths were compared according to the welding direction and weld length and TFW series with transverse fillet weld had the highest strength compared with other types(LFW series with longitudinal fillet weld and FW series with all round weld). It is known that current design specifications such as KBC 2016 and AISC2010 underestimated the strength of TFW and LFW specimens and provided unconservative estimates for FW specimens. Finally, strength equations were proposed considering material properties of STS 304L material.

• Proceedings of the Korean Society of Precision Engineering Conference
• /
• 2005.06a
• /
• pp.1560-1565
• /
• 2005

Laser beam welding is increasingly being used in welding of structural steels. The laser welding process is one of the most advanced manufacturing technologies owing to its high speed and deep penetration. The thermal cycles associated with laser welding are generally much faster than those involved in conventional arc welding processes, leading to a rather small weld zone. Experiments are performed for 304 stainless steel plates changing several process parameters such as laser power, welding speed, shielding gas flow rate, presence of surface pollution, with fixed or variable gap and misalignment between the similar and dissimilar plates, etc. The following conclusions can be drawn that laser power and welding speed have a pronounced effect on size and shape of the fusion zone. Increase in welding speed resulted in an increase in weld depth/ aspect ratio and hence a decrease in the fusion zone size. The penetration depth increased with the increase in laser power.

• Journal of Power System Engineering
• /
• v.19 no.6
• /
• pp.12-18
• /
• 2015

Austenitic stainless steels generally experience the occurrence of chromium-depleted zones at the boundaries, known as sensitization, caused by the carbide precipitation that takes place due to a welding process or heat treatment. Normally, the depleted zones become the focus of the intense corrosion. In this study, the Cr-free organic/inorganic hybrid solution was developed, and the artificially degraded STS316S and STS347H with the solution-coating investigated the corrosion resistance by salt spray test. Both the OIBD-1 and OIBD-2 solutions improved the corrosion resistance of STS310S and STS347H. The corrosion resistance with the OIBD-1 solution was better than that of OIBD-2 solution. Additionally, Both solutions have been proven excellence in adhesion ability, boiling water resistance and flexibility. However, a problem of rubbing after the boiling was found out to be overcome.

• Transactions of the Korean Society of Mechanical Engineers A
• /
• v.28 no.2
• /
• pp.165-173
• /
• 2004

Laser beam welding is increasingly being used in welding of structural steels. The laser welding process is one of the most advanced manufacturing technologies owing to its high speed and deep penetration. The thermal cycles associated with laser welding are generally much faster than those involved in conventional arc welding processes, leading to a rather small weld zone. Experiments are performed for 304 stainless steel plates changing several process parameters such as laser power, welding speed, shielding gas flow rate, presence of surface pollution, with fixed or variable gap and misalignment between the similar and dissimilar plates, etc. The following conclusions can be drawn that laser power and welding speed have a pronounced effect on size and shape of the fusion zone. Increase in welding speed resulted in an increase in weld depth/ aspect ratio and hence a decrease in the fusion zone size. The penetration depth increased with the increase in laser power.

• Nuclear Engineering and Technology
• /
• v.48 no.6
• /
• pp.1412-1422
• /
• 2016

Austenitic stainless steels (ASSs) are widely used for nuclear pipes as they exhibit a good combination of mechanical properties and corrosion resistance. However, high tensile residual stresses may occur in ASS welds because postweld heat treatment is not generally conducted in order to avoid sensitization, which causes a stress corrosion crack. In this study, round robin analyses on stress intensity factors (SIFs) were carried out to examine the appropriateness of structural integrity assessment methods for ASS pipe welds with two types of circumferential cracks. Typical stress profiles were generated from finite element analyses by considering residual stresses and normal operating conditions. Then, SIFs of cracked ASS pipes were determined by analytical equations represented in fitness-for-service assessment codes as well as reference finite element analyses. The discrepancies of estimated SIFs among round robin participants were confirmed due to different assessment procedures and relevant considerations, as well as the mistakes of participants. The effects of uncertainty factors on SIFs were deducted from sensitivity analyses and, based on the similarity and conservatism compared with detailed finite element analysis results, the R6 code, taking into account the applied internal pressure and combination of stress components, was recommended as the optimum procedure for SIF estimation.

• Journal of the Korean Magnetics Society
• /
• v.3 no.4
• /
• pp.277-283
• /
• 1993

The temperature dependence of DC magnetic susceptibilities of three austenitic Fe-Cr-Ni stainless alloys were measured in the temperature range of 4.2 and 300 K. Two alloys support a general magnetic description of austen-itic stsinless steels in terms of a two-magnetic-phase (spin glass + superparamagnetic cluster) model and one alloy shows magnetic double transition phenomena. Also this study shows that incressing the Ni/Cr ratio in Fe-Cr-Ni alloys causes a increase of the DC susceptibility peak value and a decrease of the magnetic transition temperature.

• Proceedings of the Korean Institute of Surface Engineering Conference
• /
• 2007.11a
• /
• pp.65-68
• /
• 2007

저온 플라즈마 기술을 이용하면 오스테나이트계 스테인리스강의 내식성과 표면경도를 동시에 증가 시킬 수 있다. 여러 가지 처리방법 중 질탄화와 2-step 공정으로 처리한 AISI304L강의 표면을 분석하였다. 처리한 모든 시편의 표면은 expanded austenite(${\gamma}_N$)이 형성되었고, 표면 경도도 모재보다 약 4배 이상 증가 하였다. 저온플라즈마 질탄화 공정의 경우 경화층의 두께가 최대 15 ${\mu}m$밖에 형성되지 않았지만 2-step공정의 경우 질탄화 공정보다 짧은 시간으로 약 2배의 경화층을 얻을 수 있었다. 두 가지 공정 모두 온도와 시간이 증가할수록 경화층의 두께가 두꺼워졌지만, 과도하게 높은 온도와 긴 공정시간은 석출물을 형성 시켰다. 석출물이 형성되지 않은 시편의 경우 내식성이 증가하였다.

• Journal of Advanced Marine Engineering and Technology
• /
• v.34 no.5
• /
• pp.678-685
• /
• 2010

GTAW was carried out to the austenitic 304(STS 304) and 22 APU stainless steels. In this case, difference of the corrosion characteristics of welded zone with STS 304 and 22APU mentioned above was investigated with electrochemical methods. Vickers hardness of weld metal in case of STS 304 (Hv-250) showed a relatively higher value than this of 22 APU(Hv-217). The corrosion current densities of weld metal of 22APU and heat affected zone of STS 304 were observed at the highest value compared to those of other welding zone respectively. This is probably because chromium depletion field due to chromium carbide formed to weld metal of 22APU and to heat affected zone of STS 304 can preferentially easily be corroded with more active anode than other fields. Consequently it is thought that application of the other welding methods like as laser welding or using of the optimum filler metals is necessary to improve the corrosion resistance of welding parts of these steels.

• Journal of Ocean Engineering and Technology
• /
• v.20 no.1 s.68
• /
• pp.1-6
• /
• 2006

The effects of microstructure on the damping capacity and tensile properties of 316L stainless steel were investigated. Increasing the degree of cold working, the volume fraction of $\varepsilon-martensite$ decreased after rising to maximum value at specific level of cold working, the volume fraction of d-martensite slowly increased and then dramatically increased from the point of decreasing $\varepsilon-martensite$ volume fraction. Increasing the degree of cold working, the behnvior of damping capacity is similar to that of the $\varepsilon-martensite$. After the damping capacity showing the maximum value at about $20\%$ of cold rolling, damping capacity was decreased with the volume fraction of $\varepsilon-martensite$. Tensile strength was proportional to the volume fraction of d-martensite, and elongation steeply decreased in the range low volume fraction of a'-martensite, then slowly decreased in range the above $10\%$ volume fraction of d-martensite. The damping capacity and elongation is strongly controlled by the volume fraction of $\varepsilon$ martensite with liner relationship. However, the effect of the volume fraction of d-martensite and austenite phase on the damping capacity was not observed. Tensile strength was governed by the volume fraction of d-martensite.