• Journal of Korea Foundry Society
• /
• v.9 no.6
• /
• pp.463-473
• /
• 1989

This study is aimed to investigate the effect of cyclic heat treatment which is special heat treatment on the strength and toughness in Multi-phase(Ferrite-Bainite-Martensite) Ductile cast Irons. Spceimens were austenitized at eutectoid transformation temperature range(${\alpha}+{\gamma}$) for 30min and austempered at $300^{\circ}C$ and $400^{\circ}C$ for different holding times, and then quenched in ice water to obtain the multi-phase(Ferrite-Bainite-Martensite) structure from various prior structures, which was obtained by various cyclic heat treatments. As the number of cycle in cyclic heat treatment increased, volume fraction of pearlite increased and the its morphology was refined. As the number of cycle in cyclic heat treatment increased, the multi-phase(Ferrite-Bainite-Martensite) was dispersed in whole matrix as refined island phase. Particularly, martensite among the multi-phase gradually became a spherical shape. Good combination in impact energy and tensile strength was detained in $840^{\circ}C-300^{\circ}C-15min$ condition after 10 cycles in cyclic heat treatment, and its multi-phase volume fraction is Ferrite(50%)-Martensite(l3%)-Bainite(37%).

• Journal of the Korean Society for Heat Treatment
• /
• v.11 no.4
• /
• pp.333-341
• /
• 1998

The study was investigated on the effect of austenitizing and austempering conditions on retained austenite amount and carbon contents in retained austenite and simultaneously the effect of these variation on hardness, tensile and impact properties. A material of as-cast condition is composed of bull's eye structure with ferrite surrounding spheroidized graphite having about $5-10{\mu}m$ size and matrix structure of pearlite. Then, the contents of spheroidized graphite was about 5%. The retained austenite and carbon contents in the retained austenite were increased with the increasing of austenitizing and austempering temperatures, while the retained austenite showed the peak value and is decreased with increasing of austempering time. With increasing of austenitizing temperature, tensile strength, elongation and impact absorb energy increased and hardness was almost not changed, while with increasing of austempering temperature, tensile strength and hardness decreased, whereas elongation and impact absorb energy was increased. With increasing of retained austenite amount, the tensile strength is slowly decreased but elongation was increased with direct proportion. Also, Impact absorb energy is shown identity value untile about 18%, but rapidly increased above it. Elongation and Impact absorb energy are strongly controlled by the amount of retained austenite, but tensile strength is affected with various factors such as retained austenite amount and bainitic morphology.