• Journal of IKEEE
• /
• v.21 no.3
• /
• pp.288-296
• /
• 2017

The enhancement of photoluminescence of Au-$TiO_2$ nanoparticles by surface plasmon resonance has been studied extensively by experiment in recent years. For the purpose of optimizing the photoluminescence property of Au-$TiO_2$ nanoparticles, the manufacturing parameters related to the Au nanoparticles and $TiO_2$ nanoparticles need to be considered. In this paper, Drude model and Maier's effective volume method are used to analyze the variation of the metal nanoparticle radius, separation between metal nanoparticle and dielectric molecule, and total absorption cross-section with original radiative efficiency on the photoluminescence property of Au-$TiO_2$ nanoparticles. The results show that to obtain the optimized enhancement factor for photoluminescence process, the size of Au nanoparticle is about 13 - 20 nm, the separation between Au nanoparticle and $TiO_2$ molecule is about 5 -15 nm, the total absorption cross-section of $TiO_2$ molecules is about $1-100nm^2$ and the original radiative efficiency of $TiO_2$ molecule is weak about 0.001- 0.1. With these fabrication parameters, the photoluminescence property of Au-$TiO_2$ nanoparticles can be enhanced several thousand times compared to traditional $TiO_2$ nanoparticles.

• Korean Journal of Materials Research
• /
• v.16 no.8
• /
• pp.524-528
• /
• 2006

On the synthesis of Au/$TiO_2$ core-shell structure nanoparticle, the effect of concentration of $Ti^{4+}$ and reaction temperature on the morphology and optical property of Au/$TiO_2$ core-shell nanoparticles is examined. A gold colloid was prepared by $HAuCl_4{\cdot}4H_2O\;and\;C_6H_5Na_3{\cdot}2H_2O$. Titanium stock solution was prepared by mixing solution of titanium(IV) isopropoxide (TTIP) and triethanolamine (TEOA). The concentrations of $Ti^{4+}$ stock solution were adjusted to $10.01{\sim}0.3$ mM, and then the gold colloid is added to the $Ti^{4+}$ stock solution. Au/$TiO_2$ core-shell structure nanoparticles could be prepared by the hydrolysis of the $Ti^{4+}$ stock solution at $80^{\circ}C$. The size of synthesized Au nanoparticles was 15 nm. The thickness of $TiO_2$ shell on the surface of gold particles was about 10 nm. The absorption peak of synthesized Au/$TiO_2$ core-shell nanoparticles shifted towards the red end of the spectrum by about 3 nm because of the formation of $TiO_2$ shell on the surface of gold particles. The good $TiO_2$ shell is produced when $Ti^{4+}$ concentration is varied between 0.01 and 0.05 mM, and reaction temperature is maintained at $80^{\circ}C$. The crystal structure of $TiO_2$ shell was amorphous.

• Bulletin of the Korean Chemical Society
• /
• v.28 no.6
• /
• pp.1015-1020
• /
• 2007

A simple approach to prepare arrays of Au/TiO2 composite nanoparticles by using Au-loaded block copolymers as templates combined with a sol-gel process is described. The organic-inorganic hybrid films with closely packed inorganic nanodomains in organic matrix are produced by spin coating the mixtures of polystyrene-block-poly(ethylene oxide) (PS-b-PEO)/HAuCl4 solution and sol-gel precursor solution. After removal of the organic matrix with deep UV irradiation, arrays of Au/TiO2 composite nanoparticles with different compositions or particle sizes can be easily produced. Different photoluminescence (PL) emission spectra from an organic-inorganic hybrid film and arrays of Au/TiO2 composite nanoparticles indicate that TiO2 and Au components exist as separate state in the initial hybrid film and form composite nanoparticles after the removal of the block copolymer matrix.

• Journal of the Korean Ceramic Society
• /
• v.40 no.9
• /
• pp.902-908
• /
• 2003

Au/TiO$_2$ core-shell structure nanoparticles were synthesised by sol-gel process, and the morphology and crystallinity of TiO$_2$ shell were investigated by TEM and UV-Vis. absorption spectrometer. Au/TiO$_2$ core-shell structure nanoparticles could be prepared by the hydrolysis of TOAA (Titanium Oxide Acethylacetonate) in Au colloid ethanol solution with $H_2O$. The thickness of TiO$_2$ shell on the surface of Au particles was about 1 nm. To investigate the crystallinity of TiO$_2$ shell, UV light with 254 nm and radioactive lay of $^{60}$ CO were irradiated on the TiO$_2$ coated Au colloid ethanol solution. The surface plasmon phenomenon of Au nanoparticles appeared only when the radioactive lay was irradiated on the TiO$_2$ coated Au colloid ethanol solution. From these results, it was found that the TiO$_2$ shell was amorphous and the MUA (Mercaptoundecanoic Acid) layer on the Au particle for its dispersion didn't act as an obstacle to disturb the movement of electron onto the surface of Au particle.

• Journal of Sensor Science and Technology
• /
• v.28 no.4
• /
• pp.225-230
• /
• 2019

$Au@TiO_2$ core-shell decorated rGO nanocomposite (NC) was prepared using a simple solvothermal method followed by heat treatment for gas sensor application. The crystal structure and morphology of the composites were characterized by X-ray powder diffraction and transmission electron microscopy, respectively. The $NO_2$ sensing response of the $Au@TiO_2/rGO$ NC was tested at operating temperatures from $250^{\circ}C$ to $500^{\circ}C$, and was compared with those of the bare rGO and $Au@TiO_2$ core-shell NPs. The $Au@TiO_2/rGO$ NC-based sensor showed a far higher response than the rGO or $Au@TiO_2$ core-shell based sensors, with the maximum response detected when the operating temperature was $400^{\circ}C$. This improved response was due to the high rGO gas absorption capability for $NO_2$ gas and the catalytic effect of $Au@TiO_2$ core-shell NPs in oxidizing $NO_2$ to $NO_3$.

• Journal of the Korean Crystal Growth and Crystal Technology
• /
• v.25 no.6
• /
• pp.280-284
• /
• 2015

Au doped $TiO_2$ nanoparticles have been synthesized using a reverse micelle technique combined with metal alkoxide hydrolysis and condensation. Au doped $TiO_2$ was coated with glass substrate. The size of the particles and thickness of the coating can be controlled by manipulating the relative rates of the hydrolysis and condensation reaction of TTIP within the micro-emulsion. The average size of synthesized Au doped $TiO_2$ nanoparticle was about in the size range of 15 to 25 nm and the Au particles formed mainly the range of 2 to 10 nm in diameter. The effect of synthesis parameters, such as the molar ratio of water to TTIP and the molar ratio of water to surfactant, are discussed. The synthesized nanopaticles were coated on glass substrate by a spin coating process. The thickness of thin film was about 80 nm. The degradation of MB on a $TiO_2$ thin film was enhanced over 20 % efficiency by the incorporation of Au.

• Korean Journal of Materials Research
• /
• v.16 no.12
• /
• pp.754-760
• /
• 2006

Mercaptoundecanoic acid (MUA) has been used to enhance the dispersity of Au nanoparticles in organic solvent and the affinity between the Au nanoparticles surface and titanium dioxide shell in the synthesis of $Au/TiO_2$ core-shell composite nanoparticles. The dispersity of the MUA-coated Au nanoparticles in ethanol aqueous solution with different concentration of $H_2O$ was investigated by UV-Vis. absorption spectrum and the coating amount of MUA was varied from 0.02 mM to 1.0 mM. The MUA-coated Au nanoparticles were highly dispersed in pure $H_2O$ in the wide range of the coating amount of MUA. On the contrary, the MUAcoated Au nanoparticles showed an enhanced stability in the ethanol/$H_2O$=8/2 mixed solution only when the coating amount of MUA was 0.05 mM, and in the ethanol/$H_2O$=7/3 mixed solution when the coating amount of MUA was in the range from 0.02 mM to 0.17 mM. From this systematic study, it can be inferred that the stability and the dispersibility of Au nanoparticles in organic solvents are highly sensitive towards the amount of MUA coating.

• Progress in Superconductivity and Cryogenics
• /
• v.12 no.3
• /
• pp.7-11
• /
• 2010

For many large-scale applications of high-temperature superconducting materials, large critical current density($J_c$) in high applied magnetic fields are required. A number of methods have been reported to introduce artificial pinning centers(APCs) in $YBa_2Cu_3O_{7-\delta}$(YBCO) films for enhancement of their $J_c$. In this work, we investigated electric characteristic of YBCO films on $SrTiO_3$ (100) substrates whose surfaces were modified by the introduction of Au nanoparticles (AuNPs). Au nanoparticles were uniformly dispersed on STO substrates with one of typical solution techniques, self assembled monolayer. After heating the STO substrates with Au nanoparticles, the size of Au nanoparticles was around 29~32 nm in height and 41~49 nm in diameter. XRD diffraction patterns taken on the YBCO film with Au nanoparticles show the c-axis orientation. The measured $T_c$ of YBCO /AuNPs films was around 89K and the $J_c$ was 0.75 MA/$cm^2$ at 65 K and 1 T.

• Proceedings of the Korean Vacuum Society Conference
• /
• 2010.08a
• /
• pp.209-209
• /
• 2010

금(Au) 또는 은(Ag) 금속 나노입자의 모양, 크기, 분포 상태를 조절하여 가시광선과 적외선, 자외선 영역에서 강한 표면 플라즈몬 효과을 이용할 수 있는데, 최근 이러한 금속 나노입자의 표면플라즈몬 효과를 이용하여 태양광 소자의 성능을 향상시키는 연구가 매우 활발하게 이루어지고 있다. 그 중, 높은 효율과 낮은 제작비용 그리고 간단한 공정과정의 장점을 갖고 있어서 크게 주목 받고 있는 염료감응태양전지에서도 금(Au) 또는 은(Ag) 금속 나노입자을 이용하기 위한 많은 연구가 진행되고 있다. 그 예로, Au가 코팅된 $TiO_2$ 기반의 염료감응태양전지구조를 제작하여, 입사된 빛이 표면플라즈몬 효과를 통해, Au에서 여기된 전자들이 Au/$TiO_2$ 사에의 schottky 장벽을 통과하여 $TiO_2$의 전도대 전자들의 밀도가 증가하여, charge carrier generating rate을 높여 소자의 광변환 효율의 향상을 증명하였다. 이에 본 연구에서는, $TiO_2$보다 높은 전자 이동도(mobility)와 직선통로(direct path way)의 장점을 갖고 있는 ZnO nanorod에서의 charge carrier generating rate을 높일 수 있도록, 비교적 가격이 저렴한 Ag nanoparticle을 코팅하였다. ZnO nanorod 제작은 낮은 온도에서 간단하게 성장시킬 수 있는 hydrothermal 방법을 이용하였다. 기판위에 RF magnetron 스퍼터를 이용하여 AZO seed layer를 증착한 후, zinc nitrate $Zn(NO_3)_2{\cdot}6H_2O$과 hexamethylentetramines (HMT)으로 혼합된 용액을 사용해 ZnO nanorods를 성장시켰다. 이 후, Ag를 형성할 수 있도록 열증기증착법을 이용하여 코팅하였다. Ag의 증착시간에 따른 ZnO nanorods에서의 코팅된 구조와 형태를 관찰하기 위해 field emission scanning electron microscopy (FE-SEM)을 이용하여 측정하였으며, 결정성을 조사하기 위해 X-ray diffraction (XRD)을 이용하여 분석하였다. 또한 입사된 빛에 의해, 여기된 ZnO 전도대 전자들이 다시 재결합을 통해 방출되는 photoluminescence 양을 scanning PL 장비를 통해 측정하여 Ag가 코팅된 ZnO nanorod의 광특성을 분석하였다.

• Progress in Superconductivity
• /
• v.11 no.1
• /
• pp.47-51
• /
• 2009

For many large-scale applications of high-temperature superconducting materials, large critical current density ($J_c$) in high applied magnetic fields are required. A number of methods have been reported to introduce artificial pinning centers in $YBa_2Cu_3O_{7-{\delta}}$ films for enhancement of their $J_c$. We studied the microstructures and characteristic of $YBa_2Cu_3O_{7-{\delta}}$ films fabricated on $SrTiO_3$ (100) substrates with ZnO nanorods as pinning centers. Au catalyst nanoparticles were synthesized on STO substrates with self assembled monolayer to control the number of ZnO nanorods. The density of Au nanoparticles is approximately $240{\sim}260{\mu}m^{-2}$ with diameters of $41{\sim}49nm$. ZnO nanorods were grown on STO by hot-walled PLD with Au nanoparticles. Typical size of ZnO nanorod was around 179 nm in diameter and $2{\sim}6{\mu}m$ in length respectively. YBCO films deposited directly on STO substrates show the c-axis orientation, while YBCO films with ZnO nanorods exhibit any mixed phases without any typical crystal orientation.