• Journal of Powder Materials
• /
• v.10 no.4
• /
• pp.288-293
• /
• 2003

Mechanical alloying (MA) by high energy ball mill of Pure chromium Powders was carried out under the nitrogen gas atmosphere. Cr-N amorphous alloy powders have been produced through the solid-gas reaction subjected to MA. The atomic structure during amorphization process was observed by X-ray and neutron diffractions. An advantage of the neutron diffraction technique allows us to observe the local atomic structure surrounding a nitrogen atom. The coordination number of metal atoms around a N atom turns out to be 5.5 atoms. This implies that a nitrogen atom is located at both of centers of the tetrahedron and octahedron formed by metal atoms to stabilize an amorphous Cr-N structure. Also, we have revealed that a Cr-N amorphous alloy may produced from a mixture of pure Cr and Cr nitrides powders by solid-solid reaction during mechanical alloying.

• Journal of the Korean Crystal Growth and Crystal Technology
• /
• v.14 no.4
• /
• pp.129-134
• /
• 2004

In this study, we investigated the effect of a nitrogen atom on the amorphization of V-Fe alloy through solid-gas reaction during mechanical alloying (MA). MA by planetary ball mill of $V_{70}Fe_{30}$ elemental powders was carried out under the nitrogen gas atmosphere. Amorphization has been observed after 160 hours of ball milling in this case. The DSC spectrum for the mechanically alloyed ($V_{70}Fe$_{30}$)_{0.89}N_{0.11}$ powders exhibits a sharp exothermic peak due to crystallization at about $600^{\circ}C$. Structural transformation from the bcc crystalline to amorphous states was also observed through X-ray and neutron diffractions. We take a full advantage of a negligibly small scattering length of the V atom in the neutron diffraction measurement. During amorphization process the octahedral unit, which is typical of a polyhedron formed in any crystal structures, was preferentially destroyed and transformed into the tetrahedral unit. Futhermore, neutron diffraction measurements revealed that a nitrogen atom is selectively situated at a center of the polyhedron formed by V atoms.

• Journal of Powder Materials
• /
• v.10 no.3
• /
• pp.164-167
• /
• 2003

The mechanical alloying effect has been studied on the three Cu-based alloy systems with a positive heat of mixing. The extended bcc solid solution has been formed in the Cu-V system and an amorphous phase in the Cu-Ta system. However, it is round that a mixture of nanocrystalline Cu and Mo Is formed in the Cu-Mo system. The neutron diffraction has been employed at a main tool to characterize the detailed amorphization process. The formation of an amorphous phase in Cu-Ta system can be understood by assuming that the smaller Cu atoms preferentially enter into the bcc Ta lattice during ball milling.

• Korean Journal of Mineralogy and Petrology
• /
• v.36 no.2
• /
• pp.95-106
• /
• 2023

Quartz (SiO₂) is among the major rock-forming minerals in the earth's crust. The atomistic structures of SiO₂ may evolve during diverse frictional processes. The reduction of friction of quartz-rock accompanied by its amorphization, hydration, and formation of silica gel provides mineralogical insights into earthquakes and related phenomena. Ball milling, together with rotary shear experiments have been useful to infer the atomic origins of such processes. In this study, optimal experimental conditions for ball milling for amorphization of SiO₂ were determined by taking into account various process variables. The crystallinity of SiO₂ gradually decreased and became amorphous as the ball milling time increased at a high milling speed. The degree of wear of the milling media and its effect on the amorphization of SiO₂ were analyzed using distinct milling materials (zirconia, stainless steel). The amount of ball wear increased with increasing milling time. Furthermore, the worn stainless steel particles from balls tend to interact with amorphized SiO₂ to form Si-O-Cr. These results aid in understanding the process of atomistic structural changes caused by ball milling of divserse materials with relatively high hardness, such as SiO₂, and understanding various geological friction processes.

• Korean Journal of Materials Research
• /
• v.15 no.12
• /
• pp.802-808
• /
• 2005

The hydrogen sorption speeds of $Zr_{57}V_{36}Fe_7$ amorphous alloy and its crystallized alloys were evaluated at room temperature $Zr_{57}V_{36}Fe_7$ amorphous alloy was prepared by ball milling. The amorphous alloy was crystallized through two stages. Initially, $\alpha-Zr$ solid solution was appeared from the amorphous phase. Two cubic Laves compounds were precipitated afterwards from the remained amorphous and from excessively saturated solid solution at higher temperature. The hydrogen sorption speed of the partially crystallized alloy was higher than that of amorphous. The enhanced sorption speed of partially crystallized alloy was explained in terms of surface oxygen stability which has been known to retard the activation of amorphous alloys. The retardation could be reduce by crystallization process resulting in the observed increase in sorption property.

• Journal of Powder Materials
• /
• v.6 no.4
• /
• pp.314-319
• /
• 1999

The solid state reaction by mechanical alloying(MA) generally proceeds by lowering the free energy as the result of a chemical reaction at the interface between the two adjacent layers. However, Lee et $al.^{1-5)}$ reported that a mixture of Cu and Ta, the combination of which is characterized by a positive heat of mixing of +2kJ/mol, could be amorphized by mechanical alloying. This implies that there exists an up-hill process to raise the free energy of a mixture of pure Cu and la to that of an amorphous phase. It is our aim to investigate to what extent the MA is capable of producing a non-equilibrium phase with increasing the heat of mixing. The system chosen was the ternary $Cu_{30}Ta_{ 70-x}Mo_ x$ (x=35, 10). The mechanical alloying was carried out using a Fritsch P-5 planetary mill under Ar gas atmosphere. The MA powders were characterized by the X-ray diffraction with Cu-K $\alpha$ radiation, thermal analysis, electron diffraction and TEM micrographs. In the case of x=35, where pure Cu powders were mixed with equal amount of pure Ta and Mo powders, we revealed the formation of bcc solid solution after 150 h milling but its gradual decomposition by releasing fcc-Cu when milling time exceeded 200 h. However, an amorphous phase was clearly formed when the Mo content was lowered to x=10. It is believed that the amorphization of ternary $Cu_{30}Ta_{60}Mo_{10}$ powders is essentially identical to the solid state amorphization process in binary $Cu_{30}Ta_{70}$ powders.

• Journal of Powder Materials
• /
• v.16 no.1
• /
• pp.9-15
• /
• 2009

Amorphization and crystallization behaviors of $Ti_{50}Cu_{50}Ni_{20}Al_{10}$ powders during high-energy ball milling and subsequent heat treatment were studied. Full amorphization obtained after milling for 30 h was confirmed by X-ray diffraction and transmission electron microscope. The morphology of powders prepared using different milling times was observed by field-emission scanning electron microscope. The powders developed a fine, layered, homogeneous structure with prolonged milling. The crystallization behavior showed that the glass transition, $T_g$, onset crystallization, $T_x$, and super cooled liquid range ${\Delta}T=T_x-T_g$ were 691,771 and 80 K, respectively. The isothermal transformation kinetics was analyzed by the John-Mehn-Avrami equation. The Avrami exponent was close to 2.5, which corresponds to the transformation process with a diffusion-controlled type at nearly constant nucleation rate. The activation energy of crystallization for the alloy in the isothermal annealing process calculated using an Arrhenius plot was 345 kJ/mol.

• Journal of the Korean Crystal Growth and Crystal Technology
• /
• v.9 no.1
• /
• pp.132-136
• /
• 1999

Mechanical alloying (MA) by ball mill of $Fe_{30}Cr_{70}$ elemental powders was carried out under the nitrogen gas atmosphere. Amorphization has been observed in this case, while MA under an inert argon gas atmosphere produces the bcc solid solution. The DSC spectrum for the mechanically alloyed $(Fe_{30}Cr_{70})_{0.85}N_{0.15)$powders exhibits a sharp exothermic peak due to crystallization at about $550^{\circ}C$. Structural transformation from the bcc crystalline to amorphous states was observed through X-ray and neutron diffractions. During amorphization process the octahedral unit, which is typical of a polyhedron formed in any crystal structures, was preferentially destroyed and transformed into the tetrahedral unit. Futhermore, neutron diffraction measurements revealed that a nitrogen atom is situated at a center of the tetrahedron formed by metal atoms.

• Journal of Powder Materials
• /
• v.17 no.1
• /
• pp.7-12
• /
• 2010

In this work, effect of various process-control agents (PCAs) on the mechanical alloying of amorphous alloy of $Al_{85}Y_8Ni_5Co_2$ has been investigated. The dependence of the particle shape, size and crystallization behavior of the amorphous alloy powders on the type of PCAs and their concentrations was investigated by using X-ray diffraction, field-emission scanning electron microscopy and differential scanning calorimetry. It was found that the additive of toluene could affect positively the amorphization and thermally induced crystallization processes, as well as the size refinement, morphology and particle-size distribution of as-milled powders in comparison with alloy obtained without PCA.

• Journal of Powder Materials
• /
• v.17 no.1
• /
• pp.36-43
• /
• 2010

In present work, amorphous TiCuNi powders were fabricated by mechanical alloying process. Amorphization and crystallization behaviors of the TiCuNi powders during high-energy ball milling and subsequent microstructure changes were studied by X-ray diffraction and transmission electron microscope. TEM samples were prepared by the focused ion beam technique. The morphology of powders prepared with different milling times was observed by field-emission scanning electron microscope and optical microscope. The powders developed a fine, layered, homogeneous structure with milling times. The crystallization behavior showed that glass transition, $T_g$, onset crystallization, $T_x$, and super cooled liquid range ${\Delta}T=T_x-T_g$ were 628, 755 and 127K, respectively. The as-prepared amorphous TiCuNi powders were consolidated by spark plasma sintering process. Full densified TiCuNi samples were successfully produced by the spark plasma sintering process. Crystallization of the MA powders happened during sintering at 733K.