• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2008.06a
• /
• pp.417-418
• /
• 2008

Transparent conductive oxide (TCO) are necessary as front electrode or anti-reflecting coating for increasing efficiency of LED and Photodiode. In this paper, aluminum-doped Zinc oxide films(AZO) were prepared by DC magnetron sputtering on glass(corning 1737) and Si substrate at temperature of $100^{\circ}C$ and then annealed at temperature of $400^{\circ}C$ for 1hr in Ar and vaccum. The AZO films were etched in diluted HCL (0.5 %) to examine the surface morphology properties. After annealing, Structural and electrical property were investigated. The c-axis orientation along (002) plane was enhanced and the electrical resistivity of the AZO film decreased from $1.1\times10^{-1}$ to $1.6\times10^{-2}{\Omega}cm$. We observed textured structure of AZO thin film etched for 2s.

• Journal of the Korean Institute of Electrical and Electronic Material Engineers
• /
• v.15 no.5
• /
• pp.393-397
• /
• 2002

Polyimide (PI) films have been studied widely as the interlayer dielectric materials due to a low dielectric constant, low water absorption, high gap-fill and planarization capability. The polyimide film was etched using inductively coupled plasma system. The etcying characteristics such as etch rate and selectivity were evaluated at different $CF_4/(CF_4+O_2)$chemistry. The maximum etch rate was 8300 ${\AA}/min$ and the selectivity of polyimide to SiO$_2$was 5.9 at $CF_4/(CF_4+O_2)$ of 0.2. Etch profile of polyimide film with an aluminum pattern was measured by a scanning electron microscopy. The vertical profile was approximately $90^{\circ}$ at $CF_4/(CF_4+O_2)$ of 0.2. As 20% $CF_4$ were added into $O_2$ plasma from the results of the optical emission spectroscopy, the radical densities of fluorine and oxygen increased with increasing $CF_4$ concentration in $CF_4/O_2$ from 0 to 20%, resulting in the increased etch rate. The surface reaction of etched PI films was investigated using x-ray photoelectron spectroscopy.

• Journal of Korean Vacuum Science & Technology
• /
• v.2 no.2
• /
• pp.78-84
• /
• 1998

ZnO:Al films were prepared by an rf magnetron sputtering and targets for the experiments were fabricated by sintering the mixture of ZnO and Al2O3. The most conductive film was obtained from the target with 2.0∼2.2 wt.% of Al2O3. Optical properties studied with spectroscopic ellipsometry showed band gap widening, i.e., the Burstein-Moss shift, with aluminum doping as well as with the elevation of deposition temperature. And it is found that the optical and electrical properties were related to the density of states as well as the variation of donor level. when hydrogen atoms were introduced into the films, the activation energy for the generation of oxygen vacancy was smaller for the films showing higher conductivity. This indicates that the optimum deposition condition for highly conductive ZnO:Al film has strong relation to the optimum doping condition.

• Journal of the Korean Society for Precision Engineering
• /
• v.24 no.11
• /
• pp.108-115
• /
• 2007

We have designed a high transmission C-shaped aperture using finite differential time domain (FDTD) technique. The C-shaped aperture was fabricated in the aluminum thin film on a glass substrate using a focused ion beam (FIB) milling. Nano-size patterning was demonstrated with a vacuum contact device to keep tight contact between the Al mask and the photoresist. Using 405 nm laser, we recorded a 50 nm-size dot pattern on the photoresist with the aperture and analyzed the spot size dependent on the dose illuminated on the aperture.

• Proceedings of the Korea Electromagnetic Engineering Society Conference
• /
• 2002.11a
• /
• pp.3-6
• /
• 2002

In this paper, Thin film bulk acoustic resonate.(TFBAR) fillers tuned by gold plated on-wafer inductors are presented. The air-gap type TEBAR is used with aluminum nitride(AIN) as piezoelectric material and platinum as top and bottom electrodes. Inductor equivalent model and modified Butterworth-Van Dyke(MBVD) model are employed for the frequency tuning of fabricated TFBAR bandpass filters. Fabricated inductor has inductance of 3 nH and Q factor of about 8 at 2 ㎓. It is clearly revealed that inductor tuning can enhance the bandwidth of ladder filters and improve out-of-band rejection characteristic around 10㏈.

• Proceedings of the KWS Conference
• /
• 2007.11a
• /
• pp.155-157
• /
• 2007

The Friction spot dissimilar welding of galvanized steel/Al6061-T6 was performed to investigate the mechanical characteristics of the joints. The presence of thin film of aluminum oxide on the surface and melting of zinc in the coating, made substandard joint characteristics for dissimilar Friction spot joining(FSJ) performed with out removing the coating. Where as, for dissimilar FSJ of galvanized steel/Al6061-T6 after removing the coating, superior agitation and welding quality has been obtained for a configuration of galvanized steel as the upper plate and Al6061-T6 as lower plate. The results from tensile tests and microscopic examination for various combinations of the welding parameters have been presented.

• Journal of the Korean Vacuum Society
• /
• v.11 no.2
• /
• pp.103-107
• /
• 2002

Metal/ferroelectric/semiconductor field effect transistors(MFSFET′s) with various gate electrodes, that are aluminum, platinum and poly-Si, using rapid thermal annealed $LiNbO_3$/Si(100) structures were fabricated and the properties of the FET′s have been discussed. The drain current of the "on" state of FET with Pt electrode was more than 3 orders of magnitude larger than the "off" state current at the same "read" gate voltage of 1.5 V, which means the memory operation of the MFSFET. A write voltage as low as about $\pm$4 V, which is applicable to low power integrated circuits, was used for polarization reversal. The retention properties of the FET using Al electrode were quite good up to about $10^3$ s and using Pt electrode remained almost the same value of its initial value over 2 days at room temperature.

• Journal of the Korean institute of surface engineering
• /
• v.51 no.1
• /
• pp.21-26
• /
• 2018

The $Cu_2(btc)_3$ metal-organic frameworks (MOF) coated anodic aluminum oxide (AAO) membrane was successfully prepared by layer-by-layer technique using hand spray method. It was confirmed that the $Cu_2(btc)_3$ layer, which has the pore sized in 2-3 nm, on surface of AAO exhibited the polycrystalline thin film structure by XRD analysis. More than 100 repetitive spray cycles were required to obtain more robust and thick MOFs on AAO and it was possible to uniformly coat both the top and bottom surfaces of the AAO. It should be noted that the MOFs also could be coated on surface of pores resulting in reduce the size of pore from 52 nm to 32 nm.

• Journal of the Korean Institute of Electrical and Electronic Material Engineers
• /
• v.16 no.7
• /
• pp.622-626
• /
• 2003

We report the electrical properties of organic light emitting diodes (OLEDs) depending on the crystal structure of hole injection layer of copper(II)-phthalocyanine(CuPc) and the light irradiation the carrier mobility of copper(II)-phthalocyanine(CuPc) of light source. OLEDs were constructed with indium tin oxide(ITO)/CuPc/triphenyl-diamin(TPD)/tris-(8-hydroxyquinoline)aluminum(Alq$_3$)/Al.Photocurrent multiplication of OLEDs was varied by the heat-treatment condition of CuPc thin film and the light irradiation.

• Journal of the Korean Institute of Electrical and Electronic Material Engineers
• /
• v.21 no.9
• /
• pp.789-794
• /
• 2008

Zinc oxide (ZnO) has been widely studied for its practical applications such as transparent conduction electrodes for flat panel displays and solar cells. Especially, ZnO films show good chemical stability against hydrogen plasma, absence of toxicity, abundance in nature, and then suitable for photovoltaic applications. However, the fabrication process of thin film solar cells require a high substrate temperature and/or post heat treatment. Therefore, the layers have to withstand high temperatures, requiring an excellent stability without degrading their electronic and optical properties. In this paper, we investigated the stability of zinc oxide (ZnO) films doped with aluminum and hydrogen. Doped ZnO films were prepared by r.f. magnetron sputter and followed by heat treatment at different temperatures and for various times.