• 약학회지
• /
• 제47권1호
• /
• pp.5-9
• /
• 2003

Synthetic aluminum silicate was prepared by reacting aluminum sulfate solution with Sodium silicate solution in this study. The optimum synthesis conditions based on the yield of the product were established by applying Box-Wilson experimental design. The results were found to be as follows; Reactant temperature : 50∼72$^{\circ}C$, Concentration of two reactants : 10∼17.6％, Mole ratio of two reactants, [Sod. silicate]/[Al. sulfate) : 4.6∼5.0, Temperature of washing water : 25∼4$0^{\circ}C$, and Drying temperature of product : 50∼$65^{\circ}C$. The physical and chemical properties of synthetic aluminum silicate as medicine were investigated by means of chemical analysis, adsorption test and acid consuming capacity measurements.

• 약학회지
• /
• 제39권1호
• /
• pp.68-77
• /
• 1995

Aluminum magnesium silicate was synthesized by reacting the mixed solutions of sodium aluminate and magnesium chloride with sodium silicate solution in this study. The optimal synthesis conditions based on the yield of the product has been attained according to Box-Wilson experimental design. It was found that the optimal synthetic conditions of aluminum magnesium silicate were as follows: Reaction temperature=$69~81^{\circ}C$; concentration of two reactants, sodium aluminate and magnesium chloride= 13.95~14.44 w/w%; molar concentration ratio of the two reactants, [NaAlO$_{2}$]/MgCl$_{2}$]=3.63~4.00; reaction time= 12~15 min; drying temp. of the product=$70~76^{\circ}C$. Aluminum magnesium silicate synthesized under the optimal synthesis condition was dispersed in 0.75, 1.0 and 1.5w/w% aqueous solution or suspension of six dispersing agents, and the Theological properties of the dispersed systems prepared have been investigated at $15^{\circ}C$ and $25^{\circ}C$ using Brookfield LVT Type Viscometer. The acid-consuming capacity of the most excellent product was 272~278 ml of 0.1N-HCl per gram of the antacid. The flow types of 5.0 w/w% aluminum magnesium silicate suspension were dependent upon the kind and concentration of dispersing agents added. The apparent viscosity of the suspension was generally increased with concentration of dispersing agents and was not significantly changed or decreased as the temperature was raised. A dispersing agent, hydroxypropyl cellulose suspension, exhibited an unique flow behavior of antithixotropy. The flow behavior of the suspension dispersed in a given dispersing agent not always coincided with that of the dispersing agent solution or suspension itself.

• 한국결정성장학회지
• /
• 제31권6호
• /
• pp.264-269
• /
• 2021

본 연구는 공침법을 통하여 비정질 알루미늄 실리케이트 분말을 제조하였으며, 슬러리의 알루미늄 실리케이트 분말 함량 및 분산제 첨가량을 조절하여, 슬러리의 특성에 따른 분무 건조 알루미늄 실리케이트 과립 분말 제조의 영향 분석 및 최적화 연구를 진행하였다. 연구 결과, 알루미늄 실리케이트 슬러리의 분말 함량 27.5 wt% 이하, 슬러리의 분산제 첨가량 0.8 wt% 이상, pH 6~9의 중성 분위기의 슬러리에서 안정적으로 과립 분말이 제조되었으며, 슬러리의 분말 함량 20, 22.5 wt%에서 과립 분말의 평균 입도는 약 14 ㎛, 슬러리의 분말 함량 25, 27.5 wt%에서 과립 분말의 평균 입도가 약 19 ㎛인 것을 확인하였다. 분무 건조 과립 분말의 형상은 슬러리의 분산안정성 및 점도 영향을 받으며, 분말 함량이 높을수록 평균 입자 사이즈가 증가하는 것을 확인하였다.

• 약학회지
• /
• 제15권1호
• /
• pp.1-7
• /
• 1971

When a large quantity of insoluble drugs was added into a solution containing a small amount of soluble drugs, the latter was adsorbed to the former. Their adsorption was expected to alter the drug activity. Berberine hydrochloride (BH) was selected as a soluble drug and tested with frequently combined insoluble drugs and antacids for their adsorption phenomena in prufied water, gastric and intetinal fluid test solutions, respectively. The adsorption isotherms of kaolin and natural anuminum silicate with BH in the three media fitted the Langmuir (LM) equation, and that of talc in purified water and gastric fluid fitted it, but in intestinal fluid it fitted the Freudlich quation. The adsorption isotherm of aluminum hydroxide fitted the LM equation only in intestinal fluid. The degree of adsorption of BH in purified water and gastric fluid is in the following order: magnesium trisilicate, kaolin, natural aluminum silicate and talc; in intestinal fluid: magnesium trisilicate, kaolin, talc, natural aluminum silicate and aluminum hydroxide. Magnesium stearate did not adsorb BH.

• 한국에너지공학회:학술대회논문집
• /
• 한국에너지공학회 2010년도 춘계학술 발표회
• /
• pp.193-193
• /
• 2010

• 약학회지
• /
• 제33권2호
• /
• pp.111-117
• /
• 1989

The optimum reaction conditions for the acid consuming capacity of aluminum silicate synthesized from the reaction of sodium silicate solution and potassium aluminum sulfate solution were investigated by Box-Wilson experimental design, and the micromeritic properties were examined by the means of BET $N_2$ adsorption, Hg penetrometer and methylen blue adsorption. The chemical composition of the samples were analyzed by gravitic method. The results were found to be as follows: optimum reaction temperature $54.7^{\circ}C$, both concentrations of reactant soln 15.7%, reactants molar ratio (Al/Si) 0.5 and drying temperature $65.0^{\circ}C$. The acid consuming capacity of the sample prepared by above optimum conditions was 68 ml and the chemical composition was $Al_2O_3{\cdot}3.6SiO_2{\cdot}3H_2O$. The relationship between acid consuming capacity and micromeritic properties could not found in the range of experiments. Therefore, it is assumed that the acid consuming mechanism of aluminum silicate depends on the neutralization of $Al_2O_3$ and buffer action of $SiO_2$ in sample.

• Journal of Pharmaceutical Investigation
• /
• 제15권2호
• /
• pp.83-90
• /
• 1985

The effects and the optimum manufacturing conditions for the preparation of synthetic aluminum silicate which has acid-consuming power and adsorbing capacity were investigated. The results are as follows: 1. The adsorbing capacity was affected by the mixing order of the reactants, that is, the excellent ones were obtained by the method which add the sodium silicate solution to the potassium alum solution. 2. Even though preparing by the bane manufacturing condition, the acid-consuming power is superior to the adsorbing capacity. 3. According to the Box-Wilson Plan, the optimum reaction conditions are concentration of sodium silicate solution; 38% w/w, settling time; 43 hours at room temperature, drying time; 13 hours at $110^{\circ}C$.

• Nuclear Engineering and Technology
• /
• 제45권3호
• /
• pp.295-310
• /
• 2013

Industry- or regulatory-sponsored research activities on the resolution of Generic Safety Issue (GSI)-191 were reviewed, especially on the chemical effects. Potential chemical effects on the head loss across the debris-loaded sump strainer under a post-accident condition were experimentally evidenced by small-scale bench tests, integrated chemical effects test (ICET), and vertical loop head loss tests. Three main chemical precipitates were identified by WCAP-16530-NP: calcium phosphate, aluminum oxyhydroxide, and sodium aluminum silicate. The former two precipitates were also identified as major chemical precipitates by the ICETs. The assumption that all released calcium would form precipitates is reasonable. CalSil insulation needs to be minimized especially in a plant using trisodium phosphate buffer. The assumption that all released aluminum would form precipitates appears highly conservative because ICETs and other studies suggest substantial solubility of aluminum at high temperature and inhibition of aluminum corrosion by silicate or phosphate. The industry-proposed chemical surrogates are quite effective in increasing the head loss across the debris-loaded bed and more effective than the prototypical aluminum hydroxide precipitates generated by in-situ aluminum corrosion. There appears to be some unresolved potential issues related to GSI-191 chemical effects as identified in NUREG/CR-6988. The United States Nuclear Regulatory Commission, however, concluded that the implications of these issues are either not generically significant or are appropriately addressed, although several issues associated with downstream in-vessel effects remain.

• The Korean Journal of Ceramics
• /
• 제2권2호
• /
• pp.89-94
• /
• 1996

Aluminum and zinc titanium silicate sol-gel films were fabricated for application of waveguide and the effect of additions of ZnO and $Al_2O_3$ to binary titanium silicate films was investigated. During firing, the films are densified as they shrunk and their refractive index increases in the range of 1.58-1.83 depending on the film composition. The attenuation of the waveguides is not sensitive to changes in composition except for zinc titanium silicate waveguides which have substantially higher attenuation. However, the increase in the attenuation with aging of the waveguides depend upon the composition of waveuides. The addition $Al_2O_3$ or the reduced $SiO_2$ content in the composition appears to slow the deterioration of the waveguides due to the formation of more stable bonds and increased acidity on the film surface. Also, the wavelength dependence of the attenuation of the waveguides varies with composition. The attenuation of the waveguides except for the $65SiO_2{\cdot}35TiO_2$ composition are not Rayleigh scatter limited, suggesting the absorption loss of the waveguides due to the effects of residual carbon and structural defects in the films.

• 한국세라믹학회지
• /
• 제33권8호
• /
• pp.915-920
• /
• 1996

콜로이드 졸-겔법에 의해 초미립자 mullite 분말을 제조하였다. Al2O3의 출발 물질로 aluminum isopropoxide $[Al(i-OC_3H_7)_3]$을, $SiO_2$ 출발 물질로 규산 나트륨으로부터 tetrahydrofuran(이후 THF로 약기함)으로 추출한 규산을 사용하였다. 규산 나트륨은 규산을 생성시키기 위하여 묽은 황산으로 산성화시킨 다음 THF로 추출하였다. Mullite 분말은 졸-겔법에 의해서 Si 추출율와 Na 제거율을 조사한 규산과 aluminum isopropoxide로 부터 합성되었다. THF로 추출한 규산의 불순물 함량은 0.04% 이하이었다. 합성된 mullite 분말은 $3Al_2O_3{\cdot}2SiO_2$ 조성을 갖고 불순물의 함량은 0.0462% 이하의 직경 $0.05{\mu}m$ 정도의 결정상이었다. EDS, XRD, TG/DSC, SEM, FT-IR, ICP, TEM등으로 mullite 분말의 특성을 조사하였다.