• 한국주조공학회지
• /
• 제21권3호
• /
• pp.163-178
• /
• 2001

The squeeze infiltration process is potentially of considerable industrial importance. The performance enhancements resulting from incorporation of short alumina fiber into aluminum are well documented. These are particularly significant for certain automobile components. Aluminum matrix composite automotive parts, such as diesel engine pistons or engine blocks are produced using squeeze casting apparatus or pressure die-casting apparatus. But the solidification process gets complicated with manufacturing parameters and the factors for porosity formation have not fully understood yet. In this study the formation of porosity during squeeze infiltration has been studied experimentally to achieve an improved understanding of the squeeze infiltration process for manufacture of short-fiber-reinforced components, particularly the mechanism of porosity formation. Al-based MMCs produced under a range of conditions were examined metallographically and the porosity characterised;a kind of matrix, an initial temperature of melt, and a volume fraction of reinforcement. The densimetry and the microscopic image analysis were done to measure the amount of porosity. A correlation between manufacturing parameters and defects was investigated through these.

• 소성∙가공
• /
• 제7권3호
• /
• pp.215-224
• /
• 1998

A semi-solid forming has a lot of advantages compared to the die casting. squeeze casting and conventional forging. therefore, semi-solid forming process is now becoming industrial interest for the production of metal components and metal matrix composites. However the material behaviour in the semi-solid temperature range is not sufficiently known although it controls the whole process through forces and geometry evolutions because the behaviour of metal slurries is complex. The semi-solid materials(SSMs) fabricated under electric-magnetic stirring condition is necessary to be applicated in forming process. A reheating conditions were studied with the reheating time holding time and reheating temperatures. The microstructure of SSM(specimen size : d39${\times}$h85) at the condition of heating time 10min and heating temperature 590${\circ}C$ is the most globular and finest one. The microstructure of SSM(specimen size : d76${\times}$h60) reheated under the three step reheating conditions is most globular and finest.

• 한국전기전자재료학회논문지
• /
• 제29권6호
• /
• pp.380-385
• /
• 2016

Thermal characteristics of 20 W LED module on light thermal conductive plastic (TCP) heat sink were investigated in comparison with that on aluminum die casting alloy (ADC-12). Thermal simulations of the heat sinks were conducted by using flow simulation of SolidWorks with the following input parameters: density is 1.70 and $2.82kg/m^2$, thermal conductivity is 20 and $92W/(m{\cdot}K)$ for TCP and ADC-12, respectively. The simulated and measured temperatures of the LED modules on TCP heat sink were consistent with its measured temperature, which was $3^{\circ}C$ higher that on ADC-12. The fabricated LED module on TCP heat sink with a weight of 120.5 g was 30% lighter in weight than that of the ADC-12 reference with 171.0 g.

• 한국주조공학회지
• /
• 제15권2호
• /
• pp.156-163
• /
• 1995

Solidification of aluminum alloys under moderate pressures has been investigated. Interfacial heat transfer coefficient at the casting/mold interface varies with time after pouring the molten metal into the die cavity, and therefore plays an important role in determining solidification sequence. The heat transfer coefficients were evaluated by using an inverse problem method, based on the measured temperature distribution. The calculated heat transfer coefficients were used for solidification simulation in the squeeze casting process. The effects of applied pressure and positions of insulation in the mold have also been investigated on solidification microstructures and on the formation of macrosegregation of Al-4.5wt.%Cu alloys.

• 열처리공학회지
• /
• 제34권6호
• /
• pp.281-286
• /
• 2021

Arc ion plating (AIP), laser cladding, and nitriding are methods that can prevent mold damage or repair and create cracks and breakages on the die surface. The dissolution and soldering behavior of coated SKD61 by using arc ion plating, laser cladding, and nitriding was investigated. The structure of the coating was investigated as a function of deposition conditions by X-ray diffraction and the crystallographic orientation was determined using the texture factor. The TiAlN film deposited with AIP showed excellent corrosion resistance in the molten aluminum alloy at 680℃. In this paper, we have detailed the corrosion and mass loss phenomena associated with these steel-cast metal interactions.

• 한국주조공학회지
• /
• 제28권5호
• /
• pp.237-241
• /
• 2008

This study has been carried out to investigate the wear and heat resistant properties of durable moldwash agent for Al gravity casting according to mold washing process conditions. The wear properties of coated specimen were performed by sliding wear testing machine and heat resistance were evaluated by measuring the loss of coated moldwash agent during emerging of coated specimen in Al melts. During testing, experimental variables were mold surface temperature, moldwash agent/distilled wear, and additive concentrations. The lower additive concentration and mold temperature caused the smooth surface roughness of coated specimen, It was found that the specimen coated with moldwash/water ratio 1:3, additive concentration 9wt% and mold temperature higher than $200^{\circ}C$ showed superior wear and heat treatment. Also, these results were supported by fluidity test.

• 한국재료학회지
• /
• 제13권12호
• /
• pp.812-818
• /
• 2003

The aim of this study is to investigate the fabrication processes on the microstructual changes and mechanical properties of large 7175 aluminum die forgings. The billets range from 370 to 720 mm in diameter were homogenized and hot forged after direct chill casting. The strength and elongation of the homogenized cast billets were revealed nearly same level independent of the billet diameter. However, these properties of ø370 mm cast billet were superior to those of $\Pie720$ mm billet under$ T_{6}$ / condition. The tensile strength of die forged specimens under $T_{6}$ condition increased up to 20% than that of solution treatment, however, the elongation was reduced to 50%. The fracture toughness of die forged specimens under $T_{6}$ condition was 35.6∼39.0 MPa$.$$m^{1}$2 irrespective of the billet size and free forging processes, but this property increased up to 10% by$V_{74}$ treatment. The fracture toughness of die forged specimen manufactured with ø370 mm cast billet showed nearly same level of ø720 mm billet which was processed using MF or Cog free forging followed by die forging.

• 소성∙가공
• /
• 제26권5호
• /
• pp.306-313
• /
• 2017

This study investigated the microstructure, tensile strength, and high cycle fatigue properties of ADC12 aluminum alloys with different $Mg+Al_2Ca$ contents manufactured using die casting process. Microstructural observation identified the presence of ${\alpha}-Al$, eutectic Si, $Al_2Cu$, and Fe-intermetallic phases. The increase of $Mg+Al_2Ca$ content resulted in finer pore size and decreased pore distribution. Room temperature tensile strength tests were conducted at strain rate of $1{\times}10^{-3}/sec$. For 0.6%Mg ADC12, measured UTS, YS, and El were 305.2MPa, 157.0MPa, and 2.7%, respectively. For 0.8%Mg ADC12, measured UTS, YS, and El were 311.2 MPa, 159.4 MPa, and 2.4%, respectively. Therefore, 0.8% ADC12 alloy had higher strength and slightly decreased elongation compared to 0.6% Mg ADC12. High cycle fatigue tests revealed that 0.6% Mg ADC12 alloy had a fatigue limit of 150 MPa while 0.8% Mg ADC12 had a fatigue limit of 160MPa. It was confirmed that $Mg+Al_2Ca$ added ADC12 alloy achieved finer, spherical eutectic Si particles, and $Al_2Cu$ phases with greater mechanical and fatigue properties since size and distribution of pores and shrinkage cavities decreased as $Mg+Al_2Ca$ content increased.

• 한국주조공학회지
• /
• 제31권6호
• /
• pp.342-346
• /
• 2011

A328 alloy is an attractive candidate for recycle-friendly aluminum alloy in the recycling of automotive components. In this study, A328 alloy melt was degassed by ultrasonic vibration and the effect of treatment time on the density, fluidity and mechanical properties was investigated. Experimental results reveal that a constant value of density can be reached after less than 180 seconds of ultrasonic treatment time, but the density decreased when the treatment time was 300 seconds. Ti which was dissolved from the horn during ultrasonic treatment reduced the fluidity of melt. After degassing by ultrasonic vibration for 180 seconds, tensile strength increased from 201MPa to 250MPa, and elongation increased from 2.38% to 3.50%, however, further treatment deteriorated the mechanical properties.

• 한국전산유체공학회:학술대회논문집
• /
• 한국전산유체공학회 2000년도 춘계 학술대회논문집
• /
• pp.73-77
• /
• 2000

Small-sized fans for cooling electronic components are usually produced by injection molding in unified form including blade and hub. However, in case of middle and large-sized fans, they deal ill various products with varied numbers of blade or stagger angles after designing a single blade by molding or aluminum die casting. At this occasion, it is necessary to study design method for high-performance axial fans can be operated with various numbers of blades or stagger angle using unique blade for specified conditions. Therefore, the goal in this study is developing a optimal design method which improves performance of axial fans within the large range of operating by single blade.