• Journal of Korea Foundry Society
• /
• v.33 no.3
• /
• pp.122-126
• /
• 2013

Recently, heat-resistant aluminum alloy has been re-focused as a downsizing materials for the internal combustion engines. Heat-resistant Al alloy development and many researches are still ongoing for the purpose of improving thermal stability, high-temperature mechanical strength and fatigue properties. The conventional principle of heat-resistant Al alloy is the precipitation of intermetallic compounds by adding a variety of elements is generally used to improve the mechanical properties of Al alloys. Heat resistant aluminum alloys have been produced by CrW homogeneous solid solution to overcome the limit of conventional heat resistant aluminum alloy. From EPMA, it is found that CrW homogeneous soild solution phases with the size of $50-100{\mu}m$ have been dispersed uniformly, and there is no reaction between aluminum and CrW alloy. In addition, after maintaining at high temperature of 573 K, there is no growth of hardening phase, nor desolved, but CrW still exists as a homogeneous solid solution.

• Korean Journal of Materials Research
• /
• v.22 no.2
• /
• pp.82-85
• /
• 2012

The effect of the alloy systems Al-Mg alloy and Al-Si alloy in this study on the characteristics of die-casting were investigated using solidification simulation software (MAGMAsoft). Generally, it is well known that the casting characteristics of Al-Mg based alloys, such as the fluidity, feedability and die soldering behaviors, are inferior to those of Al-Si based alloys. However, the simulation results of this study showed that the filling pattern behaviors of both the Al-Mg and Al-Si alloys were found to be very similar, whereas the Al-Mg alloy had higher residual stress and greater distortion as generated due to solidification with a larger amount of volumetric shrinkage compared to the Al-Si alloy. The Al-Mg alloy exhibited very high relative numbers of stress-concentrated regions, especially near the rib areas. Owing to the residual stress and distortion, defects were evident in the Al-Mg alloy in the areas predicted by the simulation. However, there were no visible defects observed in the Al-Si alloy. This suggests that an adequate die temperature and casting process optimization are necessary to control and minimize defects when die casting the Al-Mg alloy. A Tatur test was conducted to observe the shrinkage characteristics of the aluminum alloys. The result showed that hot tearing or hot cracking occurred during the solidification of the Al-Mg alloy due to the large amount of shrinkage.

• Transactions of the Korean Society of Automotive Engineers
• /
• v.18 no.1
• /
• pp.120-126
• /
• 2010

It was known that the excellent wear resistance of hyper eutectic aluminum alloy is based on the primary Si particles which are distributed in the base metal. When the primary Si volume fraction increases, the smaller size have excellent wear resistance characteristics. However, this trend always does not match. There is no investigation result based on the materials and methods for real using parts. In this study, using the automotive parts manufacturer currently in use hyper eutectic Al alloy tensile test specimen type sample was fabricated by 350Ton high pressure die-casting machine. Then, fluidity, tensile, impact and wear resistance properties were evaluated. If the casting quality, primary Si size, fraction and distribution are similar, mechanical properties and wear resistance are equivalent.

• Proceedings of the Korean Society of Precision Engineering Conference
• /
• 2002.10a
• /
• pp.193-197
• /
• 2002

In this study, the casting/forging process was applied to the Shift-Fork, a manual transmission part of automobiles. In the casting experiments, the effects of additives, Sr, Ti＋B and Mg, on the mechanical properties and the microstructure of a cast preform were investigated. When 0.03% Sr were added into the molten aluminum alloy, the finest silicon-structure was observed in the cast preform and the highest tensile strength and elongation accomplished. And when 0.2% Ti＋B were added into the molten Al-Si alloy, the highest values of tensile strength were obtained. The maximum hardness was in case of 0.2% Mg. In the forging experiment, it was confirmed that the optimal configuration of the cast preform could be predicted by FE analysis. To minimize the cost as the press size, the compact shape of preform was proposed to reduce the volume of flash. The modification of shape in designing preform was performed to attain a satisfactory performance in the areas where the mechanical strength were more required. By using FVM(Finite Volume Method) software, it was verified that a proposed casting design was available. To identify the relationship between effective strain and mechanical properties of the final forged product, the compression test was performed. As the result, the tensile strength and elongation of a cast preform were much higher than before forging. The minimum forging temperature was found 40$0^{\circ}C$ to save heating time.

• Journal of the Korean Society of Manufacturing Process Engineers
• /
• v.20 no.2
• /
• pp.120-125
• /
• 2021

Phylon molds are widely used for injection molding of foams used in shoe outsoles. Injection pylon molds are usually prepared by first casting the aluminum alloy and then applying an anodized coating to improve durability. This study was carried out to examine the durability of aluminum phylon molds. The aluminum materials used in this study were A771, A6061, and AC4C, and their mechanical properties were compared. Specimens for anodic oxidation tests were prepared with coating thicknesses of approximately 10 and 40 ㎛. We tried to select the optimum material and coating thickness suitable for fabricating phylon injection molds. Among the three materials, A6061 exhibited the best tensile, wear, and impact properties. The difference in the wear resistance between the soft- and hard-anodized coatings was insignificant.

• Journal of Korea Foundry Society
• /
• v.33 no.6
• /
• pp.242-247
• /
• 2013

The most widely utilized commercial, aluminum-casting alloys are based on an aluminum-silicon system due to its excellent casting, and good mechanical, properties. Unfortunately, these Al-Si based alloys are inherently poor energy conductors; compared to pure aluminum, because of their high silicon content. This means that they are not suitable for applications demanding high eletrical or thermal conductivity. Therefore, efforts are currently being made to develop new, highly-conductive aluminum-casting alloys containing no silicon. In this research, a number of properties; including potential for castability, were investigated for a number of Al-Fe-Zn-Cu alloys with varying Cu content. As the copper content was increased, the tensile strength of Al-Fe-Zn-Cu alloy tended to increase gradually, while the electrical conductivity was slightly reduced. Fluidity was found to be lower in high-Cu alloys, and susceptibility to hot-cracking was generally high in all the alloys investigated.

• Journal of Korea Foundry Society
• /
• v.38 no.2
• /
• pp.41-47
• /
• 2018

In a numerical study, equations relating the mechanical properties and cooling rate in a casting process have been applied to an AC4CH cast aluminum alloy. Good agreement was found between the measured and predicted material properties. Step-shaped steel blocks were made to comprise a casting mold with a Y-shaped cavity. Thermometers were inserted into each step of the mold to investigate temperature changes. The microstructure and mechanical properties, such as hardness and tensile stress were measured for each cut of piece. The correlation between the cooling rate and SDAS was found by curved fitting. Moreover, both the solidification time and the temperature were simulated using a commercial package, ZCast. The simulation results for yield strength, tensile strength, elongation, and hardness were compared with experimental results. Using the estimated K and n values, the hardness values of a ship propeller were simulated, and the results were similar to those obtained for actual castings.

• Journal of Korea Foundry Society
• /
• v.35 no.1
• /
• pp.8-14
• /
• 2015

Variations of nickel contents and microstructures in molten magnesium alloys on the addition of aluminum, zirconium, and manganese have been investigated. Specimens were prepared by melting under $SF_6$ and $CO_2$ atmosphere and casting into a disc of 29 mm diameter with 7~10 mm thickness from the melt acquired at the top of crucible. Before casting, the molten metal was stirred for 3 minutes after each addition of alloying elements and maintained for 30 minutes for settling down. Results showed that zirconium did not significantly affect the content of nickel while aluminum remarkably reduced it by forming $Al_3Ni_2$ phase. When manganese are added to Mg-1wt%Ni alloy along with aluminum, both elements remarkably reduced the content of nickel. The addition of 1.5 wt% manganese to Mg-1wt%Ni alloy containing aluminum further reduced the content of nickel by more than 30%, during which an additional intermetallic phase $Al_{10}Mn_3Ni$ was precipitated in the molten magnesium.

• Journal of Korea Foundry Society
• /
• v.29 no.1
• /
• pp.27-32
• /
• 2009

The microstructure of Al-7Si-0.4Mg-1Fe alloy mainly consists of aluminum dendrites, Al-Si eutectics, and $Al_5FeSi$ needles. When Mn was added to the alloy, the substantial amount of $Al_5FeSi$ phase was changed into Al(Mn,Fe)Si, however the needle-like morphology was almost unchanged. Combined additions of Cr or Sr with Mn to the base alloy resulted in rod-like Al(Mn, Fe,Si)Si phase. The tensile properties of as-cast alloys were enhanced by the Mn addition, especially when it was added with Sr. The tensile properties after T6 heat treatment was a little improved with 0.7%Mn addition, but Cr or Sr additions with Mn didn't show any positive effect on the properties of heat-treated alloys.

• Journal of Korea Foundry Society
• /
• v.36 no.5
• /
• pp.153-158
• /
• 2016

The lost foam casting process was used to fabricate Al-Si-Mg cast specimens, and the effects of the chemical composition and process variables on the tensile properties and the mold filling ability were investigated. Some porosity formation was observed in thick sections of the casting and better tensile properties were obtained for thin sections, presumably because of their lower porosity and the higher cooling rate. Tensile properties were not clearly enhanced by grain refining treatment with Ti; however, the elongation was significantly improved by Sr modification of the Al-Si-Mg alloy. The mold filling distance was generally proportional to the pouring temperature of the melt, and the distance was also increased by the addition of Ti.