• Composites Research
• /
• 제19권4호
• /
• pp.23-30
• /
• 2006

극저온 추진제 탱크를 개발하는 과정에서 복합재와 알루미늄 라이너를 접합하기 위한 접착제의 선택은 탱크의 안전성과도 직결된 매우 중요한 문제이다. 따라서 적합한 극저온용 접착제를 선택하기 위해 3종류의 접착필름이 선정되었으며 극저온용으로 개발된 탄소섬유/에폭시와 라이너 재료로 사용되는 알루미늄으로 구성된 양면 겹치기 조인트 시편을 제작하였다. 제작된 시편을 극저온 환경챔버를 사용하여 상온과 $-150^{\circ}C$에서 인장실험을 수행하여 각 접착제의 접착강도를 비교하였으며 파손 특성을 분석하였다. 또한 양면 겹치기 조인트 시편의 각 구성재료의 온도에 따른 기계적 물성변화를 측정하였으며 이를 이용하여 ABAQUS를 통한 유한요소해석을 수행하여 양면 겹치기 조인트 시편의 인장시험결과를 분석하였다.

• 한국자동차공학회논문집
• /
• 제24권4호
• /
• pp.425-431
• /
• 2016

The usage of Friction Stir Welding(FSW) technology has been increasing in order to reduce the weight in automobile industries. Previous studies that investigated on the FSW have focused on the aluminum alloy. In this study, Al6061-T6 alloy plates having 5 mm of thickness were welded under nine different conditions from three tool rotation speeds: 900, 1000 and 1100 rpm, and three feed rates: 270, 300 and 330 mm/min. Specimen size of Micro Shear Punch(MSP) test was $10{\times}10{\times}0.5mm$. The mechanical properties were evaluated by MSP test and Analysis of Variance (ANOVA). The specimens were classified by advancing side(AS), retreating side(RS), and center(C) of width of tool shoulder. The optimal welding condition of FSW based on micro strengh was obtained when the tool rotation speed was 1100 rpm and the feed rate was 300 mm/min. The maximum load measured AS, RS, and C in the weldment was measured 554.7 N, 642.9 N, and 579.2 N, respectively.

• 대한기계학회논문집A
• /
• 제34권12호
• /
• pp.1877-1883
• /
• 2010

선배열 슬릿 마스크를 이용하여 발생시킨 협대역의 레이저 여기 표면파의 주파수 특성을 이론적으로 분석하여 음향비선형성 분석에 영향을 미칠 수 있는 초기 고조파성분의 발생 기구를 규명하였다. 그리고 알루미늄 6061-T6 합금의 음향 비선형성에 대한 슬릿 열림폭과 레이저 세기의 영향을 단일 슬릿과 선배열 슬릿을 이용하여 실험적으로 분석하였다. 고조파 성분의 진폭은 슬릿 열림폭에 의존하는데 본 연구의 경우 슬릿 배열간격을 1.67 mm로 하여 1.75 MHz의 표면파를 발생시켰으며 이 경우 슬릿 열림폭이 0.5 mm에서 1.0 mm로 증가함에 따라 2차 고조파 성분의 진폭은 약 80 % 감소하였다. 또한 레이저 세기에 따라서 기본파 성분 진폭($A_1$)을 변화시키면서 2차 고조파 진폭($A_2$)의 변화를 실험한 결과 $A_1^2$과 $A_2$간에는 우수한 선형 관계를 보였으며, 이는 전형적인 음향비선형성의 특징을 잘 나타낸다.

• 한국표면공학회:학술대회논문집
• /
• 한국표면공학회 2018년도 춘계학술대회 논문집
• /
• pp.106-106
• /
• 2018

해양환경용 선박재료는 전기화학적인 부식을 발생시키는 염소이온($Cl^-$)이 다량 포함된 부식 환경에 장기간 노출되어 있어 부식에 대해 취약하다. 따라서 우수한 내식성 및 내침식성을 가진 재료를 선정하는 것은 매우 중요하다. 알루미늄 합금은 충분한 강도와 부동태 피막 형성으로 인해 내식성이 우수하여 해양환경용 선박 재료로서 널리 이용되고 있으며, 이에 따른 부식 특성에 관한 연구도 활발히 이뤄지고 있다. 그러나 선박에서는 부식에 의한 손상뿐만 아니라 전식에 의한 부식 손상도 발생할 수 있다. 특히 선미 부분은 프로펠러의 동합금과 알루미늄 합금의 이종금속 간 전위차에 의한 전식이 발생하여 선체의 다른 부위에 비해 부식이 더 심하게 진행될 수도 있다. 또한 전식은 해안 부두에 접안된 선박의 용접 시미주전류(stray current)에 의한 부식손상이 발생할 수 있으나 이에 대한 연구는 미미한 실정이다. 따라서 본 연구는 해양환경에서의 전식을 인위적으로 모사할 수 있는 부식 정전류 시험법을 이용하여 다양한 크기의 전식 손상을 유발시켰으며, 해양환경 하에서 선박재료로 주로 사용되는 알루미늄 합금인 Al5083-H321, Al5052-O, Al6061-T6에 대한 전식 특성을 비교, 분석하였다. 실험 방법으로 작동전극은 각 재료의 시험편을 $2cm{\times}2cm$ 으로 절단하여 sand paper # 2000 번까지 연마 후 아세톤과 증류수로 세척하고 건조하였으며, 제작된 시험편은 자체 제작한 홀더를 이용하여 $1cm^2$만 노출시킨 후 정전류 가속 실험을 실시하였다. 기준전극은 은/염화은(Ag/AgCl) 전극을, 대응전극은 백금(Pt) 전극을 사용하였다. 정전류 가속 조건은 $0.001mA/cm^2$, $0.1mA/cm^2$, $1mA/cm^2$, $5mA/cm^2$, $10mA/cm^2$의 전류 밀도를 천연해수에서 30분간 인가하였다. 각 재료에 대한 전식 특성은 실험 전후의 무게 감소량으로 전식의 저항 특성을 확인하였다. 그리고 3D 현미경으로 표면 손상 경향과 깊이를 측정하였으며, 주사전자현미경 (SEM)을 통해 표면 형상을 미시적으로 관찰하였다. 부식 정전류 시험 결과 모든 시편에서 $0.01mA/cm^2$에서 미세한 국부적인 부식이 일어났으며, 전류밀도가 증가할수록 표면 전반에 부식이 진행되고 성장하였다. 그리고 모든 인가 전류밀도의 조건에서 Al6061-T6가 5000계열(Al5083-H321, Al5052-O)보다 더 우수한 내식성을 나타났다.

• Journal of Astronomy and Space Sciences
• /
• 제29권3호
• /
• pp.321-328
• /
• 2012

We have designed a 30 cm cryogenic space infrared telescope for astronomical observation. The telescope is designed to observe in the wavelength range of 0.5~2.1 ${\mu}m$, when it is cooled down to 77 K. The result of the preliminary design of the support structure and support method of the mirror of a 30 cm cryogenic space infrared telescope is shown in this paper. As a Cassegrain prescription, the optical system of a 30 cm cryogenic space infrared telescope has a focal ratio of f/3.1 with a 300 mm primary mirror (M-1) and 113 mm secondary mirror (M-2). The material of the whole structure including mirrors is aluminum alloy (Al6061-T6). Flexures that can withstand random vibration were designed, and it was validated through opto-mechanical analysis that both primary and secondary mirrors, which are assembled in the support structure, meet the requirement of root mean square wavefront error < ${\lambda}/8$ for all gravity direction. Additionally, when the M-1 and flexures are assembled by bolts, the effect of thermal stress occurring from a stainless steel bolt when cooled and bolt torque on the M-1 was analyzed.

• Applied Science and Convergence Technology
• /
• 제27권1호
• /
• pp.9-13
• /
• 2018

Samples of anodic oxide film used in semiconductor and display manufacturing processes were prepared at different electrolyte temperatures to investigate the corrosion resistance. The anodic oxide film was grown on aluminum alloy 6061 by using a sulfuric acid ($H_2SO_4$) electrolyte of 1.5 M at $0^{\circ}C$, $5^{\circ}C$, $10^{\circ}C$, $15^{\circ}C$, and $20^{\circ}C$. The insulating properties of the samples were evaluated by measuring the breakdown voltage, which gradually increased from 0.43 kV ($0^{\circ}C$) to 0.52 kV ($5^{\circ}C$), 1.02 kV ($10^{\circ}C$), and 1.46 kV ($15^{\circ}C$) as the electrolyte temperature was increased from $0^{\circ}C$ to $15^{\circ}C$, but then decreased to 1.24 kV ($20^{\circ}C$). To evaluate the erosion of the film by fluorine plasma, the plasma erosion and the contamination particles were measured. The plasma erosion was evaluated by measuring the breakdown voltage after exposing the film to $CF_4/O_2/Ar$ and $NF_3/O_2/Ar$ plasmas. With exposure to $CF_4/O_2/Ar$ plasma, the breakdown voltage of the film slightly decreased at $0^{\circ}C$, by 0.41 kV; however, the breakdown voltage significantly decreased at $20^{\circ}C$, by 0.83 kV. With exposure to $NF_3/O_2/Ar$ plasma, the breakdown voltage of the film slightly decreased at $0^{\circ}C$, by 0.38 kV; however, the breakdown voltage significantly decreased at $20^{\circ}C$, by 0. 77 kV. In addition, for the entire temperature range, the breakdown voltage decreased more when sample was exposed to $NF_3/O_2/Ar$ plasma than to $CF_4/O_2/Ar$ plasma. The decrease of the breakdown voltage was lower in the anodic oxide film samples that were grown slowly at lower temperatures. The rate of breakdown voltage decrease after exposure to fluorine plasma was highest at $20^{\circ}C$, indicating that the anodic oxide film was most vulnerable to erosion by fluorine plasma at that temperature. Contamination particles generated by exposure to the $CF_4/O_2/Ar$ and $NF_3/O_2/Ar$ plasmas were measured on a real-time basis. The number of contamination particles generated after the exposure to the respective plasmas was lower at $5^{\circ}C$ and higher at $0^{\circ}C$. In particular, for the entire temperature range, about five times more contamination particles were generated with exposure to $NF_3/O_2/Ar$ plasma than for exposure to $CF_4/O_2/Ar$ plasma. Observation of the surface of the anodic oxide film showed that the pore size and density of the non-treated film sample increased with the increase of the temperature. The change of the surface after exposure to fluorine plasma was greatest at $0^{\circ}C$. The generation of contamination particles by fluorine plasma exposure for the anodic oxide film prepared in the present study was different from that of previous aluminum anodic oxide films.