• Journal of Korea Foundry Society
• /
• v.22 no.3
• /
• pp.109-113
• /
• 2002

A good fluidity of high strength Al-alloys is required to cast thin wall castings needed to reduce the weight of cast parts. The fluidity, measured as the length to which the metal flows in a standard channel, is affected by many factors, such as the pouring temperature, solidification type of the alloy, the channel thickness, melt head, mold materials and temperature, coating etc. Therefore the experimentally measured fluidity scatters very much and makes it difficult to estimate the fluidity of a melt with a few measurements. The effect of Ti content and grain refinement on the fluidity of high strength aluminum alloy was investigated with a test casting with 8 thin flow channels to reduce the scattering of the fluidity results. The fluidity of Al-4.8%Cu-0.6%Mn Al-6.2%Zn-1.6%Mg-1.0%Cu and well-known commercial aluminum alloy, A356 was tested. Initial content of Ti was varied from 0 to 0.2wt% and Al-5Ti-B master alloy was added for grain refinement. The flow length varied linearly with superheat. By adding Ti and Al-5Ti-B, the fluidity increased. The grain size decreased by adding grain refiner at the same time. The fluidity depended on the degree of grain refinement. The fluidity of the alloy solidifying in mushy type is improved by grain refinement, because grain refinement increases the solid fraction at the time of flow stoppage.

• Journal of Korea Foundry Society
• /
• v.29 no.4
• /
• pp.176-180
• /
• 2009

Effect of matrix microstructure on creep behaviors of squeeze cast magnesium matrix composites was investigated. Aluminum borate whisker was used as reinforcement and AZ31, AS52 and Sr added AS52 Mg alloys were used for matrix alloys. The reinforcement was distributed homogeneously and defect-free composite was manufactured. Creep tests were carried out at the temperature of $150^{\circ}C$ under the applied stress of 50 and 100 MPa for Mg alloys and Mg MMCs, respectively. The creep resistance of Mg MMCs was in this order: AS52-Sr > AS52 AZ31 MMCs. Void initiation during creep mainly occurred at $Mg/Mg_{17}Al_{12}$ interface and propagation went along grain boundaries. On the other hand, $Mg_2Si$ phase was not attributed to the creep void initiation.

• Journal of the Korean Ceramic Society
• /
• v.51 no.4
• /
• pp.324-331
• /
• 2014

The dispersion characteristics of AlN-4.5 wt% $Y_2O_3$ powder mixture by various dispersants were investigated in ethanol and methyethly-ketone (MEK) solvents. In general, the cationic polymer dispersants demonstrated superior dispersion of the powder as compared to the non-ionic ester-type dispersants or anionic phosphate-ester-based ones. The dispersion performance of the cationic polymer dispersants was sensitive to the type of solvent. An anhydric maleic-acid-based graft copolymer dispersant, AFB-1521, demonstrated a very good dispersion capability in ethanol but exhibited a much inferior dispersion in MEK. On the other hand, the dispersion of the powder mixture was very good with a phosphate-ester-based block polymer dispersant, BYK-111, in MEK solvent, while dispersionwas much degraded in ethanol.

• Korean Journal of Metals and Materials
• /
• v.48 no.5
• /
• pp.387-393
• /
• 2010

High-strength aluminum alloy sheets with high magnesium contents were fabricated by a strip caster equipped with an asymmetric nozzle, which has been proven to be effective for reducing surface defects and internal segregation. 4 mm thick as-cast sheets consisting of fine dendrites and minor $Al_{8}Mg_{5}$ segregation were hot-rolled successfully to 1 mm sheets and subsequently annealed at various temperatures. The sheet revealed the tensile strength and elongation of 306 MPa and 34%, respectively, when it was rolled at 250${^{\circ}C}$ and subsequently annealed at 475${^{\circ}C}$, which exhibits the feasibility of the practical application for autobodies. The observed mechanical properties were explained on the basis of the microstructural characteristics of the alloy sheets.

• Korean Journal of Materials Research
• /
• v.28 no.9
• /
• pp.534-538
• /
• 2018

The annealing characteristics of a cold rolled Al-6.5Mg-1.5Zn alloy newly designed as an automobile material is investigated in detail. The aluminum alloy in the ingot state is cut to a thickness of 4 mm, a total width of 30 mm and a length of 100 mm and then reduced to a thickness of 1 mm (reduction of 75 %) by multi-pass rolling at room temperature. Annealing after rolling is performed at temperatures ranging from 200 to $400^{\circ}C$ for 1 hour. The tensile strength of the annealed material tends to decrease with the annealing temperature and shows a maximum tensile strength of 482MPa in the material annealed at $200^{\circ}C$. The tensile elongation of the annealed material increases with the annealing temperature, while the tensile strength does not, and reaches a maximum value of 26 % at the $350^{\circ}C$ annealed material. For the microstructure, recovery and recrystallization actively occur as the annealing temperature increases. The recrystallization begins to occur at $300^{\circ}C$ and is completed at $350^{\circ}C$, which results in the formation of a fine grained structure. After the rolling, the rolling texture of {112}<111>(Cu-Orientation) develops, but after the annealing a specific texture does not develop.

• Journal of the Korea Academia-Industrial cooperation Society
• /
• v.15 no.8
• /
• pp.4713-4716
• /
• 2014

Several methods that have been used to manage a degasing process in recent years, such as an injection method that uses aluminum molten metal powder and chemicals, and the input method that supplies argon and nitrogen, or chlorine gas using a gas blow-tube. On the other hand, these methods have some problems, and it is a difficult process to handle pollution due to the production of considerable toxic gases, such as chlorine and fluoride gas, irregular effects, and lowering work efficiency due to the excessive processing time. The problems that are most fatal are the production of considerable sludge due to a reaction of aluminum molten metal with chemicals, loss of metals, and the decreasing life of refractory materials. To solve these problems, this study developed a technology that is related to continuous casting of molten aluminum metal and monolithic degasing apparatus.

• Journal of Korea Foundry Society
• /
• v.36 no.6
• /
• pp.202-207
• /
• 2016

The effects of Fe and Si additions on the microstructures and mechanical properties of aluminum bronze have been investigated. In a bar-type specimen cast in a die mold, the addition of Fe promoted the dendritic solidification of the ${\alpha}$ phase. The hardness values increased slightly in the Fe-added specimen with heat treatment, while these values was increased significantly in the specimens with Si or with combined additions of Fe and Si. When a centrifugal casting bush with combined addition of Fe and Si was heat treated, the FeSi compound within the matrix was finely dispersed, and was observed to be the origin of cup-cone type conical dimple failure in the tensile fracture surface. The mechanical properties of the heat treated centrifugal casting bushes, whose nominal alloy compositions were (Cu-7.0Al-0.8Fe-3.0Si)wt%, exhibited tensile strength of $703-781N/mm^2$, elongation of 6.6-11.7% and hardness of Hv 222.6-249.2. These high values of strength and elongation were attributed to the strengthening of the matrix due to the combined addition of Fe and Si, and to precipitation of fine the FeSi compound.

• Journal of the Korean Society of Manufacturing Process Engineers
• /
• v.17 no.3
• /
• pp.102-108
• /
• 2018

The objective of this study is to develop the mechanical properties of an AlSiCu aluminum alloy using the two-step solution heat treatment. The microstructure of the gravity casting specimen represents a typical dendrite structure with a secondary dendrite arm spacing (SDAS) of 40 um. In addition to the Al matrix, a large amount of coarsen eutectic Si phase, $Al_2Cu$ intermetallic phase, and Fe-rich phases is generated. The eutectic Si phases are fragmented and globularized with the solution heat treatment. The $Al_2Cu$ intermetallic phase is also resolutionized into the Al matrix. The $2^{nd}$ solution temperature at $525^{\circ}C$ may be an optimal condition to enhance the mechanical properties of the AlSiCu aluminum alloy.

• Journal of Korea Foundry Society
• /
• v.22 no.3
• /
• pp.130-136
• /
• 2002

The growing use of aluminum for castings over the past decade has brought with it the increased scrutiny of component properties. One area that has received much attention is the effect of in inclusions - or impurities particles held in the metal - on casting properties. A new method of electromagnetic separation for removal of inclusions in aluminum alloy melts is proposed. The principle is that as the electromagnetic force induced in metal acts on inclusions due to low electric conductivity, they are moved to the direction opposite to electromagnetic force and can be separated and removed from the melt. Experiments were carried out on A356 melt mixed alumina particles and commercial Al alloys of ADC 10 and 12. In the experiment using A356, it was proved that $Al_2O_3$ particles was separated and removed continuously from matrix melt by electromagnetic force. Based on these results, the continuous separation experiment that used ADC 10, 12 was carried and the cleanliness of melt was assessed by the amount of porosity, hydrogen contents, PoDFA and mechanical properties through tensile test. As the results of analyses, the amount of porosity and hydrogen contents decreased without variation of chemical composition in the specimen that passed the electromagnetic continuous separator. In addition, tensile strength and elongation of this specimen increased by $20{\sim}30%$ because of reduction of inclusions.

• Composites Research
• /
• v.21 no.6
• /
• pp.15-22
• /
• 2008

Reversed plane bending fatigue tests were conducted on SiC particle aluminum composite. The initiation and growth behaviors of small surface fatigue cracks were continuously monitored by the replica technique and investigated in detail. The fatigue life of MMC is shorter than that of matrix because there exists interface debonding of SiC particles and matrix on the whole face of the notch part in the casting metal matrix composite(MMC). The coalescence of micro-cracks was observed in the tests conducted at high stress levels. Due to the coalescence, a higher crack growth rate of small cracks rather than those of long cracks was recognized in da/dn-$K_{max}$ relationship.