• 한국기계가공학회지
• /
• 제12권5호
• /
• pp.86-93
• /
• 2013

Main function of the Press forming Machine is the forming for plates. The head of the Press forming machine consist of several parts. It was named Press forming-contraction and Press forming_expansion according to formability of plates. Aluminium and Titanum plates are forming by using the Press forming machine. In this study, we analyzed sheet metal forming including plastic deformation and the contact pressure in the bearing. Finite element analysis results of Press forming-contraction and Press forming_expansion show the similar results of the actual specimen plates and the bearing contact pressures show the acceptable level of stress in both aluminum and titanium specimens.

• 대한치과기공학회지
• /
• 제29권2호
• /
• pp.119-128
• /
• 2007

Although there are many different ways that restorations can be made, it can be said that the biocompatibility of abutment and crown is very important in this experiment. When placed in the actual oral cavity, the differences were obvious. Compared to In-ceram Aluminium, the structure that is obtained after firing reveals a particularly homogeneous distribution of the crystal and glass phase. The In-ceram aluminium system had many problems, such as having weak tensile strength, and having low bonding strength due to the shrinking that occurs after firing. Because of the opaque finish of the metal frame, the two may look similar from the outside, but it is evident that there are differences between using a metal frame and In-ceram. VITA VM9 has been designed as a special ceramic featuring a fine structure or stabilized Zro2 substructures, and so the VITA VM9 excels in its light refraction and reflection behavior, which is similar to natural teeth. It also has outstanding chemical balance, which presents advantages such as considerably reduced accumulation of plaque on the ceramic surface.? This ultimately results in easier care and cleaning for the patient.

• Steel and Composite Structures
• /
• 제16권3호
• /
• pp.325-337
• /
• 2014

The strength and buckling problem of a five layer sandwich beam under axial compression or bending is presented. Two faces of the beam are thin aluminium sheets and the core is made of aluminium foam. Between the faces and the core there are two thin binding glue layers. In the paper a mathematical model of the field of displacements, which includes a share effect and a bending moment, is presented. The system of partial differential equations of equilibrium for the five layer sandwich beam is derived on the basis of the principle of stationary total potential energy. The equations are analytically solved and the critical load is obtained. For comparison reasons a finite element model of the beam is formulated. For the case of bended beam the static analysis has been performed to obtain the stress distribution across the height of the beam. For the axially compressed beam the buckling analysis was carried out to determine the buckling load and buckling shape. Moreover, experimental investigations are carried out for two beams. The comparison of the results obtained in the analytical and numerical (FEM) analysis is shown in graphs and figures. The main aim of the paper is to present an analytical model of the five layer beam and to compare the results of the theoretical, numerical and experimental analyses.

• 대한방사선기술학회지:방사선기술과학
• /
• 제4권1호
• /
• pp.63-71
• /
• 1981

The metal-plates(Aluminium. Copper, Lead) of change the variation thickness have been penetrated by the collimated beam($450mm{\times}4mm{\phi}$) of Gamma-ray from $^{192}Ir$. Then, the scattered $\gamma$-ray dose in variable angle and the directly transmitted $\gamma$-ray dose were measured using the electrometer of ionization chamber. The results were summarized as follows: 1. Obtained the mass attenuation coefficients of $Al;0.0937cm^2g^{-1},\;Cu;0.0937cm^2g^{-1},\;pb;0.244cm^2g^{-1}$. 2. Total intensity of front scattered $\gamma$-ray follow the order of Al>Cu>pb. 3. The scattered $\gamma$-ray intensity with the lager angle of scattering was saturated after increase rapidly, and the scattering angle of the more larger was decreased. 4. The scattered $\gamma$-ray intensity through plates of aluminium or copper was saturated after increase with thicker scatterer, and the intensity was decreased at the more thicker. But the variation of scattered $\gamma$-ray dose in the lead plate made the fewest than Al and Cu. 5. The ratio of the scattered $\gamma$-ray dose and the directly transmitted $\gamma$-ray dose was saturated after increase with the thicker scatterer, and the scatterer of the more thicker was decreased. Degree of total intensity in these ratios was followed the order of Cu>Al>Pb.

• 전기화학회지
• /
• 제17권1호
• /
• pp.26-29
• /
• 2014

The corrosion behavior of stainless steel 304 (SS 304), titanium, nickel and aluminium is studied by immersion and anodic polarization tests in non-aqueous electrolytes. Tetraethyl ammonium tetrafluoroborate is used as a supporting electrolyte in the three kinds of solvents. The immersion test shows that chemical corrosion rate in propylene carbonate-based electrolyte is lower than those in acetonitrile- or ${\gamma}$-butyrolactone-based electrolytes. Surface analyses do not reveal any corrosion product formed after the immersion test. In the anodic polarization tests, a higher concentration of supporting electrolyte gives a higher current density. In addition, a higher temperature increases the current density in the active region and reduces the potential range in the passive region. SS 304 shows the highest corrosion potential while Al shows the lowest corrosion potential and the highest current density in all studied conditions. Based on the conducted corrosion tests, the corrosion resistance of metal substrates in the organic solvents can be sorted in descending order as follows: SS 304 - Ti - Ni - Al.

• 분석과학
• /
• 제7권2호
• /
• pp.155-164
• /
• 1994

전형적인 Grimm형 방전관을 제작하고 고주파 방전에 의한 금속 및 세라믹시료 분석에 적용하였다. 금속 알루미늄과 알루미나에 대해 방출 스펙트럼을 관찰하였고 방전에 미치는 고주파의 전력과 알곤 기체의 압력에 대한 영향을 관찰하였으며, 시료와 접촉된 전극에 나타나는 DC-bias voltage를 확인하였다. 또한 SEM 사진을 관찰함으로써 rf-sputtering에 의한 알루미나 표면의 미세구조를 확인하였다. 저합금강(BAS 404-405) 중의 망간성분과 황동시료(NIST 1108-1117) 중의 아연성분에 대해 검량곡선을 작성한 결과 양호한 직선성을 보여 주었다.

• 한국주조공학회지
• /
• 제13권3호
• /
• pp.259-267
• /
• 1993

The effects of casting processes-direct and indirect squeeze casting, permanent mold casting and die casting on the microstructure and mechanical properties were studied for the hypereutectic B390 aluminium alloy. The effects of T5 and T6 heat treatment were also examined. The direct and indirect squeeze casting showed no casting defects such as porosity and shrinkage were observed in permanent mold castings and die castings. The primary silicon phase was refined and homogeneously distributed in the order of indirect squeeze casting, diecasting, direct squeeze casting and permanent mold casting. Depletion of primary silicon phase in die casting surface was disappeared in indirect squeeze casting. Tensile strength of cast and heat treated specimens were increased in the order of direct squeeze casting, permanent mold casting, indirect squeeze casting and die casting. Hardness of indirect squeeze castings was larger than that of other castings. As indirect squeeze casting of B390 aluminium alloy, the time of T6 heat treatment to achieve high strength can be reduced.

• 한국정밀공학회:학술대회논문집
• /
• 한국정밀공학회 1997년도 추계학술대회 논문집
• /
• pp.163-166
• /
• 1997

Aluminium foam material is a highly porous material having complicated cellular structure defined by randomly distributed air pores in metallic matrix. this structure gives the aluminium a set of properties which cannot be achieved by any of conventional treatments. The properties of aluminium foam material significantly depend on its porosity, so that a desired profile of properties can be tailored by changing the foam density. Melting method is the one of foaming processes, which the production has long been considered difficult to realize becaues of such problems as the low foamability of molten metal, the varying size of. cellular structures, solidification shrinkage and so on. These problems, however, have gradually been solved by researchers and some manufacturers are now producing foamed aluminum by their own methods. Most of all, the parameters of solving problem in electric furnace were stirring temperature, stirring velocity, foaming temper:iture, and so on. But it has not considered about those in induction heating, foaming velocity and foaming temperature in semi-solid state yet. Therefore, this paper presents the effects on these parameter to control cell size, quantity and distribution.

• 대한기계학회:학술대회논문집
• /
• 대한기계학회 2001년도 춘계학술대회논문집C
• /
• pp.616-620
• /
• 2001

The wrinkling in the flange and wall of a part is a predominent failure mode in stamping of sheet metal parts. In many cases this wrinkling may be eliminated by appropriate control of the blank holding force(BHF), but BHF affects the draw depth. Although the wrinkles of flange have been made in the incipient stage of drawing, if the height of wrinkles is maintained under a prescribed limit by decrease or extinction of wrinkles in the course of drawing, small BHP can be allowed so that the depth of drawing could be increased. Authors research the variation of the wrinkles in flange in the course of square cup drawing by using aluminium A1015 and aluminium alloy A5052.

• 한국소성가공학회:학술대회논문집
• /
• 한국소성가공학회 2003년도 춘계학술대회논문집
• /
• pp.359-362
• /
• 2003

The bending phenomenon has been known to be occurred by the different of velocity at the die exit. The difference of velocity at the die exit section can be obtained by the different velocity of billets through the multi-hole container and by the cohesion of billet inside the porthole die chamber. The bending phenomenon can be controlled by the different hole diameter. The experiments using aluminium material for the curved tube product had been done. The results of the experiment show that the curved tube product can be formed by the extru-bending process without the defects such as the distortion of section and the thickness change of the wall of tube and the folding and wrinkling. It is known that the welding and extruding of each billet has done simultaneously although the curved tube is extruded with four billets.