• The Korean Journal of Ceramics
• /
• 제1권2호
• /
• pp.86-90
• /
• 1995

Theoretical predictions for thermodynamically stable phases which formed when alkali(sodium and potassium) vapors reacted with alumina-chromia refractories under coal gasifying atmosphere were confirmed experimentally using a laboratory-scale coal gasifying reaction system and a commercial alumina-chromia refractory using SEM, XRD, and EDAX. Alkali concentration profiles in the refractory as a function of time were also determined. The results showed that the compounds that formed were $X_2O{\cdot}Al_2O_3, X_2O{\cdot}Cr_2O_3, X_2O{\cdot}5Al_2O_3, X_2O{\cdot}7Al_2O_3, X_2O{\cdot}11Al_2O_3(X=Na^+ \;or\; K^+)$, depending upon the alkali concentration and time of exposure at high temperatures. The presence of sulfur in gasifying atmospheres did not appear to affect the alkali reaction produces. Alkali pentration into the alumina-chromia refractory was deep and the formation of the $Na_2O{\cdot}Al_2O_3/K_2O{\cdot}Al_2O_3$ compunds resulted in the serious deformation of the refractory due to the large volume expansion at the reaction surface. The hot face of the alumina-chromia refractory in service under an alkali environment is prone to failure by alkali attack.

• The Korean Journal of Ceramics
• /
• 제1권1호
• /
• pp.29-34
• /
• 1995

Theoretical predictions were made for thermodynamically stable phases which formed when alkali(sodium and Potassium) vapors reacted with the 90% $Al_2O_3$-10% $Cr_2O_3$ refractory under coal gasifying atmosphere using the computer program of SOLGASMIX-PV. The calculation results showed that the stable compounds that formed were $X_2O$.$Al_2O_3$ and $X_2O$.$llAl_2O_3$(X=$Na^+$ or $K^+$), depending upon the alkali concentration. The presence of sulfur in gasifying atmospheres did not appear to affect the species of alkali reaction products. Alkali attack at high temperatures is likely to cause serious degradation at the hot face of the refractory, indicating that the alkali concentration is an important factor to affect the degradation of the refroctory.