• Journal of the Korean Ceramic Society
• /
• v.28 no.9
• /
• pp.705-711
• /
• 1991

Alumina precursor sol was obtained by the reaction of Al(OC4H9)3 and acetylacetone in the solvent followed by the partial hydrolysis. This sol was measured by viscosity and the effect of pH. The powders obtained from this sol were calcined at the various temperatures. The transition of crystals and crystal state were investigated at the various temperatures. The powders dried at 90$^{\circ}C$ showed amorphous and ${\gamma}$-Al2O3 at 900$^{\circ}C$, ${\alpha}$-Al2O3 mono-phase at 1050$^{\circ}C$ respectively. As a result of Al27-MASNMR analysis, amorphous and ${\alpha}$-Al2O3 powders showed 6-coordinated Al, ${\gamma}$-Al2O3 4-coordinated Al respectively.

• Journal of the Korean Ceramic Society
• /
• v.34 no.11
• /
• pp.1113-1120
• /
• 1997

The 2, 4, 6 and 8mol% Y2O3 doped-ZrO2 powders (20 kinds) with the addedtion of Al2O3 upto 8wt% were prepared by coprecipitation method using the zirconium oxyacetate, yttrium chloride and aluminum nitrate as starting materials. The coprecipitated powders were characterized by XRD, TG-DTA, FT-IR and SEM. The sintering properties of zirconia-alumina composites prepared by 2YSZ and 8YSZ powders containing various Al2O3 contents were also investigated. With increasing the yttria stabilizer contents, the amount of exothermic heat for zirconia crystallization decreased. And it was confirmed that the crystallizing temperature of coprecipitated zirconia powders increased and the crystallization process occurred in a wide temperature range, as Al2O3 content increased in 8YSZ.

• Journal of the Korean Ceramic Society
• /
• v.32 no.1
• /
• pp.113-119
• /
• 1995

The green body was fabricated by a new forming method, pressureless powder packaing forming method, and the characteristics of sintered specimen were investigated. It was found that alumina ceramics prepared by the present method showed porous structure with narrow pore size distribution, and in case of abrasive powder sintered body, compared with dry-pressed specimen, had the nearly same density. Especially, the specimen prepared with spray-dried granules showed the characteristic that granules were not either deformed or fractured during forming and sintering process. Therefore, it was found that this new forming method was effective method in fabrication of porous ceramics on account of easy control of porosity and pore size and its high thermal stability.

• Journal of the Korean Ceramic Society
• /
• v.37 no.6
• /
• pp.545-551
• /
• 2000

Sintering behaviors of the glass-alumina composites for low firing temperature were investigated as a function of the particle size of glass frit. The system of glass frit was Pb-B-Si-Al-O. The median particle sizes of the glass frits were 2.72$\mu\textrm{m}$, 2.67$\mu\textrm{m}$ and 1.33$\mu\textrm{m}$, which were prepared with changing ball-milling times as 24 h, 48 h and 96 h. The glass-alumina composites showed maximum density at certain temperature, and further heating led to dedensification behaviors, so called over-firing. The sintering temperature, which showed maximum density, raised from 425$^{\circ}C$ to 475$^{\circ}C$ with increase of particle size of glass frit from 1.33$\mu\textrm{m}$ to 2.72$\mu\textrm{m}$. Especially, the over firing behaviors, which were occurred at high sintering temperatures, were greatly increased with decrease of particle size of glass frit.

• Tribology and Lubricants
• /
• v.10 no.3
• /
• pp.39-46
• /
• 1994

In order to investigate the effect of the ceramic reinforcements on the wear properties of aluminum bronze composites, Cu-8wt%Al aluminum bronze alloys reinforced with the Saffil alumina short fiber were produced by the powder metallurgical method and tested by a pin-ondisc wear testing machine. The wear surfaces of the pin specimens and discs, wear debris, and the cross sections of the wear specimens were observed by SEM. The wear mechanism according to various wear conditions and the change of microstructure in the composites were also discussed. In the results, the reinforcement of the composites with alumina short fiber was very effective at the higher applied load over 10N. The material transportation to the counter disc was observed in the alloy specimens without reinforcements. However, the composites reinforced with ceramic particles and fibers showed the resistance against the material transportation.

• Journal of the Korean Ceramic Society
• /
• v.38 no.2
• /
• pp.238-238
• /
• 2001

15% Syn M, sintered mullite(SM) and fused mullite(FM) was added to produce high alumina refractory materials. Mullite content of SM, FM and Syn M was 93.17%, 86.79%, 97.57% repectively. Mechanical properties of specimens (added 15wt% mullite) ware investigated to be flexural strength 338.60MPa, compressive stcngth 9,427kgf/㎠. But the specimen which imported mullite was added showed 5~10%l lower stregth than syn M added.

• Journal of the Korean Ceramic Society
• /
• v.25 no.3
• /
• pp.284-292
• /
• 1988

Alumina-zirconia composite powders for the purpose of improving fracture toughness and thermal shock resistance of alumina were prepared by the emulsion-kerosene drying method. The average particle size of composite powders was less then 1 $\mu\textrm{m}$ and their shapes were spherical. It was shown that the average particle size of composite powders decreased with the concentration of metal-salt in solution and the amount of span 80 added when preparing emulsions. The structure of all zirconia in composite powders heat-treated at 1200$^{\circ}C$ was a tetragonal form at room temperature. This result implied that fine zirconia particles were homogeneously dispersed in the alumina matrix.

• Journal of the Korean Society for Precision Engineering
• /
• v.27 no.5
• /
• pp.14-21
• /
• 2010

In this study, presintered low purity alumina ceramics were machined with various tools to clarify the effects of the tool material, cutting condition and tool geometry on machinability. The main conclusions obtained were as follows. (a)The wear of tungsten carbide tool becomes smaller with the increase of the feed and clearance angle, and with the decrease of rake angle, especially exhibiting considerably smaller wear with both the decrease of rake angle and the increase of clearance angle. (b) So far as turning the ceramic presintered at low temperature, the diamond tool shows the best performance with higher feed. (c) The effect on the tool wear of the feed, clearance angle and rake angle becomes smaller in turning the ceramic presintered at higher temperature. (d) The tool wear is not severely affected by the depth of cut.

• Journal of the Korean Ceramic Society
• /
• v.33 no.1
• /
• pp.101-109
• /
• 1996

The mechanical propertieso f sintered AlN with the addition of alumina were investigated The flexural strength of the AlN dispersed ALON specimens was higher than that of ALON and fracture toughness showed similar tendency. The high-temperature flexural strength of specimens which 50 and 64.3 mol% alumina was added to AlN was constant up to 100$0^{\circ}C$ with about 290 and 420 MPa respectively but abruptly decreased at 120$0^{\circ}C$ In the specimens which contained 5 and 30mol% alumina the flexural strength increased to about 14% at 100$0^{\circ}C$ and did not decrease at 120$0^{\circ}C$ compared to at room temperature.

• Journal of the Korean Ceramic Society
• /
• v.36 no.7
• /
• pp.711-717
• /
• 1999

Biaxial fracture behavior of alumina specimens with the diameter of 20mm and four kinds of thickness of 1.9, 2.3, 2.6 and 2.8mm was studied by the ball-on-3-ball test and the fracture results were analyzed by he analysis of variance (ANOCA), The strength measured with the down speed prescribed in ASTM showed that the measured strength was not dependent on the thickness of the specimens. Equivalent radius and crack-braching number were observed to increase lineraly with the thickness of the specimens. The jog direction was observed to study the effect of grinding direction on surface flaws. It is though that the surface finishing with #600 grit diamond wheel did not affect the surface flaws of the specimens.