• Journal of the Korean Applied Science and Technology
• /
• v.16 no.4
• /
• pp.313-316
• /
• 1999

Organic semiconductors based on conjugated thiophene oligomer have great potential to be utilized as an active layer for electronic and optoelectronic devices. In this study, a conjugated oligomer such as ${\alpha}$-sexithiophene (${\alpha}$-6T) thin films was prepared by the Organic Molecular Beam Deposition (OMBD), and various electrode materials were also deposited by a simple vacuum evaporation, respectively. Those films were photolithographically patterned for the electrical measurements. Electrical charact-erization of the thin film transistor with various channel length were executed and the field effect mobility of these thin film transistors were also calculated by the formula using the experimental data.

• Korean Journal of Metals and Materials
• /
• v.48 no.7
• /
• pp.660-666
• /
• 2010

30 nm thick Ni layers were deposited on a glass substrate by e-beam evaporation. Subsequently, 30 nm or 60 nm ${\alpha}-Si:H$ layers were grown at low temperatures ($<220^{\circ}C$) on the 30 nm Ni/Glass substrate by catalytic CVD (chemical vapor deposition). The sheet resistance, phase, microstructure, depth profile and surface roughness of the $\alpha-Si:H$ layers were examined using a four-point probe, HRXRD (high resolution Xray diffraction), Raman Spectroscopy, FE-SEM (field emission-scanning electron microscopy), TEM (transmission electron microscope) and AES depth profiler. The Ni layers reacted with Si to form NiSi layers with a low sheet resistance of $10{\Omega}/{\Box}$. The crystallinty of the $\alpha-Si:H$ layers on NiSi was up to 60% according to Raman spectroscopy. These results show that both nano-scale NiSi layers and crystalline Si layers can be formed simultaneously on a Ni deposited glass substrate using the proposed low temperature catalytic CVD process.

• Korean Journal of Materials Research
• /
• v.8 no.6
• /
• pp.538-544
• /
• 1998

The spallation of a thermal barrier coating layer depends on the formation of brittle spinels. thermal expansion mismatch between ceramic and metal. the phase transformation of a ceramic layer and residual stress of coating layer. In this work. the formation mechanism of oxide scale formed by oxidation treatment at 90$0^{\circ}C$ was investigated in order to verify oxidation behavior at the interface between E-beam coated $Zr0_2$-7wt.% $Y_20_3$ and plasma sprayed CoNiCrAIY. Some elements distributed in the bond coating layer were selectively oxidized after oxidation. At the initial time of oxidation. AI-depletion zone and $\alpha$-$Al_O_3$,O, were formed at the bond coating layer by the AI-outward diffusion. After layer grew until critical thickness. spinels. $Cr_20$, and $C0_2CrO_4$ by outward diffusion of Co. Cr, Ni were formed. It was found that the formation of spinels may be related to the spallation of $Zr0_2$-7wt.% $Y_20_3$ during isothermal oxidation.

• Imaging Science in Dentistry
• /
• v.47 no.2
• /
• pp.109-115
• /
• 2017

Purpose: The aim of this study was to assess the ex vivo diagnostic ability of 9 different cone-beam computed tomography (CBCT) settings in the detection of recurrent caries under amalgam restorations in primary teeth. Materials and Methods: Fifty-two primary teeth were used. Twenty-six teeth had dentine caries and 26 teeth did not have dentine caries. Black class II cavities were prepared and restored with amalgam. In the 26 carious teeth, recurrent caries were left under restorations. The other 26 intact teeth that did not have caries served as controls. Teeth were imaged using a $100{\times}90-mm$ field of view and a 0.2-mm voxel size with 9 different CBCT settings. Four observers assessed the images using a 5-point scale. Kappa values were calculated to assess observer agreement. CBCT settings were compared with the gold standard using a receiver operating characteristic analysis. The area under the curve (AUC) values for each setting were compared using the chi-square test, with a significance level of ${\alpha}=.05$. Results: Intraobserver kappa values ranged from 0.366 to 0.664 for observer 1, from 0.311 to 0.447 for observer 2, from 0.597 to 1.000 for observer 3, and from 0.869 to 1 for observer 4. Furthermore, interobserver kappa values among the observers ranged from 0.133 to 0.814 for the first reading and from 0.197 to 0.805 for the second reading. The highest AUC values were found for setting 5 (0.5916) and setting 3 (0.5886), and were not found to be statistically significant(P>.05). Conclusion: Variations in tube voltage and tube current did not affect the detection of recurrent caries under amalgam restorations in primary teeth.

• Journal of Korea Technical Association of The Pulp and Paper Industry
• /
• v.45 no.6
• /
• pp.17-23
• /
• 2013

The reduction of metal ion from the cotton linter for the preparation of NMMO (N-methylmorpholine N-oxide)-based dissolving pulp was investigated. The NMMO-based dissolving pulp was usually used for the manufacture of high quality fabrics, and need to have high alpha cellulose content and high brightness. NMMO, which is environmentally friendly, and reusable after recovering process, is very sensitive to the metal ions such as Cu, Fe, Mg, and Cr. Electron beam, sulfuric acid, acetic acid, and ozone treatment before bleaching were used and the concentration changes of the metal ions were compared to that of EDTA, a chelating agent. It was found that both acid treatments (sulfuric and acetic acid) were very effective and comparable to EDTA treatment at the same dosage in metal ion reduction, but electron beam and ozone treatment were not. The sulfuric acid treatment turned out to be effective in metal ion reduction, and most inexpensive.

• Imaging Science in Dentistry
• /
• v.53 no.4
• /
• pp.375-381
• /
• 2023

Purpose: This study assessed the diagnostic performance of stitched and non-stitched cross-sectional cone-beam computed tomography (CBCT) images of non-displaced ovine mandibular fractures. Materials and Methods: In this ex vivo study, non-displaced fractures were artificially created in 10 ovine mandibles (20 hemi-mandibles) using a hammer. The control group comprised 8 hemi-mandibles. The non-displaced fracture lines were oblique or vertical, <0.5 mm wide, 10-20 mm long, and only in the buccal or lingual cortex. Fracture lines in the ramus and posterior mandible were created to be at the interface or borders of the 2 stitched images. CBCT images were obtained from the specimens with an 80 mm×80 mm field of view before and after fracture induction. OnDemand software (Cybermed, Seoul, Korea) was used for stitching the CBCT images. Four observers evaluated 56 (28 stitched and 28 non-stitched) images to detect fracture lines. The diagnostic performance of stitched and non-stitched images was assessed by calculating the area under the receiver operating characteristic curve (AUC). Sensitivity and specificity values were also calculated (alpha=0.05). Results: The AUC was calculated to be 0.862 and 0.825 for the stitched and non-stitched images, respectively (P=0.747). The sensitivity and specificity were 90% and 75% for the non-stitched images and 85% and 87% for the stitched images, respectively. The inter-observer reliability was shown by a Fleiss kappa coefficient of 0.79, indicating good agreement. Conclusion: No significant difference was found in the diagnostic performance of stitched and non-stitched cross-sectional CBCT images of non-displaced fractures of the ovine mandible.

• Progress in Medical Physics
• /
• v.5 no.2
• /
• pp.13-20
• /
• 1994

The thermoluminescence(TL) glow curves and the optical absorption of $Al_2O_3$ irradiated with ${\gamma}$-ray, electron, and $Li^{+}$ ion followed by electron irradiation have been investigated to determine the relation of TL peak to its defect type. The TL glow curve of $Al_2O_3$ irradiated with ${\gamma}$-ray shows TL peaks at 380 K, 415 K, and 475 K. The UV photobleached TL glow curve of $Al_2O_3$ irradiated with ${\gamma}$-ray shows that the 380 K and 475 K TL peaks completely disappear while the 415 K TL peak still exists. The electron beam induced TL glow curve of $Al_2O_3$ after $Li^{+}$ ion implantation shows that the TL peak at 440 K is enhanced by a factor of 2 over the TL intensity of unimplanted $Al_2O_3$ while the TL peak at 380 K evidently disappears The implanted $Li^{+}$ ions are assumed to form singly charged interstitial cations and then recombine with electron trapped in F centers to produce F+ centers. The 380 K and 475 K TL peaks are proposed to be associated with F center, while the 415 K and 440 K TL peak are connected with F$^{+}$ center.

• Korean Journal of Metals and Materials
• /
• v.48 no.2
• /
• pp.133-140
• /
• 2010

10 nm thick Ni layers were deposited on 200 nm $SiO_2/Si$ substrates using an e-beam evaporator. Then, 60 nm or 20 nm thick ${\alpha}$-Si:H layers were grown at low temperature (<$200^{\circ}C$) by a Catalytic-CVD. NiSi layers were already formed instantaneously during Cat-CVD process regardless of the thickness of the $\alpha$-Si. The resulting changes in sheet resistance, microstructure, phase, chemical composition, and surface roughness with the additional rapid thermal annealing up to $500^{\circ}C$ were examined using a four point probe, HRXRD, FE-SEM, TEM, AES, and SPM, respectively. The sheet resistance of the NiSi layer was 12${\Omega}$/□ regardless of the thickness of the ${\alpha}$-Si and kept stable even after the additional annealing process. The thickness of the NiSi layer was 30 nm with excellent uniformity and the surface roughness was maintained under 2 nm after the annealing. Accordingly, our result implies that the low temperature Cat-CVD process with proposed films stack sequence may have more advantages than the conventional CVD process for nano scale NiSi applications.

• International Journal of Naval Architecture and Ocean Engineering
• /
• v.10 no.6
• /
• pp.794-802
• /
• 2018

The ice resistance series charts for icebreaking ships were developed through a series of systematic model tests in the ice tank of the Korean Research Institute of Ship and Ocean Engineering (KRISO). Spencer's (1992) component-based scaling system for ship-ice model tests was applied to extend the model ship correlations. Beam to draft ratio (B/T), length to beam ratio (L/B), block coefficient ($C_B$) and stem angle (${\alpha}$) were selected as geometric parameters for hull form development. The basic hull form (S1) of twin pod type with B/T of 3.0, L/B of 6.0, $C_B$ of 0.75 and stem angle of $25^{\circ}$ was generated with a modern hull design concept. A total of 13 hulls were designed varying the geometric parameters; B/T of 2.5 and 3.5, L/B of 5.0 and 7.0, $C_B$ from 0.65 to 0.85 in intervals of 0.05, and 5 stem angles from $15^{\circ}$ to $35^{\circ}$. Ice resistance tests were first carried out with the basic hull form in level ice with suitable speed. Four more tests for $C_B$ variations from 0.65 to 0.85 were conducted and two more for beam to draft and length to beam ratios were also performed to study the effect of the geometric parameters on ice resistance. Ice resistance tests were summarized using the volumetric coefficient, $C_V$ ($={\nabla}/L^3$), instead of L/B and $C_B$ variations. Additional model tests were also carried out to account for the effect of the stem angle, ice thickness and ice strength on ice resistance. In order to develop the ice resistance series charts with a minimum number of experiments, the trends of the ice resistance obtained from the experiments were assumed to be similar for other model ship with different geometric parameters. A total of 18 sheets composed of combinations of three different beam to draft ratios and six block coefficients were developed as a parameter of $C_V$ in the low speed regions. Three correction charts were also developed for stem angles, ice thickness and ice strength respectively. The charts were applied to estimate ice resistance for existing icebreaking ships including ARAON, and the results were satisfactory with reasonable accuracy.

• Journal of Animal Science and Technology
• /
• v.44 no.1
• /
• pp.113-122
• /
• 2002

Beef loins that retailed in market were used as experimental samples. Some beef samples in raw state were packaged with PVDC as aerobic and vacuum condition. The other beef samples were cooked until core temperature arrived at 70$^{\circ}C$ and then packaged immediately in the same way of raw samples. After these samples were irradiated by electron beam 6kGy, irradiated samples were stored in refrigerator(2～4$^{\circ}C$). Identify and quantity of cholesterol oxides were analysed stored at 0 and 7 days, respectively. During the early stage of storage, 7$\beta$-hydroxycholesterol and 7-ketocholesterol were respectively produced from the raw meat samples, and the production of these chemicals were significantly higher (P$<$0.05) from the meats with aerobic packaging than those with vacuum packaging. With the passage of storage time, 7$\alpha$-hydroxycholesterol, 20$\alpha$-hydroxycholesterol, $\beta$-epoxide, $\beta$-epoxide and some other chemicals, which were not produced during the early stage of storage, were produced, Also, the production of these chemicals were significantly increased (P$<$0.05) with the passage of storage time. Cooked meat after irradiation and irradiated meat after cooking produced cholesterol on the 7th day of storage, although this chemical was not produced during the early stage of storage. Production of cholesterol oxides was significantly increased (P$<$0.05) with the passage of storage time for all treatments, and showed significantly lower value (P$<$0.05) with the vacuum packaging than aerobic packaging. Summarizing the aforementioned results, it was found that the production of cholesterol oxides was more easily affected by packaging condition than irradiation.