• Proceedings of the Korean Powder Metallurgy Institute Conference
• /
• 2002.07a
• /
• pp.25-37
• /
• 2002

The most important industrial application of gamma radiation in characterizing green compacts is the determination of the density. Examples are given where this method is applied in manufacturing technical components in powder metallurgy. The requirements imposed by modern quality management systems and operation by the workforce in industrial production are described. The accuracy of measurement achieved with this method is demonstrated and a comparison is given with other test methods to measure the density. The advantages and limitations of gamma ray densitometry are outlined. The gamma ray densitometer measures the attenuation of gamma radiation penetrating the test parts (Fig. 1). As the capability of compacts to absorb this type of radiation depends on their density, the attenuation of gamma radiation can serve as a measure of the density. The volume of the part being tested is defined by the size of the aperture screeniing out the radiation. It is a channel with the cross section of the aperture whose length is the height of the test part. The intensity of the radiation identified by the detector is the quantity used to determine the material density. Gamma ray densitometry can equally be performed on green compacts as well as on sintered components. Neither special preparation of test parts nor skilled personnel is required to perform the measurement; neither liquids nor other harmful substances are involved. When parts are exhibiting local density variations, which is normally the case in powder compaction, sectional densities can be determined in different parts of the sample without cutting it into pieces. The test is non-destructive, i.e. the parts can still be used after the measurement and do not have to be scrapped. The measurement is controlled by a special PC based software. All results are available for further processing by in-house quality documentation and supervision of measurements. Tool setting for multi-level components can be much improved by using this test method. When a densitometer is installed on the press shop floor, it can be operated by the tool setter himself. Then he can return to the press and immediately implement the corrections. Transfer of sample parts to the lab for density testing can be eliminated and results for the correction of tool settings are more readily available. This helps to reduce the time required for tool setting and clearly improves the productivity of powder presses. The range of materials where this method can be successfully applied covers almost the entire periodic system of the elements. It reaches from the light elements such as graphite via light metals (AI, Mg, Li, Ti) and their alloys, ceramics ($AI_20_3$, SiC, Si_3N_4, $Zr0_2$, ...), magnetic materials (hard and soft ferrites, AlNiCo, Nd-Fe-B, ...), metals including iron and alloy steels, Cu, Ni and Co based alloys to refractory and heavy metals (W, Mo, ...) as well as hardmetals. The gamma radiation required for the measurement is generated by radioactive sources which are produced by nuclear technology. These nuclear materials are safely encapsulated in stainless steel capsules so that no radioactive material can escape from the protective shielding container. The gamma ray densitometer is subject to the strict regulations for the use of radioactive materials. The radiation shield is so effective that there is no elevation of the natural radiation level outside the instrument. Personal dosimetry by the operating personnel is not required. Even in case of malfunction, loss of power and incorrect operation, the escape of gamma radiation from the instrument is positively prevented.

• Journal of Welding and Joining
• /
• v.28 no.3
• /
• pp.92-98
• /
• 2010

Ferritic stainless steels, which have relatively small thermal expansion coefficient and excellent corrosion resistance, are increasingly being used in vehicle manufacturing, in order to increase the lifetime of exhaust manifold parts. But, there are limits on use because of the problem related to cosmetic resistance, corrosions of condensation and high temperature salt etc. So, Aluminum-coated stainless steel instead of ferritic stainless steel are utilized in these parts due to the improved properties. In this investigation, Al-8wt% Si alloy coated 409L ferritic stainless steel was used as the base metal during Gas Tungsten Arc(GTA) welding. The effects of coated layer on the microstructure and hardness were investigated. Full penetration was obtained, when the welding current was higher than 90A and the welding speed was lower than 0.52m/min. Grain size was the largest in fusion zone and decreased from near HAZ to base metal. As welding speed increased, grain size of fusion zone decreased, and there was no big change in HAZ. Hardness had a peak value in the fusion zone and decreased from the bond line to the base metal. The highest hardness in the fusion zone resulted from the fine re-precipitation of the coarse TiN and Ti(C, N) existed in the base metal during melting and solidification process and the presence of fine $Al_2O_3$ and $SiO_2$ formed by the migration of the elements, Al and Si, from the melted coating layer into the fusion zone.

• The korean journal of orthodontics
• /
• v.28 no.2 s.67
• /
• pp.329-341
• /
• 1998

Sterilization has received much attention in orthodontic practices over the past several years. The present study was undertaken to investigate the effects of sterilization on the physical properties of orthodontic pliers-AEZ, Unitek, and Dentronix ligature cutters. This study was designed to examine the tips of ligature cutters before and after 200 and 400 sterilization cycles using the Bowmar RHT-1000, the Dentronix DDS-5000, and the Eschmann SES-2000. The tip surface and the fracture surface were observed with a scanning electron microscope. The microstructure was observed with an optical microscope. The hardness test was carried out with the mic개-Vickers hardness tester and the Rockwell C Scale hardness tester. The chemical composition was analyzed by energy dispersive X-ray spectrometer. The results of this study were as follows : 1. The number and the size of corrosion products on the tip surface and the proportion of cleavage planes in fractured specimen increased, but the hardness of the tip decreased in proportion to sterilization cycles. From these observations, it was considered that mechanical properities decreased in proportion to sterilization cycles. 2. The number and the size of chromium carbides increased in proportion to sterilization cycles. Coarse microstructure decreased mechanical properities. 3. The AEZ and Unitek ligature cutters were Fe-Cr stainless steels, but the Dentronix ligature cutter was Co-Cr alloy. There were many differences among manufactures, but the chemical composition was .not changed after sterilization cycles. 4. The tip edge of ligature cutter used in a clinic revealed microcracks with the SEM observation. Clinical experience confirmed that ligature cutters were gradually degraded by sterilization.