• 한국수소및신에너지학회논문집
• /
• 제9권3호
• /
• pp.101-110
• /
• 1998

Ti-Cr-V 합금에서 Ti의 일부를 Zr으로 치환하는 것에 의한 수소저장 특성의 변화에 대하여 연구하였다. Zr 의 치환은 평탄압력과 히스테리시스를 감소시키나 생성된 $Cr_2Zr$상은 평탄성을 악화시키며 수소저장량의 저하를 초래하였다. 그러나, Ti/Cr의 조성비를 조절하여 $Cr_2Zr$상의 생성을 억제함으로써 수소저장용량이 매우 큰 합금을 얻을 수 있었다. 또한, 열처리에 의해 수소저장량과 유효수소저장량의 감소없이 평탄성을 크게 향상시킬 수 있었다.

• 대한금속재료학회지
• /
• 제50권11호
• /
• pp.793-800
• /
• 2012

The effect of cold rolling on the microstructural evolution in 22Cr-0.2N micro-duplex stainless steel was investigated. The 22Cr-xNi-yMn-0.2N duplex stainless steel plates with various Ni and Mn contents were fabricated. The steels were vacuum induction melted and hot rolled, followed by annealing treatment at the temperature range of $1000-1100^{\circ}C$, in which both the austenite and ferrite phases were stable. The volume fraction of the ferrite phase depending on the alloy compositions of Ni and Mn increased with an increase in the annealing temperature. Grain growth in the ferrite phase occurred markedly after cold rolling followed by annealing, while fine recrystallised grains were still found in the austenite phase. A large number of martensite laths was found in the microstructure of cold rolled steels, which should be formed by strain-induced martensite from the austenite phase. The intersections of stacking faults were revealed by TEM observation. The volume fraction of the martensite phase increased with an increase of the reduction ratio by cold rolling.

• 한국재료학회지
• /
• 제28권11호
• /
• pp.611-614
• /
• 2018

Laminate composites composed of $0.95Pb(Zr_{0.52}Ti_{0.48})O_3-0.05Pb(Mn_{1/3}Sb_{2/3})O_3$ piezoelectric ceramic and Fe-Si-B based magnetostrictive amorphous alloy are fabricated, and the effect of control of the areal dimensions and the thickness of the piezoelectric layer on the magnetoelectric(ME) properties of the laminate composites is studied. As the aspect ratio of the piezoelectric layer and the magnetostrictive layer increases, the maximum value of the ME voltage coefficient(${\alpha}_{ME}$) increases and the intensity of the DC magnetic field at which the maximum ${\alpha}_{ME}$ value appears decreases. Moreover, as the thickness of the piezoelectric layer decreases, ${\alpha}_{ME}$ tends to increase. The ME composites exhibit ${\alpha}_{ME}$ values higher than $1Vcm^{-1}Oe^{-1}$ even at the non-resonance frequency of 1 kHz. This study shows that, apart from the inherent characteristics of the piezoelectric composition, small thicknesses and high aspect ratios of the piezoelectric layer are important dimensional determinants for achieving high ME performance of the piezoelectric-magnetostrictive laminate composite.

• 대한금속재료학회지
• /
• 제49권8호
• /
• pp.619-627
• /
• 2011

The poisoning effect of Zr in aluminum alloys was investigated by analyzing the filtered cakes of aluminum alloy melt taken with the $Prefil^{(R)}$ footprinter through a variety of analytic instruments, SEM/EDX, Auger, and TEM. Experimental results indicated that the morphology and chemical composition of the aluminum alloys were not modified with the addition of Zr, which is to previous belief that Zr poisoning is caused by modification of $(Ti_{1-x}Zr_x)Al_3$. On the other hand, $TiAl_3$ surroundig $TiB_2$ particles was modified and its lattice parameter was more mismatched by increasing Zr content, leading to less nucleation rate. This is also supported by the observation that the poisoning effect is reduced when Ti is added, resulting in a lower content ratio of Zr to Ti. These results suggest that extra Ti should be added to eliminate the poisoning effect of Zr in aluminum alloys containing Zr.

• 한국진공학회지
• /
• 제1권1호
• /
• pp.106-114
• /
• 1992

여러 조성의 Co-Ni 합금과 Au-Cu 합금에 대하여 XPS와 SIMS 분석방법을 사용하 여 표면분석의 정량화 연구를 수행하였다. XPS의 경우 Co-Ni 합금에 대하여는 수정 없이 고순도 시료만으로 1~2% 상대오차 범위 내에서 정량분석이 가능하였고, Au-Cu 합금의 경 우에는 고순도 시료만을 표준시료로 사용하여서는 정량 분석이 불가능하였고 실험적인 수정 인자를 사용한 경우 1~2% 상대오차로 정량분석이 가능하였다. Au-Cu 합금의 경우 여러 조성이 표준시료가 없는 경우 이론적인 수정인자를 사용하는 경우 10%의 상대오차로 정량 분석이 가능하였다. Co-Ni 합금을 SIMS 분석하였을 때 Co와 Ni의 이차이온 세기의 비가 넓은 농도 범위에서 각 성분의 농도의 비와 직선관계를 가져 SIMS에 의한 합금의 정량분석 이 가능하였다. 또한 VAMAS-SCA Japan Project의 XPS 공동분석의 예비 결과도 주어져 있다.

• 한국표면공학회지
• /
• 제49권6호
• /
• pp.580-586
• /
• 2016

Cr-Si-Al-N coating with different Si content were deposited by hybrid physical vapor deposition (PVD) method consisting of unbalanced magnetron (UBM) sputtering and arc ion plating (AIP). The deposition temperature was $300^{\circ}C$, and the gas ratio of $Ar/N_2$ were 9:1. The CrSi alloy and aluminum targets used for arc ion plating and sputtering process, respectively. Si content of the CrSi alloy targets were varied with 1 at%, 5 at%, and 10 at%. The phase analysis, composition and microstructural analysis performed using x-ray diffraction (XRD) and field emission scanning electron microscopy (FESEM) including energy dispersive spectroscopy (EDS), respectively. All of the coatings grown with textured CrN phase (200) plane. The thickness of the Cr-Si-Al-N films were measured about $2{\mu}m$. The friction coefficient and removal rate of films were measured by a ball-on-disk test under 20N load. The friction coefficient of all samples were 0.6 ~ 0.8. Among all of the samples, the removal rate of CrSiAlN (10 at% Si) film shows the lowest values, $4.827{\times}10^{-12}mm^3/Nm$. As increasing of Si contents of the CrSiAlN coatings, the hardness and elastic modulus of CrSiAlN coatings were increased. The morphology and composition of wear track of the films was examined by scanning electron microscopy (SEM) and energy dispersive spectroscopy, respectively. The surface energy of the films were obtained by measuring of contact angle of water drop. Among all of the samples, the CrSiAlN (10 at% Si) films shows the highest value of the surface energy, 41 N/m.

• 박물관보존과학
• /
• 제30권
• /
• pp.101-126
• /
• 2023

조선시대 복전총통은 문헌 기록이 없고 비교적 근래 실물로 알려진 총통이다. 그간 상세하게 언급되지 못했던 복전총통 12점의 제원, 형태, 명문, 성분 등을 비교하여 복전총통의 구조와 재료적 특징을 검토하였다. 복전총통은 제원과 형태에 있어 일정한 규격을 가지고 있었고, 제원과 문헌자료를 비교하여 발사체의 수도 추정하였다. 모병부에는 총통 명칭과 함께 외곽선이 양각으로 새겨져 있는데, 명문 외곽선은 다른 총통에서 볼 수 없는 복전총통의 가장 큰 특징이기도 하다. 따라서 이를 토대로 제작 과정 속 시문 원리도 살펴보았다. 한편 복전총통의 재료는 구리와 주석이 주성분이며 주석의 함량은 6wt%였다. 기 조사된 조선 청동 화약 무기의 평균 성분과 매우 유사하며, 중세 유럽의 청동 화포(Gun-metal)와도 유사한 경향임을 확인하였다. 이와 같은 결과는 화약 무기에 필요한 재료적 특성을 고려한 결과로 총통 재료는 합금 비율에 따른 기능을 우선한다고 볼 수 있다.

• 한국재료학회지
• /
• 제26권12호
• /
• pp.751-756
• /
• 2016

Graphite was diffusion-bonded by hot-pressing to W-25Re alloy using a Ti interlayer. For the joining, a uniaxial pressure of 25 MPa was applied at $1600^{\circ}C$ for 2 hrs in an argon atmosphere with a heating rate of $10^{\circ}C\;min^{-1}$. The interfacial microstructure and elemental distribution of the W-25Re/Ti/Graphite joints were analyzed by scanning electron microscopy (SEM). Hot-pressed joints appeared to form a stable interlayer without any micro-cracking, pores, or defects. To investigate the high-temperature stability of the W-25Re/Ti/Graphite joint, an oxy-acetylene torch test was conducted for 30 seconds with oxygen and acetylene at a 1.3:1 ratio. Cross-sectional analysis of the joint was performed to compare the thickness of the oxide layer and its chemical composition. The thickness of W-25Re changed from 250 to $20{\mu}m$. In the elemental analysis, a high fraction of rhenium was detected at the surface oxidation layer of W-25Re, while the W-25Re matrix was found to maintain the initial weight ratio. Tungsten was first reacted with oxygen at a torch temperature over $2500^{\circ}C$ to form a tungsten oxide layer on the surface of W-25Re. Then, the remaining rhenium was subsequently reacted with oxygen to form rhenium oxide. The interfacial microstructure of the Ti-containing interlayer was stable after the torch test at a temperature over $2500^{\circ}C$.

• 한국결정성장학회지
• /
• 제25권4호
• /
• pp.135-139
• /
• 2015

단결정 ingot 성장기술 중 하나인 traveling heater method(THM) 기술을 이용하여 n형 열전소재인 $Bi_2Te_3-Bi_2Se_3$ 고용체화합물을 성장하였다. 고용체 화합물내 $CdCl_2$와 $SbI_3$을 첨가하여 dopant의 영향을 확인하였고 각각의 dopant의 최적의 첨가량[$CdCl_2$ 0.1 wt%(Z: $2.73{\times}10^{-3}/K$), $SbI_3$ 0.05 wt%(Z: $2.29{\times}10^{-3}/K$)]을 확인하였다. THM 기술을 통해 성장된 ingot의 각 부위별 열전특성을 확인해 본 결과 주요 인자들의 표준편차가 낮은 매우 균질화된 특성을 보였다. 또한 $Bi_2Te_3-Bi_2Se_3$ 고용체화합물의 비등방성 지수와 dopant와의 관계를 확인하기 위하여 $90(Bi_2Te_3)10(Bi_2Se_3)$ 조성의 고용체화합물에 donor dopant로서 $CdCl_2$(0.05~0.1 wt%)을 첨가하여 dopant의 증가에 따른 비등방성 지수의 변화를 확인해본 결과 dopant가 증가함에 따라 비등방성 지수가 변하는 것을 확인하였고 이러한 비등방성 지수의 변화가 실제 열전성능에 크게 영향을 미치는 것을 확인하였다.

• 보존과학회지
• /
• 제20권
• /
• pp.23-30
• /
• 2007

호록 미륵사지에서 출토된 동경의 성분을 분석하여 어떠한 배합비로 주조하였는지 또한 금속조직 관찰을통하여 동경의 제작기법을 그리고 납동위원소비를 분석하여 동경에 쓰인 납이 어느 지역의 방연석을 사용한 것인지를 검토하였다. 동경의 성분분석 결과, Cu의 농도는 68.8-73.3wt% Sn의 농도는 21.6-24.9wt%로 나타났으며, Pb의 함량은 시료번호 미륵 2와 3이 미륵 4에 비해 높게 나타났다. 미세조직은 미륵 2와 3의 경우는 주조조직으로서 ${\alpha}$상과 ${\alpha}+{\delta}$상으로 이루어져 있었으며, 미륵 4의 경우는 마르텐사이트 조직이 관찰되는 것으로 보아 인위적인 열처리가 있었음을 알 수 있다. 납동위원소비를 통한 산지분석결과에서는 동경의 주조시 사용된 납의 경우 일본지역에서 쓰인 방연석과 깊은 상관관계가 있는 것으로 나타났다. 이 연구 결과는 익산 미륵사지에서 출토된 동경의 제작기법 및 교류관계 등을 알아볼 수 알 수 있는 귀중한 자료로 활용될 것이다.