• Journal of the Korean Wood Science and Technology
• /
• v.35 no.5
• /
• pp.7-15
• /
• 2007

To evaluate the durability of finger-jointed woods according to change of humidity conditions, four types of finger-jointed woods glued with different kinds of adhesives and finger pitches were made with Sitka spruce, and the effect of humidity conditions on creep performances was investigated. The shape of creep curves differed among humidity conditions, and the inclination of creep curves was greatest in 85%RH, and lowest in 65%RH. Their creep curves showed a linear behavior beyond approximately one hour, regardless of humidity conditions. The A values of the creep curves fitted to power law increased with increasing relative humidity, whereas the A' values were in order of 30 > 85 > 65%RH unlike the A values. The initial deformation increased with increasing relative humidity, whereas the creep deformation unlike the initial deformation was in order of 85 > 30 > 65%RH, and it was found that the creep deformation of finger-jointed woods indicated the smaller amount in air-dry moisture content rather than in a low moisture content less than 30%RH. Finger-jointed woods with 6.8 mm (L) pitch had the greater creep amount than in those with 4.4 mm (S) pitch in all humidity conditions. The difference of creep amount between both adhesives in all humidity conditions was small. Relative creep at 240 hr was greatest as 62.2~71.9% in 85%RH, and the values indicated 2.1~2.6 times that of 30%RH and 3.0~3.6 times that of 65%RH and were equal or slightly greater than that of solid spruce.

• The Journal of Advanced Prosthodontics
• /
• v.5 no.4
• /
• pp.479-484
• /
• 2013

PURPOSE. The aim of this study was to evaluate the effects of additional acid etching and curing mechanism (light-curing or self-curing) of a composite resin on the dentin bond strength and compatibility of one-step self-etching adhesives. MATERIALS AND METHODS. Sixteen human permanent molars were randomly divided into eight groups according to the adhesives used (All-Bond Universal: ABU, Clearfil S3 Bond: CS3), additional acid etching (additional acid etching performed: EO, no additional acid etching performed: EX), and composite resins (Filtek Z-250: Z250, Clearfil FII New Bond: CFNB). Group 1: ABU-EO-Z250, Group 2: ABU-EO-CFNB, Group 3: ABU-EX-Z250, Group 4: ABU-EX-CFNB, Group 5: CS3-EO-Z250, Group 6: CS3-EO-CFNB, Group 7: CS3-EX-Z250, Group 8: CS3-EX-CFNB. After bonding procedures, composite resins were built up on dentin surfaces. After 24-hour water storage, the teeth were sectioned to make 10 specimens for each group. The microtensile bond strength test was performed using a microtensile testing machine. The failure mode of the fractured specimens was examined by means of an optical microscope at ${\times}20$ magnification. The data was analyzed using a one-way ANOVA and Scheffe's post-hoc test (${\alpha}$=.05). RESULTS. Additional etching groups showed significantly higher values than the no additional etching group when using All-Bond Universal. The light-cured composite resin groups showed significantly higher values than the self-cured composite resin groups in the Clearfil S3 Bond. CONCLUSION. The additional acid etching is beneficial for the dentin bond strength when using low acidic one-step self-etch adhesives, and low acidic one-step self-etch adhesives are compatible with self-cured composite resin. The acidity of the one-step self-etch adhesives is an influencing factor in terms of the dentin bonding strength and incompatibility with a self-cured composite resin.

• The Journal of Korean Academy of Prosthodontics
• /
• v.37 no.4
• /
• pp.465-473
• /
• 1999

Bond strength of luting cements to dentin is a critical consideration for success of complete cast crowns. This study was performed to evaluate the relationship between surface characteristics of teeth prepared for complete cast crowns and retention of cemented restorations. Eighty artificial crowns were cast for standardized complete crown tooth preparations accomplished with the use of a special device on recently extracted human teeth. Coarse diamond(#102R, Shofu) and superfine finishing diamond(#SF102R, Shofu) burs of similar shape were used. Crowns in each group were randomly subdivided into few subgroups of 10 for luting cements selected for this study: zinc phosphate cement (FLECK' S), polycarboxylate cement (Poly-F), rein-forced glass ionomer cement (Fuji PLUS). and adhesive resin cement (Panavia 21). Retention was evaluated by measuring the tensile load required to dislodge the artificial crown from tooth preparations with an Instron testing machine, and analysed by one-way ANOVA and Student's t-test. The obtained results were as follows ; 1. When tooth preparation was done with coarse diamond bur, retentive force was diminished in order of Panavia 21 Fuji PLUS, FLECK'S, and Poly-F. Retentive forces showed the significant difference between Fuji PLUS group and FLECK'S group(p<0.001). 2. When tooth preparation was done with superfine diamond bur, retentive force was diminished in order of Fuji PLUS, Panavia 21, FLECK'S, and Poly-F. Retentive forces showed the significant difference between Panavia 21 group and FLECK'S group(p<0.001). 3. Retentive force in coarse tooth surfaces was significantly higher than that in superfine tooth surface with all luting cements(p<0.001), and cement residues were almost retained with-in the cast crown in all groups.

• The Journal of Korean Academy of Prosthodontics
• /
• v.45 no.3
• /
• pp.295-302
• /
• 2007

Statement of problem. Fracture of the tooth-colored superstructure material is one of the main prosthetic complications in implant-supported prostheses. Purpose. The purpose of this in vitro study was to compare the fracture strength between the cement-retained implant-supported metal-ceramic crowns and the indirect composite resinveneered metal crowns under the vertical compressive load. Material and methods. Standard implants of external type (AVANA IFR 415 Pre-mount; Osstem Co., Busan, Korea) were embedded in stainless steel blocks perpendicular to their long axis. Customized abutments were fabricated using plastic UCLA abutments (Esthetic plastic cylinder; Osstem Co., Busan, Korea). Thirty standardized copings were cast with non-precious metal (Rexillium III, Pentron, Walling ford, Conn., USA). Copings were divided into two groups of 15 specimens each (n = 15). For Group I specimens, metal-ceramic crowns were fabricated. For Group II specimens, composite resin-veneered (Sinfony, 3M-ESPE, St. Paul, MN, USA) metal crowns (Sinfony-veneered crowns) were fabricated according to manufacturer's instructions. All crowns were temporary cemented and vertically loaded with an Instron universal testing machine (Instron 3366, Instron Corp., Norwood, MA, USA). The maximum load value (N) at the moment of complete failure was recorded and all data were statistically analyzed by independent sample t-test at the significance level of 0.05. The modes of failure were also investigated with visual analysis. Results. The fracture strength of Sinfony-veneered crowns ($2292.7{\pm}576.0N$) was significantly greater than that of metal-ceramic crowns ($1150.6{\pm}268.2N$) (P < 0.05). With regard to the failure mode, Sinfony-veneered crowns exhibited adhesive failure, while metal-ceramic crowns tended to fracture in a manner that resulted in combined failure. Conclusion. Sinfony-veneered crowns demonstrated a significantly higher fracture strength than that of metal-ceramic crowns in cement-retained implant-supported prostheses.

• Advances in pediatric surgery
• /
• v.13 no.1
• /
• pp.23-29
• /
• 2007

Tapering enteroplasty was first described by Thomas in 1969 as one method of intestinal anastomosis. The advantages of tapering enteroplasty in the intestinal atresia are: First, it makes end-to-end anastomosis possible between the atretic bowel ends with considerable differences in diameters. Second, it promotes the recover of the postoperative bowel function. Third, it prevents the possibility of the short bowel syndrome by eliminating the need of resecting the dilated bowel. A total of 22 patients with intestinal atresia who underwent tapering enteroplasty from January 1988 to December 2005 at our institute were reviewed. In 3 of 22 cases, tapering enteroplasty was the $2^{nd}$ operation after an initial end-to-oblique anastomosis. We reviewed the following items: age, sex, type and location of intestinal atresia, initial feeding and total enteral feeding start day, the length of hospital stay and complications. The average age of the patients was 7 days. Male to female ratio was 1 to 1.2 (10 cases: 12 cases). We performed the tapering enteroplasty on all types and locations of the intestinal atresia from the duodenum to the colon: type I (n=3), type II (n=4), type IIIA (n=7), type IIIB (n=5), type IIIB and IV (n=1), type IV (n=1) and type C (duodenum) and type IIIB and IV (jejunum). On the average, the oral feeds were started on the postoperative $8.8^{th}$ day, and full caloric intake via the enteric route was achieved on postoperative $13.3^{th}$ day. The average length of hospital stay was 19.6 days. There were 1 case (4.5 %) of anastomotic complication and 2 cases (9 %) of adhesive ileus among 22 patients. The tapering enteroplasty on all types of intestinal atresia is a usefull operative method when there are considerable diameter differences between the atretic bowel ends.

• The Journal of Advanced Prosthodontics
• /
• v.6 no.5
• /
• pp.333-345
• /
• 2014

PURPOSE. Bonding agents (BA) are the crucial weak link of composite restorations. Since the commercial materials' compositions are not disclosed, studies to formulize the optimum ratios of different components are of value. The aim of this study was to find a proper formula of BAs. MATERIALS AND METHODS. This explorative experimental in vitro study was composed of 4 different sets of extensive experiments. A commercial BA and 7 experimental formulas were compared in terms of degree of conversion (5 experimental formulas), shear bond strength, mode of failure, and microleakage (3 experimental formulas). Statistical analyses were performed (${\alpha}$=.05). The DC of selected formula was tested one year later. RESULTS. The two-way ANOVA indicated a significant difference between the shear bond strength (SBS) of two tissues (dentin vs. enamel, P=.0001) in a way that dentinal bonds were weaker. However, there was no difference between the four materials (P=.283). The adhesive mode of failure was predominant in all groups. No differences between the microleakage of the four materials at occlusal (P=.788) or gingival (P=.508) sites were detected (Kruskal-Wallis). The Mann-Whitney U test showed a significant difference between the microleakage of all materials (3 experimental formulas and a commercial material) together at the occlusal site versus the gingival site (P=.041). CONCLUSION. A formula with 62% bisphenol A-glycidyl methacrylate (Bis-GMA), 37% hydroxy ethyl methacrylate (HEMA), 0.3% camphorquinone (CQ), and 0.7% dimethyl-para-toluidine (DMPT) seems a proper formula for mass production. The microleakage and SBS might be respectively higher and lower on dentin compared to enamel.

• Journal of Chest Surgery
• /
• v.10 no.2
• /
• pp.315-326
• /
• 1977

From 1958 to October 1977, 294 cases of acquired heart disease were operated. There were 68 cases of pericardium, 3 trauma, 2 foreign body, one cardiac thrombus, 3 atrial myxoma, 2 left atrial and 1 right atrial, 2 Budd-Chiari syndrome, and 214 valvular heart disease. Out of 214 cases of valve operation 73 valves were replaced in 64 patients. Male to female ratio was 1.46: 1. The youngest age was 14 years in male and 18 in female. The oldest was 54 years in male and 52 in female. Fifty-five cases of single valve were replaced, consisting of 47 mitral and 8 aortic valves. There were 9 double valve replacement cases which consist of 7 mitral and aortic and 2 mitral .and tricuspid valves. Six varieties of prosthetic valves, 3 ball and 3 disc types and 3 kinds of xenograft tissue valves were utilized. Beall, BjSrk-Shiley and Starr-Edwards prosthetic valves and Hancock valves were used mainly. For single valve 34. 5% and for double valve replacement 44% mortality were noted. There were 23 operative deaths out of 64 patients, over all mortality rate of 36.9%. Mortality for mitral valve replacement was 29.5%. But in recent 12 consecutive cases one death occurred, showing 8.3% mortality. In earlier days thrombocyte anti-adhesive drug dipyramidole-persantin-aspirin and/or SP 54 were adminstered. But in recent cases after heparinization, coumadin and Persantin were prescribed routinely.

• Journal of Dental Rehabilitation and Applied Science
• /
• v.21 no.1
• /
• pp.69-81
• /
• 2005

The objective of this study was to evaluate the toothbrush abrasion characteristics of class V restorations. Thirty extracted human premolars, which were collected from oral surgery clinics were used. We mounted five teeth in a metal ring mold of 50 mm in diameter and 15 mm in height using chemically cured acrylic resin. Class V cavities were prepared in lingual cervical root surfaces and restored using one of following restorative materials : Dentin Conditioner/Fuji II LC (Group FL), All Bond II/Z-250 (Group ZT), One-up Bond F/Palfigue Estelite (Group PE), F2000 Primer/Adhesive (Group FT), and Prime & Bond 2.1/Dyract AP (Group DR). They were stored under distilled water at $37^{\circ}C$ for seven days. The toothbrush abrasion test was conducted using a wear testing machine of pin-on disk type under a load of 1.5 N for 100,000 cycles. We have examined the bonded interfaces, the changes of surface roughness and color of abraded surfaces. From this experiment, the following results were obtained. 1. The change of surface roughness showed high degree: RMGIC>compomer>composite resin (p<0.05). 2. Because of the protrusion and missing of filler particles, SEM observation of abraded surfaces of RMGIC and compomers revealed the increase of surface roughness due to the selective removal of matrix resin. 3. The color change by toothbrush abrasion was affected in large part by the change of $L^*$ and $b^*$ of resin composites (p<0.05). 4. The color change by toothbrush abrasion was so small to detect by human eyes. 5. SEM observation of abraded surfaces revealed the interface bonding was the best in the FT group.

• The korean journal of orthodontics
• /
• v.36 no.5
• /
• pp.331-338
• /
• 2006

Objective: The purpose of this study was to evaluate whether the bond strength of polycarbonate brackets can be increased through surface treatment. Methods: One hundred polycarbonate brackets (Alice) were bonded to bovine incisors with light-cured adhesive. The bracket bases were treated with one of three methods; sandblasting, plastic conditioner application, and combined treatment with sandblasting and plastic conditioner. The brackets without any suraace treatment served as the control. The shear bond strength was tested with a universal testing machine, and failure pattern was assessed with the adhesive remnant index. Results: The shear bond strength in all experimental groups was higher than that of the control group (p < 0.001). The group treated with plastic conditioner after sandblasting showed statistically higher shear bond strength than the sandblasting only group to (p < 0.05). The group treated with plastic conditioner after sandblasting showed higher shear bond strength than plastic conditioner only group, but the difference was not statistically significant. Conclusion: The above results suggest that the surface treatments of polycarbonate bracket is mandatory to improve bond strength, and the most effective method is an application of plastic conditioner after sandblasting.

• The Journal of Advanced Prosthodontics
• /
• v.12 no.4
• /
• pp.181-188
• /
• 2020

PURPOSE. The effect of core design on the fracture resistance of zirconia-lithium disilicate (LS2) bilayered crowns for anterior teeth is evaluated by comparing with that of metal-ceramic crowns. MATERIALS AND METHODS. Forty customized titanium abutments for maxillary central incisor were prepared. Each group of 10 units was constructed using the same veneer form of designs A and B, which covered labial surface to approximately one third of the incisal and cervical palatal surface, respectively. LS2 pressed-on-zirconia (POZ) and porcelain-fused-to-metal (PFM) crowns were divided into "POZ_A," "POZ_B," "PFM_A," and "PFM_B" groups, and 6000 thermal cycles (5/55 ℃) were performed after 24 h storage in distilled water at 37 ℃. All specimens were prepared using a single type of self-adhesive resin cement. The fracture resistance was measured using a universal testing machine. Failure mode and elemental analyses of the bonding interface were performed. The data were analyzed using Welch's t-test and the Games-Howell exact test. RESULTS. The PFM_B (1376. 8 ± 93.3 N) group demonstrated significantly higher fracture strength than the PFM_A (915.8 ± 206.3 N) and POZ_B (963.8 ± 316.2 N) groups (P<.05). There was no statistically significant difference in fracture resistance between the POZ_A (1184.4 ± 319.6 N) and POZ_B groups (P>.05). Regardless of the design differences of the zirconia cores, fractures involving cores occurred in all specimens of the POZ groups. CONCLUSION. The bilayered anterior POZ crowns showed different fracture resistance and fracture pattern according to the core design compared to PFM.