• 한국주조공학회지
• /
• 제31권1호
• /
• pp.18-25
• /
• 2011

Effect of Fe and Mn contents on the tensile properties has been studied in Al-9wt%Si-0.3wt%Mg alloy. As Fe content of Al-9wt%Si-0.3wt%Mg-0.5wt%Mn alloy increased from 0.15wt% to 0.45wt%, tensile strength of as-cast alloy decreased from 192 MPa to 174 MPa, and elongation of the alloy also decreased from 4.8% to 4.2%. Decrease of these properties can be explained as the formation of plate shape, ${\beta}-Al_5FeSi$ phase with high Fe/Mn ratio of the alloy. However when Mn content of Al-9wt%Si-0.3wt%Mg-0.45wt%Fe alloy increased from 0.3wt% to 0.5wt%, tensile strength of T6 aged alloy increased from 265 MPa to 275 MPa, and elongation of the alloy increased from 2.3% to 3.6%. These improvements attribute to chinese script, ${\alpha}-Al_{15}(Mn,Fe)_3Si_2$ phase shape-modified from ${\beta}-Al_5FeSi$ phase with low Fe/Mn ratio of the alloy.

• Applied Microscopy
• /
• 제44권4호
• /
• pp.144-149
• /
• 2014

A strategy for phase identification of precipitates in high Al-containing austenitic and ferritic steels using electron diffraction (ED) is studied. Comparative studies of the various Al-containing precipitates (k-carbide, $Ni_3Al$, $Fe_3Al$, FeAl) show the similarities of crystal structure and lattice parameter. However, the slight differences of lattice parameter and structure display characteristic ED patterns (EDPs) which can be identified. $L1_2$ k-carbide and $Ni_3Al$ can be differentiated by the length of ${\rightarrow}_g$ (the reciprocal lattice vector), even though they show perfectly identical shapes of EDPs. $DO_3$ $Fe_3Al$ and $B_2$ FeAl show the characteristic EDs in [110] and [112] beam directions due to the differences of Fe site occupancies in unit cells. k-carbide, $Ni_3Al$, and FeAl show also the similar EDs in [112], [112], and [110] beam directions, respectively. All the possible similarities of EDs among each phases and the strategy for phase identification are discussed on the bases of kinematical ED simulation.

• 한국재료학회지
• /
• 제22권6호
• /
• pp.316-320
• /
• 2012

$Co_3O_4$, $Al_2O_3$ and $Co_3O_4$/$Al_2O_3$ mesoporous powders were prepared by a sol-gel method with starting matierals of aluminum isopropoxide and cobalt (II) nitrate. A P123 template is employed as an active organic additive for improving the specific surface area of the mixed oxide by forming surfactant micelles. A transition metal cobalt oxide supported on alumina with and without P123 was tested to find the most active and selective conditions as a heterogeneous catalyst in the reaction of styrene epoxidation. A bBlock copolymer-P123 template was added to the staring materials to control physical and chemical properties. The properties of $Co_3O_4$/$Al_2O_3$ powder with and without P123 were characterized using an X-ray diffractometer (XRD), a Field-Emission Scanning Electron Microscope (FE-SEM), a Bruner-Emmertt-Teller (BET) surface analyzer, and $^{27}Al$ MAS NMR spectroscopy. Powders with and without P123 were compared in catalytic tests. The catalytic activity and selectivity were monitored by GC/MS, $^1H$, and $^{13}C$-NMR spectroscopy. The performance for the reaction of epoxidation of styrene was observed to be in the following order: [$Co_3O_4$/$Al_2O_3$ with P123-1173 K > $Co_3O_4$/$Al_2O_3$ with P123-973 K > $Co_3O_4$-973 K>$Co_3O_4$/$Al_2O_3$-973 K > $Co_3O_4$/$Al_2O_3$ with P123-1473 K > $Al_2O_3$-973 K]. The existence of ${\gamma}$-alumina and the nature of the surface morphology are related to catalytic activity.

• Korean Chemical Engineering Research
• /
• 제56권4호
• /
• pp.600-606
• /
• 2018

다양한 Si/Al 몰비를 지닌 MTT 제올라이트를 합성하여 methanol-to-olefin(MTO) 반응에서 촉매의 산성도가 미치는 영향을 조사하였다. Si/Al 몰비를 조절하기 위해 N,N,N',N'-테트라메틸-1,3-디아미노프로판을 구조유도물질(SDA)로 사용하였으며, 알루민산나트륨의 함량을 달리하여 $20SiO_2$ : 30SDA : x (=0.25~1.25)$NaAlO_2$ : 2NaOH : $624H_2O$ 조성으로 모액을 제조한 후 433 K에서 4일 동안 수열 합성하였다. 알루민산나트륨의 함량이 감소함에 따라 MTT 제올라이트의 입자 크기가 증가하였으며 또한 산점의 양도 감소하였다. 제조한 MTT 제올라이트의 촉매 활성을 평가하기 위해 673 K에서 공간속도(WHSV)가 $1.2h^{-1}$인 조건으로 MTO 반응을 수행한 결과, Si/Al 몰비가 24인 H-MTT (1.00Al) 촉매가 900분까지 90% 이상의 전환율을 유지함을 확인하였다.

• 한국분말재료학회지
• /
• 제5권2호
• /
• pp.98-110
• /
• 1998

$Ti_{52}Al_{48}$ and $(Ti_{52}Al_{48})_{100-x}B_x(x=0.5, 2, 5)$ alloys have been Produced by mechanical milling in an attritor mill using prealloyed powders. Microstructure of binary $Ti_{52}Al_{48}$ powders consists of grains of hexagonal phase whose structure is very close to $Ti_2Al$. $(Ti_{52}Al_{48})_{95}B_5$ powders contains TiB2 in addition to matrix grains of hexagonal phase. The grain sizes in the as-milled powders of both alloys are nanocrystalline. The mechanically alloyed powders were consolidated by vacuum hot pressing (VHP) at 100$0^{\circ}C$ for 2 hours, resulting in a material which is fully dense. Microstructure of consolidated binary alloy consists of $\gamma$-TiAl phase with dispersions of $Ti_2AlN$ and $A1_2O_3$ phases located along the grain boundaries. Binary alloy shows a significant coarsening in grain and dispersoid sizes. On the other hand, microstructure of B containing alloy consists of $\gamma$-TiAl grains with fine dispersions of $TiB_2$ within the grains and shows the minimal coarsening during annealing. The vacuum hot pressed billets were subjected to various heat treatments, and the mechanical properties were measured by compression testing at room temperature. Mechanically alloyed materials show much better combinations of strength and fracture strain compared with the ingot-cast TiAl, indicating the effectiveness of mechanical alloying in improving the mechanical properties.

• 한국재료학회지
• /
• 제12권2호
• /
• pp.153-159
• /
• 2002

The co-deposited behavior was investigated under varied bath compositions and current densities from Watt Ni plating bath containing Al and A1$_2$O$_3$powders. For single-particle bath, Al and A1$_2$O$_3$particles were agglomerated. The area percentage of A1$_2$O$_3$on plating surface decreased with increasing the current density, while that of Al on plating surface increased. On the other hand, in case of double-particle bath with 1.25g/$\ell$ of Al and 5.0g/$\ell$ of A1$_2$O$_3$5g, the area percentage of Ni-Al-A1$_2$O$_3$increased with increasing current density and the surface morphology was fine without agglomeration. Intermetallic compounds such as $\gamma$'and $\gamma$+$\gamma$' phases appeared when the co-deposited film was annealed.

• 한국세라믹학회지
• /
• 제45권12호
• /
• pp.827-831
• /
• 2008

Spark plasma sintering (SPS) of AlN ceramics were carried out with ${Y_2}{O_3}$ as sintering additive at a sintering temperature $1,550{\sim}1,700^{\circ}C$. The effect of ${Y_2}{O_3}$ addition on sintering behavior and thermal conductivity of AlN ceramics was studied. ${Y_2}{O_3}$ added AlN showed higher densification rate than pure AlN noticeably, but the formation of yttrium aluminates phases by the solid-state reaction of ${Y_2}{O_3}$ and ${Al_2}{O_3}$ existed on AlN surface could delay the densification during the sintering process. The thermal conductivity of AlN specimens was promoted by the addition of ${Y_2}{O_3}$ up to 3 wt% in spite of the formation of YAG secondary phase in AlN grain boundaries because ${Y_2}{O_3}$ addition could reduced the oxygen contents in AlN lattice which is primary factor of thermal conductivity. However, the thermal conductivity rather decreased over 3 wt% addition because an immoderate formation of YAG phases in grain boundary could decrease thermal conductivity by a phonon scattering surpassing the contribution of ${Y_2}{O_3}$ addition.

• 한국재료학회지
• /
• 제28권6호
• /
• pp.361-364
• /
• 2018

Binary Ti-Al alloys below 51.0 mass%Al content exhibit a breakaway, transferring from parabolic to linear rate law. The second $Al_2O_3$ layer might have some protectiveness before breakaway. Ti-63.1 mass%Al oxidized at 1173 K under parabolic law. Breakaway oxidation is observed in every alloy, except for Ti-63.1 mass%Al. After breakaway, oxidation rates of the binary TiAl alloys below 34.5 mass%Al obey almost linear kinetics. The corrosion rate of Ti-63.1 mass%Al appears to be almost parabolic. As content greater than 63.0 mass% is found to be necessary to form a protective alumina film. Addition of Mo improves the oxidation resistance dramatically. No breakaway is observed at 1123 K, and breakaway is delayed by Mo addition at 1173 K. At 1123 K, no breakaway, but a parabolic increase in mass gain, are observed in the Mo-added TiAl alloys. The binary Ti-34.5 mass%Al exhibits a transfer from parabolic to linear kinetics. At 1173 K, the binary alloys show vary fast linear oxidation and even the Mo-added alloys exhibit breakaway oxidation. The 2.0 mass%Mo-added TiAl exhibits a slope between linear and parabolic. At values of 4.0 and 6.0 mass% added TiAl alloys, slightly larger rates are observed than those for the parabolic rate law, even after breakaway. On those alloys, the second $Al_2O_3$ layer appears to be persistently continuous. Oxidation resistance is considerably degraded by the addition of Mn. Mn appears to have the effect of breaking the continuity of the second $Al_2O_3$ layer.

• 분석과학
• /
• 제5권1호
• /
• pp.103-110
• /
• 1992

본 연구에서는 고온용 Al-Ti 합금을 제조하기 위하여 복합금속분말의 화학적 균질성과 합금내에 형성되는 미세한 분산상에 대하여 조사하였다. Al-Ti 복합금속분말의 화학적 균질성은 400rpm의 회전속도로 10시간 이상 기계적 합금화하였을 때 나타났으며 MA Al-Ti 합금의 화학분석결과, Ti 함량은 8.2wt.%, 탄소 함량은 1.135wt.%, 그리고 산소 함량은 0.233wt.%였으며, 특히 탄소 함량은 스테아린산의 공정 제어제 중에 있는 약 90% 정도의 탄소가 최종적으로 합금 시편에 혼입되었음을 알 수 있었다. TEM 분석을 통하여 MA Al-Ti 합금의 기지조직내에 구형의 250nm 크기인 $Al_3Ti$ 금속간 화합물상과 침상형태의 폭 50nm, 길이 150nm 크기인 $Al_4C_3$ 탄화물상의 형성을 관찰하였으며 구형 모양을 갖는 약 20nm 크기의 $Al_2O_3$ 탄화물상들이 이 합금의 입내 및 입계에 균일하게 분포되었음을 알 수 있었다.

• 한국표면공학회지
• /
• 제49권5호
• /
• pp.454-460
• /
• 2016

Double-layered Al-Mg films have been deposited by using an e-beam deposition method on a cold-rolled steel sheet(CR), which the structure of the film was Al/Mg/CR. The micro-structure, alloy phase, and corrosion resistance of the Al-Mg coated CR were investigated before and after heat treatment at $400^{\circ}C$ for 2, 3, and 10 min in a nitrogen atmosphere. Total thickness of Al-Mg films was fixed at $3{\mu}m$ and the thickness ratio of Al and Mg layers(Al:Mg) has been changed from 5:1 to 1:5. The cross-sectional morphology of the films, which had the thickness ratio of 2:1(Al:Mg), 1:1, and 1:2, was changed after heat treatment from columnar to featureless structure. The x-ray diffraction data for as-deposited films showed only pure Al and Mg peaks. Al-Mg alloy peaks such as $Al_3Mg_2$ and $Al_{12}Mg_{17}$ phase appeared after the heat treatment. The Al-Mg coating with the thickness ratio of 1:1(Al:Mg) showed the best corrosion resistance of up to 500 hours by salt spray test.