• 한국주조공학회지
• /
• 제22권2호
• /
• pp.75-81
• /
• 2002

The main objectives were to investigate the suitability of CaO crucible for melting TiAl alloys and to develop investment mold for investment casting of TiAl alloys. TiAl alloy specimen were prepared by plasma arc furnace under argon atmosphere. After melting of TiAl alloy using CaO crucible, the results showed that there is little contamination of oxygen in the TiAl bulk. Conventional vacuum induction furnaces can be readily adaptable to produce cast parts of TiAl without high skilled techniques. The determination of optical metallography and microhardness profiles in investment cast TiAl alloy rods has allowed the gradation of the relative thermal stability of the oxides examined. The molds used for the present study were $ZrO_2$, $Al_2O_3$, CaO stabilized $ZrO_2$ and $ZrSiO_4$. Even although high temperature of mold preheating, $Al_2O_3$ mold is a promising mold material for investment casting of TiAl alloys in terms of thermal stability, cost and handling strength. It is important to take thermal stability and preheating temperature of mold into consideration for investment casting of TiAl alloys.

• 청정기술
• /
• 제21권1호
• /
• pp.68-75
• /
• 2015

본 연구에서는 높은 열전도성을 갖는 금속-세라믹 core-shell 구조의 CoAl₂O₄@Al 복합체를 Al 금속의 수열반응을 통하여 합성하고, 이를 Rh 촉매의 담지체로 적용하여 구조적, 촉매화학적 특성을 분석하였다. Rh/CoAl₂O₄@Al (3 wt% Rh) 촉매는 단순침적법(incipient wetness impregnation)으로 제조하였고, 특성의 비교평가를 위하여 공침법(co-precipitation)으로 합성한 CoAl₂O₄를 담지체로 하여 Rh/CoAl₂O₄ (3 wt% Rh) 촉매를 단순침적법으로 제조하였다. 이들 촉매들은 N₂ 흡착, XRD, 전자 주사현미경, temperature programmed reduction (TPR), CO 화학흡착 분석을 통해서 그 특성을 분석하였고, 글리세롤 수증기 개질 반응(550 ℃)을 통한 수소전환반응에 적용하여 촉매적 특성을 평가하고 분석하였다. 글리세롤 수증기 개질반응에 대하여 Rh/CoAl₂O₄@Al 촉매는 Rh/CoAl₂O₄ 촉매에 비하여 약 2.8배 높은 글리세롤 전환 turnover frequency (TOF)를 보여주었고, 이는 높은 열전도성을 갖는 금속-세라믹 복합체를 통한 원활한 반응열의 전달에 기인한 것으로 분석되었다. CoAl₂O₄@Al 및 CoAl₂O₄ 담지체에서도 환원에 의하여 노출된 일부 Co 금속에 의한 촉매적 활성이 관찰되었는데, Rh/CoAl₂O₄@Al과 Rh/CoAl₂O₄ 촉매에서와 마찬가지로 core-shell 구조체인 CoAl₂O₄@Al이 CoAl₂O₄ 보다 높은 촉매적 활성을 보였다. 그러나, 이들 촉매는 글리세롤 개질반응에서 비교적 높은 비활성화를 보여주었고 이는 촉매표면의 탄소침적(coking)에 기인한 것으로 판명되었다.

• 한국세라믹학회지
• /
• 제46권3호
• /
• pp.288-294
• /
• 2009

The platelet AlO(OH) nano colloids were prepared by hydrothermal reaction of the $\gamma-Al_2O_3$ obtained with dehydration of $\gamma$-AlO(OH) and dilute $CH_3COOH$ solution. In hydrothermal reaction process, reversible reaction was accompanied between $\gamma-Al_2O_3$ and AlO(OH), and hydrothermal reaction temperature, hydrothermal reaction time and $CH_3COOH$ concentration had an effect on the crystal structure, surface chemical property, surface area, pore characteristics and crystal morphology of the AlO(OH) nano colloid particles. In this study, it was investigated to the hydrothermal reaction condition of the AlO(OH) nano colloid for using catalyst support, heat resisting agent, adsorbents, binder, polishing agent and coating agent. The crystal structure, surface area, pore volume and pore size of the platelet AlO(OH) nano colloids were investigated by XRD, TEM, TG/DTA, FT-IR and $N_2$ BET method in liquid nitrogen temperature.

• 한국결정성장학회지
• /
• 제9권2호
• /
• pp.185-190
• /
• 1999

$Al_2O_3/Fe$ 복합재료 제조는 반응소결법에 의한 2단계 공정을 통해서 제조되었으며 이 공정은 장비가 간단하고 near-net-shape이 가능한 장점이 있다.$Al_2O_3/Fe$ 복합재료를 제조하기 위해서 1차로 $650^{\circ}C$에서 5시간동안 산화/환원 처리를 행하고 $1200^{\circ}C$에서 2차로 소결처리를 행하였다. 제조된 복합재료의 상분석결과 $\alpha$-Fe 와 $\alpha$-$Al_2O_3/Fe$가 주된 상이었고 소량의 $FeAl_2O_4$가 검출되었다. 이 소량의 $FeAl_2O_4$상은 Fe가 $Al_2O_4$기공을 채우는 것을 방해함으로써 소결동안 미세구조 내에 약간의 기공을 발생시킨다.

• 한국세라믹학회지
• /
• 제34권6호
• /
• pp.553-560
• /
• 1997

A fine $\alpha$-Al2O3 powder was prepared by sol-gel process for membrane application. And it was carried out by adding 1.5wt% $\alpha$-Al2O3 powders(mean size : 87 nm) as seeds to the prepared sols and by controlling the heating schedule (the heating rate and the soaking time) to prevent the microstructural change, which occured during $\theta$-to $\alpha$Al2O3 phase transformation. The seeded $\alpha$-Al2O3 particles acted as the heterogeneous nucleation sites for the $\alpha$-Al2O3 nucleation during the transformation of $\theta$- to $\alpha$-Al2O3 and resulted in increasing the driving force of phase transformation to activate the formation of $\alpha$-Al2O3 phase at 82$0^{\circ}C$. By $\alpha$-Al2O3 seeding and controlling of heating condition the phase transformation of $\theta$- to $\alpha$-Al2O3 was accomplished at low temperature and the grain growth process was depressed. Therefore, the unsupported membrane could be fabricated in $\alpha$-Al2O3 . The average diameter of pores in the fabricated membrane was 7 nm and the porosity was 47%.

• 한국세라믹학회지
• /
• 제38권10호
• /
• pp.936-941
• /
• 2001

5.31 mol% ${Y_2}{O_3}$-4.45 mo1% ${Nb_2}{O_5}$-90.31 mo1% $ZrO_2$에 ${Al_2}{O_3}$를 첨가한 복합체를 제조하여 알루미나 입도가 복합체의 균열 전파 저항성에 미치는 영향을 조사하였다. $ZrO_2/{Al_2}{O_3}$ 복합체에서는 R-cuve 거동이 관찰되었으며 0.2, $2.8{\mu}m$ ${Al_2}{O_3}$가 20 vol%가 첨가된 복합체의 인성값은 각각 7.9, $8.8MPam^{1/2}$이었다. 파괴인성값의 차이는 ${Al_2}{O_3}$ 입도 크기에 의존하는 $ZrO_2/{Al_2}{O_3}$ 복합체 내의 정방정 $ZrO_2$의 결정립 크기 차이에 의한 것으로 추정된다.

• 한국세라믹학회지
• /
• 제25권2호
• /
• pp.117-124
• /
• 1988

The properties of the powders of the system Al2O3-ZrO2-Y2O3 prepared by precipitation method were investigated. Al2(SO4)3$.$18H2O3, ZrOCl2$.$8H2O and YCl3$.$6H2O were used as starting materials. Amorphous aluminum hydrate prepared by precipitation method was completely transformed to alpha Al2O3 as a result of calcining at 1100$^{\circ}C$ for 1 hr and gamma, delta and theta phases appeared as transition phases. In ZrO2-Y2O3 system prepared by co-precipitation method, the crystallization temperature of ZrO2 was increase with Y2O3 contents. The coupled crystallization occured in coprecipitated Al2O3-ZrO2-Y2O3 system, therefore the formation temperature of alpha Al2O3 and ZrO2-Y2O3 system. In this ternary system, the powder morphology showed a particular shape which was composed of large Al2O3 grains having small spherical ZrO2 particles within large Al2O3 grain and relatively large ZrO2 particles along the grian boundaries.

• 대한화학회지
• /
• 제46권4호
• /
• pp.336-345
• /
• 2002

본 연구에서는 조합화학을 이용하여 $CaO-Gd_2O_3-Al_2O_3$계에서 $Eu^{3+}$와 $Tb^{3+}$활성 적색 및 녹색 PDP용 형광체를 탐색하였으며 탐색된 형광체의 합성온도, 최적조성,발광 특성 등을 조사하였다. $CaO-Gd_2O_3-Al_2O_3$의 삼성분계의 형광특성 라이브러리를 작성하기 위하여 210개의 다른 조성을 가진 시료를 고분자 착체 중합법으로 합성하였다. 합성된 형광체 분말을 VUV PL로 측정하여 형광 특성 라이브러리를 작성하였고 발광특성이 잘 나타난 시료를 XPD를 이용하여 결정 구조를 확인하였다. 적색 형광체로서 탐색된 $Ca_{\alpha}$G$d_{0.95-\alpha-\beta}$$Al_\beta$$O_\delta$ : Eu(0.02< $\alpha+\beta$ <0.04)형광체는 색순도 면에서 상용형광체보다 개선된 특성을 보였으며 녹색 형광체로서 탐색된 $CaGdAl_3O_7$ : Tb, Ca$Al_{12}$$O_{19}$ : Tb, $Gd_4Al_2$$O_9$ : Tb, $Gd_3Al_5$$O_{12}$ : Tb 형광체 중에서 $CaGdAl_3O_7$ : Tb, Ca$Al_{12}$$O_{19}$ : Tb형광체는 상용 형광체에 비해 잔광시간이 짧은 특성을 보였다

• 대한전자공학회논문지
• /
• 제27권6호
• /
• pp.886-894
• /
• 1990

Sinterbility, microstructure, mechenical and electrical properties of yttriastabilized zirkconiz (92 mole % ZrO2 + 8 mole % Y2O3) doped with 0.5 mole % SiO2 and 0-2.O mole% Al2O3 were studied as a functin of Al2O3 addition. Sintered density increased with increasing Al2O3 addition up to o.5 mole%but decreased up to 1.0mole% Al2O3. Vickers hardness is proportional to sintered density. The specimen added 0.5mole% Al2O3 and 0.5mole% SiO2 exhibited a maximum conductivity. And the specimen added 0.5 mole % Al2O3 and 0.5 mole% SiO2 was measured a maximum electromotive force for a characteristics of oxyzen partial pressure.

• 한국세라믹학회지
• /
• 제33권7호
• /
• pp.832-838
• /
• 1996

Thermite reaction products of MgO and Al were added to MgO-C refractory to improve the properties of corrosion against the attack of slag, oxidation and mechanical spalling. Corrosion rate of MgO-C-MgAl2O4 spinel refractory at the ratio of 3.3(CaO/SiO2) slag was smaller than that of MgO-C and MgO-C-Al refractory. The excellent corrosion resistance of the MgO-C-MgAl2O4 spinel refractory against the slag attack was appeared by Al and MgAl2O4 spinel with high melting point and corrosion resistance and the high thermal conductivity and low thermal expansion of AIN. Hot M.O.R at 140$0^{\circ}C$ and the resistance of oxidation weight loss at 90$0^{\circ}C$ were 210kg/cm2 and -12% respectively.