• E2M - 전기 전자와 첨단 소재
• /
• 제8권3호
• /
• pp.272-277
• /
• 1995

We report the properties of optically pumped stimulated emission at room temperature (RT) from column-III nitride semiconductors of GaN, AlGaN/GaN double heterostructure (DH) and AlGaN/GaInN DH which prepared on a sapphire substrate using an AIN buffer-layer by the nietalorganic vapor phase epitaxy (MOVPE) method. The peak wavelength of the stimulated emission at RT from AIGaN/GaN DH is 369nm and the threshold of excitation pumping power density (P$\_$th/) is about 84kW/cm$\^$2/, and they from AlGaN/GaInN DH are 402nm and 130kW/cm$\^$2/ at the pumping power density of 200kW/cm$\^$2/, respectively. The P$\_$th/ of AIGaN/GaN and AlGaN/GaInN DHs are lower than the single layers of GaN and GaInN due to optical confinement within the active layers of GaN and GaInN, respectively.

• 한국전기전자재료학회:학술대회논문집
• /
• 한국전기전자재료학회 1994년도 추계학술대회 논문집
• /
• pp.50-53
• /
• 1994

In this study. we report the properties of optically pumped stimulated emission at room temperature (RT) from column-III nitride semiconductors of GaN, GaInN, AlGaN/GaN double hetero-structure (DH) and AlGaN/GaInN DH which grown by low pressure metal-organic vapor phase epitaxy on sapphire substrate using an AIN buffer-layer. The peak wavelength of the stimulated emission at RT from AlGaN/GaN DH is 370nm and the threshold of excitation pumping power density (P$\_$th/) is about 89㎾/$\textrm{cm}^2$, and they from AlGaN/GaInN DH are 403nm and 130㎾/$\textrm{cm}^2$, respectively. The P$\_$th/ of AlGaN/GaN and AlGaN/GaInN DHs are lower than the bulk materials due to optical confinement within the active layers of GaN and GaInN. The optical gain and the polarization of stimulated emission characteristics are presented in this article.

• 한국결정성장학회지
• /
• 제19권1호
• /
• pp.6-10
• /
• 2009

본 논문에서는 혼합소스(mixed-source) HVPE(hydride vapor phase epitaxy)방법으로 선택성장(SAC: selective area growth) GaN/AlGaN 이종접합구조의 발광다이오드를 r-plane 사파이어 기판 위에 제작하였다. SAG-GaN/AlGaN DH(double heterostructure)는 고온 GaN 버퍼층, Te 도핑된 AlGaN n-클래딩층. Gan 활성층. Mg 도핑된 AlGaN p-클래딩층. Mg 도핑된 GaN p-캡층으로 구성되어있다. GaN/AlGaN 이종접합구조의 발광다이오드의 특성을 알아보기 위해 SEM을 통한 구조적 분석과 전류-전압 측정(I-V: current-voltage measurement), 전류-광출력(EL: electroluminescence) 측정을 통하여 전기적, 광학적 특성을 평가하였다.

• 한국재료학회지
• /
• 제5권4호
• /
• pp.445-450
• /
• 1995

AIN 완충층을 이용하여 대기압 유기금속에피텍셜 (MOVPE)법으로 사파이어 기판위에 성장시킨 AlGaN/GaN 이중 이종접합구조(double heterostructure : DH)의 고밀도 광여기에 의한 자외선 영역에서의 단면모드 유도방출 특성에 대하여 조사하였다. 실온에서 여기광 밀도 200kW/$cm^{2}$에서 방출된 AlGaN/GaN DH의 유도방출 피크파장과 반치폭은 각각 369nm와 22.4meV이었으며, 80K의 온도에서는 각각 360.1nm와 13.4meV이었다. 고밀도 광여기에 의하여 단면모드 자외영역 유도방출을 얻기에 필요한 입사광 밀도의 임계치는 실온과 80K의 온도에서 각각 89kW/$cm^{2}$와 44kW/$cm^{2}$이었다.

• Journal of Ceramic Processing Research
• /
• 제13권spc1호
• /
• pp.128-131
• /
• 2012

The selective area growth light emitting diode on GaN substrate was grown using mixed-source HVPE method with multi-sliding boat system. The GaN substrate was grown using mixed-source HVPE system. Te-doped AlGaN/AlGaN/Mg-doped AlGaN/Mg-doped GaN multi-layers were grown on the GaN substrate. The appearance of epi-layers and the thickness of the DH was evaluated by SEM measurement. The DH metallization was performed by e-beam evaporator. n-type metal and p-type metal were evaporated Ti/Al and Ni/Au, respectively. At the I-V measurement, the turn-on voltage is 3 V and the differential resistance is 13 Ω. It was found that the SAG-LED grown on GaN substrate using mixed-source HVPE method with multi-sliding boat system could be applied for developing high quality LEDs.

• 한국재료학회지
• /
• 제5권4호
• /
• pp.420-425
• /
• 1995

AlGaN/GaInN 이중이종접합구조(double heterostructure :DH)를 대기압 유기금속기상에 피텍셜(MOVPE)법으로 AIN 와충층을 이용하여 사파이어 기판위에 성장하고, 실온에서의 광여기법에 의한 청색영역의 단면모드 유도방출특성과 편광특성을 조사하였다. 여기광원의 광밀도가 증가함에 따라 청색 영역에서의 유도방출 피크는 낮은 에너지 쪽으로 이동하였고, 유도방출 피크파장은 여기광밀도가 200kW/$cm^{2}$일때 402nm 이었으며, 스펙트럼의 반치폭은 18meV 이었다. 또한 유도방출에 필요한 여기광밀도의 임계치는 130 kW/$cm^{2}$ 이었다. AlGaN/GaInN로부터 방출되는 유도방출 광은 임계치 이상에서 TE-mode로 편광 되었다.

• 한국결정성장학회지
• /
• 제22권1호
• /
• pp.11-14
• /
• 2012

AlGaN는 3.4~6.2 eV까지 넓은 밴드갭을 가지는 직접천이형 반도체이다. 최근에 자외영역의 광소자가 다양하게 응용되면서 자외선 발광이 가능한 AlGaN 역시 주목받고 있다. 이를 위해서는 고품질의 AlGaN 층이 필요하지만 GaN 층위에 AlGaN 층을 성장하는 것은 이들의 격자상수와 열팽창계수 차이로 인해 어렵다. 본 논문에서, multi-sliding boat법이 적용된 혼합소스 HVPE법을 이용하여 GaN template 위에 LED 구조를 성장하였다. 활성층의 Al 조성을 조절함으로써 AlGaN의 격자상수 변화와 광학적 변화를 관찰하고자 하였다. 에피 성장을 위해 HCl과 $NH_3$ 가스를 혼합소스 표면으로 흘려주었고, 수송가스로는 $N_2$를 사용하였다. 소스영역과 성장영역의 온도는 각각 900과 $1090^{\circ}C$로 안정화하였다. 성장 후 샘플은 x-ray diffraction(XRD)과 electro luminescence(EL) 측정을 하였다.

• 한국진공학회:학술대회논문집
• /
• 한국진공학회 1998년도 제14회 학술발표회 논문개요집
• /
• pp.93-93
• /
• 1998

III-V족 질화물반도체를 이용한 광 및 전자소자 용용에 있어서 가장 중요한 고홈위 u undoped GaN 에피충 성장과 GaN 에피충의 doping 특허 p-type doping의 복성융 고찰한다. 그리고 III-V nitride 이용한 band gap en명neertng에 있어서 가장 중요한 InGaN 생장파 81 및 :at codoplng 륙성융 평가 분석 한다. 위의 기반기술융 기본으로 하여 InGaN/AlG때 DH s$\sigma$ucture lED훌 제작하고 이의 륙성 용 명가분석하였다.

• 한국결정성장학회지
• /
• 제19권2호
• /
• pp.61-65
• /
• 2009

본 논문에서는 형광체가 없는 백색 LED의 성장과 광학적인 특성을 분석하였다. 혼합소스(miked-source) HVPE(hydride vapor phase epitaxy) 방법과 다중성장보트를 이용하여 MOCVD로 얇게 성장한 n-GaN 위에 활성층을 AlGaN으로 한 이종접합구조(DH; Doublehetero structure)를 성장하고, 패키징 단계를 거쳐 비형광체 단일칩 백색 LED 램프를 제작하였다. 패키징 한 소자를 주입전류 $10{\sim}100mA$로 변화시켜 측정한 결과 색 연색성 값은 72-93, 색좌표의 좌표값은 X값은 $0.26{\sim}0.34$, Y값은 $0.31{\sim}0.40$에서 가지며, 색온도는 $5126{\sim}10406K$ 범위에서 측정되었다. 또한 주입전류 증가 시, 형광체를 사용한 백색 LED는 청색 영역으로 이동하지만, 제작된 백색 LED는 황색영역으로 색좌표가 이동하였다. 이러한 특성을 통하여 고감도의 색 연색성 값을 가지는 비형광체 백색LED의 성장 가능성을 확인하였으며, 광 특성 분석 결과를 통하여 혼합소스의 성장 메커니즘을 제안하고자 한다.